To avoid slag sticking on the ladle immersion cover during the LATS refining and alloying process, the effect of Al2O3 on the melting point of the ladle slag was studied and the additives including CaF2, B2O3, Li2O, a...To avoid slag sticking on the ladle immersion cover during the LATS refining and alloying process, the effect of Al2O3 on the melting point of the ladle slag was studied and the additives including CaF2, B2O3, Li2O, and CaO were used to decrease the melting point of the ladle slag. The melting point was measured using the hemisphere method. The results show that the addition of Al2O3 to the ladle slag increases the melting point. The fluxing action is not remarkable if only CaF2 or CaO is used as the additive. The fluxing action of the composite additive obtained by the mixing of CaO and CaF2 in the mass proportion of ωCaO：ωCaF2=2 ： 1 is preferred. The fluxing action of B2O3 is also notable. When the B2O3 content in mass percent is in the range from 2% to 10%, the corresponding melting point is 1 380 ℃ to 1 290℃. The fluxing action of Li2O is the most remarkable. When the Li2O content is up to 5%, the melting point of the slag is lower than 1 300 ℃.展开更多
Some differences in slag splashing between BOF steel works in US and China were investigated. The slag composition,melting point, and mineralogical phases of final slags from both countries were studied. The control o...Some differences in slag splashing between BOF steel works in US and China were investigated. The slag composition,melting point, and mineralogical phases of final slags from both countries were studied. The control of slag superheat is important to an effective slag coating.展开更多
To reduce the slag sticking onto the snorkel of the ladle during the ladle alloying treatment station （LATS） process, CaO- CaF2 （the mass ratio of CaO/CaF2 is 1：1） was employed as the modifier of the LATS refinin...To reduce the slag sticking onto the snorkel of the ladle during the ladle alloying treatment station （LATS） process, CaO- CaF2 （the mass ratio of CaO/CaF2 is 1：1） was employed as the modifier of the LATS refining ladle slag. The effect of CaO-CaF2 on the melting point, viscosity, and desulfurizing capability of the ladle slag was investigated. The melting point of the unmodified ladle slag is 1439℃. When adding 20wt% CaO-CaF2, the melting point is decreased to 1327℃. At 1500℃. the viscosity of the unmodified ladle slag is 6.5 Pa.s, which can be decreased lower than 2 Pa.s by adding more than 10wt% CaO-CaF2. The experimental results of desulfu- rization of the melts show that the desulfurizing power of the ladle slag can be enhanced by adding CaO-CaF2.展开更多
基金Item Sponsored by National Natural Science Foundation of China (50474037) Natural Science Foundation of Jiangsu Higher Education Institutions of China (04KJB430022 ,05KJD450043)
文摘To avoid slag sticking on the ladle immersion cover during the LATS refining and alloying process, the effect of Al2O3 on the melting point of the ladle slag was studied and the additives including CaF2, B2O3, Li2O, and CaO were used to decrease the melting point of the ladle slag. The melting point was measured using the hemisphere method. The results show that the addition of Al2O3 to the ladle slag increases the melting point. The fluxing action is not remarkable if only CaF2 or CaO is used as the additive. The fluxing action of the composite additive obtained by the mixing of CaO and CaF2 in the mass proportion of ωCaO：ωCaF2=2 ： 1 is preferred. The fluxing action of B2O3 is also notable. When the B2O3 content in mass percent is in the range from 2% to 10%, the corresponding melting point is 1 380 ℃ to 1 290℃. The fluxing action of Li2O is the most remarkable. When the Li2O content is up to 5%, the melting point of the slag is lower than 1 300 ℃.
文摘Some differences in slag splashing between BOF steel works in US and China were investigated. The slag composition,melting point, and mineralogical phases of final slags from both countries were studied. The control of slag superheat is important to an effective slag coating.
基金This study was financially supported by Baosteel, College Natural Science Research Project of Jiangsu Province (No. 04KJB430022,05KJD450043)the National Natural Science Foundation of China (No.50474037)
文摘To reduce the slag sticking onto the snorkel of the ladle during the ladle alloying treatment station （LATS） process, CaO- CaF2 （the mass ratio of CaO/CaF2 is 1：1） was employed as the modifier of the LATS refining ladle slag. The effect of CaO-CaF2 on the melting point, viscosity, and desulfurizing capability of the ladle slag was investigated. The melting point of the unmodified ladle slag is 1439℃. When adding 20wt% CaO-CaF2, the melting point is decreased to 1327℃. At 1500℃. the viscosity of the unmodified ladle slag is 6.5 Pa.s, which can be decreased lower than 2 Pa.s by adding more than 10wt% CaO-CaF2. The experimental results of desulfu- rization of the melts show that the desulfurizing power of the ladle slag can be enhanced by adding CaO-CaF2.