This paper aims at exploring the effects of anti-seismic reinforcement with the fiber-reinforced polymer （FRP） material bonded to the dam surface in dam engineering. Time-history analysis was performed to simulate t...This paper aims at exploring the effects of anti-seismic reinforcement with the fiber-reinforced polymer （FRP） material bonded to the dam surface in dam engineering. Time-history analysis was performed to simulate the seismic failure process of a gravity dam that was assumed to be reinforced at the locations of slope discontinuity at the downstream surface, part of the upstream face, and the dam heel. A damage model considering the influence of concrete heterogeneity was used to model the nonlinearity of concrete. A bond-slip model was applied to the interface between FRP and concrete, and the reinforcement mechanism was analyzed through the bond stress and the stress in FRP. The results of the crack pattern, displacement, and acceleration of the reinforced dam were compared with those of the original one. It is shown that FRP, as a reinforcement material, postpones the occurrence of cracks and slows the crack propagation, and that cracks emanating from the upstream surface and downstream surface are not connected, meaning that the reinforced dam can retain water-impounding function when subjected to the earthquake. Anti-seismic reinforcement with FRP is therefore beneficial to improving the seismic resistant capability of concrete dams.展开更多
The use of a natural white juice, taken from magrabe banana stem, as concrete admixture to improve mechanical and physicrvchemical properties of concrete has been studied. The compressive strength, bulk density the fr...The use of a natural white juice, taken from magrabe banana stem, as concrete admixture to improve mechanical and physicrvchemical properties of concrete has been studied. The compressive strength, bulk density the free lime liberated during hydration and the combined water content were determined. The results indicate that the admixture acts as a retarder in most cases and as accelerator in some ones. Also, the admixture effect on the corrosion resistance of the reinforcing steel against surrounding aggressive media has been investigated using galvanostatic polarization technique. The addition of 0.2% admixture leads to the more inhibition of the steel展开更多
Corrosion and electrochemical behaviour of reinforcing steel embedded in cement pastes with and without concrete admixtures used in Egypt to modify concrete properties have been studied. The influence of the admixtur...Corrosion and electrochemical behaviour of reinforcing steel embedded in cement pastes with and without concrete admixtures used in Egypt to modify concrete properties have been studied. The influence of the admixtures on the corrosion resistance of the steel against chloride attack has been studied by using impressed current and impressed voltage techniques. The results indicate that the type and concentration of the used admixture have an important effect on the extent of chloride induced corrosion of the steel. The mechanism of corrosion of steel due to chloride attack was discussed. (Edited author abstract) 16 Refs.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.51009019)the State Key Development Program for Basic Research of China(Grant No.2013CB035905)
文摘This paper aims at exploring the effects of anti-seismic reinforcement with the fiber-reinforced polymer （FRP） material bonded to the dam surface in dam engineering. Time-history analysis was performed to simulate the seismic failure process of a gravity dam that was assumed to be reinforced at the locations of slope discontinuity at the downstream surface, part of the upstream face, and the dam heel. A damage model considering the influence of concrete heterogeneity was used to model the nonlinearity of concrete. A bond-slip model was applied to the interface between FRP and concrete, and the reinforcement mechanism was analyzed through the bond stress and the stress in FRP. The results of the crack pattern, displacement, and acceleration of the reinforced dam were compared with those of the original one. It is shown that FRP, as a reinforcement material, postpones the occurrence of cracks and slows the crack propagation, and that cracks emanating from the upstream surface and downstream surface are not connected, meaning that the reinforced dam can retain water-impounding function when subjected to the earthquake. Anti-seismic reinforcement with FRP is therefore beneficial to improving the seismic resistant capability of concrete dams.
文摘The use of a natural white juice, taken from magrabe banana stem, as concrete admixture to improve mechanical and physicrvchemical properties of concrete has been studied. The compressive strength, bulk density the free lime liberated during hydration and the combined water content were determined. The results indicate that the admixture acts as a retarder in most cases and as accelerator in some ones. Also, the admixture effect on the corrosion resistance of the reinforcing steel against surrounding aggressive media has been investigated using galvanostatic polarization technique. The addition of 0.2% admixture leads to the more inhibition of the steel
文摘Corrosion and electrochemical behaviour of reinforcing steel embedded in cement pastes with and without concrete admixtures used in Egypt to modify concrete properties have been studied. The influence of the admixtures on the corrosion resistance of the steel against chloride attack has been studied by using impressed current and impressed voltage techniques. The results indicate that the type and concentration of the used admixture have an important effect on the extent of chloride induced corrosion of the steel. The mechanism of corrosion of steel due to chloride attack was discussed. (Edited author abstract) 16 Refs.