A test for crumb rubber modified asphalt containing 20% crumb rubber particles（30 mesh） was performed using a scanning electron microscope（SEM）.The experimental results indicate that the crumb rubber particles are...A test for crumb rubber modified asphalt containing 20% crumb rubber particles（30 mesh） was performed using a scanning electron microscope（SEM）.The experimental results indicate that the crumb rubber particles are evenly distributed in the asphalt.Shear rate sweep and shear-temperature sweep tests on the crumb rubber modified asphalt at-20-80 ℃ using a dynamic shear rheology（DSR） instrument,were carried out.The tests show that the complex modulus decreases with increasing temperature;at equivalent temperature,higher load frequencies lead to a larger complex modulus,and this value increasingly decreases as the temperature increases;the phase angle increases with temperature and decreases as the load frequency increases.It can be concluded that the rutting resistance limiting temperature of crumb rubber modified asphalt is 78 ℃,and the anti-fatigue limiting temperature is 16 ℃,which shows that the asphalt has preferable rutting resistance characteristics at high temperature,as well as anti-fatigue characteristics.In addition,the complex modulus master curve at different temperatures was plotted according to the time temperature equivalence principle,which allows the study of the dynamic state behavior of crumb rubber modified asphalt at a wide range of load frequency.展开更多
Based on the rheology characteristic and the resistivity variation under alternating electric-field of Portland cement hydration by means of AR2000 advanced rheometer and non-contacting electrical resistivity device, ...Based on the rheology characteristic and the resistivity variation under alternating electric-field of Portland cement hydration by means of AR2000 advanced rheometer and non-contacting electrical resistivity device, the influence of cement kinds and the chemical admixtures on the initial rheology characteristic and structure forming and developing of cement hydration was studied. The relationship between the rheology characteristic, the initial hydration structure forming and the hydration process at very early ages was analyzed by macro properties and microstructure tests. The results showed that, the storage modulus, acted as S, could be described more subtle distinction accompanying with hydration of fresh paste model at very early period. Combining the resistivity alterations, a sudden change on structure forming emerged when the hydration of cement becoming inducing age. The rheology characteristic was interrelated to the hydration structure forming, development and the physical mechanics properties. The sudden change on storage modulus moved up due to the addition of retarder, but the structure forming and developing was retarded to a certain extent.展开更多
基金Funded by the Communication Science and Technology Foundation of Inner Mongolia (NJ-2005-25)
文摘A test for crumb rubber modified asphalt containing 20% crumb rubber particles（30 mesh） was performed using a scanning electron microscope（SEM）.The experimental results indicate that the crumb rubber particles are evenly distributed in the asphalt.Shear rate sweep and shear-temperature sweep tests on the crumb rubber modified asphalt at-20-80 ℃ using a dynamic shear rheology（DSR） instrument,were carried out.The tests show that the complex modulus decreases with increasing temperature;at equivalent temperature,higher load frequencies lead to a larger complex modulus,and this value increasingly decreases as the temperature increases;the phase angle increases with temperature and decreases as the load frequency increases.It can be concluded that the rutting resistance limiting temperature of crumb rubber modified asphalt is 78 ℃,and the anti-fatigue limiting temperature is 16 ℃,which shows that the asphalt has preferable rutting resistance characteristics at high temperature,as well as anti-fatigue characteristics.In addition,the complex modulus master curve at different temperatures was plotted according to the time temperature equivalence principle,which allows the study of the dynamic state behavior of crumb rubber modified asphalt at a wide range of load frequency.
文摘Based on the rheology characteristic and the resistivity variation under alternating electric-field of Portland cement hydration by means of AR2000 advanced rheometer and non-contacting electrical resistivity device, the influence of cement kinds and the chemical admixtures on the initial rheology characteristic and structure forming and developing of cement hydration was studied. The relationship between the rheology characteristic, the initial hydration structure forming and the hydration process at very early ages was analyzed by macro properties and microstructure tests. The results showed that, the storage modulus, acted as S, could be described more subtle distinction accompanying with hydration of fresh paste model at very early period. Combining the resistivity alterations, a sudden change on structure forming emerged when the hydration of cement becoming inducing age. The rheology characteristic was interrelated to the hydration structure forming, development and the physical mechanics properties. The sudden change on storage modulus moved up due to the addition of retarder, but the structure forming and developing was retarded to a certain extent.