Structure, Formation, Properties, and Application of Calcium and Magnesium Silicate Hydrates System—A Review

In order to expand the advantages of strong durability and high compressive strength of calcium silicate hydrates(C-S-H),at the same time to make up for the poor early mechanical strength of magnesium silicate hydrates (M-S-H),we present the features and advantages of C-S-H and M-S-H and a comprehensive review of the progress on CaO-MgO-SiO_(2)-H_(2)O.Moreover,we systematically describe natural calcium and magnesium silicate minerals and thermodynamic properties of CaO-MgO-SiO_(2)-H_(2)O.The effect of magnesium on C-S-H and calcium on M-S-H is summarized deeply;the formation and structural feature of CaO-MgO-SiO_(2)-H_(2)O is also explained in detail.Finally,the development of calcium and magnesium silicate hydrates in the future is pointed out,and the further research is discussed and estimated.

Carbonation of Dicalcium Silicate Enhanced by Ammonia Bicarbonate and Its Mechanism

The strength development law of γ-type dicalcium silicate (γ-C_(2)S) under different carbonation processes was investigated,and the carbonation mechanism of γ-C_(2)S under the action of NH_(4)HCO_(3) was clarified by using a wide range of test methods,including XRD and SEM.A method of saturated NH_(4)HCO_(3) solution as a curing agent was identified to improve the carbonation efficiency and enhance the carbonation degree of γ-C_(2)S,and then a high-strength carbonated specimen was obtained.Microhardness analysis and SEM morphology analysis were conducted on the carbonised specimens obtained under atmospheric pressure carbonisation conditions using the curing agent.It was found that γ-C_(2)S could perform carbonisation well under atmospheric pressure,which promoted the carbonisation efficiency and decreased the carbonisation cost simultaneously.Therefore,a new carbonisation process solution was proposed for the rapid carbonisation of γ-C_(2)S.

Natural Silicate as a Solid Support for the Calix[4]Thiophosphorus Derivative for Removal Mercury (II), as Picrate from Water

Currently a technique widely used for gold extraction is mercury by amalgamation technique, the tailing produced pollutes water of all kinds, so it is necessary to develop a form of selective mitigation, for which it is necessary to use complexing agents based on calixarene functionalized with mercury sequestering agents. These are immobilized by adding supports based on natural silica to form polymers and make them insoluble in all types of solvents, so that they can be used as an extractor and at the same time regenerate to their original properties for continuous reuse.

Effectiveness of Sodium Silicate on the Corrosion Protection of AA7075-T6 Aluminium Alloy in Sodium Chloride Solution

The influence of sodium silicate on the corrosion behaviour of aluminium alloy 7075-T6 in 0.1 M sodium chloride solution was studied by open circuit potential (OCP) and electrochemical impedance spectroscopy (EIS) techniques. Scanning electron microscopy (SEM) was used to characterize the AA7075-T6 surface. Silicate can significantly reduce corrosion deterioration and the inhibition efficiency increases with the concentration of Na2SiO3. The corrosion inhibition mechanism involves the formation of a protective film over the alloy surface by adsorption of aluminosilicate anions from solution, as has also been suggested by others in literature.

ERK phosphorylation functions in invadopodia formation in tongue cancer cells in a novel silicate fibre-based 3D cell culture system

To screen for additional treatment targets against tongue cancer, we evaluated the contributions of extracellular signal-related kinase(ERK), AKT and ezrin in cancer development. Immunohistochemical staining showed that ERK and ezrin expressions were significantly higher in invasive squamous cell carcinoma than in carcinoma in situ. To investigate the roles of ERK and ezrin in cancer development, we used the non-woven silica fibre sheet Cellbedwith a structure resembling the loose connective tissue morphology in a novel 3 D culture system. We confirmed that the 3 D system using CellbedTMaccurately mimicked cancer cell morphology in vivo. Furthermore, cell projections were much more apparent in 3 D-cultured tongue cancer cell lines than in 2 D cultures. Typically, under conventional 2 D culture conditions, F-actin and cortactin are colocalized in the form of puncta within cells.However, in the 3 D-cultured cells, colocalization was mainly observed at the cell margins, including the projections. Projections containing F-actin and cortactin colocalization were predicted to be invadopodia. Although suppressing ezrin expression with small interfering RNA transfection caused no marked changes in morphology, cell projection formation was decreased, and the tumour thickness in vertical sections after 3 D culture was markedly decreased after suppressing ERK activity because both the invasion ability and proliferation were inhibited. An association between cortactin activation as well as ERK activity and invadopodia formation was detected. Our novel 3 D culture systems using Cellbed? are simple and useful for in vitro studies before conducting animal experiments. ERK contributes to tongue cancer development by increasing both cancer cell proliferation and migration via cortactin activation.

Selecting the Technology of Sodium Silicate Modified Poplar with the Highest Performance by Fuzzy Orthogonal Method

Sodium silicate modification can improve the overall performance of wood.The modification process has a great influence on the properties of modified wood.In this study,a new method was introduced to analyze the wood modification process,and the properties of modified wood were studied.Poplar wood was modified with sodium silicate by vacuum-pressure impregnation.After screening using single-factor experiments,an orthogonal experiment was carried out with solution concentration,impregnation time,impregnation pressure,and the cycle times as experimental factors.The modified poplar with the best properties was selected by fuzzy mathematics and characterized by SEM,FT-IR,XRD and TG.The results showed that some lignin and hemicellulose were removed from the wood due to the alkaline action of sodium silicate,and the orderly crystal area of poplar became disorderly,resulting in the reduction of crystallinity of the modified poplar wood.FT-IR analysis showed that sodium silicate was hydrolyzed to form polysilicic acid in wood,and structural analysis revealed the formation of Si-O-Si and Si-O-C,indicating that sodium silicate reacted with fibers on the wood cell wall.TG-DTG curves showed that the final residual mass of modified poplar wood increased from 25%to 67%,and the temperature of the maximum loss rate decreased from 343℃ to 276℃.The heat release and smoke release of modified poplar wood decreased obviously.This kind of material with high strength and fire resistance can be used in the outdoor building and indoor furniture.

Effect of Pb Ions on the Ionic Conductivity of Some Silicate Glass Systems

Conductivity of glasses in the systems SiO2.PbO.RO, (where R=Ca, Sr or Ba) was investigated between room temperature and 530 K. The dependence of log resistivity as well as the activation energy on the PbO content has been studied. Based on the present experimental results, the possible different conduction mechanisms in such glasses are discussed. It was postulated that Pb2+ ions may represent the major charge carrying species in these glasses. This assumption was confirmed by the calculations of the mean distance between the interstitial Pb2+ ions and the effective center of the O2- ions in the glass networks. The variation in the values of the density and the molar volume with PbO content is also discussed in view of the obtained activation energies for the studied glass-systems.

Influence of Na_(2)SiO_(3)/NaOH Ratio on Calcined Magnesium Silicate Based Geopolymer——Experimental and Predictive Study

This study aims to investigate the behavior of alkali activated mortar,which is made of naturally available magnesium silicate as source material.For magnesium silicate,ultrafine natural steatite powder(UFNSP)is used as the primary source of binder,and the activation is initiated through the alkali liquid which is proportioned in various combinations of silicate to hydroxide ratio(Na_(2)SiO_(3)/Na OH)ratio,and this ratio in this study varies from 1 to 3.The UFNSP is calcined at two difierent temperatures,700 and 1000℃.The mortar mix is proportioned as 1:3 between powder and the fine aggregate,and the mortar is prepared with hydroxide molarity(M)of 10 M.The mortar is cured for 48 hours at 60℃and the compressive strength was studied.All the mix were studied for its microstructural behavior along with compressive strength.The mix proportion of the mortar,and the results obtained through microstructural characterization were combinedly formed as input for artificial neural network(ANN)predictive modelling.The model is designed to predict the compressive strength,which is trained through Bayesian regularization algorithm with varying hidden neurons of 7 to 10.This experimental and predictive study shows that the strength is influenced by both Na_(2)SiO_(3)/Na OH ratio and calcination process.And the ANN is influenced by mainly calcination temperature and uncorrelation occurs in selected samples of 1000℃calcined UFNSP mix.

Thermoluminescent response of gamma irradiated Na^(+)–Cu^(+) ionexchanged silicate glass in large dose range

The introduction of metals into vitreous matrices is the origin of various interesting phenomena;in particular,the presence of copper ions in glass has been the subject of considerable research because of its numerous applications.The ion-exchange process is primarily used to introduce copper ions into glass matrices.The thermoluminescence(TL)of silicate glass was studied to evaluate its potential as gamma-sensitive material for dosimetric applications;the effect of copper doping on the thermoluminescent sensitivity was investigated using the Cu-Na ion-exchange technique for different concentrations and doping conditions,over a wide dose range of 10 mGy to 100 kGy.The results showed that Cu doping significantly improved the sensitivity of the glasses to gamma radiation.After the ion-exchange,two peaks appeared in the glow curves at approximately 175 and 230°C,respectively,which possibly originated from the Cu^(+) centers,along with a weak TL peak at around 320℃.We also attempted to explain the origin of the observed thermoluminescence by exploiting the Electron paramagnetic resonance(EPR)spectra.The results clearly show quenching of the TL emission with increasing copper concentrations.The present work indicates that the thermoluminescence response of these glasses to gamma rays can be reasonably measured in the range of 0.001-100 kGy.This study also facilitates the understanding of the basic TL mechanism in this glass system.

Variation in concentration of dissolved silicate in the Eastern Philippine deep sea

Upper Circumpolar Deep Water(UCDW)and North Pacifi c Deep Water(NPDW)coexist in the upper deep layer(i.e.,with a 1.2-2.0-℃potential temperature range and a 2000-4100-dbar pressure range)of the Eastern Philippine Sea.They have similar properties in potential temperature and salinity,while have a signifi cant diff erence in dissolved silicate.Based on the repeated observations along a 137°E transect from the World Ocean Database(WOD18),this study revealed the interannual variability of dissolved silicate in the upper deep layer of the Eastern Philippine Sea.Dissolved silicate increased in 1995,1996,2005,2006,and 2007,and decreased in 1997,2000,2001,2002,and 2004.Composition analysis showed that the large diff erence between positive and negative dissolved silicate anomalies occurred mainly at~15°N and north of 25°N,with the concentration reaching 4.25μmol/g.Further analysis indicated that the interannual dissolved silicate variability was related to the zonal current variation in the upper deep layer.The relatively strong(weak)westward current transport increased(decreased)NPDW to the Eastern Philippine Sea,thereby resulting in increased(decreased)dissolved silicate.

Reclamation of CO_(2) sodium silicate used sands by steam leaching

The bond film on the surface of the CO_(2) sodium silicate used sands is not easy to decompose,therefore,it is difficult to reclaim used sands.A new reclamation method of CO_(2) sodium silicate used sands was developed by steam leaching,which can reduce the water consumption of reclamation and improve the removal effect of sodium silicate bond film.Firstly,the leaching effect of the sodium silicate sands after 20/200/400/600/800/1,000°C heat preservation treatment was simulated.Furthermore,the influence of the leaching time on the removal effect of the sodium silicate bond film was studied.Finally,the casting properties of the reclaimed sands after the leaching reclamation treatment were tested.The results show for simulated used sands after 30 min of steam leaching,the removal ratio of the alkali exceeds 84.1%,the removal ratio of silicate is 86.2%,and the removal ratio of carbonate is 93.6%.The removal rate of alkali,silicate and carbonate is relatively low in the leaching time of 30-50 min.Considering the reclamation effect and cost,the leaching time is controlled in 30 min.Water consumption is only 60%of the mass of used sands for 30 min steam leaching,while it is 200%for wet reclamation.Morphological analysis shows that most of the hazardous substances in the used sands are removed in 30 min steam leaching,and the reclaimed sands surface after steam leaching in 50 min is as smooth as new sands.After 30 min of steam leaching,the alkali removal effect of the factory used sands can reach 81.5%,the water consumption by the steam leaching reclamation is 58%of the mass of the used sand,which is similar to the result of simulated used sands.The performance of reclaimed sands obtained after 30 min steam leaching is better than that of new sands when the amount of sodium silicate added is 6%of the mass of the reclaimed sands and the CO_(2) blowing time is 15 s:the 24 h ultimate compressive strength of reclaimed sands is 5.6 MPa(equated with new sands),and the collapsibility compressive strength is 5.2 MPa,which is lower than the collapsibility compressive strength of new sands(7.7 MPa).This indicates that the reclamation of CO_(2) sodium silicate used sands by steam leaching is a feasible method.

Improvement of Selected Morphological, Physiological, and Biochemical Parameters of Banana (Musa acuminata L.) Using Potassium Silicate under Drought Stress Condition Grown in vitro

Drought stress has become more common in recent years as a result of climate change impacts on the production of banana crops and other fruit trees.The growth and productivity of Musa spp are severely impacted by the gradual degradation of water resources and the erratic distribution pattern of annual precipitation amount.The aim of the work includes increased drought tolerance in light of water scarcity in the world as a result of the bananas’being gluttonous for water needs.This investigation was carried out from 2019 to 2020 to study the effect of potassium silicate on morphological growth and biochemical parameters of Musa acuminata L under drought stress by PEG.As a result,drought stress reduced the morphological characteristics such as shoots number,shoot length,roots number,and survival percentage and biochemical characteristics such as chlorophyll a,b,carotenoids,stomatal status,and RWC.While proline content increased in the leaf of M.acuminata L.Media complemented with K2SiO3(2 to 6 mM)either individually or in combination with PEG led to an improvement in all morphological and biochemical characteristics.The activities of CAT,POD,and PPO enzymes increased significantly compared to control.Furthermore,the lowest PPO,CAT,and POD activity were achieved.Additionally,K2SiO3 treatments under drought stress successfully enhanced the leaf stomatal behavior.Our results suggest that K2SiO3 can help to maintain plant integrity in the tested cultivar under drought stress.

Study on the Attack of Molten Silicates on Plasma-Sprayed Thermal Barrier Coatings

Thermal barrier coating (TBC) revolutionized the industry by allowing higher operating temperatures for equipment, such as gas turbines in the aeronautical industry. However, at high temperatures, the TBC is exposed to the attack of molten silicates, known as CMAS (Calcium-Magnesium-Alumino-Silicate), which are particles from the environment that infiltrate the TBC, causing delamination. In this study, samples coated with TBC by thermal spray and covered with CMAS were evaluated at temperatures of 1200˚C and 1250˚C. For each temperature, exposure times of 1 h and 5 h were used. Samples with longer exposure time had a considerable volume increase. The main contribution of this work was to demonstrate the non-wettability of the CMAS, even in the 5-h heat treatments, which prevented its infiltration in the deeper regions. The conditions to guarantee the formation of the silicate and its consequent wettability are also discussed.

Study on Multi-Scale Tensile Strength and Tensile Strain of Calcium Silicate Hydrate Layered Nanocomposites Under External Physical Field

Calcium silicate hydrate(C-S-H)is the mainly strength source of cement-based materials,but there is little basic research.In this paper,molecular dynamics method is applied to analyze the multi-scale tensile strength and tensile strain of C-S-H layered materials under the condition of external physical fields(temperature and strain rate).The results show that the tensile strength and strain of C-S-H model decrease with temperature raises.The temperature(from 1 K to 600 K)has obvious influence on the tensile strain and strength of C-S-H layered materials.In addition,at(0.00025 ps^(-1)-0.001 ps^(-1)),the tensile strain and strength of C-S-H layered materials are less sensitive to strain rate.The whole model is closer to a 3-dimensional deformation.However,at(0.001 ps^(-1)-0.005 ps^(-1)),the dynamic load effect begins to increase,and the work done by the load per unit time increased.The tensile strain and strength of C-S-H layered materials indicates intensified by the change of strain rate.The energies are randomly distributed in the system,not concentrated in a certain area.

Development of Kaolin and Glass Fiber Reinforced Composites for Thermal Insulating Panels

In our modern world, where conserving energy is highly valued, thermal insulation panels play a crucial role in reducing heat transfer between two spaces, surfaces, or materials. They are used to enhance the energy efficiency of various industrial applications by minimizing heat loss and temperature control. These panels function as silent protectors, aiding in reducing energy consumption and making things more sustainable and better for the environment. This is where composite materials come in;they are known for their lightweight nature, high strength-to-weight ratio, and excellent thermal insulation properties and have gained significant attention. Researchers are actively engaged in various studies aimed at enhancing these materials further. This research project focuses on the development of kaolin and glass fiber-reinforced composites for thermally insulating panels, to which natural strengthening materials like corn husk and bamboo fibers are added. The aim is to create cost-effective and efficient composite materials for thermal insulation applications by incorporating these components with a binder consisting of potassium silicate, hydroxide, and distilled water. This project involves conducting compression tests, bending tests, impact tests, thermal conductivity measurements, and microscopic analysis to evaluate the mechanical and thermal properties of the developed composites. The profound impact of these engineered composites on thermal insulation panels stands to revolutionize energy conservation efforts, offering a potent avenue to minimize heat loss and enhance overall energy efficiency across an array of industrial sectors.

Adsorption of Methylene Blue on magnesium silicate: Kinetics, equilibria and comparison with other adsorbents

Batch adsorption from aqueous solutions in a slightly basic medium of Methylene Blue, up to 2500 mg/L, onto synthetic magnesium silicate （Florisil） of three particle size ranges （mean diameters of 112, 200 and 425 μm） was compared to the corresponding adsorption onto activated carbon and Amberlite XAD-2. The best fit of the kinetic results was achieved by a pseudo second-order equation. The equilibrium data were found to be well represented by the Langmuir isotherm equation. Amberlite XAD-2, an unspecific adsorbent capable of adsorbing exclusively through a surface effect, exhibited a poor dye uptake, confirming that the adsorption mechanism on Florisil was due to electrostatic attraction and ion exchange. Moreover, the comparison between Florisil and the other adsorbents was performed on the basis of the evaluation of the surface area and pore volume occupied by the adsorbed dye.

Fractionation and solubility of cadmium in paddy soils amended with porous hydrated calcium silicate

Previous studies have shown that porous hydrated calcium silicate （PS） is very effective in decreasing cadmium （Cd） content in brown rice. However, it is unclear whether the PS influences cadmium transformation in soil. The present study examined the effect of PS on pH, cadmium transformation and cadmium solubility in Andosol and Alluvial soil, and also compared its effects with CaCO3, acidic porous hydrated calcium silicate （APS） and silica gel. Soil cadmium was operationally fractionationed into exchangeable （Exch）, bound to carbonates （Carb）, bound to iron and manganese oxides （FeMnOx）, bound to organic matters （OM） and residual （Res） fraction. Application of PS and CaCO3 at hig rates enhanced soil pH, while APS and silica gel did not obviously change soil pH. PS and CaCO3 also increased the FeMnOx-Cd in Andosol and Carb-Cd in Alluvial soil, thus reducing the Exch-Cd in the tested soils. However, PS was less effective than CaCO3 at the same application rate. Cadmium fractions in the two soils were not changed by the treatments of APS and silica gel. There were no obvious differences in the solubility of cadmium in soils treated with PS, APS, silica gel and CaCO3 except Andosol treated 2.0% CaCO3 at the same pH of soil-CaC12 suspensions. These findings suggested that the decrease of cadmium availability in soil was mainly attributed to the increase of soil pH caused by PS.

Properties and coagulation mechanisms of polyferric silicate sulfate with high concentration

Polyferric silicate sulfate （PFSS） with high concentration was prepared using the composite-poly method. The coagulation properties and mechanisms of this new complex were probed using TEM, Fe-Ferron timed complex-colorimetric method, and infrared spectrum method. The results showed that the flocculating effect of polyferric silicate sulfate had an advantage over polyferric sulfate （PFS）, as the optimum coagulation effect could be obtained when the Si/Fe mole ratio was 0.75 in accordance with its macrostructure of PFSS. According to the Fe-Ferron timed complex-colorimetric method, the Si species was mainly Sic, whereas, the Fe species were Fea and Fec in the copolymerization system. The infrared spectra indicated that the structure of these new flocculants was formed by polymers, mainly by olation, which was different from polyferric sulfate, and the vibration of M-OH-M of around 1100 cm^-1, also proved that there existed Fe-OH-Fe and its polymers in some forms.

The effect of sodium silicate concentration on microstructure and corrosion properties of MAO-coated magnesium alloy AZ31 in simulated body fluid

In recent years,magnesium and its alloys are considered as biodegradable implants.However magnesium implants may rapidly corrode before the natural healing process of the tissue is completed.In this investigation,micro arc oxidation process has been studied for avoiding primary corrosion of the magnesium alloy in simulated body fluid.Anodized coating was formed on AZ31 alloy in nontoxic silicate-alkaline solution at constant current.The effects of silicate concentration and conductivity of electrolyte solution on microstructure and corrosion properties of coating were evaluated.Scanning electron microscopy showed that a thick and condensed coating is formed after enough anodizing period.Energy dispersive spectroscopy showed that Si,O and Mg are the main components of the coating.Corrosion resistance of the coated and uncoated samples was assessed using potentiodynamic polarization and electrochemical impedance spectroscopy tests in SBF at 37℃ and pH of 7.4.Maximum corrosion resistance was achieved at 30 g/L concentration of sodium silicate in anodizing solution.It was observed that further increase in silicate concentration decreased the corrosion resistance.

Effect of C/S Ratio on Morphology and Structure of Hydrothermally Synthesized Calcium Silicate Hydrate

The samples of the C-S-H series were synthesized by hydrothermal reaction of fumed silica, CaO and deionized water at initial C/S ratios between 1.0-1.7. Phase composition and structural and morphology characteristics of C-S-H samples were analyzed by XRD, IR and SEM. The experimental results showed that the d-spacing of （002）, （110） and （020） decreased, the d-spacing of （200） increased, and the d-spacing of （310） varied randomly, the polymerization of silica tetrahedra of C-S-H decreased, and morphology of C-S-H samples varied from sheet shapes to long reticular fibers as C/S ratio increased.