The Processing Mineralogy for Lead and Zinc Oxide Ore in Sichuan

Using variety of modern testing methods, the processing mineralogical characteristics for a lead and zinc oxide ore in Sichuan were studied systematically. The chemical analysis result shows that the lead and zinc oxide content exceeding the minimum industrial grade and iron ore, total iron content reaches a minimum industrial grade and associated with gold and silver; The mineralogical analysis result shows that lead and zinc mineral composition and configuration are very complexity. The zinc minerals and zinciferous minerals are sphalerite, hemimorphite, Smithsonite, Hydrozincite, zinc chlorite, limonite, zinc dolomite and zincocalcite; lead minerals and plumbiferous minerals are mainly galena, cerussite, anglesite, limonite and Coronadite; The minerals disseminated grain size are very fine and mineral dissemination characteristics are very complex ; expected theoretical recoveries for lead and zinc were 72% and 67% respectively. The results of this study provide basic data and theoretical basis for ore dressing.

攀西某强蚀变钒钛磁铁矿钛的赋存状态及理论指标预测

攀西四大矿区是我国战略资源铁、钛主产区,铁、钛均可综合利用,矿集区内铁主要从钛磁铁矿中回收,钛主要从钛铁矿中回收,从其他矿物中回收的类型鲜有报道。对攀西某地强蚀变矿石研究发现,矿石中铁含量低,主要赋存于绿泥石中,无利用价值;钛可有效利用,钛的赋存机制与四大矿集区差异较大。为查清该矿石中钛的赋存状态,采用多种矿物学研究手段对矿石进行了深入研究。研究结果表明:矿石中钛的主要载体矿物为锐钛矿及钛铁矿,分别占总钛的51.39%、21.54%,二者或紧密共生,或独立存在,粒间普遍分布不规则填隙状碳酸盐等脉石矿物;锐钛矿与钛铁矿粒径0.074 mm以上含量低,分别占35.64%、43.92%,细磨单体解离度较差。此外,因矿石发生重度蚀变,少量钛还分布在结晶较差无法有效利用的锐钛矿-绿泥石过度相及榍石等矿物中,即矿石为细粒难选冶、钛赋存状态复杂的钒钛磁铁矿矿石。基于矿石的嵌布特性,最终制定了原矿棒磨后摇床富集钛,预富集产品焙烧-磨矿-酸洗-浮钛-酸浸的混合选钛工艺流程,获得了TiO_(2)品位及回收率均在50%以上的钛精矿,研究成果为该区钛的后续选冶工艺制定提供了新的理论支撑,释放了呆滞钛资源,对同类型矿石综合利用具有重要的参考意义。

新疆某铜钴矿矿石基因特性及其对磨选的影响

为查明新疆某铜钴矿的矿石基因特性,为后续选矿工艺设计提供理论指导,本文利用电子探针、矿物自动分析系统及X射线衍射仪等对该矿床矿石的基因特性进行了研究。研究结果表明:矿石中的金属矿物主要为黄铜矿、毒砂-辉砷钴矿系列矿物和黄铁矿;矿石中的Cu赋存于黄铜矿中,93.30%的Co赋存于毒砂-辉砷钴矿系列矿物中,其余6.70%赋存于黄铁矿中,黄铜矿和毒砂-辉砷钴矿系列矿物粒度均以中细粒为主(0.010~0.300 mm),在-0.074 mm占70%的磨矿细度下,目的矿物均有一定的解离,但仍有部分为连生体,为降低磨矿成本、保证回收率和精矿品质,建议采用在磨矿细度下进行全硫化物浮选,然后粗精矿再磨后进行Cu、Co分离的选矿工艺;Co的赋存状态特征指示,浮选过程中As与Co的走向相同,会造成钴精矿中As超标,且由于毒砂-辉砷钴矿系列矿物与黄铜矿嵌布关系密切,两者很难达到完全单体解离,易造成铜精矿中As也偏高。本文通过研究新疆某铜钴矿的矿石基因特性,指出了影响磨选的矿物学因素,对后续矿物加工具有理论指导意义。

江西石坞金矿床地质特征和金的赋存状态及对选矿工艺的指示意义

石坞金矿床位于钦杭结合带东段北部万年推覆体中金山推覆构造的中部位置,矿体严格受次级韧性剪切带控制,矿石类型主要为糜棱岩和超糜棱岩型。利用光学显微镜观察、X射线衍射(X-ray diffraction,XRD)分析、化学成分分析、扫描电镜(scanning electron microscope,SEM)分析等手段,对石坞金矿床矿石特征及金矿物的赋存状态进行研究。结果表明,矿石中金属矿物以黄铁矿为主,次为毒砂,粒径范围0.04~0.4 mm。脉石矿物以石英为主,金矿物只有自然金一种。金矿物的赋存状态以裂隙金(64.92%)和粒间金(23.99%)为主。按粒度分类,以细粒金(57.24%)和微粒金(27.01%)为主,粒径范围0.005~0.037 mm。在0.074 mm的磨矿细度达到75%的情况下通过全硫化物浮选,可以较好地对金矿物进行富集和回收。通过选矿工艺对比研究,“快速浮选-快浮尾矿再浮选”的选矿工艺的金回收率最高,达到93.89%。

新疆某铜镍矿工艺矿物学研究

以新疆某铜镍矿为研究对象,对该矿石的化学组成进行探究,重点关注矿物的嵌布特征,以及铜、镍的存在状态和嵌布粒度等方面展开了深入的研究。结果表明,该矿石主要含有铜和镍两种重要有价元素,铜的品位为0.96%,镍的品位为0.55%。铜主要以黄铜矿的形式存在于矿石中,少量铜分布在蓝辉铜矿和铜蓝矿中,偶尔还可见到一些孔雀石和赤铜矿;而镍则主要存在于镍黄铁矿中,其次是紫硫镍矿。此外,其他金属矿物主要包括褐铁矿,而非金属矿物则主要是以蛇纹石为主(其中部分含有镍)。

锂矿石基因特性及其对选矿的影响

锂是重要的战略性新能源矿产,锂矿床主要有卤水型、伟晶岩型、花岗岩型、隐爆角砾岩型和黏土型等五种类型。对于后四类固体矿床来说,因成矿条件及过程的差异,其矿石基因特性具有明显不同。伟晶岩型锂矿Li2O品位高,锂矿物主要为锂辉石、透锂长石、磷锂铝石和锂云母等;花岗岩型锂矿Li2O品位通常较低,但矿床规模大,锂主要赋存于锂白云母、铁锂云母和锂云母中;隐爆角砾岩型锂矿Li2O品位也较高,矿石中的含锂矿物较单一,通常为锂云母;黏土型锂矿中的锂主要赋存在锂的独立矿物(锂绿泥石、羟硼硅钠锂石等)中,或以类质同象和/或吸附形式赋存于黏土矿物(高岭石、伊利石、蒙脱石等)和一水硬铝石中。矿石中锂的回收利用工艺与锂的赋存状态密切相关。花岗岩型锂矿和黏土型锂矿资源在我国广泛分布,随着提锂技术的发展,这两种类型的锂资源具有广阔的开发利用前景。

四川李家沟锂辉石矿Ⅰ号矿脉矿石工艺矿物学研究

为了高效开发利用四川李家沟锂辉石矿,通过偏光显微镜观察、化学多元素分析、X射线衍射分析(XRD)等手段,对李家沟锂辉石矿床Ⅰ号脉矿石进行了工艺矿物学特性研究。研究结果表明:矿石中Li_(2)O含量0.82%,属于低品位矿石;矿石中的矿物主要为锂辉石,整体呈中粗粒嵌布,晶体粒度较为粗大;脉石矿物为石英、长石和云母,云母和长石中含有极其微量的锂。锂辉石虽然嵌布粒度粗细不均,但320~1280μm中粒产率达78.174%,属易解离的矿石类型。矿石中的锂主要赋存于锂辉石中,配分比97.998%,其中Rb_(2)O平均品位0.082%,达到了综合回收伴生铷的工业品位指标;锂辉石单矿物化学分析结果显示,Li_(2)O含量7.68%,低于锂辉石理论含量,其中可能发生类质同象替代,矿石中还含有Fe、Mn、Na等杂质,以及部分铁锰质填充在锂辉石的解理和裂隙中,这将对锂辉石的品级产生一定程度的影响。

某红土型镍矿中镍钴的赋存状态对其回收的影响

褐铁矿型红土镍矿是一种富含镍、钴、铁的重要资源,综合利用价值巨大。探究红土型镍矿中镍和钴的赋存状态,以深入了解赋存状态对镍和钴回收利用的影响。通过详细的工艺矿物学研究,明确镍和钴主要赋存于褐铁矿、锰的水合氧化物和锰镍矿中,根据该红土型镍矿特征判断最佳冶炼回收方法为高压酸浸工艺。研究为红土型镍矿的资源高效利用提供了重要参考,为相关工业应用和环境保护提供了有益启示。

某锌矿中锌及稀散元素镓、锗的赋存状态

这是一篇工艺矿物学领域的论文。采用化学分析、显微镜分析和MLA矿物自动定量检测技术,对国内某锌矿石中锌及伴生稀散元素镓、锗的赋存状态和主要载体矿物的嵌布特征进行详细研究。结果表明,该锌矿石中含Zn 4.87%、Ga 4.10 g/t、Ge 59.00 g/t,未发现稀散元素镓、锗的独立矿物,镓、锗主要赋存在闪锌矿中。从该矿石中分选闪锌矿(包含异极矿),锌、镓、锗的理论回收率分别为95%、56%、93%左右。少部分微细粒状胶态闪锌矿不易获得解离,易损失于尾矿中,对锌的回收率有一定影响。

山阳秦金氧化金矿石选矿工艺研究

本文系统地研究了山阳秦金矿业有限公司氧化金矿石的矿物组成、结构、金的赋存状态以及矿石类型,并依据这些特性探讨了相应的选矿工艺。通过详细的化学分析和物理性质测试,结合矿石的工业类型,本文提出了适用于氧化金矿石的多阶段选矿工艺流程,包括破碎、磨矿、浓缩、浸出、吸附、解吸、电解和冶炼步骤,旨在提高金的回收率同时考虑环境保护和经济效益的平衡。

四川党坝锂辉石矿Ⅵ号脉工艺矿物学及锂的赋存状态研究

党坝锂辉石矿床位于四川可尔因矿田的东南部,其Ⅵ号脉是矿区新发现的稀有金属伟晶岩脉,矿石研究程度低。为合理开发利用党坝锂辉石矿床锂资源并且为选矿工艺流程的制定提供理论依据,文章以党坝锂辉石矿床Ⅵ号脉锂辉石矿石为研究对象,采用显微镜下观察、电子探针(EPMA)、激光剥蚀等离子质谱(LA-ICP-MS)、X射线衍射分析(XRD)、矿物自动定量分析系统(TIMA)和矿物解离分析仪(MLA)等测试手段,开展了详细的工艺矿物学研究。结果显示,矿石中Li_(2)O含量为0.99%,锂辉石是主要的矿石矿物,脉石矿物主要为长石和石英,其次为云母。锂辉石晶体虽然粒度粗细不均,但是多集中在中粗粒范围内(320~1280μm),属于均匀较易解离矿石类型。矿石中锂主要赋存于锂辉石中,锂辉石中锂的配分比为97.80%,伴生有Nb、Be等有益组分且达到综合回收指标值。LA-ICP-MS实测锂辉石中Li_(2)O的平均含量为6.88%,锂辉石单矿物电子探针结果显示锂辉石中含有FeO(0.45%~0.73%),且少量Fe、Mn等杂质充填在锂辉石的解理、裂隙中,会一定程度上限制锂辉石精矿品级。

安徽某铜银铅多金属矿石工艺矿物学研究

为了更好地选别回收安徽某铜银铅多金属矿,对该矿石进行了工艺矿物学研究,查明了矿石的矿物组成、主要矿物的嵌布特征及铜、银、铅元素赋存状态。结果表明:矿石铜、银、铅品位分别为0.64%、116.63 g/t、0.20%,可回收的有用矿物主要为铜矿物,银可作为伴生元素进行回收,铅品位较低,只能作为杂质脱除;矿石主要铜矿物为斑铜矿、辉铜矿和黄铜矿,常常两者或3种矿物共生嵌布并形成不规则片状,三种铜矿物集合体的嵌布粒度粗细不均,在+0.07 mm粒级的分布率为44.60%;元素Cu主要赋存在斑铜矿中,分布率为79.37%,其次分布在辉铜矿和黄铜矿中,分布率分别为9.52%和6.35%;元素Ag主要赋存在辉银矿中,元素Pb主要赋存在方铅矿中。根据工艺矿物学研究结果,斑铜矿、辉铜矿和黄铜矿是回收的主要目的矿物,辉银矿主要分布在斑铜矿或黄铜矿中,因此大多辉银矿可与铜矿物一起得到回收。由于方铅矿相对易浮,大多方铅矿也会进入铜精矿中从而影响最终精矿品级,因此建议采用浮铜抑铅浮选工艺。

秘鲁某矽卡岩型难选铜钼矿石工艺矿物学研究

为制定合理的铜钼矿选矿工艺流程和选矿指标,采用光学显微镜、化学多元素分析、物相分析等分析测试手段对秘鲁某矽卡岩型难选铜钼矿进行了系统的工艺矿物学研究。研究结果表明,矿石主要有用元素为Cu和Mo,品位分别为0.58%和0.019%。矿石矿物组成复杂,主要有用矿物为黄铜矿、辉铜矿、辉钼矿等,脉石矿物为石英、长石、云母、蛇纹石、透闪石、绿泥石等。铜钼矿物嵌布粒度细小,且常沿黄铁矿或磁铁矿或脉石矿物的边缘、孔洞及裂隙分布,少量微细粒黄铜矿呈稀疏浸染状分布在脉石矿物中,嵌布关系复杂,影响铜钼矿的选矿回收。

矿石中关键金属钴赋存状态研究方法流程的建立:以庐枞盆地龙桥富钴矽卡岩铁矿床为例

关键金属钴的赋存状态是研究关键金属成矿作用的核心问题之一。由于含钴矿物粒度较小,难以在矿床尺度查明关键金属矿物的种类、含量、粒度、分布特征以及与其他矿石矿物和脉石矿物的共生关系,因此亟需建立一套成本低且效率高的钴赋存状态研究流程。本次工作以龙桥铁矿床为例,建立了新的采样与制样流程,提高了样品的代表性,并大幅缩短了样品前处理与制样的时间。通过综合矿物分析技术(TIMA)分析,查明了不同钴含量的三类矿石样品中矿物的含量,在6个实验矿石样品中寻找到了辉砷钴矿、铁硫砷钴矿和硫铜钴矿三种钴矿物共753颗,并使用扫描电镜和能谱分析(SEM-EDS)对钴矿物进行了核验与半定量分析。最后,在同一个树脂靶上利用激光剥蚀-等离子体质谱仪(LA-ICP-MS)对磁铁矿和黄铁矿进行了原位点分析,进一步查明了样品中钴的赋存状态。本次研究建立了关键金属钴在矿石中赋存状态的研究方法和技术流程,具有制样简单便捷、分析时间短、分析费用低和分析精度高等诸多优点,为矿床尺度上关键金属空间分布规律和赋存状态研究提供了可靠的技术支撑。

赣东北银山矿田铜矿石中伴生金赋存状态研究

银山多金属矿田可划分为铜和铅锌2个成矿系列。为深入了解银山矿田铜矿石中伴生金的赋存状态和主要矿石矿物的工艺特性,在实地考察和室内测试的基础上,采用岩矿鉴定和扫描电镜等技术手段,对银山矿田九区—西山区铜矿石工艺矿物学特性进行了研究。结果表明:金矿物赋存状态以包裹金(46.41%)为主,其次为粒间金(44.17%)和裂隙金(9.42%)。金矿物粒度以微粒金(94.61%)为主,辅以少量细粒金和中粒金,尚未发现粗粒金和巨粒金。金矿物中Au元素含量为75.87%~95.68%,Ag元素含量为4.32%~24.13%,Ag和Au元素含量比值为0.05~0.32。银山矿田金矿物以银金矿为主,含有少量自然金,金平均成色达到843.7。通过梳理伴生金的赋存状态,有助于优化矿石选矿流程,从而提高金的回收率,增加矿山经济效益。

甘肃某金矿石工艺矿物学研究

为高效合理利用碲化金矿石,通过化学多元素分析、MLA、扫描电镜等手段对甘肃某金矿石进行了系统的工艺矿物学研究。研究结果表明:该矿石中金主要以针碲金银矿形式存在,金矿物的嵌布粒度主要分布在0.037 mm以下;该矿石中主要金属硫化物为黄铁矿,主要脉石矿物为石英,且黄铁矿是主要载体矿物,金的赋存形态主要为黄铁矿粒间金、黄铁矿裂隙金及黄铁矿包裹金。该矿石含有一定量的易泥化矿物(如绢云母、绿泥石),浮选过程易随精矿产品一起上浮,降低精矿品位,且该矿石在浸出过程中具有难以溶解、不易解离的特点,需要在细磨、高碱度且大充气量的条件下才能实现有效回收利用。综合考虑,将该矿石磨至粒度-0.074 mm占95%时,可获得较佳的选矿指标。

甘肃某高硫高砷微细粒金矿石工艺矿物学研究

甘肃某地金矿石为典型的高硫高砷微细粒型难处理金矿石,为探明其工艺矿物学特性,采用化学多元素分析、矿物自动分析系统(MLA)、扫描电子显微镜(SEM)、能谱分析仪(EDS)等分析手段对化学组成、矿物组成、粒度组成、矿物赋存状态及嵌布特征等方面对矿石进行了研究。结果表明:矿石中主要含有Si、Fe、As、S、Au、Ag等元素,其中Au品位为3.75 g/t、Ag品位为110 g/t,具有综合回收价值;S含量为12.53%,As含量为8.40%。矿石中主要金属矿物有毒砂、黄铁矿等;非金属矿物主要为石英。金以自然金的形式存在且粒度微细,经统计的颗粒全部为显微金。外形形态主要以角粒状为主,其次为长角粒状;自然金多包裹于硫化物中(以黄铁矿为主,少量为毒砂),少量分布于黄铁矿裂隙中;矿石中银主要以独立矿物自然银、自然金存在,并嵌布于黝铜矿裂隙中。结合工艺矿物学研究结果综合分析得出结论:该矿石的分选难点在于自然金粒度微细、原矿中含有大量毒砂、自然金主要以包裹金形式存在、黄铁矿和毒砂嵌布密切、含有易泥化矿石。基于以上研究结果,推荐采用氧化焙烧—氰化浸出工艺进行分选。本文从矿物学的角度对甘肃某地高硫高砷金矿石进行了剖析,为该种类型矿物的高效开发利用提供了理论指导。

云南某金矿矿石工艺矿物学特征

利用化学分析、X射线衍射和光学显微镜等方法,系统研究了云南省某金矿的矿物学特征。结果表明,该矿石的金品位为3.55 g/t,伴生元素银为2.96 g/t,可综合回收。黄金矿产以天然金和银金为主,其细粒级分布特性复杂。金的主要载体矿物为黄铁矿等硫化物矿物,粒度也都很细,还有一些自然金以细小颗粒和微颗粒嵌入脉石矿物。通过浮选磨矿细度探索性试验,确定该矿样合适的磨矿细度为-0.045 mm含量占70%。试验研究结果为制定合理的选矿工艺提供了依据。

蚀变岩型低品位金矿中金的赋存状态量化研究

蚀变岩型金矿是一种重要的金矿石类型。采用化学分析、X射线衍射(XRD)、工艺矿物学参数自动分析系统(BPMA)、扫描电子显微镜(SEM)、X射线能谱(EDS)等技术,对胶东地区新立蚀变岩型金矿石中金的赋存状态进行量化研究。结果表明,矿石金品位为2.2 g/t,金属硫化物主要为黄铁矿(9.42%),含少量方铅矿(0.34%)和微量黄铜矿(0.05%)等;脉石矿物主要为石英(57.49%)和绢云母(23.31%),含少量钾长石(5.13%)等。金矿物为金-银互化物,其中银金矿占85.33%、金银矿占13.84%、自然金占0.83%;金矿物平均成色为620.8‰;载金矿物以黄铁矿为主,与黄铁矿存在镶嵌关系的金矿物占有率高达96.42%;金矿物在0~2 mm矿石综合样中以包裹金、粒间金为主,含少量裂隙金,其占有率分别为34.81%、34.73%和11.01%,并可见裸露连生金(19.39%)和微量单体金(0.06%);金矿物粒度分布不均匀,粗粒金(>74μm)、中粒金(74~37μm)、细粒金(37~10μm)、微粒金(<10μm)的占有率分别为30.56%、12.96%、46.84%和9.64%;黄铁矿的嵌布粒度较粗,主要呈中粒—粗粒嵌布,易于解离,有利于浮选。研究表明,浮选富集黄铁矿等硫化物可以有效富集金矿物,对精矿再磨,有利于金的回收;同时应注意对粗粒金的回收。

四川某金矿矿石工艺矿物学特征研究

为了查明四川某金矿矿石的工艺矿物学特征,采用化学分析、偏光显微镜下鉴定、AMICS、电子探针等手段,对该矿石进行了系统的工艺矿物学研究。结果表明:矿石中金品位为2.40 g/t,金属矿物主要为黄铁矿、磁铁矿、毒砂,脉石矿物主要为石英、白云母、铁菱镁矿、高岭石等;矿石中的金主要以不可见金的形式分布在黄铁矿和毒砂中,占83.75%,其中黄铁矿也普遍含有少量的砷;少量金以独立金矿物的形式存在,占16.25%,主要为银金矿,少量为自然金和金银矿,嵌布粒度很细,且和硫化物的共生关系紧密。因此,该矿不宜直接采用氰化浸出的方式回收金,需采用选冶结合的方法,即全硫化物浮选—金精矿氧化预处理—湿法冶金提金工艺。