In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The...In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The microstructures,XRD patterns,FTIR spectra,UV-Vis-NIR spectra thermo-conductivity,thermo-stability and photothermal effects of these composite films were all characterized.These results indicated that Ti_(2)O_(3) particles were well dispersed throughout the polyvinyl alcohol(PVA)matrix in the PVA/Ti_(2)O_(3) composite films.And Ti_(2)O_(3) particles could also effectively improve the photothermal properties of the composite films which exhibited high light absorption and generated a high temperature(about 57.4℃for film with 15 wt%Ti_(2)O_(3) amount)on the surface when it was irradiated by a simulated sunlight source(1 kW/m^(2)).展开更多
Tin oxide (SnO<sub>2</sub>) thin films were deposited on glass substrate by Chemical Bath Deposition (CBD), Drop-Cast and Dip-Coating method. The thin films were post-annealed at 500°C for 2 hours....Tin oxide (SnO<sub>2</sub>) thin films were deposited on glass substrate by Chemical Bath Deposition (CBD), Drop-Cast and Dip-Coating method. The thin films were post-annealed at 500°C for 2 hours. The structural, optical, and electrical properties of the SnO<sub>2</sub> thin films were investigated by using XRD, FTIR, SEM, EDX, UV-Vis spectroscopy, and Electrometer experiment. The XRD patterns of SnO<sub>2</sub> thin films deposited on glass substrate by CBD method, Drop-Cast method and Dip-Coating method showed cubic, tetragonal and amorphous structures respectively. The FTIR spectrum exhibited the strong presence of SnO<sub>2</sub> with the characteristic vibrational mode of Sn-O-Sn. The SEM analysis was observed that the surface morphology of the thin films toughly depends on the deposition methods of the SnO<sub>2</sub> thin films. EDX measurement confirmed that the thin films are the composition of Tin (Sn) and Oxygen (O<sub>2</sub>). The optical band gap of SnO<sub>2 </sub>thin films deposited by CBD method, Drop-Cast method and Dip-Coating method is found to be 3.12 eV, 3.14 eV and 3.16 eV respectively. Thin films deposited by Dip-Coating method showed the highest band gap. The electrical results confirmed that the SnO<sub>2</sub> thin films are good conductors and pursued Ohm’s Law. These properties of the SnO<sub>2</sub> thin films brand are appropriate for application in solar cell assembly, gas sensor devices and transparent electrodes of panel displays.展开更多
基金Funded by the Youth Backbone Teacher Training Plan in University of Henan Province(No.21220028)Science and Technology Research Project of Henan Province(No.242102321066)+2 种基金Natural Science Foundation of Henan Province(No.232300420312)Henan University of Technology Young Backbone Teacher Training Plan(No.21421260)the Innovation Training Program for College Students in Henan Province(No.202310463046)。
文摘In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The microstructures,XRD patterns,FTIR spectra,UV-Vis-NIR spectra thermo-conductivity,thermo-stability and photothermal effects of these composite films were all characterized.These results indicated that Ti_(2)O_(3) particles were well dispersed throughout the polyvinyl alcohol(PVA)matrix in the PVA/Ti_(2)O_(3) composite films.And Ti_(2)O_(3) particles could also effectively improve the photothermal properties of the composite films which exhibited high light absorption and generated a high temperature(about 57.4℃for film with 15 wt%Ti_(2)O_(3) amount)on the surface when it was irradiated by a simulated sunlight source(1 kW/m^(2)).
文摘Tin oxide (SnO<sub>2</sub>) thin films were deposited on glass substrate by Chemical Bath Deposition (CBD), Drop-Cast and Dip-Coating method. The thin films were post-annealed at 500°C for 2 hours. The structural, optical, and electrical properties of the SnO<sub>2</sub> thin films were investigated by using XRD, FTIR, SEM, EDX, UV-Vis spectroscopy, and Electrometer experiment. The XRD patterns of SnO<sub>2</sub> thin films deposited on glass substrate by CBD method, Drop-Cast method and Dip-Coating method showed cubic, tetragonal and amorphous structures respectively. The FTIR spectrum exhibited the strong presence of SnO<sub>2</sub> with the characteristic vibrational mode of Sn-O-Sn. The SEM analysis was observed that the surface morphology of the thin films toughly depends on the deposition methods of the SnO<sub>2</sub> thin films. EDX measurement confirmed that the thin films are the composition of Tin (Sn) and Oxygen (O<sub>2</sub>). The optical band gap of SnO<sub>2 </sub>thin films deposited by CBD method, Drop-Cast method and Dip-Coating method is found to be 3.12 eV, 3.14 eV and 3.16 eV respectively. Thin films deposited by Dip-Coating method showed the highest band gap. The electrical results confirmed that the SnO<sub>2</sub> thin films are good conductors and pursued Ohm’s Law. These properties of the SnO<sub>2</sub> thin films brand are appropriate for application in solar cell assembly, gas sensor devices and transparent electrodes of panel displays.