Ore-proportioning optimization technique with high proportion of Yandi ore in sintering

The basic sintering characteristics of Yandi ore from Australia, including assimilation ability, liquid phase fluidity, self-strength of bonding phase, forming ability of silico ferrite of calcium and aluminum （SFCA）, and so on, were investigated in detail. Besides, the high temperature behavior and function of sintering were obtained. As a result, the techniques for ore-proportioning in sintering were obtained. The results show that Yandi ore possessing higher assimilation ability, better liquid phase fluidity, lower self-strength of bonding phase, and better forming ability of SFCA, should be mixed with iron ores whose properties are opposite to those of Yandi ore. In the optimization of sintering ore-proportioning, Yandi ore, whose price is relatively low, can be mixed as high as 40wt%.

Reduction of NO_(x)emission based on optimized proportions of mill scale and coke breeze in sintering process

Reducing NO_(x) emission of iron ore sintering process in a cost effective manner is a challenge for the iron and steel industry at present.Effects of the proportion of mill scale and coke breeze on the NO_(x) emission,strength of sinter,and sinter indexes were studied by com-bustion and sinter pot tests.Results showed that the peak value of NO concentration,total of NO emission,and fuel-N conversion rate gradu-ally decreased as the proportions of the mill scale increased because NO was reduced to N_(2) by Fe_(3)O_(4),FeO,and Fe in the mill scale.The strength of sinter reached the highest value at 8.0wt%mill scale due to the formation of minerals with low melting point.The fuel-N conver-sion rate slightly fluctuated and total NO_(x) emission significantly decreased with the decreased proportions of coke breeze because CO forma-tion and content of N element in the sintered mixture decreased.However,the sinter strength also decreased due to the decrease in the amount of the melting minerals.Furthermore,results of the sinter pot tests indicated that NO_(x) emission decreased.The sinter indexes performed well when the proportions of mill scale and coke breeze were 8.0wt%and 3.70wt%respectively in the sintered mixture.

Comprehensive evaluation of sintering basic characteristics of iron ore based on grey relational analysis

Sintering basic characteristics of fourteen iron ores were comprehensively evaluated using micro-sinter and grey relational analysis methods. The results show that magnetite has a low assimilability, high bonding phase strength, and high crystal strength. Hematite presents a good assimilability, while limonite exhibits a strong assimilability, but the bonding phase strength and crystal strength of these two kinds of iron ores are comparatively low. Great difference in liquid flowability exists for the same kind of iron ores. When the assimilation temperature of the sinter mixture is too high, limonite can be added;when the bonding phase strength or crystal strength of the sinter mixture is too low, magnetite can be added. The liquid fluidity of the sinter mixture can be adjusted according to the ratios of corresponding iron ores. Grey relational analysis is an effective method to evaluate the comprehensive sintering characteristics of iron ores, which can provide theoretical basis for the purchasing department of the steel enterprises.