The influence of rare earth( RE) content on mechanical properties and abrasion resistance of low chromium semi-steel was studied by means of metallographic examination,scanning electron microscopic examination and mec...The influence of rare earth( RE) content on mechanical properties and abrasion resistance of low chromium semi-steel was studied by means of metallographic examination,scanning electron microscopic examination and mechanical property test. The experiment results show that RE can improve the comprehensive properties,especially in combination with proper heat treatment. The optimum properties of low chromium semi-steel modified by RE of 0. 25 % could be obtained by normalization at 950 ℃ for 3 h. The main reason is the change in morphology and distribution of eutectic carbide and the precipitation of granular carbides.展开更多
The preparing method,rolling technology and mechanical properties of low chromium semi-steel grinding ball by cross rolling were studied.The results show that when the low chromium semi-steel bar is forged from55mm to...The preparing method,rolling technology and mechanical properties of low chromium semi-steel grinding ball by cross rolling were studied.The results show that when the low chromium semi-steel bar is forged from55mm to50mm,cross-rolled into grinding ball at 1 000-1 050℃,air cooled and tempered at 550℃for 2h,the best mechanical properties,especially the abrasive resistance under the action of hard abrasive,can be obtained.展开更多
In heat treatment process,the effect of rare earth elements on the formation and growth of granular carbides in cast semi-steel and the growing mechanism of granular carbides were studied. The experimental results sho...In heat treatment process,the effect of rare earth elements on the formation and growth of granular carbides in cast semi-steel and the growing mechanism of granular carbides were studied. The experimental results show that RE is helpful to the formation of granular carbides during high-temperature heat treatment process,but in following isothermal process,it has little effect on the growth of granular carbides. The feature of the growth of carbide proceeds is the size increment and the amount decrement of carbide particles,the volume fraction of carbides keeps constant. And the mathematical model of the growth rate of granular carbides is put forward.展开更多
The formation and growth of thermal fatigue crack in low-chromium semi-steel were investigated by means of optical microscope and scanning electron microscope, and the function of RE in low-chromium semi-steel was ana...The formation and growth of thermal fatigue crack in low-chromium semi-steel were investigated by means of optical microscope and scanning electron microscope, and the function of RE in low-chromium semi-steel was analyzed. The results show that the thermal fatigue cracks are mainly generated at eutectic carbides, and the cracks not only grow and spread but also join each other. RE can improve the eutectic carbide′s morphology, inhibit the generation and propagation of thermal fatigue cracks, and therefore promote the activation energy for the crack′s propagation, which is especially more noticeable in case of the RE modification in combination with heat treatment. The mathematical model of the crack propagation is put forward.展开更多
The low-energy multi-impact fracture resistance of the cross rolled low chromium cast semi-steel containing RE grinding balls was studied. Moreover, its damage mode was analyzed by means of metallographic examination,...The low-energy multi-impact fracture resistance of the cross rolled low chromium cast semi-steel containing RE grinding balls was studied. Moreover, its damage mode was analyzed by means of metallographic examination, scanning electron microscopic examination and drop ball test. The results show that it can obtain extractive impact fracture resistance after proper heat treatment. More advantages were obtained for the ball worked in the condition of low-imp ductility act. The main reasons are the function of RE and the change in morphology of eutectic carbide network.展开更多
Experiments were carried out on carburizing and temperature rising of the semi steel melt in a plasma induction furnace.Influence of many factors, such as power supply mode,position of the plasma torch and bottom b...Experiments were carried out on carburizing and temperature rising of the semi steel melt in a plasma induction furnace.Influence of many factors, such as power supply mode,position of the plasma torch and bottom blown gas stirring,on heating efficiency and melt temperature distribution was studied. Melt temperature could be effectively controlled by plasma heating,and carbon content of semi steel melt increased from 1.92 % to 4.58 %, and the utilization rate of carbon reached up to 61.57 % during carburizing of the melt.展开更多
The effect of rare earth elements on eutectic carbide′s morphology of low chromium semi steel in as cast state and after heat treatment was investigated, and accordingly, the thermal fatigue property of this mater...The effect of rare earth elements on eutectic carbide′s morphology of low chromium semi steel in as cast state and after heat treatment was investigated, and accordingly, the thermal fatigue property of this material was studied. The results show that RE can improve the eutectic carbide′s morphology, inhibit the formation and propagation of thermal fatigue cracks, therefore, promote the thermal fatigue property, which is more noticeable in case of the RE modification in combination with heat treatment. The optimal thermal fatigue property can be obtained when treated with 0.2% RE modification as well as normalization at 950 ℃ for 3 h.展开更多
The desulfurization and resulfurization of slag containing oxides of vanadium and titanium(CaO–SiO_(2)–MgO–Al_(2)O_(3)–V_(2)O_(3)–TiO_(2)–FeO)in the pretreatment of semi-steel desulfurization at 1623 K were inve...The desulfurization and resulfurization of slag containing oxides of vanadium and titanium(CaO–SiO_(2)–MgO–Al_(2)O_(3)–V_(2)O_(3)–TiO_(2)–FeO)in the pretreatment of semi-steel desulfurization at 1623 K were investigated.Based on the ionic structure theory of slag,it could be concluded that V_(2)O_(3) and TiO_(2) combined with(O_(2)–)to form complex anions including VO_(3)^(3–),TiO_(4)^(4–),etc.,which reduced the activity of(O_(2)–)and decreased the sulfur partition ratio(LS).And FeO enhanced the activity of[O]at the slag–metal interface,which decreased the desulfurization capacity of the slag.Compared to the binary basicity,the presented basicity expression containing V_(2)O_(3) and TiO_(2) described the relationship between LS and basicity more accurately.Considering the problems of dilute slag,a large amount of residual slag and much resulfurization in the slagging-off process after pretreatment,the effect of CaO+C-based slag modifier on the resulfurization,melting point and viscosity of the desulfurization slag was investigated.It was proposed that adding 5%–10%of the slag modifier to the desulfurization slag after desulfurization decreased the resulfurization effectively.And the added modifier adjusted the slag viscosity well,which helped to reduce iron loss and residual slag.展开更多
基金Item Sponsored by Science and Technology Guiding Project of Hebei Province of China(94122123)
文摘The influence of rare earth( RE) content on mechanical properties and abrasion resistance of low chromium semi-steel was studied by means of metallographic examination,scanning electron microscopic examination and mechanical property test. The experiment results show that RE can improve the comprehensive properties,especially in combination with proper heat treatment. The optimum properties of low chromium semi-steel modified by RE of 0. 25 % could be obtained by normalization at 950 ℃ for 3 h. The main reason is the change in morphology and distribution of eutectic carbide and the precipitation of granular carbides.
基金Item Sponsored by Guiding Program of Science and Technology Research of Hebei of China(94122123)
文摘The preparing method,rolling technology and mechanical properties of low chromium semi-steel grinding ball by cross rolling were studied.The results show that when the low chromium semi-steel bar is forged from55mm to50mm,cross-rolled into grinding ball at 1 000-1 050℃,air cooled and tempered at 550℃for 2h,the best mechanical properties,especially the abrasive resistance under the action of hard abrasive,can be obtained.
文摘In heat treatment process,the effect of rare earth elements on the formation and growth of granular carbides in cast semi-steel and the growing mechanism of granular carbides were studied. The experimental results show that RE is helpful to the formation of granular carbides during high-temperature heat treatment process,but in following isothermal process,it has little effect on the growth of granular carbides. The feature of the growth of carbide proceeds is the size increment and the amount decrement of carbide particles,the volume fraction of carbides keeps constant. And the mathematical model of the growth rate of granular carbides is put forward.
文摘The formation and growth of thermal fatigue crack in low-chromium semi-steel were investigated by means of optical microscope and scanning electron microscope, and the function of RE in low-chromium semi-steel was analyzed. The results show that the thermal fatigue cracks are mainly generated at eutectic carbides, and the cracks not only grow and spread but also join each other. RE can improve the eutectic carbide′s morphology, inhibit the generation and propagation of thermal fatigue cracks, and therefore promote the activation energy for the crack′s propagation, which is especially more noticeable in case of the RE modification in combination with heat treatment. The mathematical model of the crack propagation is put forward.
文摘The low-energy multi-impact fracture resistance of the cross rolled low chromium cast semi-steel containing RE grinding balls was studied. Moreover, its damage mode was analyzed by means of metallographic examination, scanning electron microscopic examination and drop ball test. The results show that it can obtain extractive impact fracture resistance after proper heat treatment. More advantages were obtained for the ball worked in the condition of low-imp ductility act. The main reasons are the function of RE and the change in morphology of eutectic carbide network.
文摘Experiments were carried out on carburizing and temperature rising of the semi steel melt in a plasma induction furnace.Influence of many factors, such as power supply mode,position of the plasma torch and bottom blown gas stirring,on heating efficiency and melt temperature distribution was studied. Melt temperature could be effectively controlled by plasma heating,and carbon content of semi steel melt increased from 1.92 % to 4.58 %, and the utilization rate of carbon reached up to 61.57 % during carburizing of the melt.
文摘The effect of rare earth elements on eutectic carbide′s morphology of low chromium semi steel in as cast state and after heat treatment was investigated, and accordingly, the thermal fatigue property of this material was studied. The results show that RE can improve the eutectic carbide′s morphology, inhibit the formation and propagation of thermal fatigue cracks, therefore, promote the thermal fatigue property, which is more noticeable in case of the RE modification in combination with heat treatment. The optimal thermal fatigue property can be obtained when treated with 0.2% RE modification as well as normalization at 950 ℃ for 3 h.
文摘The desulfurization and resulfurization of slag containing oxides of vanadium and titanium(CaO–SiO_(2)–MgO–Al_(2)O_(3)–V_(2)O_(3)–TiO_(2)–FeO)in the pretreatment of semi-steel desulfurization at 1623 K were investigated.Based on the ionic structure theory of slag,it could be concluded that V_(2)O_(3) and TiO_(2) combined with(O_(2)–)to form complex anions including VO_(3)^(3–),TiO_(4)^(4–),etc.,which reduced the activity of(O_(2)–)and decreased the sulfur partition ratio(LS).And FeO enhanced the activity of[O]at the slag–metal interface,which decreased the desulfurization capacity of the slag.Compared to the binary basicity,the presented basicity expression containing V_(2)O_(3) and TiO_(2) described the relationship between LS and basicity more accurately.Considering the problems of dilute slag,a large amount of residual slag and much resulfurization in the slagging-off process after pretreatment,the effect of CaO+C-based slag modifier on the resulfurization,melting point and viscosity of the desulfurization slag was investigated.It was proposed that adding 5%–10%of the slag modifier to the desulfurization slag after desulfurization decreased the resulfurization effectively.And the added modifier adjusted the slag viscosity well,which helped to reduce iron loss and residual slag.