The amino poly-siloxane was modified with self-made polyether silicones by the crafts of emulsion polymerization. We studied the emulsifier, the dosage of emulsifier initiator, polyether/silane coupling agent, pH valu...The amino poly-siloxane was modified with self-made polyether silicones by the crafts of emulsion polymerization. We studied the emulsifier, the dosage of emulsifier initiator, polyether/silane coupling agent, pH value. There are some results of the research indicated in the following. First, there are many factors for the hydrophilic amino-silicone softener both on the polymerization process and the performance, such as the proportion and amount of emulsifier, initiator dosage, the mass ratio of the polyether and hydrogen silicone oil, the choice of silicone coupling agent, and the ratio and dosage of polyether silicones silane coupling agent. Second, the amount of hydrogen of the hydrogen silicones and the choice of catalyst are the key points on the synthesis of polyether silicones. The amount of hydrogen should be low and the catalyst must be economical and efficient and its introduction should be small and times, other more the holding time is not too long. The next one is that, in the process of hydrolysis of silane coupling agent, we need some acid to adjust pH value, or they will be broken down. The most important one but not the last is that the epoxy group can improve the products low-temperature supple and the persistence of the finishing fabric, furthermore it can reduce yellowing and has a good stability of the inorganic salt, however, it will be destroyed if the reaction temperature for epoxy is too high. What’s more, it is very economical and environmental that the process of emulsion is simple and with less emulsifier.展开更多
Allyl terminated polyether was used to improve the hydrophilicity of addition-cured room temperature vulcanization silicone rubber. With the increasing of the polyether, both the hydrophilicity and water absorbed of t...Allyl terminated polyether was used to improve the hydrophilicity of addition-cured room temperature vulcanization silicone rubber. With the increasing of the polyether, both the hydrophilicity and water absorbed of the vulcanizates were increased. The mechanical properties were also improved by adding the polyether. The result showed that 1.5wt% of the polyether provided the silicone rubber with proper hydrophilicity.展开更多
1 Scope This standard specifies the definition, classifica- tion, technical requirements, test methods, quality appraisal procedures, packing, marking, transportation, storage, and quality certificate of silicon nitri...1 Scope This standard specifies the definition, classifica- tion, technical requirements, test methods, quality appraisal procedures, packing, marking, transportation, storage, and quality certificate of silicon nitride bonded silicon carbide bricks.展开更多
The sliding wear behavior of hypoeutectic, eutectic and hypereutectic Al - Si alloys under lubricating condition was investigated. The wear mechanism of three kinds of alloys was discussed and an effective way to impr...The sliding wear behavior of hypoeutectic, eutectic and hypereutectic Al - Si alloys under lubricating condition was investigated. The wear mechanism of three kinds of alloys was discussed and an effective way to improve the wear reslstance of Al - Si alloys was put forward, that is increasing the silicon content.展开更多
A1203-Si composite specimens were prepared using fused corundum, ultra-fine α-A1203 and Si powder as starting materials and resin as binder. Effects of sintering atmospheres on properties, phase composition and micro...A1203-Si composite specimens were prepared using fused corundum, ultra-fine α-A1203 and Si powder as starting materials and resin as binder. Effects of sintering atmospheres on properties, phase composition and microstructure of specimens after firing at 1 500 ℃ were investigated. The results show that： （ 1 ） after .firing in oxidizing or weak oxidizing atmosphere, there is some Si in the specimens and some glass phases containing mullite form on specimen surface, the density and strength at room temperature are relatively high, but hot modulus of rupture and thermal shock resistance are relatively poor; （2） after firing in, weak reducing or reducing atmosphere, Si reacts completely with CO or N2forming whisk-phere, Si reacts completely with CO or N2forming whisk-er-like SiC, granular Si2N20 or 0＇-SiAION, and the er-like SiC, granular Si2N20 or O＇-SiMON, and the thermo-mechanical properties of specimens are enhanced;（3） after firing in nitrogen atmosphere, Si reacts completely with N2, CO or G forming wbisker-like SiC and columnar β-SiA10N crystals, the hot modulus of rupture and thermal shock resistance of specimens are enhanced noticeably.展开更多
The Al2O3 -SiC-C bricks for iron ladles were pre-pared asing bauxite, fused corundum,pyrophyllite, SiC powder and flake graphite as main starting materials, and phenolic resin as binder. The effect of pyroph,yllite pa...The Al2O3 -SiC-C bricks for iron ladles were pre-pared asing bauxite, fused corundum,pyrophyllite, SiC powder and flake graphite as main starting materials, and phenolic resin as binder. The effect of pyroph,yllite particle size on permanent change in dimensions, cold crushing strength, oxidation resistance, and corrosion resistance of Al2O3 - SiC - C bricks was investigated. The results show that with the decrease of the pyrophyllite particle size, the permanent change in dimensions of Al2O3 - SiC - C bricks decreases, cold crushing strength increases, the oxidation resistance at 1400 ℃ increases, and the corrosion resistance at 1500℃ decreases.展开更多
Al2 O3 - SiC - SiAION composite specimens have been prepared using fused alumina, ultra fine α-Al2O3, Si and Al powders as starting materials and liquid phenol formaldehyde resin as binder and firing at 1 500 ℃ for ...Al2 O3 - SiC - SiAION composite specimens have been prepared using fused alumina, ultra fine α-Al2O3, Si and Al powders as starting materials and liquid phenol formaldehyde resin as binder and firing at 1 500 ℃ for 3 h in carbon embedded condition. Thermo-mechanical properties of Al2 O3 - SiC - SiAlON composites have been studied. The results show ： （ 1 ） Al2 O3 - SiC - SiAION composites can be prepared and sintered at 1 500 ℃ under carbon embedded condition. When Si/Al ratio is 8/0 and 7/1, the prepared composite is Al2O3 - SiC - O＇ -SiAlON; when Si/Al ratio is 5/3 and 3/5, the pre- pared composite is Al2 O3 - SiC - β-SiAION. （ 2 ） The composites possess high temperature strength properties. Hot modulus of rupture at 1 400 ℃ is 10 - 30 MPa. They are in elastic range up to 1 000 ℃, after which plastic deformation is observed; even at 1 400 ℃, amount of deformation is relatively low. （3） The com- posites possess good thermal shock resistance, their resid- ual strength ratio （AT = 1 100 ℃ ） is 65% - 80%. （4） The marked improvement in thermo-mechanical properties of Al2O3 - SiC - SiAlON composites may be at- tributed to the in-situ formation of SiC, SiAlON and AIN, the fibrous SiC, columnar SiAlON and tabular-like AlN fill in the corundum skeleton structure creating strengthening and toughening effects.展开更多
文摘The amino poly-siloxane was modified with self-made polyether silicones by the crafts of emulsion polymerization. We studied the emulsifier, the dosage of emulsifier initiator, polyether/silane coupling agent, pH value. There are some results of the research indicated in the following. First, there are many factors for the hydrophilic amino-silicone softener both on the polymerization process and the performance, such as the proportion and amount of emulsifier, initiator dosage, the mass ratio of the polyether and hydrogen silicone oil, the choice of silicone coupling agent, and the ratio and dosage of polyether silicones silane coupling agent. Second, the amount of hydrogen of the hydrogen silicones and the choice of catalyst are the key points on the synthesis of polyether silicones. The amount of hydrogen should be low and the catalyst must be economical and efficient and its introduction should be small and times, other more the holding time is not too long. The next one is that, in the process of hydrolysis of silane coupling agent, we need some acid to adjust pH value, or they will be broken down. The most important one but not the last is that the epoxy group can improve the products low-temperature supple and the persistence of the finishing fabric, furthermore it can reduce yellowing and has a good stability of the inorganic salt, however, it will be destroyed if the reaction temperature for epoxy is too high. What’s more, it is very economical and environmental that the process of emulsion is simple and with less emulsifier.
文摘Allyl terminated polyether was used to improve the hydrophilicity of addition-cured room temperature vulcanization silicone rubber. With the increasing of the polyether, both the hydrophilicity and water absorbed of the vulcanizates were increased. The mechanical properties were also improved by adding the polyether. The result showed that 1.5wt% of the polyether provided the silicone rubber with proper hydrophilicity.
文摘1 Scope This standard specifies the definition, classifica- tion, technical requirements, test methods, quality appraisal procedures, packing, marking, transportation, storage, and quality certificate of silicon nitride bonded silicon carbide bricks.
文摘The sliding wear behavior of hypoeutectic, eutectic and hypereutectic Al - Si alloys under lubricating condition was investigated. The wear mechanism of three kinds of alloys was discussed and an effective way to improve the wear reslstance of Al - Si alloys was put forward, that is increasing the silicon content.
基金financially supported by Henan Scientific and Technological Research Projects (112102210095 )Science Fund for Distinguished Young Scholars of Henan Province ( No.124100510019) the Education Department of Henan Province Foundation (14A430030)
文摘A1203-Si composite specimens were prepared using fused corundum, ultra-fine α-A1203 and Si powder as starting materials and resin as binder. Effects of sintering atmospheres on properties, phase composition and microstructure of specimens after firing at 1 500 ℃ were investigated. The results show that： （ 1 ） after .firing in oxidizing or weak oxidizing atmosphere, there is some Si in the specimens and some glass phases containing mullite form on specimen surface, the density and strength at room temperature are relatively high, but hot modulus of rupture and thermal shock resistance are relatively poor; （2） after firing in, weak reducing or reducing atmosphere, Si reacts completely with CO or N2forming whisk-phere, Si reacts completely with CO or N2forming whisk-er-like SiC, granular Si2N20 or 0＇-SiAION, and the er-like SiC, granular Si2N20 or O＇-SiMON, and the thermo-mechanical properties of specimens are enhanced;（3） after firing in nitrogen atmosphere, Si reacts completely with N2, CO or G forming wbisker-like SiC and columnar β-SiA10N crystals, the hot modulus of rupture and thermal shock resistance of specimens are enhanced noticeably.
文摘The Al2O3 -SiC-C bricks for iron ladles were pre-pared asing bauxite, fused corundum,pyrophyllite, SiC powder and flake graphite as main starting materials, and phenolic resin as binder. The effect of pyroph,yllite particle size on permanent change in dimensions, cold crushing strength, oxidation resistance, and corrosion resistance of Al2O3 - SiC - C bricks was investigated. The results show that with the decrease of the pyrophyllite particle size, the permanent change in dimensions of Al2O3 - SiC - C bricks decreases, cold crushing strength increases, the oxidation resistance at 1400 ℃ increases, and the corrosion resistance at 1500℃ decreases.
基金the financial support of Science Fund for International Cooperation Project(No.152102410014)the Education Department of Henan Province Foundation(14A430030)Research Foundation of Zhengzhou City(131PPTGG-409-3)
文摘Al2 O3 - SiC - SiAION composite specimens have been prepared using fused alumina, ultra fine α-Al2O3, Si and Al powders as starting materials and liquid phenol formaldehyde resin as binder and firing at 1 500 ℃ for 3 h in carbon embedded condition. Thermo-mechanical properties of Al2 O3 - SiC - SiAlON composites have been studied. The results show ： （ 1 ） Al2 O3 - SiC - SiAION composites can be prepared and sintered at 1 500 ℃ under carbon embedded condition. When Si/Al ratio is 8/0 and 7/1, the prepared composite is Al2O3 - SiC - O＇ -SiAlON; when Si/Al ratio is 5/3 and 3/5, the pre- pared composite is Al2 O3 - SiC - β-SiAION. （ 2 ） The composites possess high temperature strength properties. Hot modulus of rupture at 1 400 ℃ is 10 - 30 MPa. They are in elastic range up to 1 000 ℃, after which plastic deformation is observed; even at 1 400 ℃, amount of deformation is relatively low. （3） The com- posites possess good thermal shock resistance, their resid- ual strength ratio （AT = 1 100 ℃ ） is 65% - 80%. （4） The marked improvement in thermo-mechanical properties of Al2O3 - SiC - SiAlON composites may be at- tributed to the in-situ formation of SiC, SiAlON and AIN, the fibrous SiC, columnar SiAlON and tabular-like AlN fill in the corundum skeleton structure creating strengthening and toughening effects.