Pyrolysis of biomass followed by combustion of pyrolytic vapors to replace fossil fuels is an economic low-carbon solution.However,the polycyclic aromatic hydrocarbons and N-containing species in biomass pyrolysis vapors result in the soot and NO emissions.The flue gas recirculation(FGR)technology,having the potential to reduce the soot and NO emissions,was introduced to the biomass pyrolysis-combustion system.In addition,it was numerically studied by simulating the biomass pyrolysis vapors based co-flow diffusion flames with CO_(2)addition.Both the experimental and simulated results showed that the FGR had significant suppression effects on the soot formation.When the FGR ratio(i.e.,CO_(2)addition ratio)increased from 0%to 15%,the experimental and simulated soot volume fraction respectively decreased by 32%and 21%,which verified the models used in this study.The decrease in OH concentration caused by the CO_(2)addition was responsible for the decrease in the decomposition rate of A2(A2+OH=A2–+H_(2)O).Hence,more benzo(ghi)fluoranthene(BGHIF)was generated through A1C_(2)H–+A2→BGHIF+H_(2)+H,leading to the increase in inception rate.The decrease in benzo(a)pyrene(BAPYR)concentration was the major factor in the decrease in soot condensation rate.Moreover,the decrease in the C_(2)H_(2) and OH concentrations was responsible for the decrease in the HACA surface growth rate.Furthermore,the simulated results showed that the NO concentration decreased by 0.4%when the content of CO_(2)was increased by 1 vol.%.The decrease in OH concentration suppressed the NO formation via decreasing reaction rates of N+OH=NO+H and HNO+OH=NO+H_(2)O and enhanced the NO consumption via increasing reaction rate of HO_(2)+NO=NO_(2)+OH.

Mechanical Properties and Oxidation Behaviors of Self-Healing SiCf/SiC-SiBCN Composites Exposed to H_(2)O/O_(2)/Na_(2)SO_(4)Environments

The oxidation behaviors and their influence on the mechanical properties of self-healing SiCf/SiC-SiBCN composites were investigated in H_(2)O/O_(2)and H_(2)O/O_(2)/Na_(2)SO_(4)environments at 1200‒1350℃for 100 h.As the temperatures increase from 1200 to 1350℃,the oxidation rate constants increase from 0.45×10^(–7)to 1.58×10^(–7)mg^(2)/(mm^(4) h)in H_(2)O/O_(2),and from 1.02×10^(–7)to 3.42×10^(–7)mg^(2)/(mm^(4) h)in H_(2)O/O_(2)/Na_(2)SO_(4).The involvement of Na_(2)SO_(4)leads to the formation of a loose lamellar oxide layer,the breakage of the SiBCN/CVI-SiC interface and the decrease in the oxide viscosity,thus accelerating the oxidation of the composites.The composites show the maximum retention rate of strength(102%,535.71 MPa)after oxidation in H_(2)O/O_(2)at 1200℃due to the good self-healing capacity of the produced glass,while the minimum(82%,430.56 MPa)in H_(2)O/O_(2)/Na_(2)SO_(4)at 1350℃caused by the severe microstructural corrosion derived from Na_(2)SO_(4).