Seawater pumped storage systems have bright prospect for energy storage in the coming years.The operational conditions of seawater pumped storage system are complex and harsh,where metal materials suff er from severe ...Seawater pumped storage systems have bright prospect for energy storage in the coming years.The operational conditions of seawater pumped storage system are complex and harsh,where metal materials suff er from severe general and local corrosion.The corrosion behavior of Q235B carbon steel in simulated seawater pumped storage system under operational conditions was studied by potentiodynamic polarization,cyclic potentiodynamic polarization,and scanning electron microscope(SEM).The results confi rm that the working pressure aff ected the corrosion resistance of Q235B carbon steel during the whole immersion period.The pressure promoted the electrochemical reaction of corrosion process and the corrosion rate increased with pressure at the initial immersion period.However,the stable rust layer formed after longtime immersion at diff erent pressures increased the corrosion resistance of carbon steel,and decreased the corrosion degree of carbon steel.Meanwhile,the working pressure aff ected the pitting corrosion behavior of Q235B carbon steel during the whole immersion period.The pitting corrosion potential was more negative and the tendency of pitting corrosion was higher at 4 MPa during the whole immersion period.However,pressure also accelerated the formation rate of protective rust layer on the steel surface.Q235B carbon steel has higher susceptibility to pitting corrosion at 4 MPa in the static seawater.展开更多
基金Supported by the National Key R&D Program of China(Nos.2017YFB0903700,2017YFB0903702)。
文摘Seawater pumped storage systems have bright prospect for energy storage in the coming years.The operational conditions of seawater pumped storage system are complex and harsh,where metal materials suff er from severe general and local corrosion.The corrosion behavior of Q235B carbon steel in simulated seawater pumped storage system under operational conditions was studied by potentiodynamic polarization,cyclic potentiodynamic polarization,and scanning electron microscope(SEM).The results confi rm that the working pressure aff ected the corrosion resistance of Q235B carbon steel during the whole immersion period.The pressure promoted the electrochemical reaction of corrosion process and the corrosion rate increased with pressure at the initial immersion period.However,the stable rust layer formed after longtime immersion at diff erent pressures increased the corrosion resistance of carbon steel,and decreased the corrosion degree of carbon steel.Meanwhile,the working pressure aff ected the pitting corrosion behavior of Q235B carbon steel during the whole immersion period.The pitting corrosion potential was more negative and the tendency of pitting corrosion was higher at 4 MPa during the whole immersion period.However,pressure also accelerated the formation rate of protective rust layer on the steel surface.Q235B carbon steel has higher susceptibility to pitting corrosion at 4 MPa in the static seawater.