Grain refinement of primary silicon in hypereutectic Al-Si alloys by different P-containing compounds

The grain refinement behavior of Si-3 P,Si-25 Mn-10 P,and Al-10 Si-2 Fe-3 P master alloys on hypereutectic Al-24 Si alloy was studied.Microstructure analysis indicates that the P-containing compounds in the three master alloys are Si P,Mn P,and Al P,respectively.The coarse flower-like primary silicon in the Al-24 Si alloy transforms into smaller,well-distributed blocks with the addition of various master alloys.When pouring at 840°C,the average grain size of the primary silicon refined by Si-25 Mn-10 P master alloy with a holding time of 30 min is about 18μm,which is significantly smaller than those refined by Si-3 P and Al-10 Si-2 Fe-3 P master alloys.The grain size shows an increasing trend when the holding time is further prolonged.Higher holding temperature has a positive effect on the grain refinement of Si-25 Mn-10 P master alloy.The grain refinement mechanism of the three master alloys was also discussed.

Effects of individual and combined additions of phosphorus,boron and cerium on primary and eutectic silicon in an Al-30Si alloy

The modification of silicon in an Al-30Si alloy was studied using optical microscopy, electron probe micro-analysis, transmission electron microscopy and differential scanning calorimetry. It is found that phosphorus master alloys combined with boron master alloys have good modification effect on primary silicon but no evident modification effect on eutectic silicon, while boron combined with cerium has good modification effect on eutectic silicon. The results of differential scanning calorimetry show that phosphorus, boron or cerium addition and their combined addition have different undercooling effects on eutectic silicon. Many scholars thought that AlP particles were the nuclei of eutectic silicon when phosphorus was enough in the alloy. Our results show that β-（Al,Si,Fe） can still be the nucleus of plate-like entectic silicon while AlP is the nucleus of primary silicon when there is enough phosphorus in the melt. In addition, the mechanism about the modification was also discussed.

Effect of neodymium on primary silicon and mechanical properties of hypereutectic Al-15%Si alloy

The mechanical properties of hypereutectic Al-Si alloys are mainly determined by size and morphology of the primary silicon phase.So,optical microscopy(OM) and X-ray diffraction(XRD) were adopted to study affection of Nd on primary silicon of hypereutectic Al-15%Si alloy in this paper.The results of OM showed that pure Nd could effectively refine primary silicon of hypereutectic Al-15%Si alloy.When Nd addition was 0.3%,the average size of primary silicon reduced from 20-40 μm of initial sample to 10-20 μm of modified sample.XRD pattern showed that no new phase was formed after Nd modification.The results of mechanical properties test showed that whole properties of modified samples were significantly improved.Tensile strength increased about 32.6% from 147 MPa to 195 MPa.Elongation was increased about 160% from 1.0% to 2.6%.The improvement of mechanical properties should attribute to primary silicon refinement after modification.

Effect of solidification cooling rate on microstructure and tribology characteristics of Zn-4Si alloy

The main objective of this work was to modify the microstructure and enhance the tribological properties of a new Zn-4Si al-loy through a high solidification cooling rate(SCR).According to the results,by increasing the SCR from 2.0 to 59.5℃/s the average size of primary Si particles and that of the grains reduced from 76.1 and 3780μm to less than about 14.6 and 460μm,respectively.Augment-ing the SCR also enhanced the microstructural homogeneity,decreased the porosity content(by 50%),and increased the matrix hardness(by 36%).These microstructural changes enhanced the tribological behavior.For instance,under the applied pressure of 0.5 MPa,an in-crease in the SCR from 2.0 to 59.5℃/s decreased the wear rate and the average friction coefficient of the alloy by 57%and 23%,respect-ively.The wear mechanism was also changed from the severe delamination,adhesion,and abrasion in the slowly-cooled alloy to the mild tribolayer delamination/abrasion in the high-cooling-rate-solidified sample.

Effects of P+Cr complex modification and solidification conditions on microstmcture of hypereutectic Al-Si alloys by wedge-shaped copper mould casting

Large and segregated primary Si particles may drastically decrease the mechanical properties of Al-Si alloys. To solve this problem, a P-Cr complex modif ier was added into the alloy, and the effects of P-Cr complex modification and solidification conditions on the microstructure of hypereutectic Al-Si alloys casting produced in wedge-shaped copper mould were studied. The thermal analysis technique was applied to calculate the cooling rate during solidification. The microstructures were observed by means of optical and scanning electron microscopies. Results showed that the primary Si segregates in the as-cast hypereutectic Al-Si alloys. The segregation of primary Si can be inhibited by adding a P+Cr complex modif ier and increasing the cooling rate during solidif ication. The ref inement of primary Si particles by P+Cr complex modif ication is due to the formation of CrS i2 and AlP particles which act as the heterogeneous nuclei for the primary Si phase. The segregation of Si was also inhibited through the adherence of heavier CrS i2 particles to the primary Si particles.

Effect of Nd on Microstructure and Mechanical Properties of Hypereutectic Al-25Si Alloy

The modification mechanism of Nd on Al-25Si alloy was studied. The result showed that pure Nd (0.3%) could significantly refine primary silicon in hypereutectic Al-25Si alloy. And the morphology of primary silicon was transformed from star-shaped to block and the size of primary silicon changed from 150～200 μm to 40～80 μm after modification. The morphology of silicon and elements presence was detected by means of SEM-EDS, XRD was carried out to detect the phase constitution before and after modification. It was found that no new phase formed and the lattice of silicon and aluminum increased after modification and most of Nd may exist as solids solute element of silicon and absorb on the surface of silicon. Mechanical property test results showed that after modification with 0.3% Nd, Tensile strength increased about 33% from 138 to 184 MPa, yield strength increased about 15% from 126 to 145 MPa, and elongation change was not obvious. The improvement of mechanical property should attribute to fine grain strength and purification of base metal after modification.

Refinement and migrating behaviors in Al-Si hypereutectic alloys solidified under electromagnetic vibration

The effects of electromagnetic vibration （EMV） on the refinement and migration of primary silicons in the A1-18 wt pct Si alloy were investigated systematically. It was found that EMV could effectively refine primary silicons. The equivalent diameter of primary silicon first decreases slowly with the current increasing from 1 A to 3 A, but then drops rapidly between 3 A and 10 A, next gradually decreases with increasing current intensity. When the EMV intensity was low, the primary silicons were agglomerated and expelled to the top of a sample, the segregation of silicon grains gradually decreased and the agglomerating phenomena disappeared with the increase of EMV intensity, and the star-like coarse primary silicons turned refined flake or square morphology. The refinement and migration of primary silicons depended on the Lorentz force, gravity and the effective viscous force.