A Li-B alloy has been prepared using a pretreated amorphous B powder and pure Li ingot as starting materials by continually slow addition of B powder and intensified stirring in the process of melting. The microstruct...A Li-B alloy has been prepared using a pretreated amorphous B powder and pure Li ingot as starting materials by continually slow addition of B powder and intensified stirring in the process of melting. The microstructure and the discharge characteristic of the materials have been investigated- Results show that the problem of temperature control in synthesis would be modified by means of continual addition of B powder, the Li7B6 would be more finely distributed in the metal Li by means of intensified stirring. The discharge characteristic of the Li-B alloy using amorphous B as starting materials is almost the same with that of using crystalline B.展开更多
ZnO single crystals were grown by vapor phase reaction of Zno powder with active carbon powdei at an elevated temperature The typical crystals were colorless and transparent with maximum size o4 0.1 mm in diameter and...ZnO single crystals were grown by vapor phase reaction of Zno powder with active carbon powdei at an elevated temperature The typical crystals were colorless and transparent with maximum size o4 0.1 mm in diameter and 25 mm in length, The gas-sensing characteristics of Na+-doped anc undoped single crystals were investigated in 1 %H2. Co and CH, in air between 1 50 and 600℃. It was found that the undoped ZnO single crystals showed little gas sensitivity in air. and Na+-doping can greatly enhance the senstivity by increasing the resistivities. The maximum sensitivity of the samples is 22 (Ra/ Rg) for H2. 1 2 for CO and 4 for CH4展开更多
基金State Ministry of Education Under contract No. 96053311.
文摘A Li-B alloy has been prepared using a pretreated amorphous B powder and pure Li ingot as starting materials by continually slow addition of B powder and intensified stirring in the process of melting. The microstructure and the discharge characteristic of the materials have been investigated- Results show that the problem of temperature control in synthesis would be modified by means of continual addition of B powder, the Li7B6 would be more finely distributed in the metal Li by means of intensified stirring. The discharge characteristic of the Li-B alloy using amorphous B as starting materials is almost the same with that of using crystalline B.
文摘ZnO single crystals were grown by vapor phase reaction of Zno powder with active carbon powdei at an elevated temperature The typical crystals were colorless and transparent with maximum size o4 0.1 mm in diameter and 25 mm in length, The gas-sensing characteristics of Na+-doped anc undoped single crystals were investigated in 1 %H2. Co and CH, in air between 1 50 and 600℃. It was found that the undoped ZnO single crystals showed little gas sensitivity in air. and Na+-doping can greatly enhance the senstivity by increasing the resistivities. The maximum sensitivity of the samples is 22 (Ra/ Rg) for H2. 1 2 for CO and 4 for CH4