Effects of rare earth element La on the microstructure of Cumatrix diamond tools were researched under the conditions of variousmaterials components and the process parameters in order to improvematerials properties. ...Effects of rare earth element La on the microstructure of Cumatrix diamond tools were researched under the conditions of variousmaterials components and the process parameters in order to improvematerials properties. SEM, XPS and X-ray were used to investigate thefracture section, microstructure and the element valence inmaterials. The Results shown that the combination of rare earthelement La and transition element Ti is advantageous to the bondingstate Between diamond particles and matrix, so it can improve thematerials properties. Suitable sintering temperature is 790 deg. C.展开更多
The Cu-Mn catalysts doped with different amounts of lanthanum（La） for water-gas shift reaction（WGSR） were prepared, and characterized by X-ray diffraction（XRD）, temperature-programmed reduction（TPR）, temperatu...The Cu-Mn catalysts doped with different amounts of lanthanum（La） for water-gas shift reaction（WGSR） were prepared, and characterized by X-ray diffraction（XRD）, temperature-programmed reduction（TPR）, temperature-programmed reduction of oxidized surfaces（s-TPR）, temperature-programmed desorption of CO_2（CO_2-TPD）, infrared spectrum（FT-IR） and X-ray photoelectron spectroscopy（XPS）. Catalytic activities were tested for a water-gas shift reaction. The results showed that the introduction of 0.5 mol.% La could significantly improve the catalyst activity for low-temperature shift reaction compared with the undoped catalyst, which might be from the introduction of La making the Cu and Mn components distribute uniformly and the synergistic effect between Cu and Mn increasing the dispersion of Cu on the surface of the catalyst. The apparent CuO phases besides Cu_（1.5）Mn_（1.5）O_4 were found in the samples with at least 3.0 mol.% La content, and the basic sites increased with the increasing of La contents at a decreased rate. With excessive La doping, La particles would aggregate and cover some active sites, resulting in that Mn could not effectively inhibit the gathering together and growing up of Cu crystalline grain, and decreased the dispersion of Cu on the surface, which resulted in the poor activity of the catalyst for WGSR.展开更多
As an interconnector of solid oxide fuel cell, La 1-x Ca x CrO 3( x =0 0～0 5) were prepared by sol gel method. The crystal structures of La 1-x Ca x CrO 3 at room temperature are the or...As an interconnector of solid oxide fuel cell, La 1-x Ca x CrO 3( x =0 0～0 5) were prepared by sol gel method. The crystal structures of La 1-x Ca x CrO 3 at room temperature are the orthorhombic perovskite GdFeO 3 type. XPS analysis indicates that chrome ions are in different valence state. The introduction of Ca 2+ into the lattice induces the oxidation of Cr 3+ to Cr 6+ . With x increasing, the amount of Cr 6+ increases. The present of the more Cr 6+ is one of the important factors that effect electric conductivity of La 1-x Ca x CrO 3.展开更多
Samples of manganese oxides La（1-x）2/3Ca1/3MnO3（x 〈 0.10） with Lavacancy were prepared by standard solid-state reaction method. All the samples are single phase, with orthorhombic symmetry （Pnma ）, analyzed by ...Samples of manganese oxides La（1-x）2/3Ca1/3MnO3（x 〈 0.10） with Lavacancy were prepared by standard solid-state reaction method. All the samples are single phase, with orthorhombic symmetry （Pnma ）, analyzed by XRD and with Rietveld Refinement. The effect of different La-site vacancies concentration on electronic transport of La（1-x）2/3Ca1/3MnO3 was investigated. The insulator-metal transition temperature （about 267 K） nearly remains unchanged with the increase of vacancy concentration, which indicates that small La-vacancy does not destroy the double exchange interaction. But the electronic resistance increases and MR value decreases with La-vacancy content x 〉 0.04. The maximum of the MR value （8 T） is about 220% at transition temperature （TMI）.展开更多
Rare earth doped B2O3-Al2O3-SiO2 glass （RExBAS, x=5, 10, 20; RE=La, Sm） were prepared by solid state reaction method. Optical transmission spectra of such glass were characterized by ultraviolet spectrometers, and 1...Rare earth doped B2O3-Al2O3-SiO2 glass （RExBAS, x=5, 10, 20; RE=La, Sm） were prepared by solid state reaction method. Optical transmission spectra of such glass were characterized by ultraviolet spectrometers, and 1064 nm laser induced damage performance was investigated through the method of ＂1-on-1＂. The results indicated that there was a strong absorptive peak near 1064 nm in SmxBAS glass, the peak was enhanced with increasing x. While LaxBAS glass was transparent to 1064 nm laser, at the same time, the results of laser induced damage showed that the anti-laser induced damage performance of such glass was strengthened with the addition of rare earth oxide. Furthermore, the laser induced damage threshold （LIDT） of SmxBAS glass was significantly higher than that of LaxBAS glass. Consequently, Sm^3＋ doping was favor in the improvement of anti-laser induced damage performance for BAS glass.展开更多
文摘Effects of rare earth element La on the microstructure of Cumatrix diamond tools were researched under the conditions of variousmaterials components and the process parameters in order to improvematerials properties. SEM, XPS and X-ray were used to investigate thefracture section, microstructure and the element valence inmaterials. The Results shown that the combination of rare earthelement La and transition element Ti is advantageous to the bondingstate Between diamond particles and matrix, so it can improve thematerials properties. Suitable sintering temperature is 790 deg. C.
基金Project supported by the National Natural Science Foundation of China(21266017,21566028,21566029)Research Fund for the Doctoral Program of Higher Education of China(20111514110001)Inner Mongolia Natural Science Foundation(2014MS0220,2015BS0206)
文摘The Cu-Mn catalysts doped with different amounts of lanthanum（La） for water-gas shift reaction（WGSR） were prepared, and characterized by X-ray diffraction（XRD）, temperature-programmed reduction（TPR）, temperature-programmed reduction of oxidized surfaces（s-TPR）, temperature-programmed desorption of CO_2（CO_2-TPD）, infrared spectrum（FT-IR） and X-ray photoelectron spectroscopy（XPS）. Catalytic activities were tested for a water-gas shift reaction. The results showed that the introduction of 0.5 mol.% La could significantly improve the catalyst activity for low-temperature shift reaction compared with the undoped catalyst, which might be from the introduction of La making the Cu and Mn components distribute uniformly and the synergistic effect between Cu and Mn increasing the dispersion of Cu on the surface of the catalyst. The apparent CuO phases besides Cu_（1.5）Mn_（1.5）O_4 were found in the samples with at least 3.0 mol.% La content, and the basic sites increased with the increasing of La contents at a decreased rate. With excessive La doping, La particles would aggregate and cover some active sites, resulting in that Mn could not effectively inhibit the gathering together and growing up of Cu crystalline grain, and decreased the dispersion of Cu on the surface, which resulted in the poor activity of the catalyst for WGSR.
文摘As an interconnector of solid oxide fuel cell, La 1-x Ca x CrO 3( x =0 0～0 5) were prepared by sol gel method. The crystal structures of La 1-x Ca x CrO 3 at room temperature are the orthorhombic perovskite GdFeO 3 type. XPS analysis indicates that chrome ions are in different valence state. The introduction of Ca 2+ into the lattice induces the oxidation of Cr 3+ to Cr 6+ . With x increasing, the amount of Cr 6+ increases. The present of the more Cr 6+ is one of the important factors that effect electric conductivity of La 1-x Ca x CrO 3.
文摘Samples of manganese oxides La（1-x）2/3Ca1/3MnO3（x 〈 0.10） with Lavacancy were prepared by standard solid-state reaction method. All the samples are single phase, with orthorhombic symmetry （Pnma ）, analyzed by XRD and with Rietveld Refinement. The effect of different La-site vacancies concentration on electronic transport of La（1-x）2/3Ca1/3MnO3 was investigated. The insulator-metal transition temperature （about 267 K） nearly remains unchanged with the increase of vacancy concentration, which indicates that small La-vacancy does not destroy the double exchange interaction. But the electronic resistance increases and MR value decreases with La-vacancy content x 〉 0.04. The maximum of the MR value （8 T） is about 220% at transition temperature （TMI）.
基金the Natural Science Fund of Jangsu Provinence (BK2004121) Trans-Century Training Programme Foundation for the Talents by the Chinese Ministry of Education
文摘Rare earth doped B2O3-Al2O3-SiO2 glass （RExBAS, x=5, 10, 20; RE=La, Sm） were prepared by solid state reaction method. Optical transmission spectra of such glass were characterized by ultraviolet spectrometers, and 1064 nm laser induced damage performance was investigated through the method of ＂1-on-1＂. The results indicated that there was a strong absorptive peak near 1064 nm in SmxBAS glass, the peak was enhanced with increasing x. While LaxBAS glass was transparent to 1064 nm laser, at the same time, the results of laser induced damage showed that the anti-laser induced damage performance of such glass was strengthened with the addition of rare earth oxide. Furthermore, the laser induced damage threshold （LIDT） of SmxBAS glass was significantly higher than that of LaxBAS glass. Consequently, Sm^3＋ doping was favor in the improvement of anti-laser induced damage performance for BAS glass.