THE SLUMP RETENTION OF N-2000 HIGH-RANGE WATER-REDUCING AND RETARDING ADMIXTURE

N-2000 is an admixture for concrete, with a low slump loss, high range water-reducing ratio and long-time retarding. The N-2000 is made up of naphthalene-sulfonic-maldehyde polycondensation (NSMP) and ATMP. Its characteristic results from the synergistic effects of NSMP and ATMP. The results show that when 0.7%-1.2% of N-2000 is added to concrete (by mass of cement), the water reducing ratio is up to 20%-30%, and the slump of fresh concrete can be retained for 2 hours without significant loss. N-2000 can not only improve the workability of fresh concrete but also increase the strength of the hardened concrete, especially early strength. It is also proved to have a good compatibility with various cements.

STUDY ON OPTIMIZATION OF HIGH PERFORMANCE CONCRETE ADMIXTURES

Influences of admixtures on the workability and strength of high performance concrete （HPC） are in- vestigated. The types of investigated admixtures include naphthalene series high range water reducing agent, polycarboxlic series high range water reduce agent and sodium sulfate hardening accelerating agent. Two kinds of curing condition, namely steam curing condition and standard curing condition, are adopted. The result shows that HPC, added with polycarboxlic series of high performance water reducer, has high workability and strength, while sodium sulfate accelerating agent causes poor workability and low strength. Thus for vapor-cured HPC and its formulations, naphthalene series high range water reducing agent with less sodium sulfate should be given pri- ority. Therefore, the differences of curing conditions should be considered when selecting HPC admixtures.

Early calcium monocarboaluminate hydrate formation in cement paste:effect of polycarboxylate type admixture

Effects of polycarboxylate type admixture（PCA）on calcium monocarboaluminate hydrate（AFmc）formation in hydrated cement paste containing limestone filler（LF）are investigated by the Fourier transform infrared spectroscopy（FTIR）,the scanning electron microscopy（SEM）,the derivative thermogravimetric（DTG）analysis and the adsorption amount measurement.Experimental results indicate that AFmc forms during the initial hydration period of cement as early as 15 min.It is found that PCA accelerates the early age AFmc formation and enhances cement hydration by promoting C4AF hydration at the early age,and,as a consequence,the iron associated AFmc phase forms more readily.The phenomenon is not observed when PCA is replaced by a naphthalene formaldehyde sulphonate condensate water reducer.Compatibility between PCA and cement is modified due to the presence of AFmc along with ettringite（AFt）,which results in a less adsorption amount of PCA on the surface of cement minerals.As a kind of high-range water reducer,PCA may be the preferred choice for concrete containing LF.

Treatment of black liquor from the papermaking industry by acidification and reuse

Two different kinds of black liquor from the papermaking industry were treated by acidification and reuse. The experimental parameters and conditions were discussed in detail. The experimental results indicated that the treatment process mentioned in this article is an effective process for the treatment of black liquor from the papermaking industry. By the treatment, the solid materials in black liquor are transferred into two by products and the other components are reused or evaporated. Thus, no wastewater except some condensation water would be discharged in pulping process and the problem of pollution of black liquor would be effectively solved.

The Permeability and Strength of Green High Performance Concrete

The permeability,alkali silica reaction,workability and strength of GHPC(green high performance concrete) were studied in this paper.The results show that GHPC has an excellent durability and the effects of mass ratio of flyash to high calcium slag,water binder ratio,content of water reducer,and crushed coarse aggregate type on the workability and strength of GHPC were considerably evident.A new path for the concretes continuous development was put forward.