Optimization of the content of tricalcium silicate（C 3 S）of high cementing clinker was investigated.The content of free-CaO（f-CaO）,mineral composite,the content of C 3 S in the clinker and the hydration product we...Optimization of the content of tricalcium silicate（C 3 S）of high cementing clinker was investigated.The content of free-CaO（f-CaO）,mineral composite,the content of C 3 S in the clinker and the hydration product were analyzed by chemical analysis and X-ray diffraction（XRD）.＂K Value＂method of QXRD was selected as a quantitative analysis way to measure the content of C 3 S,and the strength of cement paste was determined.The results show that at a water cement ratio of 0.29,the strength of cement paste with 73%C 3 S can be up to 97.5 MPa at 28 days age.The strength at 28 d of cement with 73%C 3 S is 16%higher than that with 78%C 3 S at water requirement for normal consistency.The relationship between the strength of high cementing Portland cement and the content of C 3 S in the clinker is nonlinear.According to the strength of cement paste,the optimal content of C 3 S in cement clinker is around 73%in this paper.展开更多
基金Funded by National Basic Research Program of China(No. 2009CB623100)National Eleventh Five-Year Scientific and Technical Support Plans(No.2006BAF02A24)+2 种基金Natural Science Fund for Colleges and Universities in Jiangsu Province(No.08KJB430006)Open Fund for the Key Laboratory of Inorganical and Composite Materials in Jiangsu Province(No. wjjqfhxc1200801)Innovation Fund of Doctoral Dissertation of Nanjing University of Technology(No.BSCX200705)
文摘Optimization of the content of tricalcium silicate（C 3 S）of high cementing clinker was investigated.The content of free-CaO（f-CaO）,mineral composite,the content of C 3 S in the clinker and the hydration product were analyzed by chemical analysis and X-ray diffraction（XRD）.＂K Value＂method of QXRD was selected as a quantitative analysis way to measure the content of C 3 S,and the strength of cement paste was determined.The results show that at a water cement ratio of 0.29,the strength of cement paste with 73%C 3 S can be up to 97.5 MPa at 28 days age.The strength at 28 d of cement with 73%C 3 S is 16%higher than that with 78%C 3 S at water requirement for normal consistency.The relationship between the strength of high cementing Portland cement and the content of C 3 S in the clinker is nonlinear.According to the strength of cement paste,the optimal content of C 3 S in cement clinker is around 73%in this paper.