A series of stearates with different rare-earth ion were investigated as thermal stabilizers for rigid PVC at 180 ℃ in air. Their stabilizing efficiency was based on measuring the rate of dehydrochlorination. The res...A series of stearates with different rare-earth ion were investigated as thermal stabilizers for rigid PVC at 180 ℃ in air. Their stabilizing efficiency was based on measuring the rate of dehydrochlorination. The resulted revealed the higher stabilizing efficiency of the investigated rare-earth stearates as thermal stabilizers for rigid PVC compared with the thermal stabilizers for industry: calcium stearate, zinc stearate, butyl stannum mercaptide, phosphite esters, β-diketone and epoxidized sunflower oil. This was well illustrated by longer incubation period (T_S) values and lower rate of dehydrochlorination. The stable efficiency was affected by the nature of rare-earth element's individual electronic shell. The mechanism for the stabilizing effect of rare-earth stearates was proposed. The result was experimentally proved based on IR spectrum.展开更多
To overcome the limitation in formability at room temperature,manufacturers have developed magnesium alloys with remarkable properties by adding rare-earth elements.The rare-earth magnesium alloys behave differently f...To overcome the limitation in formability at room temperature,manufacturers have developed magnesium alloys with remarkable properties by adding rare-earth elements.The rare-earth magnesium alloys behave differently from the conventional alloys,especially with respect to their coupled anisotropic and strain rate sensitive behavior.In the current work,such behavior of the rare-earth Mg alloy ZEK100 sheet at room temperature is investigated with the aid of the elastic viscoplastic self-consistent polycrystal plasticity model.Different strain rate sensitivities(SRSs)for various deformation modes are employed by the model to simulate the strain rate sensitive behaviors under different loading directions and loading rates.Good agreement between the experiments and simulations reveals the importance and necessity of using different SRSs for each deformation mode in hexagonal close-packed metals.Furthermore,the relative activities of each deformation mode and the texture evolution during different loadings are discussed.The anisotropic and strain rate sensitive behavior is ascribed to the various operating deformation modes with different SRSs during loading along different directions.展开更多
Rare-earth nickelates(RENiO_(3))show widely tunable metal-to-insulator transition(MIT)properties with ignorable variations in lattice constants and small latent heat across the critical temperature(TMIT).Particularly,...Rare-earth nickelates(RENiO_(3))show widely tunable metal-to-insulator transition(MIT)properties with ignorable variations in lattice constants and small latent heat across the critical temperature(TMIT).Particularly,it is worth noting that compared with the more commonly investigated vanadium oxides,the MIT of RENiO_(3)is less abrupt but usually across a wider range of temperatures.This sheds light on their alternative applications as negative temperature coefficient resistance(NTCR)thermistors with high sensitivity compared with the current NTCR thermistors,other than their expected use as critical temperature resistance thermistors.In this work,we demonstrate the NTCR thermistor functionality for using the adjustable MIT of Nd_(x)Sm_(1-x)NiO_(3)within 200–400 K,which displays larger magnitudes of NTCR(e.g.,more than 7%/K)that is unattainable in traditional NTCR thermistor materials.The temperature dependence of resistance(R–T)shows sharp variation during the MIT of Nd_(x)Sm_(1-x)NiO_(3)with no hysteresis via decreasing the Nd content(e.g.,x≤0.8),and such a R–T tendency can be linearized by introducing an optimum parallel resistor.The sensitive range of temperature can be further extended to 210–360 K by combining a series of Nd_(x)Sm_(1-x)NiO_(3)with eight rare-earth co-occupation ratios as an array,with a high magnitude of NTCR(e.g.,7%–14%/K)covering the entire range of temperatures.展开更多
Rare-earth silicates are promising environmental barrier coatings(EBCs)that can protect SiC_(f)/Si C_(m)substrates in next-genera tion gas turbine blades.Notably,RE_(2)Si_(2)O_(7)(RE=Yb and Ho)shows potential as an EB...Rare-earth silicates are promising environmental barrier coatings(EBCs)that can protect SiC_(f)/Si C_(m)substrates in next-genera tion gas turbine blades.Notably,RE_(2)Si_(2)O_(7)(RE=Yb and Ho)shows potential as an EBC due to its coefficient of thermal expansion(CTE)compatible with substrates and high resistance to water vapor corrosion.The target operating temperature for next-generation tur bine blades is 1400°C.Corrosion is inevitable during adhesion to molten volcanic ash,and thus,understanding the corrosion behavior o the material is crucial to its reliability.This study investigates the high-temperature corrosion behavior of sintered RE_(2)Si_(2)O_(7)(RE=Yb and Ho).Samples were prepared using a solid-state reaction and hot-press method.They were then exposed to volcanic ash at 1400°C for 224,and 48 h.After 48 h of exposure,volcanic ash did not react with Yb_(2)Si_(2)O_(7)but penetrated its interior,causing damage.Meanwhile Ho_(2)Si_(2)O_(7)was partially dissolved in the molten volcanic ash,forming a reaction zone that prevented volcanic ash melts from penetrating the interior.With increasing heat treatment time,the reaction zone expanded,and the thickness of the acicular apatite grains increased The Ca:Si ratios in the residual volcanic ash were mostly unchanged for Yb_(2)Si_(2)O_(7)but decreased considerably over time for Ho_(2)Si_(2)O_(7).Th Ca in volcanic ash was consumed and formed apatite,indicating that RE^(3+)ions with large ionic radii(Ho>Yb)easily precipitated apatit from the volcanic ash.展开更多
Waste shell stacking with odor and toxicity is a serious hazard to our living environment. To make effective use of the natural resources, the shell powder was applied as a filler of outdoor thermal insulation coating...Waste shell stacking with odor and toxicity is a serious hazard to our living environment. To make effective use of the natural resources, the shell powder was applied as a filler of outdoor thermal insulation coatings. Sodium stearate(SS) was used to modify the properties of shell powder to reduce its agglomeration and to increase its compatibility with the emulsion. The oil absorption rate and the spectrum reflectance of the shell powder show that the optimized content of SS as a modifier is 1.5wt%. The total spectrum reflectance of the coating made with the shell powder that is modified at this optimum SS content is 9.33% higher than that without any modification. At the optimum SS content of 1.5wt%, the thermal insulation of the coatings is improved by 1.0℃ for the cement mortar board and 1.6℃ for the steel plate, respectively. The scouring resistance of the coating with the 1.5wt% SS-modified shell powder is three times that of the coating without modification.展开更多
During the past decades,with the increasing demands in lightweight structural materials,Mg alloys with low density and high performance have been extensively investigated and partly applied in some industries.Especial...During the past decades,with the increasing demands in lightweight structural materials,Mg alloys with low density and high performance have been extensively investigated and partly applied in some industries.Especially when rare earth(RE)elements are added as major alloying elements to Mg alloys,the alloy strength and creep resistance are greatly improved,which have promoted several series of Mg-RE alloys.This paper reviews the progress and developments of high-performance Mg-RE alloys in recent years with emphasis on cast alloys.The main contents include the alloy design,melt purification,grain refinement,castability,novel liquid casting and semisolid forming approaches,and the industrial applications or trials made of Mg-RE alloys.The review will provide insights for future developments of new alloys,techniques and applications of Mg alloys.展开更多
In this study, the barite nanoparticles were successfully modified with stearate and the influence of stearate addition on the performance of barite nanoparticles was systematically investigated. The products were cha...In this study, the barite nanoparticles were successfully modified with stearate and the influence of stearate addition on the performance of barite nanoparticles was systematically investigated. The products were characterized by activating factor analysis, contact angle test, surface energy calculation, sedimentation rate calculation, rheological measurement, and FT-IR analysis, etc. As the quantity of added stearate increased, both the activating factor and contact angle of barite nanoparticles increased first then decreased. When the stearate content was 5% of the mass of barite nanoparticles, the activating factor and water contact angle of modified particles reached maximum value, 97% and 126% respectively. At this time, the sedimentation rate reached minimum, and so did the surface energy. The rheological test reveals that the viscosity of modified barite nanoparticles/petronol system decreases greatly, indicating the surface performance of barite nanoparticles has changed from hydrophilicity to lipophilicity after modification. C=O and COO stretching vibration peaks were found in the FT-IR spectra, which proves that the stearate has combined onto the surface of barite nanoparticles. Finally, according to the zeta potential result of unmodified barite, the possible modification mechanism was provided.展开更多
文摘A series of stearates with different rare-earth ion were investigated as thermal stabilizers for rigid PVC at 180 ℃ in air. Their stabilizing efficiency was based on measuring the rate of dehydrochlorination. The resulted revealed the higher stabilizing efficiency of the investigated rare-earth stearates as thermal stabilizers for rigid PVC compared with the thermal stabilizers for industry: calcium stearate, zinc stearate, butyl stannum mercaptide, phosphite esters, β-diketone and epoxidized sunflower oil. This was well illustrated by longer incubation period (T_S) values and lower rate of dehydrochlorination. The stable efficiency was affected by the nature of rare-earth element's individual electronic shell. The mechanism for the stabilizing effect of rare-earth stearates was proposed. The result was experimentally proved based on IR spectrum.
基金supported by the National Natural Science Foundation of China(No.51975365)the Shanghai Pujiang Program(18PJ1405000)+1 种基金supported by the Natural Sciences and Engineering Research Council of Canada(NSERC)the Province of Ontario
文摘To overcome the limitation in formability at room temperature,manufacturers have developed magnesium alloys with remarkable properties by adding rare-earth elements.The rare-earth magnesium alloys behave differently from the conventional alloys,especially with respect to their coupled anisotropic and strain rate sensitive behavior.In the current work,such behavior of the rare-earth Mg alloy ZEK100 sheet at room temperature is investigated with the aid of the elastic viscoplastic self-consistent polycrystal plasticity model.Different strain rate sensitivities(SRSs)for various deformation modes are employed by the model to simulate the strain rate sensitive behaviors under different loading directions and loading rates.Good agreement between the experiments and simulations reveals the importance and necessity of using different SRSs for each deformation mode in hexagonal close-packed metals.Furthermore,the relative activities of each deformation mode and the texture evolution during different loadings are discussed.The anisotropic and strain rate sensitive behavior is ascribed to the various operating deformation modes with different SRSs during loading along different directions.
基金the National Key Research and Development Program of China(No.2021YFA0718900)the National Natural Science Foundation of China(No.62074014)。
文摘Rare-earth nickelates(RENiO_(3))show widely tunable metal-to-insulator transition(MIT)properties with ignorable variations in lattice constants and small latent heat across the critical temperature(TMIT).Particularly,it is worth noting that compared with the more commonly investigated vanadium oxides,the MIT of RENiO_(3)is less abrupt but usually across a wider range of temperatures.This sheds light on their alternative applications as negative temperature coefficient resistance(NTCR)thermistors with high sensitivity compared with the current NTCR thermistors,other than their expected use as critical temperature resistance thermistors.In this work,we demonstrate the NTCR thermistor functionality for using the adjustable MIT of Nd_(x)Sm_(1-x)NiO_(3)within 200–400 K,which displays larger magnitudes of NTCR(e.g.,more than 7%/K)that is unattainable in traditional NTCR thermistor materials.The temperature dependence of resistance(R–T)shows sharp variation during the MIT of Nd_(x)Sm_(1-x)NiO_(3)with no hysteresis via decreasing the Nd content(e.g.,x≤0.8),and such a R–T tendency can be linearized by introducing an optimum parallel resistor.The sensitive range of temperature can be further extended to 210–360 K by combining a series of Nd_(x)Sm_(1-x)NiO_(3)with eight rare-earth co-occupation ratios as an array,with a high magnitude of NTCR(e.g.,7%–14%/K)covering the entire range of temperatures.
基金supported by JSPS KAKENHI(No.23K19087)“Dynamic Alliance for Open Innovation Bridging Human,Environment and Materials”from the Ministry of Education,Culture,Sports,Science and Technology o f Japan(MEXT).
文摘Rare-earth silicates are promising environmental barrier coatings(EBCs)that can protect SiC_(f)/Si C_(m)substrates in next-genera tion gas turbine blades.Notably,RE_(2)Si_(2)O_(7)(RE=Yb and Ho)shows potential as an EBC due to its coefficient of thermal expansion(CTE)compatible with substrates and high resistance to water vapor corrosion.The target operating temperature for next-generation tur bine blades is 1400°C.Corrosion is inevitable during adhesion to molten volcanic ash,and thus,understanding the corrosion behavior o the material is crucial to its reliability.This study investigates the high-temperature corrosion behavior of sintered RE_(2)Si_(2)O_(7)(RE=Yb and Ho).Samples were prepared using a solid-state reaction and hot-press method.They were then exposed to volcanic ash at 1400°C for 224,and 48 h.After 48 h of exposure,volcanic ash did not react with Yb_(2)Si_(2)O_(7)but penetrated its interior,causing damage.Meanwhile Ho_(2)Si_(2)O_(7)was partially dissolved in the molten volcanic ash,forming a reaction zone that prevented volcanic ash melts from penetrating the interior.With increasing heat treatment time,the reaction zone expanded,and the thickness of the acicular apatite grains increased The Ca:Si ratios in the residual volcanic ash were mostly unchanged for Yb_(2)Si_(2)O_(7)but decreased considerably over time for Ho_(2)Si_(2)O_(7).Th Ca in volcanic ash was consumed and formed apatite,indicating that RE^(3+)ions with large ionic radii(Ho>Yb)easily precipitated apatit from the volcanic ash.
文摘Waste shell stacking with odor and toxicity is a serious hazard to our living environment. To make effective use of the natural resources, the shell powder was applied as a filler of outdoor thermal insulation coatings. Sodium stearate(SS) was used to modify the properties of shell powder to reduce its agglomeration and to increase its compatibility with the emulsion. The oil absorption rate and the spectrum reflectance of the shell powder show that the optimized content of SS as a modifier is 1.5wt%. The total spectrum reflectance of the coating made with the shell powder that is modified at this optimum SS content is 9.33% higher than that without any modification. At the optimum SS content of 1.5wt%, the thermal insulation of the coatings is improved by 1.0℃ for the cement mortar board and 1.6℃ for the steel plate, respectively. The scouring resistance of the coating with the 1.5wt% SS-modified shell powder is three times that of the coating without modification.
基金This work is supported by the National Natural Science Foundation of China(Grant Nos.51775334,51821001 and 51701124)National Key Research and Development Program of China(Grant No.2016YFB0701205)+3 种基金China Postdoctoral Science Foundation(Grant No.2020M671360)Natural Science Foundation for Young of Jiangsu Province(Grant No.BK20190863)Jiangsu“Mass Innovation and Entrepreneurship”Talent Program(Shuang Chuang Ph.Ds,2018)Open Research Fund of the State Key Laboratory of Metal Matrix Composites(Grant No.sklmmc-kf18-08).
文摘During the past decades,with the increasing demands in lightweight structural materials,Mg alloys with low density and high performance have been extensively investigated and partly applied in some industries.Especially when rare earth(RE)elements are added as major alloying elements to Mg alloys,the alloy strength and creep resistance are greatly improved,which have promoted several series of Mg-RE alloys.This paper reviews the progress and developments of high-performance Mg-RE alloys in recent years with emphasis on cast alloys.The main contents include the alloy design,melt purification,grain refinement,castability,novel liquid casting and semisolid forming approaches,and the industrial applications or trials made of Mg-RE alloys.The review will provide insights for future developments of new alloys,techniques and applications of Mg alloys.
基金supported by the International Corporation Project (Grant No.07SU07001)the Science Foundation of Science and Technology Commission of Shanghai Municipality (Grant No.0552nm011)
文摘In this study, the barite nanoparticles were successfully modified with stearate and the influence of stearate addition on the performance of barite nanoparticles was systematically investigated. The products were characterized by activating factor analysis, contact angle test, surface energy calculation, sedimentation rate calculation, rheological measurement, and FT-IR analysis, etc. As the quantity of added stearate increased, both the activating factor and contact angle of barite nanoparticles increased first then decreased. When the stearate content was 5% of the mass of barite nanoparticles, the activating factor and water contact angle of modified particles reached maximum value, 97% and 126% respectively. At this time, the sedimentation rate reached minimum, and so did the surface energy. The rheological test reveals that the viscosity of modified barite nanoparticles/petronol system decreases greatly, indicating the surface performance of barite nanoparticles has changed from hydrophilicity to lipophilicity after modification. C=O and COO stretching vibration peaks were found in the FT-IR spectra, which proves that the stearate has combined onto the surface of barite nanoparticles. Finally, according to the zeta potential result of unmodified barite, the possible modification mechanism was provided.