The effect of adding RE to plating bath on microstructure and corrosion resistance of Ni-Co alloy coatings prepared by pulse reversal current electrodeposition was studied by means of SEM/EDS, electrochemical analysis...The effect of adding RE to plating bath on microstructure and corrosion resistance of Ni-Co alloy coatings prepared by pulse reversal current electrodeposition was studied by means of SEM/EDS, electrochemical analysis and corrosion mass loss etc. The results show that adding proper RE to plating solution can promote the microstructure of coatings compacter, the surface smoother and the crystal finer, and improve the corrosion resistance. The coatings exhibite the highest corrosion resistance when the concentration of RE reaches 0.25 g·L -1. The reason of increasing corrosion resistance by adding RE was also investigated.展开更多
The poor corrosion resistance of biodegradable magnesium alloys is the dominant factor that limits theirclinical application. In this study, to deal with this challenge, fluoride coating was prepared on MgeZneCa alloy...The poor corrosion resistance of biodegradable magnesium alloys is the dominant factor that limits theirclinical application. In this study, to deal with this challenge, fluoride coating was prepared on MgeZneCa alloy as the inner coating and then hydroxyapatite (HA) coating as the outer coating was depositedon fluoride coating by pulse reverse current electrodeposition (PRC-HA/MgF2). As a comparative study,the microstructure and corrosion properties of the composite coating with the outer coating fabricatedby traditional constant current electrodeposition (TED-HA/MgF2) were also investigated. Scanningelectron microscopy (SEM) images of the coatings show that the morphology of PRC-HA/MgF2 coating isdense and uniform, and presents nano-rod-like structure. Compared with that of TED-HA/MgF2, thecorrosion current density of Mg alloy coated with PRC-HA/MgF2 coatings decreases from 5.72× 10^-5 A/cm2 to 4.32× 10^-7 A/cm^2, and the corrosion resistance increases by almost two orders of magnitude. Inimmersion tests, samples coated with PRC-HA/MgF2 coating always show the lowest hydrogen evolutionamount, and could induce deposition of the hexagonal structure-apatite on the surface rapidly. Theresults show that the corrosion resistance and the bioactivity of the coatings have been improved byadopting double-pulse current mode in the process of preparing HA on fluoride coating, and the PRC-HA/MgF2 coating is worth of further investigation.展开更多
文摘The effect of adding RE to plating bath on microstructure and corrosion resistance of Ni-Co alloy coatings prepared by pulse reversal current electrodeposition was studied by means of SEM/EDS, electrochemical analysis and corrosion mass loss etc. The results show that adding proper RE to plating solution can promote the microstructure of coatings compacter, the surface smoother and the crystal finer, and improve the corrosion resistance. The coatings exhibite the highest corrosion resistance when the concentration of RE reaches 0.25 g·L -1. The reason of increasing corrosion resistance by adding RE was also investigated.
基金We are grateful for the financial support of the National Hightech Research and Development Projects(863)(2015AA033603,2015AA020301)the National Key Research and Development Program of China(2016YFC1102403)the Major Science and Technology Projects in Henan Province(141100310900).
文摘The poor corrosion resistance of biodegradable magnesium alloys is the dominant factor that limits theirclinical application. In this study, to deal with this challenge, fluoride coating was prepared on MgeZneCa alloy as the inner coating and then hydroxyapatite (HA) coating as the outer coating was depositedon fluoride coating by pulse reverse current electrodeposition (PRC-HA/MgF2). As a comparative study,the microstructure and corrosion properties of the composite coating with the outer coating fabricatedby traditional constant current electrodeposition (TED-HA/MgF2) were also investigated. Scanningelectron microscopy (SEM) images of the coatings show that the morphology of PRC-HA/MgF2 coating isdense and uniform, and presents nano-rod-like structure. Compared with that of TED-HA/MgF2, thecorrosion current density of Mg alloy coated with PRC-HA/MgF2 coatings decreases from 5.72× 10^-5 A/cm2 to 4.32× 10^-7 A/cm^2, and the corrosion resistance increases by almost two orders of magnitude. Inimmersion tests, samples coated with PRC-HA/MgF2 coating always show the lowest hydrogen evolutionamount, and could induce deposition of the hexagonal structure-apatite on the surface rapidly. Theresults show that the corrosion resistance and the bioactivity of the coatings have been improved byadopting double-pulse current mode in the process of preparing HA on fluoride coating, and the PRC-HA/MgF2 coating is worth of further investigation.