Objective To investigate the effect of multiple coatings of the one-step self-etching adhesive on immediate microtensile bond strength to primary dentin.Methods Twelve caries-free human primary molars were randomly di...Objective To investigate the effect of multiple coatings of the one-step self-etching adhesive on immediate microtensile bond strength to primary dentin.Methods Twelve caries-free human primary molars were randomly divided into 2 groups with 6 teeth each.In group 1,each tooth was hemisected into two halves.One half was assigned to control subgroup 1,which was bonded with a single-step self-etching adhesive according to the manufacturer's instructions;the other half was assigned to experimental subgroup 1 in which the adhesive was applied three times before light curing.In group 2,the teeth were also hemisected into two halves.One half was assigned to control subgroup 2,which was bonded with the single-step self-etching adhesive according to the manufacturer's instructions;the other half was assigned to experimental subgroup 2 in which three layers of adhesive were applied with light curing each successive layer.Microtensile bond strength was immediately tested after specimen preparation.Results When the adhesive was applied three times before light curing,the bond strength of the experimental subgroup 1(n=33,57.49±11.61 MPa) was higher than that of the control subgroup 1(n=31,49.71±11.43 MPa,P<0.05).When using the technique of applying multiple layers of adhesive with light curing each successive layer,no difference of immediate bond strength was observed between the control subgroup 2 and the experimental subgroup 2(P>0.05).Conclusion Multiple coatings of one-step self-etching adhesive can increase the immediate bond strength to primary dentin when using the technique of light-curing after applying three layers of adhesive.展开更多
Objective To investigate whether multiple coatings can improve the bond durability of one-step self-etching adhesive to primary dentin. Methods Twelve caries-free human primary molars were randomly divided into 2 gro...Objective To investigate whether multiple coatings can improve the bond durability of one-step self-etching adhesive to primary dentin. Methods Twelve caries-free human primary molars were randomly divided into 2 groups. In group 1, each tooth was hemisected into 2 halves. One half was assigned to the control subgroup 1, which was bonded with a commercially available one-step self-etching adhesive according to the manufacturer＇s instruc- tions; the other half was assigned to experimental subgroup 1, in which the adhesive was applied three times before light curing. In group 2, one split half tooth was bonded with a commercially available one-step self-etching adhesive according to the manufacturer＇s instructions; for the other half, three layers of adhesive were applied with each successive layer of light curing. Specimens were stored in 0.9% NaC1 containing 0.02% sodium azide at 37℃ for 18 months and then were subjected to microtensile bond strength test and the fracture mode analysis. Results When the adhesive was applied three times before light curing, the bond strength of the ex- perimental subgroup 1 was significantly higher than that of the control subgroup 1 （47.46__＋13.91 vs. 38.12＋11.21 MPa, P〈O.05）. When using the technique of applying multiple layers of adhesive with each successive layer of light curing, no difference was observed in bond strength between the control subgroup and the experimental subgroup （39.40＋8.87 vs. 40.87-＋9.33 MPa, P〉O.05）. Conclusion Multiple coatings can improve the bond durability of one-step self-etching adhesive to primary dentin when using the technique of light-curing after applying 3 layers of adhesive.展开更多
The experiments were conducted to investigate the behavior of airborne particles adhering to the glass slides which were coated by several reagent films. The results showed that the adhesion level could be significant...The experiments were conducted to investigate the behavior of airborne particles adhering to the glass slides which were coated by several reagent films. The results showed that the adhesion level could be significantly changed by the reagent films. There were no evident rules between the average size of particles and sampling time interval, the placing angle and reagent concentration. The average particle size on the surface coated by composite reagent （2-3 μm） was smaller than that on the single reagent coated surface, while the largest particle size （4-5 μm） was observed on the surface coated with the Tween 60. The experiment also demonstrated that the best adhesive performance was obtained on the surface which was coated with 0.5% SDBS and 0.5% fluorocarbon composite reagents. The experiment results indicated that each reagent had a certain optimum adhesive range to the particle. The composite reagents with different proportion of single reagents exhibited some particular physical and chemical properties, which could effectively change the adhesive performance between the solid surface and the particles.展开更多
Pulp capping is one of the solving for keeping vital pulp in the case of dentin caries,reversible pulpitis or traumatic pulp exposure.The presence of bacteria on the cavity walls or in the pulp was the major factor th...Pulp capping is one of the solving for keeping vital pulp in the case of dentin caries,reversible pulpitis or traumatic pulp exposure.The presence of bacteria on the cavity walls or in the pulp was the major factor that leads to the failure of pulp capping.Traditional pulp capping agent,calcium hydroxide,may not prevent microleakage.Selfetching system is a newly developed adhesive system,which could provide less microleakage and would not break down or dissolve,preventing the oral fluids and bacteria from the pulp along the cavity wall.This may reduce such clinical problems as postoperative sensitivity,secondary caries and marginal discoloration.Researches showed that some kinds of self-etching adhesives induced the mild to moderate inflammatory pulp response,with negative bacterial staining.Inclusion of antibacterial components into self-etching system,such as 12-methacryloyloxydodecylpyridinium bromide(MDPB)may inhibit bacteria and provide better clinical effects.It is speculated that using the self-etching adhesive system containing the antibacterial agent,such as MDPB,to the dental pulp directly or indirectly,may inhibit bacteria after the placement of restoration as well as residual bacteria in the cavity.展开更多
文摘Objective To investigate the effect of multiple coatings of the one-step self-etching adhesive on immediate microtensile bond strength to primary dentin.Methods Twelve caries-free human primary molars were randomly divided into 2 groups with 6 teeth each.In group 1,each tooth was hemisected into two halves.One half was assigned to control subgroup 1,which was bonded with a single-step self-etching adhesive according to the manufacturer's instructions;the other half was assigned to experimental subgroup 1 in which the adhesive was applied three times before light curing.In group 2,the teeth were also hemisected into two halves.One half was assigned to control subgroup 2,which was bonded with the single-step self-etching adhesive according to the manufacturer's instructions;the other half was assigned to experimental subgroup 2 in which three layers of adhesive were applied with light curing each successive layer.Microtensile bond strength was immediately tested after specimen preparation.Results When the adhesive was applied three times before light curing,the bond strength of the experimental subgroup 1(n=33,57.49±11.61 MPa) was higher than that of the control subgroup 1(n=31,49.71±11.43 MPa,P<0.05).When using the technique of applying multiple layers of adhesive with light curing each successive layer,no difference of immediate bond strength was observed between the control subgroup 2 and the experimental subgroup 2(P>0.05).Conclusion Multiple coatings of one-step self-etching adhesive can increase the immediate bond strength to primary dentin when using the technique of light-curing after applying three layers of adhesive.
文摘Objective To investigate whether multiple coatings can improve the bond durability of one-step self-etching adhesive to primary dentin. Methods Twelve caries-free human primary molars were randomly divided into 2 groups. In group 1, each tooth was hemisected into 2 halves. One half was assigned to the control subgroup 1, which was bonded with a commercially available one-step self-etching adhesive according to the manufacturer＇s instruc- tions; the other half was assigned to experimental subgroup 1, in which the adhesive was applied three times before light curing. In group 2, one split half tooth was bonded with a commercially available one-step self-etching adhesive according to the manufacturer＇s instructions; for the other half, three layers of adhesive were applied with each successive layer of light curing. Specimens were stored in 0.9% NaC1 containing 0.02% sodium azide at 37℃ for 18 months and then were subjected to microtensile bond strength test and the fracture mode analysis. Results When the adhesive was applied three times before light curing, the bond strength of the ex- perimental subgroup 1 was significantly higher than that of the control subgroup 1 （47.46__＋13.91 vs. 38.12＋11.21 MPa, P〈O.05）. When using the technique of applying multiple layers of adhesive with each successive layer of light curing, no difference was observed in bond strength between the control subgroup and the experimental subgroup （39.40＋8.87 vs. 40.87-＋9.33 MPa, P〉O.05）. Conclusion Multiple coatings can improve the bond durability of one-step self-etching adhesive to primary dentin when using the technique of light-curing after applying 3 layers of adhesive.
基金Project (50974132) supported by the National Natural Science Foundation of ChinaProject (2011QNZT094) supported by the Fundamental Research Funds for the Central Universities, China
文摘The experiments were conducted to investigate the behavior of airborne particles adhering to the glass slides which were coated by several reagent films. The results showed that the adhesion level could be significantly changed by the reagent films. There were no evident rules between the average size of particles and sampling time interval, the placing angle and reagent concentration. The average particle size on the surface coated by composite reagent （2-3 μm） was smaller than that on the single reagent coated surface, while the largest particle size （4-5 μm） was observed on the surface coated with the Tween 60. The experiment also demonstrated that the best adhesive performance was obtained on the surface which was coated with 0.5% SDBS and 0.5% fluorocarbon composite reagents. The experiment results indicated that each reagent had a certain optimum adhesive range to the particle. The composite reagents with different proportion of single reagents exhibited some particular physical and chemical properties, which could effectively change the adhesive performance between the solid surface and the particles.
文摘Pulp capping is one of the solving for keeping vital pulp in the case of dentin caries,reversible pulpitis or traumatic pulp exposure.The presence of bacteria on the cavity walls or in the pulp was the major factor that leads to the failure of pulp capping.Traditional pulp capping agent,calcium hydroxide,may not prevent microleakage.Selfetching system is a newly developed adhesive system,which could provide less microleakage and would not break down or dissolve,preventing the oral fluids and bacteria from the pulp along the cavity wall.This may reduce such clinical problems as postoperative sensitivity,secondary caries and marginal discoloration.Researches showed that some kinds of self-etching adhesives induced the mild to moderate inflammatory pulp response,with negative bacterial staining.Inclusion of antibacterial components into self-etching system,such as 12-methacryloyloxydodecylpyridinium bromide(MDPB)may inhibit bacteria and provide better clinical effects.It is speculated that using the self-etching adhesive system containing the antibacterial agent,such as MDPB,to the dental pulp directly or indirectly,may inhibit bacteria after the placement of restoration as well as residual bacteria in the cavity.