In this study, slow strain rate tensile testing at elevated temperature is used to evaluate the influence of temperature and strain rate on deformation behaviour in two different austenitic alloys. One austenitic stai...In this study, slow strain rate tensile testing at elevated temperature is used to evaluate the influence of temperature and strain rate on deformation behaviour in two different austenitic alloys. One austenitic stainless steel （AISI 316L） and one nickel-base alloy （Alloy 617） have been investigated. Scanning electron microscopy related techniques as electron channelling contrast imaging and electron backscattering diffraction have been used to study the damage and fracture micromechanisms. For both alloys the dominante damage micromech- anisms are slip bands and planar slip interacting with grain bounderies or precipitates causing strain concentrations. The dominante fracture micromechanism when using a slow strain rate at elevated temperature, is microcracks at grain bounderies due to grain boundery embrittlement caused by precipitates. The decrease in strain rate seems to have a small influence on dynamic strain ageing at 650℃.展开更多
China’s energy demand growth rate is expected to slow down next year, with the government’s efforts to curb energy consumption intensive industries taking effect, executives from State oil and power companies said y...China’s energy demand growth rate is expected to slow down next year, with the government’s efforts to curb energy consumption intensive industries taking effect, executives from State oil and power companies said yesterday. Refined oil product consumption in China is likely展开更多
The stress corrosion of S355 steel in 3.5% NaCl solution under the different strain rates was analyzed with the slow strain rate test（SSRT）, the stress corrosion cracking（SCC） behaviors of S355 steel under the dif...The stress corrosion of S355 steel in 3.5% NaCl solution under the different strain rates was analyzed with the slow strain rate test（SSRT）, the stress corrosion cracking（SCC） behaviors of S355 steel under the different strain rates in the solution were investigated, and the fracture morphologies and compositions of corrosion products under the different strain rates were analyzed with scanning electron microscopy（SEM） and energy dispersive spectrometerry（EDS）, respectively. The experimental results show that the SCC sensitivity index is the highest when the strain rate is 2×10-6, and the medium corrosion is the main reason resulting in the highest SCC sensitivity index. The SCC sensitivity index is the least when the strain rate is 5×10-6, and the stress is the main reason resulting in the stress corrosion. The SCC sensitivity index is the middle when the strain rate is 9×10-6, the interaction of stress and medium is the stress corrosion fracture mechanism.展开更多
基金supported by AB Sandvik Material Technology in Sweden and the Swedish Energy Agency through the Research Consortium of Materials Technology for Thermal Energy Processes(KME-501)Agora Materiae and the Strategic Faculty Grant AFM(SFO-MAT-LiU#2009-00971)at Linkping University
文摘In this study, slow strain rate tensile testing at elevated temperature is used to evaluate the influence of temperature and strain rate on deformation behaviour in two different austenitic alloys. One austenitic stainless steel （AISI 316L） and one nickel-base alloy （Alloy 617） have been investigated. Scanning electron microscopy related techniques as electron channelling contrast imaging and electron backscattering diffraction have been used to study the damage and fracture micromechanisms. For both alloys the dominante damage micromech- anisms are slip bands and planar slip interacting with grain bounderies or precipitates causing strain concentrations. The dominante fracture micromechanism when using a slow strain rate at elevated temperature, is microcracks at grain bounderies due to grain boundery embrittlement caused by precipitates. The decrease in strain rate seems to have a small influence on dynamic strain ageing at 650℃.
文摘China’s energy demand growth rate is expected to slow down next year, with the government’s efforts to curb energy consumption intensive industries taking effect, executives from State oil and power companies said yesterday. Refined oil product consumption in China is likely
基金Funded by the Key Research and Development Project of Jiangsu Province(BE2016052)
文摘The stress corrosion of S355 steel in 3.5% NaCl solution under the different strain rates was analyzed with the slow strain rate test（SSRT）, the stress corrosion cracking（SCC） behaviors of S355 steel under the different strain rates in the solution were investigated, and the fracture morphologies and compositions of corrosion products under the different strain rates were analyzed with scanning electron microscopy（SEM） and energy dispersive spectrometerry（EDS）, respectively. The experimental results show that the SCC sensitivity index is the highest when the strain rate is 2×10-6, and the medium corrosion is the main reason resulting in the highest SCC sensitivity index. The SCC sensitivity index is the least when the strain rate is 5×10-6, and the stress is the main reason resulting in the stress corrosion. The SCC sensitivity index is the middle when the strain rate is 9×10-6, the interaction of stress and medium is the stress corrosion fracture mechanism.