Optimum Calcination Condition of Waste Stabilized Adobe for Alkali Activated High Volume Adobe-Slag Binder Cured at Room Temperature

This study aims to determine the most convenient calcination temperature and calcination duration of wastestabilized Adobe(AB)to produce a new alkali-activated binder.Waste-stabilized Adobe mainly consists of soil,CaCO3 as a stabilizer,and straw(for strengthening).The availability of raw materials for making Adobe presents the waste-stabilized Adobe as a potential product for a new alkali-activated binder.Waste-stabilized Adobe collected from an abandoned damaged building in the village of Inonu in Northern Cyprus,ground and calcined at the following temperatures:450,550,650,750,850,and 950℃.The calcination at each temperature was held for different durations 1,3,5,and 7 h.Raw and calcined waste stabilized Adobe structures were investigated using XRF,TGA-DTA,XRD,FTIR,and SEM.Considering technical and environmental views related to energy consumption,waste stabilized Adobe calcined at 750℃ for 1 h presented the most promising results regarding the production of a new precursor for alkali-activated binder.This study also presents the effect of ground granulated blast furnace slag(GGBFS)usage on the fresh and hardened properties of optimum calcined AB-based alkali-activated pastes cured at room temperature.GGBFS was used to partially replace AB to form a binary composite raw material system and seven experimental groups were designed according to replacement levels of 0%,5%,10%,15%,20%,25%and 30%(by mass).Alkali-activated high volume waste-stabilized Adobe-slag pastes prepared using Na2SiO3-to-NaOH ratio of 2 and 12 M concentration of Sodium Hydroxide.The fresh property as flowability and the hardened property as the compressive strength of the alkali-activated pastes with different GGBFS contents were investigated.The results indicated that the incorporation of GGBFS increased the flowability of fresh alkali-activated pastes.A 28-day compressive strength of 43.75 MPa can be obtained by a 30%replacement level of GGBFS.

Robust Polystyrene/Fluorinated Silica Superhydrophobic Composite Coatings with Rapid Curing at Room Temperature Prepared by One-Step Spraying

Superhydrophobic materials are severely limited in their applications due to their weak mechanical properties and complex preparation process.In this paper,polystyrene/fluorinated silica(PS/SiO_(2))superhydrophobic composite coatings were prepared on the surface of 304 stainless steel using a simple one-step spraying method.The effects of different PS contents on the wettability as well as the wear properties of the samples were investigated.SiO_(2) was encapsulated in polystyrene to form a structure similar to cement encapsulated stones.With the addition of PS,a mound-like structure was formed on the sample surface,and a more optimized micro–nano structure was obtained when the content of PS was 0.6 g.At this time,the sample exhibited excellent wettability with a contact angle of 157.86°and a sliding angle of 0.84°.In addition,the contact angle of 151.09°was achieved after 180 cm of friction under a 100 g load and the composite coating prepared by this method also has excellent chemical stability,water impact resistance,corrosion resistance,and self-cleaning properties.This opens up new possibilities for the development of simple and robust superhydrophobic materials.