Silicone-acrylate copolymer latex was prepared through three different polymerization processes, i.e., the batch process, preemulsified monomer addition and the monomer addition process. The results revealed that the ...Silicone-acrylate copolymer latex was prepared through three different polymerization processes, i.e., the batch process, preemulsified monomer addition and the monomer addition process. The results revealed that the monomer addition process is a desirable approach to produce narrow particle size distribution latex with higher polymerization conversion and less amount of coagulum. The effect of silicone content on the glossiness and water absorption of latex film was investigated and the results showed that the glossiness of latex film is improved up to a silicone content of 10% of total monomers, but becomes impaired thereafter, whereas water absorption is reduced accordingly.展开更多
A silicone acrylate micro-emulsion of multipolymer was prepared by seed emulsion polymerization. The effects of polymerization process, emulsifier rate and amount, initiator rate and amount, polymerization temperature...A silicone acrylate micro-emulsion of multipolymer was prepared by seed emulsion polymerization. The effects of polymerization process, emulsifier rate and amount, initiator rate and amount, polymerization temperature, functional monomers, titration time on performances of emulsion have been discussed in detail.展开更多
The title compound,（Z）-methyl-3-methoxy-2-{2-[（4-（E-3-p-tolylacryloyl）phenoxy）-methyl]phenyl}acrylate,was synthesized and determined by X-ray single-crystal diffraction. The crystal belongs to the triclinic syst...The title compound,（Z）-methyl-3-methoxy-2-{2-[（4-（E-3-p-tolylacryloyl）phenoxy）-methyl]phenyl}acrylate,was synthesized and determined by X-ray single-crystal diffraction. The crystal belongs to the triclinic system,space group P1 with a = 8.0157（8）,b = 12.5748（13）,c = 13.3768（14） ,α = 64.770（2）,β = 75.720 （2）,γ = 89.784（2）°,μ = 0.085 mm-1,Mr = 442.49,V = 1174.1（2） 3,Z = 2,Dc = 1.252 g/cm3,F（000） = 468,T = 294（2） K,R = 0.0603 and wR = 0.1498 for 2644 observed reflections with I 〉 2σ（I）. X-ray diffraction analysis reveals that the single crystal contains strong non-classical hydrogen bonds. The preliminary bioassay showed that the title compound exhibits inhibitory activity against the Pseudoperoniospora cubensis and Rhizoctonia solani at the test concentration of 200 mg/L.展开更多
Poly(1,1,2,2- tetrahydroperfluorodecyl acrylate) (poly (TA-N)) was synthesized in laboratory. The resulting morphology of rapid expansion of supercritical solution (RESS) sprays of poly(TA - N) was investigated. At ap...Poly(1,1,2,2- tetrahydroperfluorodecyl acrylate) (poly (TA-N)) was synthesized in laboratory. The resulting morphology of rapid expansion of supercritical solution (RESS) sprays of poly(TA - N) was investigated. At apre - expansion temperature of 45℃), amorphous polymer was formed. At temperature around 60 ℃ to 80 ℃ , fibers were formed. Increase of temperature increasesparticle size slightly. At temperature of 105℃ , most of particles are spheres. The RESS is an attractive process. To apply the polymers desired for coating applications in an organic solvent - free process that is economically viable , and it will have implications for pollution prevention during polymer film展开更多
Two new C2-symmetrical bidentate phosphoramidite ligands were synthesized and employed in the Rh-catalyzed asymmetric hydrogenation of β-（acylamino）acrylates, up to 89% ee with full conversions was obtained.
The reaction of 3-（3-pyridyl）acrylic acid （H（3-PYA）） with Co（NO3）2.6H2O or MnCl2.4H2O yielded two new complexes： [Co（3-PYA）2（H2O）4.H2O] 1 and [Mn（3-PYA）2（H2O）4] 2. Complex 1 crystallizes in monoclinic...The reaction of 3-（3-pyridyl）acrylic acid （H（3-PYA）） with Co（NO3）2.6H2O or MnCl2.4H2O yielded two new complexes： [Co（3-PYA）2（H2O）4.H2O] 1 and [Mn（3-PYA）2（H2O）4] 2. Complex 1 crystallizes in monoclinic, space group C2/c with a = 9.9473（12）, b = 13.7227（16）, c = 14.7376（18） A, β = 99.043（2）°, V = 1986.7（4） A^3, Z = 4, Dc= 1.549 g/cm^3,μ = 0.921 mm^-1, F（000） = 964, R = 0.0786 and wR = 0.1443. Six types of hydrogen bonds and π-π packing interactions connect the mononuclear units [Co（Ⅱ）（3-PYA）2（H2O）4·H2O] into a three-dimensional supramolecular architecture. Complex 2 crystallizes in monoclinic, space group P21/n with a = 11.3630（16）, b = 7.0346（10）, c = 12.1365（18） A, β = 112.545（3）°, V = 896.0（2） A^3, Z = 2, D, = 1.997 g/cm^3,μ = 0.785 mm^-1, F（000） = 438, R = 0.0787 and wR = 0.1550. The discrete entity Mn（Ⅱ）（3-PYD）2（H2O）4 is extended into a 3-D supramolecular architecture by four kinds of hydrogen bonds.展开更多
1 Scope This standard specifies the definition, classifica- tion, technical requirements, test methods, quality appraisal procedures, packing, marking, transportation, storage, and quality certificate of silicon nitri...1 Scope This standard specifies the definition, classifica- tion, technical requirements, test methods, quality appraisal procedures, packing, marking, transportation, storage, and quality certificate of silicon nitride bonded silicon carbide bricks.展开更多
The sliding wear behavior of hypoeutectic, eutectic and hypereutectic Al - Si alloys under lubricating condition was investigated. The wear mechanism of three kinds of alloys was discussed and an effective way to impr...The sliding wear behavior of hypoeutectic, eutectic and hypereutectic Al - Si alloys under lubricating condition was investigated. The wear mechanism of three kinds of alloys was discussed and an effective way to improve the wear reslstance of Al - Si alloys was put forward, that is increasing the silicon content.展开更多
文摘Silicone-acrylate copolymer latex was prepared through three different polymerization processes, i.e., the batch process, preemulsified monomer addition and the monomer addition process. The results revealed that the monomer addition process is a desirable approach to produce narrow particle size distribution latex with higher polymerization conversion and less amount of coagulum. The effect of silicone content on the glossiness and water absorption of latex film was investigated and the results showed that the glossiness of latex film is improved up to a silicone content of 10% of total monomers, but becomes impaired thereafter, whereas water absorption is reduced accordingly.
基金Ministry of Science and Technology of China for Major State Basic Research Projects (2002AA322020)
文摘A silicone acrylate micro-emulsion of multipolymer was prepared by seed emulsion polymerization. The effects of polymerization process, emulsifier rate and amount, initiator rate and amount, polymerization temperature, functional monomers, titration time on performances of emulsion have been discussed in detail.
基金supported by the Science Foundation of the Southern Medical University for New Excellent Talents (No. B1000374)
文摘The title compound,（Z）-methyl-3-methoxy-2-{2-[（4-（E-3-p-tolylacryloyl）phenoxy）-methyl]phenyl}acrylate,was synthesized and determined by X-ray single-crystal diffraction. The crystal belongs to the triclinic system,space group P1 with a = 8.0157（8）,b = 12.5748（13）,c = 13.3768（14） ,α = 64.770（2）,β = 75.720 （2）,γ = 89.784（2）°,μ = 0.085 mm-1,Mr = 442.49,V = 1174.1（2） 3,Z = 2,Dc = 1.252 g/cm3,F（000） = 468,T = 294（2） K,R = 0.0603 and wR = 0.1498 for 2644 observed reflections with I 〉 2σ（I）. X-ray diffraction analysis reveals that the single crystal contains strong non-classical hydrogen bonds. The preliminary bioassay showed that the title compound exhibits inhibitory activity against the Pseudoperoniospora cubensis and Rhizoctonia solani at the test concentration of 200 mg/L.
文摘Poly(1,1,2,2- tetrahydroperfluorodecyl acrylate) (poly (TA-N)) was synthesized in laboratory. The resulting morphology of rapid expansion of supercritical solution (RESS) sprays of poly(TA - N) was investigated. At apre - expansion temperature of 45℃), amorphous polymer was formed. At temperature around 60 ℃ to 80 ℃ , fibers were formed. Increase of temperature increasesparticle size slightly. At temperature of 105℃ , most of particles are spheres. The RESS is an attractive process. To apply the polymers desired for coating applications in an organic solvent - free process that is economically viable , and it will have implications for pollution prevention during polymer film
基金The authors would like to thank the National Natural Science Foundation of China （No. 20472083） for financial support of this work.
文摘Two new C2-symmetrical bidentate phosphoramidite ligands were synthesized and employed in the Rh-catalyzed asymmetric hydrogenation of β-（acylamino）acrylates, up to 89% ee with full conversions was obtained.
基金Financially supported by NNSFC (No. 20031020), NSF of Fujian Province and the Key Project from CAS
文摘The reaction of 3-（3-pyridyl）acrylic acid （H（3-PYA）） with Co（NO3）2.6H2O or MnCl2.4H2O yielded two new complexes： [Co（3-PYA）2（H2O）4.H2O] 1 and [Mn（3-PYA）2（H2O）4] 2. Complex 1 crystallizes in monoclinic, space group C2/c with a = 9.9473（12）, b = 13.7227（16）, c = 14.7376（18） A, β = 99.043（2）°, V = 1986.7（4） A^3, Z = 4, Dc= 1.549 g/cm^3,μ = 0.921 mm^-1, F（000） = 964, R = 0.0786 and wR = 0.1443. Six types of hydrogen bonds and π-π packing interactions connect the mononuclear units [Co（Ⅱ）（3-PYA）2（H2O）4·H2O] into a three-dimensional supramolecular architecture. Complex 2 crystallizes in monoclinic, space group P21/n with a = 11.3630（16）, b = 7.0346（10）, c = 12.1365（18） A, β = 112.545（3）°, V = 896.0（2） A^3, Z = 2, D, = 1.997 g/cm^3,μ = 0.785 mm^-1, F（000） = 438, R = 0.0787 and wR = 0.1550. The discrete entity Mn（Ⅱ）（3-PYD）2（H2O）4 is extended into a 3-D supramolecular architecture by four kinds of hydrogen bonds.
文摘1 Scope This standard specifies the definition, classifica- tion, technical requirements, test methods, quality appraisal procedures, packing, marking, transportation, storage, and quality certificate of silicon nitride bonded silicon carbide bricks.
文摘The sliding wear behavior of hypoeutectic, eutectic and hypereutectic Al - Si alloys under lubricating condition was investigated. The wear mechanism of three kinds of alloys was discussed and an effective way to improve the wear reslstance of Al - Si alloys was put forward, that is increasing the silicon content.