Pulsed electrochemical machining(PECM)has attracted increasing interest as a technique to improve material dissolution localization and surface quality.This work systematically investigates the effects of pulse curren...Pulsed electrochemical machining(PECM)has attracted increasing interest as a technique to improve material dissolution localization and surface quality.This work systematically investigates the effects of pulse current on the surface morphology,profile accuracy,and corrosion behavior of Inconel 718(IN718)in NaNO_(3)solution.Polarization behavior reveals that IN718 in NaNO_(3)solution during pulse current machining exhibited significant passive,transpassive,and re-passive characteristics.The passive film generated at the re-passive state contained some oxides and had a loose porous structure.The critical value for the quantity of electric charge to rupture the passive film was determined to be 26.88℃cm^(−2).The current efficiency indicates that the material removal rate of IN718 in NaNO_(3)solution during pulse current machining was nonlinear.The PECM experiments indicate that the loading process of the electrical double layer was prolonged with an increased workpiece scale,i.e.,the loading process of the electrical double layer lasted for the entire pulse-on time when the workpiece scale was 100 mm^(2)at a frequency of more than 10 kHz regardless of the duty cycle.A pulse current with a short pulse length and short pulse period improved the profile accuracy,as did the low applied voltage and small workpiece scale.The dissolution mechanism of IN718 in NaNO_(3)solution was also investigated based on the effective pulse current time.Finally,the leading-edge structure of a ruled blade with good dimensional accuracy and surface quality was successfully fabricated.The maximum deviations of the machined profile were effectively restricted within 0.057 mm,and the surface roughness was Ra=0.358μm.展开更多
Machining of micro holes with micro electro- chemical machining （micro ECM） process has been carried out with an indigenously developed set up. This paper describes relevant problems and solutions for the circular m...Machining of micro holes with micro electro- chemical machining （micro ECM） process has been carried out with an indigenously developed set up. This paper describes relevant problems and solutions for the circular micro holes machining process on 304 stainless steel sheets with 60 μm thickness using high speed steel cylindrical tool of diameter 500 ~tm and using dilute I-I2SO4 as elec- trolyte. The taper angle variation of the machined hole is analyzed and reported for different experimental setting parameters. The minimum value of the taper angle of machined holes is achieved at the parameter setting of 0.4 mol/L H2504, 700 kHz, 600 ns and 21 V, for stainless steel sheets and HSS tool.展开更多
基金supported by the National Natural Science Foundation of China (Grant No. 91960204)the National Natural Science Foundation of China for Creative Research Groups (Grant No. 51921003)the Postgraduate Research & Practice Innovation Program of Jiangsu Province (Grant No. KYCX21_0191)
文摘Pulsed electrochemical machining(PECM)has attracted increasing interest as a technique to improve material dissolution localization and surface quality.This work systematically investigates the effects of pulse current on the surface morphology,profile accuracy,and corrosion behavior of Inconel 718(IN718)in NaNO_(3)solution.Polarization behavior reveals that IN718 in NaNO_(3)solution during pulse current machining exhibited significant passive,transpassive,and re-passive characteristics.The passive film generated at the re-passive state contained some oxides and had a loose porous structure.The critical value for the quantity of electric charge to rupture the passive film was determined to be 26.88℃cm^(−2).The current efficiency indicates that the material removal rate of IN718 in NaNO_(3)solution during pulse current machining was nonlinear.The PECM experiments indicate that the loading process of the electrical double layer was prolonged with an increased workpiece scale,i.e.,the loading process of the electrical double layer lasted for the entire pulse-on time when the workpiece scale was 100 mm^(2)at a frequency of more than 10 kHz regardless of the duty cycle.A pulse current with a short pulse length and short pulse period improved the profile accuracy,as did the low applied voltage and small workpiece scale.The dissolution mechanism of IN718 in NaNO_(3)solution was also investigated based on the effective pulse current time.Finally,the leading-edge structure of a ruled blade with good dimensional accuracy and surface quality was successfully fabricated.The maximum deviations of the machined profile were effectively restricted within 0.057 mm,and the surface roughness was Ra=0.358μm.
文摘Machining of micro holes with micro electro- chemical machining （micro ECM） process has been carried out with an indigenously developed set up. This paper describes relevant problems and solutions for the circular micro holes machining process on 304 stainless steel sheets with 60 μm thickness using high speed steel cylindrical tool of diameter 500 ~tm and using dilute I-I2SO4 as elec- trolyte. The taper angle variation of the machined hole is analyzed and reported for different experimental setting parameters. The minimum value of the taper angle of machined holes is achieved at the parameter setting of 0.4 mol/L H2504, 700 kHz, 600 ns and 21 V, for stainless steel sheets and HSS tool.