A two-step equal channel angular extrusion(ECAE) procedure was used to process pure Mg. The effects of ECAE processing temperature on the microstructure, mechanical properties, and corrosion behavior of pure Mg were...A two-step equal channel angular extrusion(ECAE) procedure was used to process pure Mg. The effects of ECAE processing temperature on the microstructure, mechanical properties, and corrosion behavior of pure Mg were studied. The results show that the average grain size of pure Mg decreases with decreasing extrusion temperature. After ECAE processing at 473 K, fine and equiaxed grains(~9 μm) are obtained. The sample processed at 473 K exhibits the excellent mechanical properties, whereas the sample processed at 633 K has the lowest corrosion rate. The improved corrosion resistance and mechanical properties of pure Mg by ECAE are ascribed to grain refinement and microstructural modification.展开更多
In this study, the influence of hot isostatic pressing(HIP) process on the 418 alloy produced by metal injection molding(MIM) technique(named as MIM 418)was investigated based on the characteristic analysis of 4...In this study, the influence of hot isostatic pressing(HIP) process on the 418 alloy produced by metal injection molding(MIM) technique(named as MIM 418)was investigated based on the characteristic analysis of 418 alloy powder. And comparison analysis of the microstructure and mechanical property between the MIM 418 and as-cast 418 alloys was performed by scanning electron microscopy(SEM), energy-dispersive spectroscopy(EDS),and X-ray diffraction(XRD). The results show that MIM418 alloy exhibits fine grain(~30 μm) and uniform microstructure. The defects existing in MIM 418 alloy formed during sintering process can be eliminated through HIP treatment, and the relative density increases from97.0 % to 99.5 %. The mechanical property can be improved significantly because of the elimination of defects, and the tensile strength and elongation are1,271 MPa and 16.8 %, respectively, which are increased by 34.5 % and 180 % compared with K418 alloy after solution heat treatment.展开更多
Accumulative press bonding(APB) is a novel variant of severe plastic deformation processes,which is devised to produce materials with ultra-fine grain.In the present work,the mechanical properties and microstructura...Accumulative press bonding(APB) is a novel variant of severe plastic deformation processes,which is devised to produce materials with ultra-fine grain.In the present work,the mechanical properties and microstructural evolution of AA1100 alloy,which is produced by APB technique,were investigated.The study of the microstructure of AA1100 alloy was performed by optical microscopy.The results revealed that the grain size of the samples decreased to 950 nm after six passes of APB process.The yield strength of AA1100 alloy after six passes of the process increased up to 264 MPa,which is three times higher than that of the as-cast material(89 MPa).After six passes,microhardness values of AA1100 alloy increased from 38 to 61 HV.Furthermore,the results showed that the behavior of variations in mechanical properties is in accordance with the microstructural changes and it can be justified by using the Hall-Patch equation.Moreover,the rise in the yield strength can be attributed to the reduction in the grain size leading to the strain hardening.展开更多
基金financially supported by the National Natural Science Foundation of China (Nos. 81330031 and 81271701)
文摘A two-step equal channel angular extrusion(ECAE) procedure was used to process pure Mg. The effects of ECAE processing temperature on the microstructure, mechanical properties, and corrosion behavior of pure Mg were studied. The results show that the average grain size of pure Mg decreases with decreasing extrusion temperature. After ECAE processing at 473 K, fine and equiaxed grains(~9 μm) are obtained. The sample processed at 473 K exhibits the excellent mechanical properties, whereas the sample processed at 633 K has the lowest corrosion rate. The improved corrosion resistance and mechanical properties of pure Mg by ECAE are ascribed to grain refinement and microstructural modification.
基金financially supported by the National High Technology Research and Development Program of China (No. 2012AA03AA514)
文摘In this study, the influence of hot isostatic pressing(HIP) process on the 418 alloy produced by metal injection molding(MIM) technique(named as MIM 418)was investigated based on the characteristic analysis of 418 alloy powder. And comparison analysis of the microstructure and mechanical property between the MIM 418 and as-cast 418 alloys was performed by scanning electron microscopy(SEM), energy-dispersive spectroscopy(EDS),and X-ray diffraction(XRD). The results show that MIM418 alloy exhibits fine grain(~30 μm) and uniform microstructure. The defects existing in MIM 418 alloy formed during sintering process can be eliminated through HIP treatment, and the relative density increases from97.0 % to 99.5 %. The mechanical property can be improved significantly because of the elimination of defects, and the tensile strength and elongation are1,271 MPa and 16.8 %, respectively, which are increased by 34.5 % and 180 % compared with K418 alloy after solution heat treatment.
文摘Accumulative press bonding(APB) is a novel variant of severe plastic deformation processes,which is devised to produce materials with ultra-fine grain.In the present work,the mechanical properties and microstructural evolution of AA1100 alloy,which is produced by APB technique,were investigated.The study of the microstructure of AA1100 alloy was performed by optical microscopy.The results revealed that the grain size of the samples decreased to 950 nm after six passes of APB process.The yield strength of AA1100 alloy after six passes of the process increased up to 264 MPa,which is three times higher than that of the as-cast material(89 MPa).After six passes,microhardness values of AA1100 alloy increased from 38 to 61 HV.Furthermore,the results showed that the behavior of variations in mechanical properties is in accordance with the microstructural changes and it can be justified by using the Hall-Patch equation.Moreover,the rise in the yield strength can be attributed to the reduction in the grain size leading to the strain hardening.