Silicon fines, boron acid solid powders and microfine SiO 2 as sintering agents were incorporated into Al 2O 3-SiC-C ramming mix in order to investigated their effects on the microstructure, mechanical properties a...Silicon fines, boron acid solid powders and microfine SiO 2 as sintering agents were incorporated into Al 2O 3-SiC-C ramming mix in order to investigated their effects on the microstructure, mechanical properties and sintering behavior of the ramming mix. Results show that all the three agents could improved both densification and mehanical properties markedly, compared to that of non-agent specimens and the effect of the composite of boron acid solid powders and microfine SiO 2 is the best. The oxidation resistance increased with the addition of agents, which is supported by densification. Microstructures showed that agent powders could fill pores or produce liquid phases at high temperature, therefore, improve the sintering of the ramming mix.展开更多
In this paper, the influences of catch-color agent content on glass-ceramic decorated material in the system of CaO-Al2O3-SiO2 were studied. By ladder temperature furnace and sintering shrinkage curve measurement . th...In this paper, the influences of catch-color agent content on glass-ceramic decorated material in the system of CaO-Al2O3-SiO2 were studied. By ladder temperature furnace and sintering shrinkage curve measurement . the influence of catch-color agent content on sintering and crystallization temperature was discussed. By means of XRD, three point bending strength and density measurement, the properties of the decorated material were investigated.展开更多
文摘Silicon fines, boron acid solid powders and microfine SiO 2 as sintering agents were incorporated into Al 2O 3-SiC-C ramming mix in order to investigated their effects on the microstructure, mechanical properties and sintering behavior of the ramming mix. Results show that all the three agents could improved both densification and mehanical properties markedly, compared to that of non-agent specimens and the effect of the composite of boron acid solid powders and microfine SiO 2 is the best. The oxidation resistance increased with the addition of agents, which is supported by densification. Microstructures showed that agent powders could fill pores or produce liquid phases at high temperature, therefore, improve the sintering of the ramming mix.
文摘In this paper, the influences of catch-color agent content on glass-ceramic decorated material in the system of CaO-Al2O3-SiO2 were studied. By ladder temperature furnace and sintering shrinkage curve measurement . the influence of catch-color agent content on sintering and crystallization temperature was discussed. By means of XRD, three point bending strength and density measurement, the properties of the decorated material were investigated.