A new electric arc furnace （EAF） steelmaking process with increasing hot metal charging ratio and improving slagging regime simultaneously was developed and applied in a 50 t electric arc furnace for more than a yea...A new electric arc furnace （EAF） steelmaking process with increasing hot metal charging ratio and improving slagging regime simultaneously was developed and applied in a 50 t electric arc furnace for more than a year at No. 1 Steelmaking Plant of Shanxi Taigang Stainless Corporation Limited. The essential fact of the new EAF steelmaking process was to charge hot metal in two portions or steps： firstly, 35wt%-40wt% hot metal was pretreated by blowing oxygen in a specially designed reactor for decar burization and improving hot metal temperature and melting premelted slag; secondly, 30wt% hot metal was charged into EAF with high basicity refining slags from ladle furnace （LF）-vacuum degassing furnace （VD） refining process. The results show that the hot metal charging ratio can reach to about 65wt%-70wt% for the new EAF steelrnaking process; meanwhile, the tap-to-tap time of a 50 t EAF can shorten by 5-10 min, the electricity consumption can decrease by 35-50 kW·h/t, the lime consumption can reduce by 10.5 kg/t of molten steel, and the content of harmful heavy metals in molten steel can be easily controlled to less than the upper limits of aimed steel specification or grade compared with the traditional EAF steelmaking process. In addition, the dephosphorization ability shows a slight strengthening, however, a small degree of lessening for desulphurization ability is observed for the new EAF steelmaking process, but the weakness of desulphurization ability cannot become an obstacle to its further application since a stronger desulphurization ability can be achieved during secondary refining of LF coupled with VD after EAF steelmaking process.展开更多
Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass r...Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.展开更多
The liquid iron containing elements Nb,Mn and Si has been equilibrated with MgO-SiO_2-MnO slag melts at 1600℃ in a Mo wire-wound resistance furnace with a duration of 4h.The oxygen activities in liquid iron were meas...The liquid iron containing elements Nb,Mn and Si has been equilibrated with MgO-SiO_2-MnO slag melts at 1600℃ in a Mo wire-wound resistance furnace with a duration of 4h.The oxygen activities in liquid iron were measured with oxygen sensors.Using the known equilibrium constants of concerning reactions and the oxygen activities in liquid iron,the activities of components in the slag melts can be calculated.It was found that the par- tition ratios of Nb.Mn and Si have a close linear relationship with α_(FeO) in logarithmic scale.The dependence of Nb partition ratio on mole fractions of the slag components was al- so obtained.展开更多
To provide basic data for the reasonable mixing design of the alkali-activated (AA) foamed concrete as a thermal insulation material for a floor heating system, 9 concrete mixes with a targeted dry density less than 4...To provide basic data for the reasonable mixing design of the alkali-activated (AA) foamed concrete as a thermal insulation material for a floor heating system, 9 concrete mixes with a targeted dry density less than 400 kg/m3 were tested. Ground granulated blast-furnace slag (GGBS) as a source material was activated by the following two types of alkali activators: 10% Ca(OH)2 and 4% Mg(NO3)2, and 2.5% Ca(OH)2 and 6.5% Na2SiO3. The main test parameters were water-to-binder (W/B) ratio and the substitution level (RFA) of fly ash (FA) for GGBS. Test results revealed that the dry density of AA GGBS foamed concrete was independent of the W/B ratio an RFA, whereas the compressive strength increased with the decrease in W/B ratio and with the increase in RFA up to 15%, beyond which it decreased. With the increase in the W/B ratio, the amount of macro capillaries and artificial air pores increased, which resulted in the decrease of compressive strength. The magnitude of the environmental loads of the AA GGBS foamed concrete is independent of the W/B ratio and RFA. The largest reduction percentage was found in the photochemical oxidation potential, being more than 99%. The reduction percentage was 87% - 93% for the global warming potential, 81% - 84% for abiotic depletion, 79% - 84% for acidification potential, 77% - 85% for eutrophication potential, and 73% - 83% for human toxicity potential. Ultimately, this study proved that the developed AA GGBS foamed concrete has a considerable promise as a sustainable construction material for nonstructural element.展开更多
文摘A new electric arc furnace （EAF） steelmaking process with increasing hot metal charging ratio and improving slagging regime simultaneously was developed and applied in a 50 t electric arc furnace for more than a year at No. 1 Steelmaking Plant of Shanxi Taigang Stainless Corporation Limited. The essential fact of the new EAF steelmaking process was to charge hot metal in two portions or steps： firstly, 35wt%-40wt% hot metal was pretreated by blowing oxygen in a specially designed reactor for decar burization and improving hot metal temperature and melting premelted slag; secondly, 30wt% hot metal was charged into EAF with high basicity refining slags from ladle furnace （LF）-vacuum degassing furnace （VD） refining process. The results show that the hot metal charging ratio can reach to about 65wt%-70wt% for the new EAF steelrnaking process; meanwhile, the tap-to-tap time of a 50 t EAF can shorten by 5-10 min, the electricity consumption can decrease by 35-50 kW·h/t, the lime consumption can reduce by 10.5 kg/t of molten steel, and the content of harmful heavy metals in molten steel can be easily controlled to less than the upper limits of aimed steel specification or grade compared with the traditional EAF steelmaking process. In addition, the dephosphorization ability shows a slight strengthening, however, a small degree of lessening for desulphurization ability is observed for the new EAF steelmaking process, but the weakness of desulphurization ability cannot become an obstacle to its further application since a stronger desulphurization ability can be achieved during secondary refining of LF coupled with VD after EAF steelmaking process.
基金Project(51204115)supported by the National Natural Science Foundation of ChinaProject(BK20130308)supported by the Basic Research Program of Jiangsu Province,ChinaProject(2014M561710)supported by China Postdoctoral Science Foundation
文摘Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.
文摘The liquid iron containing elements Nb,Mn and Si has been equilibrated with MgO-SiO_2-MnO slag melts at 1600℃ in a Mo wire-wound resistance furnace with a duration of 4h.The oxygen activities in liquid iron were measured with oxygen sensors.Using the known equilibrium constants of concerning reactions and the oxygen activities in liquid iron,the activities of components in the slag melts can be calculated.It was found that the par- tition ratios of Nb.Mn and Si have a close linear relationship with α_(FeO) in logarithmic scale.The dependence of Nb partition ratio on mole fractions of the slag components was al- so obtained.
文摘To provide basic data for the reasonable mixing design of the alkali-activated (AA) foamed concrete as a thermal insulation material for a floor heating system, 9 concrete mixes with a targeted dry density less than 400 kg/m3 were tested. Ground granulated blast-furnace slag (GGBS) as a source material was activated by the following two types of alkali activators: 10% Ca(OH)2 and 4% Mg(NO3)2, and 2.5% Ca(OH)2 and 6.5% Na2SiO3. The main test parameters were water-to-binder (W/B) ratio and the substitution level (RFA) of fly ash (FA) for GGBS. Test results revealed that the dry density of AA GGBS foamed concrete was independent of the W/B ratio an RFA, whereas the compressive strength increased with the decrease in W/B ratio and with the increase in RFA up to 15%, beyond which it decreased. With the increase in the W/B ratio, the amount of macro capillaries and artificial air pores increased, which resulted in the decrease of compressive strength. The magnitude of the environmental loads of the AA GGBS foamed concrete is independent of the W/B ratio and RFA. The largest reduction percentage was found in the photochemical oxidation potential, being more than 99%. The reduction percentage was 87% - 93% for the global warming potential, 81% - 84% for abiotic depletion, 79% - 84% for acidification potential, 77% - 85% for eutrophication potential, and 73% - 83% for human toxicity potential. Ultimately, this study proved that the developed AA GGBS foamed concrete has a considerable promise as a sustainable construction material for nonstructural element.