MODIFIED LAYER REMOVAL METHOD FOR MEASUREMENT OF RESIDUAL STRESS DISTRIBUTION IN THICK PRE-STRETCHED ALUMINUM PLATE

The integrated structure parts are widely used in aircraft. The distortion caused by residual stresses in thick pre-stretched aluminum plates during machining integrated parts is a common and serious problem. To predict and control the machining distortion, the residual stress distribution in the thick plate must be measured firstly. The modified removal method for measuring residual stress in thick pre-stretched aluminum plates is proposed and the stress-strain relation matrix is deduced by elasticity theory. The residual stress distribution in specimen of 7050T7451 plate is measured by using the method, and measurement results are analyzed and compared with data obtained by other methods. The method is effective to measure the residual stress.

Residual stress with asymmetric spray quenching for thick aluminum alloy plates

Solution and quenching heat treatments are generally carried out in a roller hearth furnace for large-scale thick aluminum alloy plates.However,the asymmetric or uneven spray water flow rate is inevitable under industrial production conditions,which leads to an asymmetric residual stress distribution.The spray quenching treatment was conducted on self-designed spray equipment,and the residual stress along the thickness direction was measured by a layer removal method based on deflections.Under the asymmetric spray quenching condition,the subsurface stress of the high-flow rate surface was lower than that of the low-flow rate surface,and the difference between the two subsurface stresses increased with the increase in the difference in water flow rates.The subsurface stress underneath the surface with a water flow rate of 0.60 m^(3)/h was 15.38 MPa less than that of 0.15 m^(3)/h.The simulated residual stress by finite element(FE)method of the high heat transfer coefficient(HTC)surface was less than that of the low HTC surface,which is consistent with the experimental results.The FE model can be used to analyze the strain and stress evolution and predict the quenched stress magnitude and distribution.

Effect of non-uniform stress characteristics on stress measurement in specimen

There is a remarkable difference in stress distribution between a specimen and a plate removed from the specimen.The plate presents a uniform stress distribution whereas the specimen presents a non-uniform stress distribution.Firstly,the real stress distributions in plates with thickness of 30,40 and 50 mm and then in the specimens were obtained through simulation and X-ray surface stress measurement.Secondly,in order to study the impact of specimens shapes and processing ways on the results accuracy,two irregular shapes (parallelogram and trapezoid) and two processing ways (saw and electron discharge machining (EDM)) were compared and analyzed by simulation and experiment using layer removal method,then the specimen effects on measurement results were evaluated.The results show that:1) the non-uniform stress distribution characteristics of the specimen near the surface of the cut is significant,the range of non-uniform stress distribution is approximately one-thickness distance away from the cut,and it decreases gradually along the depth;2) In order to ensure the stability in the results,it is suitable to take the specimen plane size 2-3 times of its thickness;3) Conventional processing methods have little effect on experimental results and the average deviation is less than 5%.