The rare earth ion Yb^3+ doped Bi2WO6 photocatalysts were synthesized by hydrothermal method.Moreover,XRD,XPS,FESEM,TEM,Ramam,N2 adsorption-desorption isotherm measurements and UV-vis diffusion reflectance spectra wer...The rare earth ion Yb^3+ doped Bi2WO6 photocatalysts were synthesized by hydrothermal method.Moreover,XRD,XPS,FESEM,TEM,Ramam,N2 adsorption-desorption isotherm measurements and UV-vis diffusion reflectance spectra were used to characterize the Yb^3+ doped Bi2WO6 photocatalysts.The morphology,specific surface area,and pore volume distribution were greatly affected after Yb3+ ions doping.Photocatalytic performance of Bi2WO6 was effectively enhanced after Yb3+ ions doping,6% Yb^3+ doped Bi2WO6 had the best photocatalytic performance,and 96.2% Rhodamine B was degradated after irradiated 30 min,which was 1.29 times that of the pristine one.The enhanced photocatalytic performance was due to the increased specific surface area,decreased energy band gap and inhibition of photoelectron-hole recombination after Yb3+ ions doping.展开更多
Ca1-xRxCu3Ti4O12(R=La,Y,Gd;x=0,0.1,0.2,0.3) electronic ceramics were fabricated by conventional solid-state reaction method.The microstructure and dielectric properties as well as impedance behavior were carefully inv...Ca1-xRxCu3Ti4O12(R=La,Y,Gd;x=0,0.1,0.2,0.3) electronic ceramics were fabricated by conventional solid-state reaction method.The microstructure and dielectric properties as well as impedance behavior were carefully investigated.XRD results showed that the secondary phases with the general formula R2Ti2O7 existed at grain boundaries of rare earth doped ceramics,which inhibited abnormal grain growth.The dielectric constant decreased from 4×105 in pure CaCu3Ti4O12(CCTO) ceramics to 2×103 with rare earth doping....展开更多
LiFe0.99RE0.01PO4/C cathode material was synthesized by solid-state reaction method using FeC2O4-2H2O, Li2CO3, NH4H2PO4, RE（NO3）3·nH2O as raw materials and glucose as a carbon source. The doping effects of rare...LiFe0.99RE0.01PO4/C cathode material was synthesized by solid-state reaction method using FeC2O4-2H2O, Li2CO3, NH4H2PO4, RE（NO3）3·nH2O as raw materials and glucose as a carbon source. The doping effects of rare earth ions, such as La3＋, Ce3＋, Nd3＋, on the structure and electrochemical properties of LiFePO4/C cathode material were systematically investigated. The as-prepared samples were characterized by means of X-ray diffraction （XRD）, scanning electron microscopy （SEM） and particle size analysis. The electrochemical properties were investigated in terms of constant-current charge/discharge cycling tests. The XRD results showed that the rare earth ions doping did not change the olivine structure of LiFePO4, and all the doped samples were of single-phase with high crystallinity. SEM and particle size analysis results showed that the doping of La3＋, Ce3＋ and Nds＋ led to the decrease of particle size. The electrochemical results exhibited that the doping of La3＋ and Ce3＋ could improve the high-rate capability of LiFePO4/C cathode material, among which, the material doped with 1% Ce3＋ exhibited the optimal electrochemical properties, whose specific discharge capacities could reach 128.9, 119.5 and 104.4 mAh/g at 1C, 2C and 5C rates, respectively.展开更多
The synthesis of co-doped KEu0.01Gd0.19Yb0.8（WO4）2 was achieved by a modified Pechini method at 750℃. The structure of obtained compound was confirmed using X-ray diffraction measurement and Raman spectroscopy. Th...The synthesis of co-doped KEu0.01Gd0.19Yb0.8（WO4）2 was achieved by a modified Pechini method at 750℃. The structure of obtained compound was confirmed using X-ray diffraction measurement and Raman spectroscopy. The Scherrer＇s formula was used to confirm the grain sizes visualized by TEM technique. The grain sizes of about 100 nm of monoclinic KGW were successfully obtained by this meth- odology. In order to study spectroscopic properties of the prepared system the emission spectra were measured. The effective down- and up-conversion processes in non-resonant system were investigated.展开更多
基金the National Natural Science Foundation of China(No.51662005)。
文摘The rare earth ion Yb^3+ doped Bi2WO6 photocatalysts were synthesized by hydrothermal method.Moreover,XRD,XPS,FESEM,TEM,Ramam,N2 adsorption-desorption isotherm measurements and UV-vis diffusion reflectance spectra were used to characterize the Yb^3+ doped Bi2WO6 photocatalysts.The morphology,specific surface area,and pore volume distribution were greatly affected after Yb3+ ions doping.Photocatalytic performance of Bi2WO6 was effectively enhanced after Yb3+ ions doping,6% Yb^3+ doped Bi2WO6 had the best photocatalytic performance,and 96.2% Rhodamine B was degradated after irradiated 30 min,which was 1.29 times that of the pristine one.The enhanced photocatalytic performance was due to the increased specific surface area,decreased energy band gap and inhibition of photoelectron-hole recombination after Yb3+ ions doping.
基金supported by the National Basic Research Program of China (973) (2007CB31407)Foundation for Innovative Research Groups of the NSFC (60721001)+1 种基金the Young Fund of Sichuan Province (08ZQ026-013)the National Natural Science Foundation of China (50972023, 50872078)
文摘Ca1-xRxCu3Ti4O12(R=La,Y,Gd;x=0,0.1,0.2,0.3) electronic ceramics were fabricated by conventional solid-state reaction method.The microstructure and dielectric properties as well as impedance behavior were carefully investigated.XRD results showed that the secondary phases with the general formula R2Ti2O7 existed at grain boundaries of rare earth doped ceramics,which inhibited abnormal grain growth.The dielectric constant decreased from 4×105 in pure CaCu3Ti4O12(CCTO) ceramics to 2×103 with rare earth doping....
基金Technology Innovation Foundation Project for Outstanding Youth of Hebei Uninversity of Technology for financial support
文摘LiFe0.99RE0.01PO4/C cathode material was synthesized by solid-state reaction method using FeC2O4-2H2O, Li2CO3, NH4H2PO4, RE（NO3）3·nH2O as raw materials and glucose as a carbon source. The doping effects of rare earth ions, such as La3＋, Ce3＋, Nd3＋, on the structure and electrochemical properties of LiFePO4/C cathode material were systematically investigated. The as-prepared samples were characterized by means of X-ray diffraction （XRD）, scanning electron microscopy （SEM） and particle size analysis. The electrochemical properties were investigated in terms of constant-current charge/discharge cycling tests. The XRD results showed that the rare earth ions doping did not change the olivine structure of LiFePO4, and all the doped samples were of single-phase with high crystallinity. SEM and particle size analysis results showed that the doping of La3＋, Ce3＋ and Nds＋ led to the decrease of particle size. The electrochemical results exhibited that the doping of La3＋ and Ce3＋ could improve the high-rate capability of LiFePO4/C cathode material, among which, the material doped with 1% Ce3＋ exhibited the optimal electrochemical properties, whose specific discharge capacities could reach 128.9, 119.5 and 104.4 mAh/g at 1C, 2C and 5C rates, respectively.
文摘The synthesis of co-doped KEu0.01Gd0.19Yb0.8（WO4）2 was achieved by a modified Pechini method at 750℃. The structure of obtained compound was confirmed using X-ray diffraction measurement and Raman spectroscopy. The Scherrer＇s formula was used to confirm the grain sizes visualized by TEM technique. The grain sizes of about 100 nm of monoclinic KGW were successfully obtained by this meth- odology. In order to study spectroscopic properties of the prepared system the emission spectra were measured. The effective down- and up-conversion processes in non-resonant system were investigated.