Corrosion is a primary cause of the slippage of friction⁃type high⁃strength bolted(FHSB)T⁃stub connections.This paper attempts to quantify the residual capacity of FHSB T⁃stub connections with corroded nuts.Firstly,co...Corrosion is a primary cause of the slippage of friction⁃type high⁃strength bolted(FHSB)T⁃stub connections.This paper attempts to quantify the residual capacity of FHSB T⁃stub connections with corroded nuts.Firstly,corrosion simulation tests were conducted on 48 manually cut nuts to find out the relationship between the damage degree of nut section and the residual clamping force(RCF)of bolt.Then,static load tests were carried out on 24 FHSB T⁃stub connections with nuts of different degrees of damage to obtain the failure modes.By finite⁃element(FE)models,a comparative analysis was performed on the initial friction load(IFL)and ultimate strength(US)of each connection with corroded nuts.Finally,the parameters of 96 FE models for FHSB T⁃stub connections were analyzed and used to derive the calculation formulas for the degree of damage for each nut and the IFL and US of each connection.The results show that the RCF decay of a bolt is a quadratic function of the equivalent radius loss ratio and the shear failure after nut corrosion;the IFL of each connection had a clear linear correlation with the RCF of the corresponding bolts,and the correlation depends on the applied load and static friction on connecting plate interface induced by the clamping force;the static friction had little impact on the US of the connection;the proposed IFL and US formulas can effectively derive the residual anti⁃slip capacity of FHSB T⁃stub connections from the degree of damage of the corroded nut section.The research results provide a scientific basis for the replacement and maintenance of corroded bolts of FHSB T⁃stub connections.展开更多
with the constant popularity of the precast assembly gasification, the application of the composite section beam which can change into different sections is wilder. This passage, based on the hypothesis that the inter...with the constant popularity of the precast assembly gasification, the application of the composite section beam which can change into different sections is wilder. This passage, based on the hypothesis that the interface is smooth, simplify the double composite section beam and deduce the anchorage-bolt-shear and composite-section-beam-bending-capacity formulas when there is a slip on the interface in elastic stage. Moreover, it contains some prospect and summarizes of the later research.展开更多
文摘Corrosion is a primary cause of the slippage of friction⁃type high⁃strength bolted(FHSB)T⁃stub connections.This paper attempts to quantify the residual capacity of FHSB T⁃stub connections with corroded nuts.Firstly,corrosion simulation tests were conducted on 48 manually cut nuts to find out the relationship between the damage degree of nut section and the residual clamping force(RCF)of bolt.Then,static load tests were carried out on 24 FHSB T⁃stub connections with nuts of different degrees of damage to obtain the failure modes.By finite⁃element(FE)models,a comparative analysis was performed on the initial friction load(IFL)and ultimate strength(US)of each connection with corroded nuts.Finally,the parameters of 96 FE models for FHSB T⁃stub connections were analyzed and used to derive the calculation formulas for the degree of damage for each nut and the IFL and US of each connection.The results show that the RCF decay of a bolt is a quadratic function of the equivalent radius loss ratio and the shear failure after nut corrosion;the IFL of each connection had a clear linear correlation with the RCF of the corresponding bolts,and the correlation depends on the applied load and static friction on connecting plate interface induced by the clamping force;the static friction had little impact on the US of the connection;the proposed IFL and US formulas can effectively derive the residual anti⁃slip capacity of FHSB T⁃stub connections from the degree of damage of the corroded nut section.The research results provide a scientific basis for the replacement and maintenance of corroded bolts of FHSB T⁃stub connections.
文摘with the constant popularity of the precast assembly gasification, the application of the composite section beam which can change into different sections is wilder. This passage, based on the hypothesis that the interface is smooth, simplify the double composite section beam and deduce the anchorage-bolt-shear and composite-section-beam-bending-capacity formulas when there is a slip on the interface in elastic stage. Moreover, it contains some prospect and summarizes of the later research.
