The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron mi...The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron microscopy(SEM)and laboratory computed tomography(CT).Results showed that the newly developed AlSi9MnMoV alloy exhibited improved mechanical properties when compared to the AlSi10MnMg alloy.The AlSi9MnMoV alloy,which was designed with trace multicomponent additions,displays a notable grain refining effect in comparison to the AlSi10MnMg alloy.Refining elements Ti,Zr,V,Nb,B promote heterogeneous nucleation and reduce the grain size of primaryα-Al.At a lower slow shot speed,the large ESCs are easier to form and gather,developing into the dendrite net and net-shrinkage.With an increase in slow shot speed,the size and number of ESCs and porosities significantly reduce.In addition,the distribution of ESCs is more dispersed and the net-shrinkage disappears.The tensile property is greatly improved by adopting a higher slow shot speed.The ultimate tensile strength is enhanced from 260.31 MPa to 290.31 MPa(increased by 11.52%),and the elongation is enhanced from 3.72%to 6.34%(increased by 70.52%).展开更多
Aluminum high pressure die casting(HPDC)technology has evolved in the past decades,enabling stronger and larger one-piece casting with significant part consolidation.It also offers a higher design freedom for more mas...Aluminum high pressure die casting(HPDC)technology has evolved in the past decades,enabling stronger and larger one-piece casting with significant part consolidation.It also offers a higher design freedom for more mass-efficient thin-walled body structures.For body structures that require excellent ductility and fracture toughness to be joined with steel sheet via self-piercing riveting(for instance,shock towers and hinge pillars,etc.),a costly T7 heat treatment comprising a solution heat treatment at elevated temperatures(450℃-500℃)followed by an over-ageing heat treatment is needed to optimize microstructure for meeting product requirement.To enable cost-efficient mass production of HPDC body structures,it is important to eliminate the expensive T7 heat treatment without sacrificing mechanical properties.Optimizing die cast alloy chemistry is a potential solution to improve fracture toughness and ductility of the HPDC components.The present study intends to tailor the Mg and Cu additions for a new Al-Si-Cr type die casting alloy(registered as A379 with The Aluminum Association,USA)to achieve the desired tensile properties without using T7 heat treatment.It was found that Cu addition should be avoided,as it is not effective in enhancing strength while degrades tensile ductility.Mg addition is very effective in improving strength and has minor impact on tensile ductility.The investigated Al-Si-Cr alloy with a nominal composition of Al-8.5wt.%Si-0.3wt.%Cr-0.2wt.%Fe shows comparable tensile properties with the T7 treated AlSi10MnMg alloy which is currently used for manufacturing shock towers and hinge pillars.展开更多
Considering the components produced by high pressure die casting(HPDC)process usually with ultra-large sizes and complex morphologies,high temperature solid solution treatment is not a suitable method to further impro...Considering the components produced by high pressure die casting(HPDC)process usually with ultra-large sizes and complex morphologies,high temperature solid solution treatment is not a suitable method to further improve their mechanical properties.In this study,two-stage aging treatment with different pre-aging times was designed and employed to further improve the mechanical properties of HPDC Al8SiMgCuZn alloy.The characteristics of precipitates were evaluated by a transmission electron microscope(TEM),and the precipitation strengthening mechanism was discussed.The results reveal that the strengthening is mainly contributed by the precipitation ofβ″phase after two-stage aging,and the number density and size of the precipitates are significantly depended on the pre-aging time.The number density of precipitates is increased with the pre-aging time prolonged from 0 h to 4 h,and then decreases with the further increase of pre-aging time from 4 h to 6 h.The precipitates with the highest density and smallest size are observed after pre-aging for 4 h.After pre-aged at 100℃for 4 h and then artificial aged at 200℃for 30 min,the yield strength of 207 MPa,ultimate tensile strength of 325 MPa and elongation of 7.6%are achieved.展开更多
In this paper,the research progress of the interfacial heat transfer in high pressure die casting(HPDC)is reviewed.Results including determination of the interfacial heat transfer coefficient(IHTC),influence of castin...In this paper,the research progress of the interfacial heat transfer in high pressure die casting(HPDC)is reviewed.Results including determination of the interfacial heat transfer coefficient(IHTC),influence of casting thickness,process parameters and casting alloys on the IHTC are summarized and discussed.A thermal boundary condition model was developed based on the two correlations:(a)IHTC and casting solid fraction and(b)IHTC peak value and initial die surface temperature.The boundary model was then applied during the determination of the temperature field in HPDC and excellent agreement was found.展开更多
The development of lightweight magnesium(Mg)alloys capable of operating at elevated temperatures of 200-300℃and the ability of using high pressure die casting for high-volume manufacturing are the most advanced devel...The development of lightweight magnesium(Mg)alloys capable of operating at elevated temperatures of 200-300℃and the ability of using high pressure die casting for high-volume manufacturing are the most advanced developments in manufacturing critical parts for internal combustion engines used in power tools.Here we report the microstructure and mechanical properties of a newly developed die-cast Mg-RE(La,Ce,Nd,Gd)-Al alloy capable of working at higher elevated temperatures of 200-300℃.The new alloy delivers the yield strength of 94 MPa at 300℃,which demonstrates a 42%increase over the benchmark AE44 high temperature die-cast Mg alloy.The new alloy also has good stiffness at elevated temperatures with its modulus only decreasing linearly by 13%from room temperature up to 300℃.Thermal analysis shows a minor peak at 364.7℃in the specific heat curve of the new alloy,indicating a good phase stability of the alloy up to 300℃.Nd and Gd have more affinity to Al for the formation of the minority of divorced Al-RE(Nd,Gd)based compounds,and the stable Al-poor Mg_(12)RE(La_(0.22)Ce_(0.13)Nd_(0.31)Gd_(0.31))Zn_(0.39)Al_(0.13)compound acts as the continuous inter-dendritic network,which contribute to the high mechanical performance and stability of the new die-cast Mg alloy at 200-300℃.展开更多
The morphology and content of the divorced eutectic in the microstructure of high pressure die casting(HPDC) magnesium alloy have a great influence on the final performance of castings. Based on the previous work conc...The morphology and content of the divorced eutectic in the microstructure of high pressure die casting(HPDC) magnesium alloy have a great influence on the final performance of castings. Based on the previous work concerning simulation of the nucleation and dendritic growth of primary α-Mg during the solidification of magnesium alloy under HPDC process, an extension was made to the formerly established CA(Cellular Automaton) model with the purpose of modeling the nucleation and growth of Mg-Al eutectic. With a temperature field and solute field obtained during simulation of the primary α-Mg dendrites as the initial condition of the modified CA model, modeling of the Mg-Al eutectic with a divorced morphology was achieved. Moreover, the simulated results were in accordance with the experimental ones regarding the distribution and content of the divorced eutectic. Taking a "cover-plate" die casting with AM60 magnesium alloy as an example, the rapid solidification with a high cooling rate at the surface layer of the casting led to a fine and uniform grain size of primary α-Mg, while the divorced eutectic at the grain boundary revealed a more dispersed and granular morphology. Islands of divorced eutectic were observed at the central region of the casting, due to the existence of ESCs(Externally Solidified Crystals) which contributed to a coarse and non-uniform grain size of primary α-Mg. The volume percentage of the eutectic β-Mg_(17)Al_(12) phase is about 2%-6% in the die casting as a whole. The numerical model established in this study is of great significance to the study of the divorced eutectic in the microstructure of die cast magnesium alloy.展开更多
Both a conventional flow distributer and an improved one with a flow buffer were applied respectively during the high pressure die casting(HPDC)process,and samples of AZ91D magnesium alloy with different microstructur...Both a conventional flow distributer and an improved one with a flow buffer were applied respectively during the high pressure die casting(HPDC)process,and samples of AZ91D magnesium alloy with different microstructure mainly consisting ofα-Mg grains,β-phase and porosities were obtained.According to the grain orientation analysis,the predominant deformation behavior inα-Mg grains was dislocation slip,supplemented by deformation twinning.Dislocation slip was more difficult to occur in the samples with the improved flow distributer on account of the fact that the size ofα-Mg grains in the microstructure was finer and more uniform.During the in situ tensile deformation test,cracks were observed to initiate from gas-shrinkage pore and island-shrinkage,and two main crack propagation mechanisms,porosity growth and coalescence were found accordingly.When the crack was in contact with theβ-phase,it would pass through and fracture the networkβ-phase,whereas bypass the islandβ-phase by detaching it from the surroundingα-Mg grains.Mechanical property tests showed that the samples with relatively more homogeneous microstructure would perform higher mechanical properties,which was the combined effect of matrixα-Mg grains,β-phase,and porosities.展开更多
Microstructural and hardness evolutions of a vacuum-assistant die-cast A380(Al-8.67 wt.%Si-3.27 wt.%Cu) alloy during heat treatment were investigated. Isothermal DSC test at 200 °C revealed that the precipitation...Microstructural and hardness evolutions of a vacuum-assistant die-cast A380(Al-8.67 wt.%Si-3.27 wt.%Cu) alloy during heat treatment were investigated. Isothermal DSC test at 200 °C revealed that the precipitation reaction in the surface layer was faster than that in the central region. This corresponded with the hardness evolution that the surface layer hardened faster. The hardness increment in the surface layer was higher than that in the central region. Further experimental evidences indicated that the differences were due to the different amounts of heterogeneous nucleation sites for precipitation in the two parts. The influence of the characteristic as-cast microstructure on the artificial aging process is analyzed and discussed in detail.展开更多
The characteristics of defect bands in the microstructure of high pressure die casting(HPDC)AE44 magnesium alloy were investigated.Special attention was paid to the effects of process parameters during the HPDC proces...The characteristics of defect bands in the microstructure of high pressure die casting(HPDC)AE44 magnesium alloy were investigated.Special attention was paid to the effects of process parameters during the HPDC process and casting structure on the distribution of defect bands.Results show that the defect bands are solute segregation bands with the enrichment of Al,Ce and La elements,which are basically in the form of Al_(11)RE_(3) phase.There is no obvious aggregation of porosities in the defect bands.The width of the inner defect band is 4-8 times larger than that of the outer one.The variation trends of the distribution of the inner and outer defect bands are not consistent under different process parameters and at different locations of castings.This is due to the discrepancy between the formation mechanisms of double defect bands.The filling and solidification behavior of the melt near the chilling layer is very complicated,which finally leads to a fluctuation of the width and location of the outer defect band.By affecting the content and aggregation degree of externally solidified crystals(ESCs)in the cross section of die castings,the process parameters and casting structure have a great influence on the distribution of the inner defect band.展开更多
A method based on die casting experiments and mathematic modeling is presented for the determination of the heat flow density (HFD) and interfacial heat transfer coefficient (IHTC) during the high pressure die cas...A method based on die casting experiments and mathematic modeling is presented for the determination of the heat flow density (HFD) and interfacial heat transfer coefficient (IHTC) during the high pressure die casting (HPDC) process.Experiments were carried out using step shape casting and a commercial magnesium alloy,AM50.Temperature profiles were measured and recorded using thermocouples embedded inside the die. Based on these temperature readings,the HFD and IHTC were successfully determined and the calculation results show that the HFD and IHTC at the metal-die interface increases sharply right after the fast phase injection process until approaching their maximum values,after which their values decrease to a much lower level until the dies are opened.Different patterns of heat transfer behavior were found between the die and the casting at different thicknesses.The thinner the casting was,the more quickly the HFD and IHTC reached their steady states.Also,the values for both the HFD and IHTC values were different between die and casting at different thicknesses.展开更多
The mold filling and solidification simulation for the high pressure die casting (HPDC) and low pressure die casting (LPDC) processes were studied. A mathematical model considering the turbulent flow and heat transfer...The mold filling and solidification simulation for the high pressure die casting (HPDC) and low pressure die casting (LPDC) processes were studied. A mathematical model considering the turbulent flow and heat transfer phenomenon during the HPDC process has been established and parallel computation technique was used for the mold filling simulation of the process. The laminar flow characteristics of the LPDC process were studied and a simplified model for the mold filling process of wheel castings has been developed. For the solidification simulation under pressure conditions, the cyclic characteristics and the complicated boundary conditions were considered and techniques to improve the computational efficiency are discussed. A new criterion for predicting shrinkage porosity of Al alloy under low pressure condition has been developed in the solidification simulation process.展开更多
Few studies were reported on the phases'relationships of AE44(Mg-4.0Al-4.1RE-0.3Mn,wt.%)and its composites.In this work,AE44 alloy and Saffil(6-Al2O3)/AE44 Metal matrix composite(MMC)were both prepared by slow sho...Few studies were reported on the phases'relationships of AE44(Mg-4.0Al-4.1RE-0.3Mn,wt.%)and its composites.In this work,AE44 alloy and Saffil(6-Al2O3)/AE44 Metal matrix composite(MMC)were both prepared by slow shot high pressure die casting(SS-HPDC)technology and their phase constitutions were all studied in detail using experimental techniques combined with CALPHAD(Calculation of Phase Diagram)modeling.The results revealed that the alloy consists of the a-Mg matrix,A1hRE3 intermetallic phase,and one trace phase AI3RE,while the composite contains five major phases:a-Mg,5-AI2O3,AI3RE,MgO and Mg2Si.and two trace phases of A12RE and AI11RE3,respectively.A1hRE3 is partly derived from ALRE,while A13RE is a product of the peritectoid reaction between the two precipitates.The presence of MgO and Mg2Si is due to the interfacial reaction between the SiO2 binder in the fiber preforms and the molten magnesium during infiltration.The use of SiO2 binder in the preform manufacturing was limited/minimized to reduce the MgO formation in the MMC casting process,which can be detrimental to the fatigue performance of the MMC materials.展开更多
X-ray tomography was used to characterize the porosity in high pressure die casting of AM60B alloy. In situ tensile deformation was performed to observe the change of porosities and their influences on crack initiatio...X-ray tomography was used to characterize the porosity in high pressure die casting of AM60B alloy. In situ tensile deformation was performed to observe the change of porosities and their influences on crack initiation, propagation and subsequent fracture of specimen. Results showed that four types of porosi- ties, including gas-shrinkage pore, gas pore, net-shrinkage and island-shrinkage, could be identified according to the formation mechanism and morphology characterization. During tensile deformation, it was shown that the gas-shrinkage pore and net-shrinkage, rather than gas pore or island-shrinkage, were the main sources for crack initiation. In addition, the crack propagated by interconnecting the po- rosities at the cross section with minimum efficient force bearing area. At these locations where externally solidified crystals (ESCs) were present, the crack would propagate along the ESC boundaries in an inter- granular mode, while at these locations without ESCs, the crack would propagate roughly along the direction perpendicular to the tensile stress in a combination of trans-granular and inter-granular modes.展开更多
The interfacial heat transfer behavior at the metalJshot sleeve interface in the high pressure die casting (HPDC) process of AZ91D alloy is carefully investigated. Based on the temperature measurements along the sho...The interfacial heat transfer behavior at the metalJshot sleeve interface in the high pressure die casting (HPDC) process of AZ91D alloy is carefully investigated. Based on the temperature measurements along the shot sleeve, inverse method has been developed to determine the interfacial heat transfer coefficient in the shot sleeve. Under static condition, Interracial heat transfer coefficient (IHTC) peak values are 11.9, 7,3, 8.33kWm-2K-1 at pouring zone (S2), middle zone (S5), and end zone (510), respectively. During the casting process, the IHTC curve displays a second peak of 6.1 kWm-2 K-1 at middle zone during the casting process at a slow speed of 0.3 ms 1 Subsequently, when the high speed started, the IHTC curve reached a second peal〈 of 12.9 kW m-2K-1 at end zone. Furthermore, under different slow casting speeds, both the calculated initial temperature (TIDs) and the maximum temperature (Tsimax) of shot sleeve surface first decrease from 0.1 ms-1 to 0.3 ms-1, but increase again from 0.3 ms-1 to 0.6 ms-1. This result agrees with the experimental results obtained in a series of "plate-shape" casting experiments under different slow speeds, which reveals that the amount of ESCs decreases to the minimum values at 0.3 m s-1 and increase again with the increasing casting slow speed.展开更多
Effects of natural aging and test temperature on the tensile behaviors have been studied for a highperformance cast aluminum alloy Al–10Si–1.2Cu–0.7Mn. Based on self-strengthening mechanism and spheroidization micr...Effects of natural aging and test temperature on the tensile behaviors have been studied for a highperformance cast aluminum alloy Al–10Si–1.2Cu–0.7Mn. Based on self-strengthening mechanism and spheroidization microstructures, the alloy tested at room temperature(RT) exhibits higher 0.2% proof stress(YS) of 206 MPa, ultimate tensile strength(UTS) of 331 MPa and elongation of 10%. Increasing aging time improves the YS and UTS and reduces the ductility of the alloy. Further increasing aging time beyond72 h does not signi?cantly increase the tensile strengths. Increasing test temperature significantly decreases the tensile strengths and increases the ductility of the alloy. The UTS of the alloy can be estimated by using the hardness. The Portevin–Le Chatelier effect occurs at RT due to the interactions between solid solution atoms and dislocations. Similar behaviors occurring at 250℃ are attributed to dynamic strain aging mechanism. Increasing aging time leads to decrease in the strain-hardening exponent(n) value and increase in the strain-hardening coeficient(k) value. Increasing test temperature apparently decreases the n and k values. Eutectic phase particles cracking and debonding determine the fracture mechanism of the alloy. Final failure of the alloy mainly depends on the global instability(high temperature, necking) and local instability(RT, shearing). Different tensile behaviors of the alloy are mainly attributed to different matrix strengths, phase particle strengths and damage rate.展开更多
Under the cold-chamber high pressure die casting (HPDC) process, samples were produced with AM60B magnesium alloy to investigate the microstructure characteristics of the eutectics, especially focusing on the consti...Under the cold-chamber high pressure die casting (HPDC) process, samples were produced with AM60B magnesium alloy to investigate the microstructure characteristics of the eutectics, especially focusing on the constitution, morphology and distribution of the eutectics over cross section of the castings. Attentions were also paid to study the effect of heat treatment on the eutectics in the die castings. Based on experimental analysis using optical microscopy (OM), X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS), it was determined that fully divorced eutectics consisting of c^-Mg and l%MglzA112 appeared at the grain boundary of the primary c^-Mg in the as-cast microstructure. Islands and networks of β-Mg17Al12 phase were observed in the central region of the castings, while the β-Mg17Al12 phase revealed a more dispersed and granular morphology on the surface layer. The two phases ratio β/α in the central region of the castings was approximately 10%, which was higher than that on the surface layer. Besides, the defect bands contained a higher percentage of the eutectics than the adjacent regions. After aging treatment (T6), only α-Mg phase was detected by XRD in the AM60B magnesium alloy, though a small amount of precipitated β-MgITAI12 phase was observed at the grain boundary. In contrast to the microstructure of die cast AZ91D magnesium alloy under the same T0 heat treatment, no discontinuous precipitation of the β-MgITAI12 phase was observed in AMO0B magnesium alloy die castings.展开更多
The objective of this study is to predict grain size and heat transfer coefficient at the metal-die interface during high pressure die casting process and solidification of the magnesium alloy AM60. Multiple runs of t...The objective of this study is to predict grain size and heat transfer coefficient at the metal-die interface during high pressure die casting process and solidification of the magnesium alloy AM60. Multiple runs of the commercial casting simulation package, ProCASTTM, were used to model the mold filling and solidification events employing a range of interfacial heat transfer coefficient values. The simulation results were used to estimate the centerline cooling curve at various locations through the casting. The centerline cooling curves, together with the die temperature and the thermodynamic properties of the alloy, were then used as inputs to compute the solution to the Stefan problem of a moving phase boundary, thereby providing the through-thickness cooling curves at each chosen location of the casting, Finally, the local cooling rate was used to calculate the resulting grain size via previously established relationships. The effects of die temperature, filling time and heat transfer coefficient on the grain structure in skin region and core region were quantitatively characterized. It was observed that the grain size of skin region strongly depends on above three factors whereas the grain size of core region shows dependence on the interracial heat transfer coefficient and thickness of the samples. The grain size distribution from surface to center was estimated from the relationship between grain size and the predicted cooling rate. The prediction of grain size matches well with experimental results. A comparison of the predicted and experimentally determined grain size profiles enables the determination of the apparent interracial heat transfer coefficient for different locations.展开更多
Both microstructural characteristics and fracture behavior of Fe-rich phases in a high-pressure die-cast hypoeutectic Al-Si alloy were investigated.Attention was focused on the morphology and formation mechanism of Fe...Both microstructural characteristics and fracture behavior of Fe-rich phases in a high-pressure die-cast hypoeutectic Al-Si alloy were investigated.Attention was focused on the morphology and formation mechanism of Fe-rich phases,together with their influence on fracture.Results show that primary Ferich phases exhibited in blocky shape precipitated from liquid while secondary Fe-rich phase in a large net shape was distributed along eutectic boundary participating in a ternary eutectic reaction.Through synchrotron X-ray tomography characterization,three Fe-rich phases with different morphologies,i.e.,polyhedral shape,fine compact shape and Chinese script-type shape were extracted along the radial direction.Lower slow-shot speed promoted the polyhedral Fe-rich phase to precipitate in slow-shot sleeve while decreased the formation of fine compact and Chinese script-type Fe-rich phases in die cavity.Because of a worse deformation compatibility,polyhedral Fe-rich phases fractured and became stress concentration sources before the failure of the casting.展开更多
As one of the most important forming technologies for industrial bulk metallic glass (BMG) parts withcomplex shapes, high-pressure die casting (HPDC) can fill a die cavity with a glass-forming metallic liquidin millis...As one of the most important forming technologies for industrial bulk metallic glass (BMG) parts withcomplex shapes, high-pressure die casting (HPDC) can fill a die cavity with a glass-forming metallic liquidin milliseconds. However, to our knowledge, the correlation between flow and crystallization behavior inthe HPDC process has never been established. In this study, we report on the solidification behavior ofZr_(55)Cu_(30)Ni_(5)Al_(10) glass forming liquid under various flow rates. Surprisingly, the resulting alloys display adecreasing content of amorphous phase with increase of flow rate, i.e. increase of cooling rate, suggestingthat crystallization kinetics of glass-forming metallic liquids in the HPDC process is strongly dependenton the flow field. Analysis reveals that the accelerated crystallization behavior is mainly ascribed to therapid increase in viscosity with a decreasing temperature as well as to the huge shear effect in the glassforming liquid at the end stage of the filling process when the temperature is close to the glass-transitionpoint;this results in a transition from diffusion- to advection-dominated transport. The current investigation suggests that flow-related crystallization must be considered to assess the intrinsic glass-formingability of BMGs produced via HPDC. The obtained results will not only improve the understanding ofcrystallization dynamics but also promote the high-quality production and large-scale application of BMGparts.展开更多
The relationship between the as-cast microstructure and mechanical properties of the Al-12Si-3.SCu- 2Ni-0.8Mg alloys produced by permanent mold casting (PMC) and high pressure die casting (HPDC) is investigated. T...The relationship between the as-cast microstructure and mechanical properties of the Al-12Si-3.SCu- 2Ni-0.8Mg alloys produced by permanent mold casting (PMC) and high pressure die casting (HPDC) is investigated. The alloys in both PMC and HPDC consist of Al, Si, A15 Cu2 MgsSi6, Al3 CuNi, and Al Cu4Ni phase. However, the microstructure of the HPDC alloy is significantly refined. Compared to the PMC alloy, the ultimate tensile strength of the HPDC alloy is significantly increased from 244 MPa to 310 MPa, while the elongation shows a reverse trend at room temperature. At low stress and temperature range, slight variations of stress exponent and activation energy indicate that the minimum creep rate is controlled by the grain boundary creep. Then the minimum creep rate is higher for the specimen with the smaller grain size, where grain boundary creep is the dominant creep mechanism. At high stress region, the stress exponent for the PMC alloy and HPDC alloy is 5.18 and 3.07, respectively. The different stress exponents and activation energies measured at high stress and high temperature range indicates that the creep mechanism varies with the casting technologies.2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.展开更多
基金financially supported by the National Key Research and Development Program of China(2022YFB3404201)the Major Science and Technology Project of Changchun City,Jilin Province(Grant No.20210301024GX)。
文摘The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron microscopy(SEM)and laboratory computed tomography(CT).Results showed that the newly developed AlSi9MnMoV alloy exhibited improved mechanical properties when compared to the AlSi10MnMg alloy.The AlSi9MnMoV alloy,which was designed with trace multicomponent additions,displays a notable grain refining effect in comparison to the AlSi10MnMg alloy.Refining elements Ti,Zr,V,Nb,B promote heterogeneous nucleation and reduce the grain size of primaryα-Al.At a lower slow shot speed,the large ESCs are easier to form and gather,developing into the dendrite net and net-shrinkage.With an increase in slow shot speed,the size and number of ESCs and porosities significantly reduce.In addition,the distribution of ESCs is more dispersed and the net-shrinkage disappears.The tensile property is greatly improved by adopting a higher slow shot speed.The ultimate tensile strength is enhanced from 260.31 MPa to 290.31 MPa(increased by 11.52%),and the elongation is enhanced from 3.72%to 6.34%(increased by 70.52%).
文摘Aluminum high pressure die casting(HPDC)technology has evolved in the past decades,enabling stronger and larger one-piece casting with significant part consolidation.It also offers a higher design freedom for more mass-efficient thin-walled body structures.For body structures that require excellent ductility and fracture toughness to be joined with steel sheet via self-piercing riveting(for instance,shock towers and hinge pillars,etc.),a costly T7 heat treatment comprising a solution heat treatment at elevated temperatures(450℃-500℃)followed by an over-ageing heat treatment is needed to optimize microstructure for meeting product requirement.To enable cost-efficient mass production of HPDC body structures,it is important to eliminate the expensive T7 heat treatment without sacrificing mechanical properties.Optimizing die cast alloy chemistry is a potential solution to improve fracture toughness and ductility of the HPDC components.The present study intends to tailor the Mg and Cu additions for a new Al-Si-Cr type die casting alloy(registered as A379 with The Aluminum Association,USA)to achieve the desired tensile properties without using T7 heat treatment.It was found that Cu addition should be avoided,as it is not effective in enhancing strength while degrades tensile ductility.Mg addition is very effective in improving strength and has minor impact on tensile ductility.The investigated Al-Si-Cr alloy with a nominal composition of Al-8.5wt.%Si-0.3wt.%Cr-0.2wt.%Fe shows comparable tensile properties with the T7 treated AlSi10MnMg alloy which is currently used for manufacturing shock towers and hinge pillars.
基金financially supported by the Natural Science Foundation of Guangdong Province(Nos.2021A151510042,2021A1515011728)the China Postdoctoral Science Foundation(2022M711190)+1 种基金the National Natural Science Foundation of China(No.51875211)the Key Area Research and Development Program of Guangdong Province(No.2020B010186002)。
文摘Considering the components produced by high pressure die casting(HPDC)process usually with ultra-large sizes and complex morphologies,high temperature solid solution treatment is not a suitable method to further improve their mechanical properties.In this study,two-stage aging treatment with different pre-aging times was designed and employed to further improve the mechanical properties of HPDC Al8SiMgCuZn alloy.The characteristics of precipitates were evaluated by a transmission electron microscope(TEM),and the precipitation strengthening mechanism was discussed.The results reveal that the strengthening is mainly contributed by the precipitation ofβ″phase after two-stage aging,and the number density and size of the precipitates are significantly depended on the pre-aging time.The number density of precipitates is increased with the pre-aging time prolonged from 0 h to 4 h,and then decreases with the further increase of pre-aging time from 4 h to 6 h.The precipitates with the highest density and smallest size are observed after pre-aging for 4 h.After pre-aged at 100℃for 4 h and then artificial aged at 200℃for 30 min,the yield strength of 207 MPa,ultimate tensile strength of 325 MPa and elongation of 7.6%are achieved.
基金supported by the National Major Science and Technology Program of China(2012ZX04012011)the National Nature Science Foundation of China(51275269)
文摘In this paper,the research progress of the interfacial heat transfer in high pressure die casting(HPDC)is reviewed.Results including determination of the interfacial heat transfer coefficient(IHTC),influence of casting thickness,process parameters and casting alloys on the IHTC are summarized and discussed.A thermal boundary condition model was developed based on the two correlations:(a)IHTC and casting solid fraction and(b)IHTC peak value and initial die surface temperature.The boundary model was then applied during the determination of the temperature field in HPDC and excellent agreement was found.
文摘The development of lightweight magnesium(Mg)alloys capable of operating at elevated temperatures of 200-300℃and the ability of using high pressure die casting for high-volume manufacturing are the most advanced developments in manufacturing critical parts for internal combustion engines used in power tools.Here we report the microstructure and mechanical properties of a newly developed die-cast Mg-RE(La,Ce,Nd,Gd)-Al alloy capable of working at higher elevated temperatures of 200-300℃.The new alloy delivers the yield strength of 94 MPa at 300℃,which demonstrates a 42%increase over the benchmark AE44 high temperature die-cast Mg alloy.The new alloy also has good stiffness at elevated temperatures with its modulus only decreasing linearly by 13%from room temperature up to 300℃.Thermal analysis shows a minor peak at 364.7℃in the specific heat curve of the new alloy,indicating a good phase stability of the alloy up to 300℃.Nd and Gd have more affinity to Al for the formation of the minority of divorced Al-RE(Nd,Gd)based compounds,and the stable Al-poor Mg_(12)RE(La_(0.22)Ce_(0.13)Nd_(0.31)Gd_(0.31))Zn_(0.39)Al_(0.13)compound acts as the continuous inter-dendritic network,which contribute to the high mechanical performance and stability of the new die-cast Mg alloy at 200-300℃.
基金financially supported by the Fundamental Research Funds for the Central Universities(WUT:2017IVA036)111 Project(B17034)State Key Laboratory of Materials Processing and Die&Mould Technology,Huazhong University of Science and Technology(P2018-003)
文摘The morphology and content of the divorced eutectic in the microstructure of high pressure die casting(HPDC) magnesium alloy have a great influence on the final performance of castings. Based on the previous work concerning simulation of the nucleation and dendritic growth of primary α-Mg during the solidification of magnesium alloy under HPDC process, an extension was made to the formerly established CA(Cellular Automaton) model with the purpose of modeling the nucleation and growth of Mg-Al eutectic. With a temperature field and solute field obtained during simulation of the primary α-Mg dendrites as the initial condition of the modified CA model, modeling of the Mg-Al eutectic with a divorced morphology was achieved. Moreover, the simulated results were in accordance with the experimental ones regarding the distribution and content of the divorced eutectic. Taking a "cover-plate" die casting with AM60 magnesium alloy as an example, the rapid solidification with a high cooling rate at the surface layer of the casting led to a fine and uniform grain size of primary α-Mg, while the divorced eutectic at the grain boundary revealed a more dispersed and granular morphology. Islands of divorced eutectic were observed at the central region of the casting, due to the existence of ESCs(Externally Solidified Crystals) which contributed to a coarse and non-uniform grain size of primary α-Mg. The volume percentage of the eutectic β-Mg_(17)Al_(12) phase is about 2%-6% in the die casting as a whole. The numerical model established in this study is of great significance to the study of the divorced eutectic in the microstructure of die cast magnesium alloy.
基金financially the National Natural Science Foundation of China(No.51805389)Natural Science Foundation of Hubei Province of China(No.2018CFB210)111 Project(B17034)。
文摘Both a conventional flow distributer and an improved one with a flow buffer were applied respectively during the high pressure die casting(HPDC)process,and samples of AZ91D magnesium alloy with different microstructure mainly consisting ofα-Mg grains,β-phase and porosities were obtained.According to the grain orientation analysis,the predominant deformation behavior inα-Mg grains was dislocation slip,supplemented by deformation twinning.Dislocation slip was more difficult to occur in the samples with the improved flow distributer on account of the fact that the size ofα-Mg grains in the microstructure was finer and more uniform.During the in situ tensile deformation test,cracks were observed to initiate from gas-shrinkage pore and island-shrinkage,and two main crack propagation mechanisms,porosity growth and coalescence were found accordingly.When the crack was in contact with theβ-phase,it would pass through and fracture the networkβ-phase,whereas bypass the islandβ-phase by detaching it from the surroundingα-Mg grains.Mechanical property tests showed that the samples with relatively more homogeneous microstructure would perform higher mechanical properties,which was the combined effect of matrixα-Mg grains,β-phase,and porosities.
基金financially supported by the National Natural Science Foundation of China-China Aerospace Science and Technology Corporation Aerospace Advanced Manufacturing Technology Research Foundation(NO.U1537202)the Special Funding Program on Transformation of Scientific and Technological Achievements at Jiangsu Province(No.BA2015041)
文摘Microstructural and hardness evolutions of a vacuum-assistant die-cast A380(Al-8.67 wt.%Si-3.27 wt.%Cu) alloy during heat treatment were investigated. Isothermal DSC test at 200 °C revealed that the precipitation reaction in the surface layer was faster than that in the central region. This corresponded with the hardness evolution that the surface layer hardened faster. The hardness increment in the surface layer was higher than that in the central region. Further experimental evidences indicated that the differences were due to the different amounts of heterogeneous nucleation sites for precipitation in the two parts. The influence of the characteristic as-cast microstructure on the artificial aging process is analyzed and discussed in detail.
基金the National Natural Science Foundation of China(No.51805389)the Key R&D Program of Hubei Province,China(No.2021BAA048)+1 种基金the 111 Project(No.B17034)the fund of the Hubei Key Laboratory of Advanced Technology for Automotive Components,Wuhan University of Technology(No.XDQCKF2021011).
文摘The characteristics of defect bands in the microstructure of high pressure die casting(HPDC)AE44 magnesium alloy were investigated.Special attention was paid to the effects of process parameters during the HPDC process and casting structure on the distribution of defect bands.Results show that the defect bands are solute segregation bands with the enrichment of Al,Ce and La elements,which are basically in the form of Al_(11)RE_(3) phase.There is no obvious aggregation of porosities in the defect bands.The width of the inner defect band is 4-8 times larger than that of the outer one.The variation trends of the distribution of the inner and outer defect bands are not consistent under different process parameters and at different locations of castings.This is due to the discrepancy between the formation mechanisms of double defect bands.The filling and solidification behavior of the melt near the chilling layer is very complicated,which finally leads to a fluctuation of the width and location of the outer defect band.By affecting the content and aggregation degree of externally solidified crystals(ESCs)in the cross section of die castings,the process parameters and casting structure have a great influence on the distribution of the inner defect band.
基金This work was financially supported by the National Natural Science Foundation of China (No. 50675114) the National Basic Research Program of China (2006CB605208-2) The experiments were conducted at the Tsinghua-TOYO R&D Center of Magnesium and Aluminum Alloys Processing Technology with the help of engineers from the TOYO Machiuery & Metal Co., Ltd.
文摘A method based on die casting experiments and mathematic modeling is presented for the determination of the heat flow density (HFD) and interfacial heat transfer coefficient (IHTC) during the high pressure die casting (HPDC) process.Experiments were carried out using step shape casting and a commercial magnesium alloy,AM50.Temperature profiles were measured and recorded using thermocouples embedded inside the die. Based on these temperature readings,the HFD and IHTC were successfully determined and the calculation results show that the HFD and IHTC at the metal-die interface increases sharply right after the fast phase injection process until approaching their maximum values,after which their values decrease to a much lower level until the dies are opened.Different patterns of heat transfer behavior were found between the die and the casting at different thicknesses.The thinner the casting was,the more quickly the HFD and IHTC reached their steady states.Also,the values for both the HFD and IHTC values were different between die and casting at different thicknesses.
基金The work was financially supported by the Significant Fundamental Research Development & Planning of China (G2000067208-3) the Significant Project of the National Natural Science Foundation of China (59990470-3)and the internal research fund of Tsing
文摘The mold filling and solidification simulation for the high pressure die casting (HPDC) and low pressure die casting (LPDC) processes were studied. A mathematical model considering the turbulent flow and heat transfer phenomenon during the HPDC process has been established and parallel computation technique was used for the mold filling simulation of the process. The laminar flow characteristics of the LPDC process were studied and a simplified model for the mold filling process of wheel castings has been developed. For the solidification simulation under pressure conditions, the cyclic characteristics and the complicated boundary conditions were considered and techniques to improve the computational efficiency are discussed. A new criterion for predicting shrinkage porosity of Al alloy under low pressure condition has been developed in the solidification simulation process.
基金This work was co-funded by,The National Key Research and Development Program of China(NO.2016YFB0301002)and General Motors Global Research and Development.
文摘Few studies were reported on the phases'relationships of AE44(Mg-4.0Al-4.1RE-0.3Mn,wt.%)and its composites.In this work,AE44 alloy and Saffil(6-Al2O3)/AE44 Metal matrix composite(MMC)were both prepared by slow shot high pressure die casting(SS-HPDC)technology and their phase constitutions were all studied in detail using experimental techniques combined with CALPHAD(Calculation of Phase Diagram)modeling.The results revealed that the alloy consists of the a-Mg matrix,A1hRE3 intermetallic phase,and one trace phase AI3RE,while the composite contains five major phases:a-Mg,5-AI2O3,AI3RE,MgO and Mg2Si.and two trace phases of A12RE and AI11RE3,respectively.A1hRE3 is partly derived from ALRE,while A13RE is a product of the peritectoid reaction between the two precipitates.The presence of MgO and Mg2Si is due to the interfacial reaction between the SiO2 binder in the fiber preforms and the molten magnesium during infiltration.The use of SiO2 binder in the preform manufacturing was limited/minimized to reduce the MgO formation in the MMC casting process,which can be detrimental to the fatigue performance of the MMC materials.
基金the National Natural Science Foundation of China (No.51275269)the Tsinghua University Initiative Scientific Research Program (No.20121087918)the National Science and Technology Major Project of the Ministry of Science and Technology of the People’s Republic of China (No.2012ZX04012011) for financial support
文摘X-ray tomography was used to characterize the porosity in high pressure die casting of AM60B alloy. In situ tensile deformation was performed to observe the change of porosities and their influences on crack initiation, propagation and subsequent fracture of specimen. Results showed that four types of porosi- ties, including gas-shrinkage pore, gas pore, net-shrinkage and island-shrinkage, could be identified according to the formation mechanism and morphology characterization. During tensile deformation, it was shown that the gas-shrinkage pore and net-shrinkage, rather than gas pore or island-shrinkage, were the main sources for crack initiation. In addition, the crack propagated by interconnecting the po- rosities at the cross section with minimum efficient force bearing area. At these locations where externally solidified crystals (ESCs) were present, the crack would propagate along the ESC boundaries in an inter- granular mode, while at these locations without ESCs, the crack would propagate roughly along the direction perpendicular to the tensile stress in a combination of trans-granular and inter-granular modes.
基金financially supported by the National Major Science and Technology Program of China(No.2012ZX04012011)the National Natural Science Foundation of China(No.51275269)
文摘The interfacial heat transfer behavior at the metalJshot sleeve interface in the high pressure die casting (HPDC) process of AZ91D alloy is carefully investigated. Based on the temperature measurements along the shot sleeve, inverse method has been developed to determine the interfacial heat transfer coefficient in the shot sleeve. Under static condition, Interracial heat transfer coefficient (IHTC) peak values are 11.9, 7,3, 8.33kWm-2K-1 at pouring zone (S2), middle zone (S5), and end zone (510), respectively. During the casting process, the IHTC curve displays a second peak of 6.1 kWm-2 K-1 at middle zone during the casting process at a slow speed of 0.3 ms 1 Subsequently, when the high speed started, the IHTC curve reached a second peal〈 of 12.9 kW m-2K-1 at end zone. Furthermore, under different slow casting speeds, both the calculated initial temperature (TIDs) and the maximum temperature (Tsimax) of shot sleeve surface first decrease from 0.1 ms-1 to 0.3 ms-1, but increase again from 0.3 ms-1 to 0.6 ms-1. This result agrees with the experimental results obtained in a series of "plate-shape" casting experiments under different slow speeds, which reveals that the amount of ESCs decreases to the minimum values at 0.3 m s-1 and increase again with the increasing casting slow speed.
基金supported by the Project Funded by China Postdoctoral Science Foundation(No.2015M571562)
文摘Effects of natural aging and test temperature on the tensile behaviors have been studied for a highperformance cast aluminum alloy Al–10Si–1.2Cu–0.7Mn. Based on self-strengthening mechanism and spheroidization microstructures, the alloy tested at room temperature(RT) exhibits higher 0.2% proof stress(YS) of 206 MPa, ultimate tensile strength(UTS) of 331 MPa and elongation of 10%. Increasing aging time improves the YS and UTS and reduces the ductility of the alloy. Further increasing aging time beyond72 h does not signi?cantly increase the tensile strengths. Increasing test temperature significantly decreases the tensile strengths and increases the ductility of the alloy. The UTS of the alloy can be estimated by using the hardness. The Portevin–Le Chatelier effect occurs at RT due to the interactions between solid solution atoms and dislocations. Similar behaviors occurring at 250℃ are attributed to dynamic strain aging mechanism. Increasing aging time leads to decrease in the strain-hardening exponent(n) value and increase in the strain-hardening coeficient(k) value. Increasing test temperature apparently decreases the n and k values. Eutectic phase particles cracking and debonding determine the fracture mechanism of the alloy. Final failure of the alloy mainly depends on the global instability(high temperature, necking) and local instability(RT, shearing). Different tensile behaviors of the alloy are mainly attributed to different matrix strengths, phase particle strengths and damage rate.
基金the financial support of the National High Technology Research and Development Program of China (Grant No. 2009AA03Z114)the Ministry of Science and Technology of China (Grant Nos. 2011ZX04014-052, 2011BAE22B02 and 2010DFA72760)
文摘Under the cold-chamber high pressure die casting (HPDC) process, samples were produced with AM60B magnesium alloy to investigate the microstructure characteristics of the eutectics, especially focusing on the constitution, morphology and distribution of the eutectics over cross section of the castings. Attentions were also paid to study the effect of heat treatment on the eutectics in the die castings. Based on experimental analysis using optical microscopy (OM), X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS), it was determined that fully divorced eutectics consisting of c^-Mg and l%MglzA112 appeared at the grain boundary of the primary c^-Mg in the as-cast microstructure. Islands and networks of β-Mg17Al12 phase were observed in the central region of the castings, while the β-Mg17Al12 phase revealed a more dispersed and granular morphology on the surface layer. The two phases ratio β/α in the central region of the castings was approximately 10%, which was higher than that on the surface layer. Besides, the defect bands contained a higher percentage of the eutectics than the adjacent regions. After aging treatment (T6), only α-Mg phase was detected by XRD in the AM60B magnesium alloy, though a small amount of precipitated β-MgITAI12 phase was observed at the grain boundary. In contrast to the microstructure of die cast AZ91D magnesium alloy under the same T0 heat treatment, no discontinuous precipitation of the β-MgITAI12 phase was observed in AMO0B magnesium alloy die castings.
基金jointly supported by Canadian Network for Research and Innovation in Machining TechnologyNatural Sciences and Engineering Research Council of Canada-Automotive Partnership Canada programNRCan’s Office of Energy R&D through the Program on Energy R&D
文摘The objective of this study is to predict grain size and heat transfer coefficient at the metal-die interface during high pressure die casting process and solidification of the magnesium alloy AM60. Multiple runs of the commercial casting simulation package, ProCASTTM, were used to model the mold filling and solidification events employing a range of interfacial heat transfer coefficient values. The simulation results were used to estimate the centerline cooling curve at various locations through the casting. The centerline cooling curves, together with the die temperature and the thermodynamic properties of the alloy, were then used as inputs to compute the solution to the Stefan problem of a moving phase boundary, thereby providing the through-thickness cooling curves at each chosen location of the casting, Finally, the local cooling rate was used to calculate the resulting grain size via previously established relationships. The effects of die temperature, filling time and heat transfer coefficient on the grain structure in skin region and core region were quantitatively characterized. It was observed that the grain size of skin region strongly depends on above three factors whereas the grain size of core region shows dependence on the interracial heat transfer coefficient and thickness of the samples. The grain size distribution from surface to center was estimated from the relationship between grain size and the predicted cooling rate. The prediction of grain size matches well with experimental results. A comparison of the predicted and experimentally determined grain size profiles enables the determination of the apparent interracial heat transfer coefficient for different locations.
基金the National Natural Science Foundation of China(Grant No.51775297)the National Science and the Tsinghua University Initiative Scientific Research Program(20151080370)UK Royal Academy of Engineering/Royal Society through the Newton International Fellowship Scheme。
文摘Both microstructural characteristics and fracture behavior of Fe-rich phases in a high-pressure die-cast hypoeutectic Al-Si alloy were investigated.Attention was focused on the morphology and formation mechanism of Fe-rich phases,together with their influence on fracture.Results show that primary Ferich phases exhibited in blocky shape precipitated from liquid while secondary Fe-rich phase in a large net shape was distributed along eutectic boundary participating in a ternary eutectic reaction.Through synchrotron X-ray tomography characterization,three Fe-rich phases with different morphologies,i.e.,polyhedral shape,fine compact shape and Chinese script-type shape were extracted along the radial direction.Lower slow-shot speed promoted the polyhedral Fe-rich phase to precipitate in slow-shot sleeve while decreased the formation of fine compact and Chinese script-type Fe-rich phases in die cavity.Because of a worse deformation compatibility,polyhedral Fe-rich phases fractured and became stress concentration sources before the failure of the casting.
基金L.H.Liu would like to thank the financial support from the National Natural Science Foundation of China(No.52001123)the China Postdoctoral Science Foundation(Nos.2019TQ0099 and 2019M662908)+5 种基金Guangdong Basic and the Applied Basic Research Foundation(No.2019A1515110215)the Foundation for Distinguished Young Talents in Higher Education of Guangdong(No.2019KQNCX003)the Fundamental Research Funds for the Central Universities(No.2020ZYGXZR030)the Open Fund of National Engineering Research Center of Near-net-shape Forming for Metallic Materials(No.2019003)C.Yang would like to thank the financial support from the Key Basic and Applied Research Program of Guangdong Province(No.2019B030302010)the National Natural Science Foundation of China(No.51971149).
文摘As one of the most important forming technologies for industrial bulk metallic glass (BMG) parts withcomplex shapes, high-pressure die casting (HPDC) can fill a die cavity with a glass-forming metallic liquidin milliseconds. However, to our knowledge, the correlation between flow and crystallization behavior inthe HPDC process has never been established. In this study, we report on the solidification behavior ofZr_(55)Cu_(30)Ni_(5)Al_(10) glass forming liquid under various flow rates. Surprisingly, the resulting alloys display adecreasing content of amorphous phase with increase of flow rate, i.e. increase of cooling rate, suggestingthat crystallization kinetics of glass-forming metallic liquids in the HPDC process is strongly dependenton the flow field. Analysis reveals that the accelerated crystallization behavior is mainly ascribed to therapid increase in viscosity with a decreasing temperature as well as to the huge shear effect in the glassforming liquid at the end stage of the filling process when the temperature is close to the glass-transitionpoint;this results in a transition from diffusion- to advection-dominated transport. The current investigation suggests that flow-related crystallization must be considered to assess the intrinsic glass-formingability of BMGs produced via HPDC. The obtained results will not only improve the understanding ofcrystallization dynamics but also promote the high-quality production and large-scale application of BMGparts.
基金financial support of the National Key Research and Development Project of China (No. 2016YFB0301001)the Opening Fund of State Key Laboratory of Metal Matrix Composite (No. mmc-kdf16-03)Shanghai Jiao Tong University startup funding (No. 13x100040023)
文摘The relationship between the as-cast microstructure and mechanical properties of the Al-12Si-3.SCu- 2Ni-0.8Mg alloys produced by permanent mold casting (PMC) and high pressure die casting (HPDC) is investigated. The alloys in both PMC and HPDC consist of Al, Si, A15 Cu2 MgsSi6, Al3 CuNi, and Al Cu4Ni phase. However, the microstructure of the HPDC alloy is significantly refined. Compared to the PMC alloy, the ultimate tensile strength of the HPDC alloy is significantly increased from 244 MPa to 310 MPa, while the elongation shows a reverse trend at room temperature. At low stress and temperature range, slight variations of stress exponent and activation energy indicate that the minimum creep rate is controlled by the grain boundary creep. Then the minimum creep rate is higher for the specimen with the smaller grain size, where grain boundary creep is the dominant creep mechanism. At high stress region, the stress exponent for the PMC alloy and HPDC alloy is 5.18 and 3.07, respectively. The different stress exponents and activation energies measured at high stress and high temperature range indicates that the creep mechanism varies with the casting technologies.2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.