A new kind of polycarboxylate superplasticizer with high slump loss resistance was obtained by designing scheduled molecular structure.The number average molecular mass of the polymer was characterized by the gel perm...A new kind of polycarboxylate superplasticizer with high slump loss resistance was obtained by designing scheduled molecular structure.The number average molecular mass of the polymer was characterized by the gel permeation chromatography measurements.And chemical structure of the polymer was observed by the Fourier transform infrared spectroscopy(FT-IR).The results show that the good workable maintaining of self-compacting concrete could be achieved through direct adjustment of number average molecular mass and different unsaturated monomer in synthetic process.The FT-IR analysis illustrated that the high slump loss resistance of polycarboxylate superplasticizers with ester and carboxyl group and expectations of molecular structure were designed.展开更多
N-2000 is an admixture for concrete, with a low slump loss, high range water-reducing ratio and long-time retarding. The N-2000 is made up of naphthalene-sulfonic-maldehyde polycondensation (NSMP) and ATMP. Its charac...N-2000 is an admixture for concrete, with a low slump loss, high range water-reducing ratio and long-time retarding. The N-2000 is made up of naphthalene-sulfonic-maldehyde polycondensation (NSMP) and ATMP. Its characteristic results from the synergistic effects of NSMP and ATMP. The results show that when 0.7%-1.2% of N-2000 is added to concrete (by mass of cement), the water reducing ratio is up to 20%-30%, and the slump of fresh concrete can be retained for 2 hours without significant loss. N-2000 can not only improve the workability of fresh concrete but also increase the strength of the hardened concrete, especially early strength. It is also proved to have a good compatibility with various cements.展开更多
文摘A new kind of polycarboxylate superplasticizer with high slump loss resistance was obtained by designing scheduled molecular structure.The number average molecular mass of the polymer was characterized by the gel permeation chromatography measurements.And chemical structure of the polymer was observed by the Fourier transform infrared spectroscopy(FT-IR).The results show that the good workable maintaining of self-compacting concrete could be achieved through direct adjustment of number average molecular mass and different unsaturated monomer in synthetic process.The FT-IR analysis illustrated that the high slump loss resistance of polycarboxylate superplasticizers with ester and carboxyl group and expectations of molecular structure were designed.
基金Key Science and Technology Development Fund Project of Hubei Province.China(No.941PO106).
文摘N-2000 is an admixture for concrete, with a low slump loss, high range water-reducing ratio and long-time retarding. The N-2000 is made up of naphthalene-sulfonic-maldehyde polycondensation (NSMP) and ATMP. Its characteristic results from the synergistic effects of NSMP and ATMP. The results show that when 0.7%-1.2% of N-2000 is added to concrete (by mass of cement), the water reducing ratio is up to 20%-30%, and the slump of fresh concrete can be retained for 2 hours without significant loss. N-2000 can not only improve the workability of fresh concrete but also increase the strength of the hardened concrete, especially early strength. It is also proved to have a good compatibility with various cements.