Microstructure of Steel 5Cr21Mn9Ni4N Alloyed by Rare Earth

The microstructure, composition and shape of precipitated phase under as-cast and finished product state of 5Cr21Mn9Ni4N steel with different rare earth （RE） amount were studied. Mechanical properties of 5Cr21Mn9Ni4N steels withont RE addition and with RE added by 0. 2% in mass percent were tested respectively. The results indicate that the solid solution amount of RE is about 10^-6 -10^-5 order of magnitude in 5Cr21Mn9Ni4N steel. Dendrite of as-cast condition is refined obviously and dimension of interstitial phase is shortened when RE is added by 0.10%-0.20%. But the microstructure will be coarser if surplus RE is added. Precipitated phase under finished product state distributes evenly in nearly same size with RE added by 0. 2% which leads to a largely improved high temperature mechanical property.

Observation and Analysis of the Microstructure in CarburizedSurface Layer of Steel 20Cr2Ni4A Treated with ConventionalAnd Rare Earth Carburizing Processes

Observation and analysis with TEM show that the fine granular dispersed carbides in hypereutectoid zone of steel 20Cr2Ni4A are distributed in the matrix of large number of lath martensite after rare earth carburizing. But while treating by conventional carburization and double quench hardening the retained carbides are finer and more dispersive, and its matrix is perfectly twin martersite. The different micrcotructures of matrix around carbide are formed with different kinds of carburization processes.

Rare earth and silane as chromate replacers for corrosion protection on galvanized steel

The present work aimed at using rare earth lanthanum salt and trimethoxy（viny）silance as chromate substitutes for galvanized steel passivation, in contrast to zinc coating samples treated with chromate.The corrosion resistance was assessed by electrochemical impedance spectroscopy（EIS） and neutral salt spray tests（NSS）.Scanning electron microscopy（SEM） was used to characterize the sample surfaces.The organic coating adhesion on the panel was also investigated via varnishes-cross cut tests.The results indicated that rare earth and silane two-step treatment gave more effective anticorrosion performance than Cr, which also provided good paint adhesion.The coating formation mechanism was also discussed.

Effect of Rare Earth on Thermal Shock Resistance of Steel 9Cr2Mo

The effect of rare earth elements on thermal shock resistance of cold roller steel 9Cr2Mo was investigated by means of X-ray diffractometry and optical microscopy. Experimental results show that the process of carbide precipitation of heat effect zone is restrained by adding RE elements in steel 9Cr2Mo. Therefore, thermal shock resistance of this steel can be improved.

Effect of Rare Earth Elements on Quenching Crack Resistance of Steel 9Cr2Mo

The effect of rare earth elements on quenching crack resistance of steel 9Cr2Mo was investigated by means of scanning electron microscopy (SEM) and optical microscopy. Experimental results show that, by adding RE elements to steel 9Cr2Mo, the number of quenching for crack initiation is increased. Meanwhile the propagation of quenching cracks is postponed and the paths of crack propagation are changed. Therefore, quenching crack resistance can be improved by adding RE elements to steel 9Cr2Mo.

Effect of Rare Earth Elements on Low Frequency Fatigue Cyclic Softening of Hot Rolled Steel 60CrMnMo at High Temperature

The effect of rare earth (RE) on cyclic softening of low frequency fatigue of the hot rolled steel 60CrMnMo at high temperature was investigated. The hardness of specimens before thermal fatigue test and being cycled 180 times from room temperature to 650℃ was compared. The results show that by adding a certain amount of RE in steel 60CrMnMo, the cyclic softening during low frequency fatigue test at high temperature can be restrained considerly. The carbide particles were refined during tempering treatment and the agglomeration and growth of carbide particles can be obstructed during thermal cycle.

Effect of CeO_2 on heat transfer and crystallization behavior of rare earth alloy steel mold fluxes

To improve the heat transfer capability and the crystallization property of the traditional mold flux, CaF_2 was replaced with B_2O_3. Then, the influences of CeO_2 on the heat transfer and the crystallization of the CaF_2-bearing mold flux and the new mold flux with 10 wt% B_2O_3 were studied using a slag film heat flux simulator and X-ray diffraction(XRD). The results revealed that the addition of CeO2 reduced the heat transfer by increasing the solid slag thickness and the crystallization of two mold fluxes. However, CeO_2 had less effect on the B_2O_3-containing mold flux compared with the CaF_2-bearing mold flux. According to the analyses, the CeO_2 contents in the CaF_2-bearing mold flux and the B_2O_3-containing mold flux should not exceed 8 wt% and 12 wt%, respectively. Therefore, these experimental results are beneficial to improve and develop the mold flux for casting rare earth alloy steels.

RESEARCH ON THE APPLICATION OF RARE EARTHS IN IRON AND STEEL IN RECENT YEARS

China has the biggest rare earths resource in the world,no wonder she pays much at-tention to the application of rare earth metals (REM).The application of REM in iron andsteel in China began at the end of 1950’s.The production of REM-treated iron and steelhad been made steady progress in the period of 1980’s.The production of REM-treatediron and steel in 1989 was 1.4 million tons and 250,000 tons respectively.The interest oftreating steel with REM in China keeps growing even in these years,It comes from the nat-

Application of Rare Earth in Steel in China

Application of rare earth in steels has gone through three stages in China.The investigation of rare earth adding method begun at the late 1970's has solved the technical problems caused by rare earth addition.Control ling sulphide morphology,several rare earth treated steel grades with improved properties have been developed and put into production.Rare earth exerts remarkable effect on the performance of low sulphur steel and on the hydrogen behavior in steel.Rare earth used for surface treatment of iron and steel materials expands rare earth utilization.

Study on Heterogeneous Nuclei in Cast H13 Steel Modified by Rare Earth

The dendrite segregation in cast H13 steel was weakened with RE modification treatment. Grain boundary carbide during quenching was also under control and impact toughness was improved greatly. By thermodynamic calculation, analysis of two-dimensional lattice misfitting and electron probe analysis, it is found that Ce2O3 may act as the heterogeneous nuclei of modified cast H13 steel.

Effect of Rare Earth Elements on Austenite Growth Dynamics of Steel 9Cr2Mo

The growth dynamics of austenite grain was investigated in steel 9Cr2 Mo with different rare earth(RE)element addition.The results show that austenite grains of steel 9Cr2 Mo can be refined and their growth can be restrained by adding a certain amount of RE.According to the results,the n and Q were calculated and the mechanism of the refinement of austenite grains was discussed.

Effect of Rare Earths on Properties of BNbRE Rail Steel

The development and properties of BNbRE rail steel and the effect of RE on rail steel were studied. The results show that the properties of rail steel ( σ b≥980 MPa, δ 5≥8%) can be improved by adding RE and niobium and adjusting the content of C, Si and Mn in steel. At the same time, the abrasion resistance, contact fatigue and fatigue property of BNbRE rail steel are excellent. It also shows that RE in rail steel has the functions of purifying steel, modifying inclusion and micro alloy action effect. The improved steel making process enhances the quality of molten steel. Although the content of RE is low, excellent properties of BNbRE rail steel are achieved.

Effect of Rare Earths on Tensile Behavior of Hot Roller Steel 60CrMnMo and Estimation of Roll's Fati

The effect of rare earth(RE) on tensile behavior of hot roller steel 60CrMnMo was investigated at the temperature when roll served The roll′s fatigue at 500 ℃ was estimated The results show that elongation δ of hot roller steel 60CrMnMo can be increased by adding RE It is possible to estimate the fatigue life with tensile behavior of hot roller steel 60CrMnMo

Accelerating Effect of Rare Earth in Steel on Its Surface-Carburizing Process

The carburization of steel type 20 with and without RE addition was investigated. The results show that RE in steel can accelerate carburizing process at 850 and 910 ℃. The optimum RE content in steel is about 0 032%. The mechanism of enhancing effect of RE on carburizing process was discussed.

Behavior of Rare Earthsin UltraLowSulfur Microalloyed Steel

The investigation on the behavior of RE in microalloyed steel containing Nb and Ti indicates RE still have the effect of purifying molten steel and metamorphose inclusions even when the composition of S is pretty low(S<0 003%). The optimum performance of the experimental steels can be obtained when w RE / w O+S is controlled around 3 9. The content of solid solution RE can reach 1×10 -5 ～1×10 -4 order of magnitude in ultra low sulfur steel. The additions of RE can reduce the segregation of S and P at the grain boundary, delay the dynamic recrystallization, refine the grain and second phase particles, and promote the precipitation of (Nb, Ti)(C, N). RE also exhibit the microalloying effect in steel.

Effect of Rare Earth Elements on Growth Dynamics of Austenite in 60CrMnMo Steel

The growth dynamics of austenite grains was investigated in 60CrMnMo steel with different RE elements. The results show that austenite grains of 60CrMnMo steel can be refined and their growth can be restrained by adding a certain amount of RE. From the experimental results, the values of n and Q were evaluated.

Morphology and Forming Mechanism of Rare Earth Inclusions During Solidification of Steel

RE inclusions formed during the solidification of molten steel was studied with TEM and SEM.The results show that with increasing of the ratio of sulphur to oxygen, the reaction products of RE with sulphur and oxygen will be successively RE2O3, composites of RE2O3 and RE2O2S, RE2S3, and a few particles of REO2.

RARE EARTH DISSOLVED IN SOLID SOLUTION OF STEEL AND ITS EFFECT ON MICROSTRUCTURE

The amounts of rare earth in the solid solution in steel 16Mn were determined by means of inductive coupling plasma(ICP)spectroscopy.While the RE/S ratio was less than 1.9,the amounts of rare earth in solid solution were not more than 8 ppm,which rised slightly with the increase of the rare earth content in the steel.While the RE/S was more than 1.9,MnS disappeared completely in the steel and the amounts of rare earth in solid solution increased rapidly with the increasing of the rare earth content.The solubility of cerium in steel 16 Mn(St 52)is less than 0.011 wt% at room temperature.The results also indicate that rare earth in solid solution can reduce the amount of pearlite and increase that of ferrite and its mierohardness.The rela- tionship between microhardness(Hv)and the amount of rare earth in solid solution can be expressed by the equation of Hv=117+7 RE(ppm).

Influence of Rare Earth Elements on Microstructure and Mechanical Properties of Cast High-Speed Steel Rolls

The influence of rare earth （RE） elements on the solidification process and eutectic transformation and mechanical properties of the high-V type cast, high-speed steel roll was studied. Test materials with different RE additions were prepared on a horizontal centrifugal casting machine. The solidification process, eutectic structure transformation, carbide morphology, and the elements present, were all investigated by means of differential scanning calorimetry （DSC） and scanning electron microscopy energy dispersive spectrometry （SEM-EDS）. The energy produced by crack initiation and crack extension was analyzed using a digital impact test machine. It was found that rare earth elements increased the tensile strength of the steel by inducing crystallization of earlier eutectic γ-Fe during the solidification process, which in turn increased the solidification temperature and thinned the dendritic grains. Rare earth elements with large atomic radius changed the lattice parameters of the MC carbide by forming rare earth carbides. This had the effect of dispersing longpole M C carbides to provide carbide grains, thereby, reducing the formation of the gross carbide and making more V available, to increase the secondary hardening process and improve the hardness level. The presence of rare earth elements in the steel raised the impact toughness by changing the mechanism of MC carbide formation, thereby increasing the crack initiation energy.

Effects of Rare Earths on Toughness of 31Mn2SiRE Wear- Resistance Cast Steel

The toughness of 31Mn2SiRE wear-resistance cast steel were increased by means of RE compound modification and high temperature austenitizing. The results show that the microstructures can be refined, needle and network ferrite are eliminated, the dislocation density and the quantity of dislocated martensite are increased remarkably, and the shape and distribution of inclusions are improved by the addition of RE. Therefore, the mechanical properties of the modified steel can be greatly increased, especially the toughness (αK) by 44%, yield strength (σs) by 10%, and elongation (δ5) by 42%.