The rupture behavior of a cast Ni-base superalloy M963 at high temperature has been investi- gated. The microstructure examination shows that there exists a large amount of the carbide and γ-γ' eutectic, which i...The rupture behavior of a cast Ni-base superalloy M963 at high temperature has been investi- gated. The microstructure examination shows that there exists a large amount of the carbide and γ-γ' eutectic, which is very harmful to the mechanical properties of M963 superalloy. The tensile strength of M963 superalloy both at room temperature and at high temperatures is higher than that of K17G alloy, but the tensile ductility of the former is much lower than that of the latter. In tensile fracture process with the high strain rate, the open carbides are the initiation site and the carbide/matrix interface is the propagation path of cracks. But in fracture process with the low strain rate, the carbide/matrix interface and cast microvoids are the initiation sites, and the carbide/matrix interface is the propagation path of cracks. The effective ways to improve ductility of M963 superalloy are also suggested.展开更多
The acoustic emission(AE)technique can perform non-destructive monitoring of the internal damage development of bamboo and wood materials.In this experiment,the mechanical properties of different bamboo and wood(bambo...The acoustic emission(AE)technique can perform non-destructive monitoring of the internal damage development of bamboo and wood materials.In this experiment,the mechanical properties of different bamboo and wood(bamboo scrimber,bamboo plywood and SPF(Spruce-pine-fir)dimension lumber)during four-point loading tests were compared.The AE activities caused by loadings were investigated through the single parameter analysis and K-means cluster analysis.Results showed that the bending strength of bamboo scrimber was 3.6 times that of bam-boo plywood and 2.7 times that of SPF dimension lumber,respectively.Due to the high strength and toughness of bamboo,the AE signals of the two bamboo products were more abundant than those of SPF dimension lumber.However,the AE evolution trend of the three materials was similar,which all experienced three stages,including gentle period,steady period and steep period,and the area of rupture precursor characteristics could be recognized before the specimen destroyed.Due to the bottom layer was first tensile failure,the main structure of bamboo plywood was destroyed after the stress redistribution.The rupture precursor characteristics could be observed before each peak.Findings put in evidence a good correlation between AE clusters of two bamboo products,while the amplitude and energy of wood signals were lower than those of bamboo.The amplitude and energy from the propagation and aggregation of cracks were greater than those related to micro-cracks initiation.展开更多
基金supported by the Postdoctoral Science Foundation of China
文摘The rupture behavior of a cast Ni-base superalloy M963 at high temperature has been investi- gated. The microstructure examination shows that there exists a large amount of the carbide and γ-γ' eutectic, which is very harmful to the mechanical properties of M963 superalloy. The tensile strength of M963 superalloy both at room temperature and at high temperatures is higher than that of K17G alloy, but the tensile ductility of the former is much lower than that of the latter. In tensile fracture process with the high strain rate, the open carbides are the initiation site and the carbide/matrix interface is the propagation path of cracks. But in fracture process with the low strain rate, the carbide/matrix interface and cast microvoids are the initiation sites, and the carbide/matrix interface is the propagation path of cracks. The effective ways to improve ductility of M963 superalloy are also suggested.
基金This paper was supported in part by Project funded by the National Natural Science Foundation of China(Grant Nos.32071700 and 31570559).
文摘The acoustic emission(AE)technique can perform non-destructive monitoring of the internal damage development of bamboo and wood materials.In this experiment,the mechanical properties of different bamboo and wood(bamboo scrimber,bamboo plywood and SPF(Spruce-pine-fir)dimension lumber)during four-point loading tests were compared.The AE activities caused by loadings were investigated through the single parameter analysis and K-means cluster analysis.Results showed that the bending strength of bamboo scrimber was 3.6 times that of bam-boo plywood and 2.7 times that of SPF dimension lumber,respectively.Due to the high strength and toughness of bamboo,the AE signals of the two bamboo products were more abundant than those of SPF dimension lumber.However,the AE evolution trend of the three materials was similar,which all experienced three stages,including gentle period,steady period and steep period,and the area of rupture precursor characteristics could be recognized before the specimen destroyed.Due to the bottom layer was first tensile failure,the main structure of bamboo plywood was destroyed after the stress redistribution.The rupture precursor characteristics could be observed before each peak.Findings put in evidence a good correlation between AE clusters of two bamboo products,while the amplitude and energy of wood signals were lower than those of bamboo.The amplitude and energy from the propagation and aggregation of cracks were greater than those related to micro-cracks initiation.