Recycling water glass from wet reclamation sewage of waste sodium silicate-bonded sand

Wet reclamation of waste sodium silicate-bonded sand produces much alkaline sewage and causes pollution. Recycling water glass from wet reclamation sewage of the waste sodium silicate-bonded sand can solve pollution issues and generate economic benefits. In this work, the wet reclamation sewage was filtered, and the filtrate was causticized with a quicklime powder to produce a lye. The effects of causticization temperature, causticization time, and the amount of quicklime powder on the causticization rate were studied. The lye was used to dissolve the silica in the filtration residue to prepare a sodium silicate solution. The effects of the mass of filtration residue, dissolution temperature, and dissolution time on sodium silicate modulus were studied. Finally, the recycled water glass was obtained by concentrating the sodium silicate solution, and the bonding strength of the recycled water glass was tested. The results showed that the causticization rate could be improved by increasing the amount of quicklime powder, causticization temperature, and causticization time, and the highest causticization rate was above 92%. Amorphous silica in the filtration residue dissolved in the lye. Increasing the amount of the filtration residue, dissolution temperature, and dissolution time could improve the sodium silicate modulus. The bonding strength of the recycled water glass was close to that of commercial water glass. The recycled water glass could be used as a substitute for the commercial water glass.

水玻璃固化冰碛物的强度及固结机理分析

为解决普朗铜矿在开采过程中地表松散冰碛物堆积造成地面塌陷和泥石流的问题,本文采用水玻璃复合酯类固化剂制备固结材料固结冰碛物,对冰碛物固结体的抗压强度进行了研究,并通过XRD、FTIR、DSC-TG和SEM对水玻璃复合酯类固化剂固结材料固结冰碛物的固结机理进行了探究。结果表明,冰碛物固结体28 d抗压强度最高可达2.05 MPa,具有较好的固结性能。酯类固化剂作用下,水玻璃水解产物与酯类固化剂的水解产物反应生成乙酸钠和硅凝胶,硅凝胶起到了填充冰碛物颗粒之间的空隙、胶结冰碛物颗粒的作用。

玻璃酒瓶析钠原因分析及解决方案实践

玻璃酒瓶析钠是玻璃行业长期面临的难题之一。分析了酒瓶析钠现象的表观特征,并采用原子发射光谱仪(ICP)分析析出物的元素组成,研究组分对玻璃瓶耐水性能的影响。通过定点存储实验,发现不同点位取瓶、打包、装托时玻璃瓶的温度、环境的温度和湿度、存储时间等条件均对玻璃瓶析钠程度有影响。对玻璃存储条件提出了优化方案,找出了车间适合存储玻璃瓶的位置与条件,并要求控制库房的存储湿度,使玻璃酒瓶的正常存储周期达到1个月以上,基本解决了本公司的玻璃酒瓶析钠问题。研究结果可为玻璃酒瓶生产企业克服玻瓶析钠难题、延长产品正常存储周期提供参考。

氢氧化钾-钠水玻璃激发剂对碱激发矿渣胶凝材料性能的影响

采用氢氧化钾调节钠水玻璃模数制备复合碱激发剂,以钠水玻璃模数、碱掺量为变量,分析氢氧化钾对钠水玻璃激发矿渣胶凝材料性能的影响,研究氢氧化钾-钠水玻璃激发矿渣胶凝材料在流动度、凝结时间及抗压强度等方面的变化规律。结果表明,氢氧化钾-钠水玻璃复合激发剂的激发效果优于单一钠水玻璃激发剂。当钠水玻璃模数为1.2、碱掺量为8%(质量分数)时,氢氧化钾-钠水玻璃激发矿渣胶凝材料流动度可达240 mm,7 d、28 d抗压强度可达98.88 MPa和104.59 MPa,比同等条件下的钠水玻璃激发矿渣胶凝材料7 d、28 d抗压强度分别提高了16.7%和22.9%。

无机盐对硅酸凝胶形成的影响

用１０ 种无机盐对酸性和碱性硅酸溶胶进行处理，研究了无机盐对胶凝时间的影响。研究结果表明，一般情况下无机盐使胶凝时间缩短，但ＦｅＣｌ３ 使酸性硅酸凝胶形成时间延长。本文还分析了正、负离子的作用机理，排列了各离子影响力的大小顺序。

喷射混凝土液体速凝剂研究现状

概述了国内外液体速凝剂的发展现状,按主要促凝组分把液体速凝剂分为4大类:水玻璃型、铝酸钠(钾)型、硫酸铝型和无硫无碱型液体速凝剂,针对每类液体速凝剂,分别从制备、性能特点和促凝机制研究3个方面对其国内外研究进展和最新成果进行了阐述。指出目前液体速凝剂尤其是无碱液体速凝剂在掺量、价格、储存稳定性和安全环保等几个方面存在的问题,并提出了今后液体速凝剂研究方向。

两种捕收剂反浮选菱镁矿的效果对比

分别以水玻璃或六偏磷酸钠为抑制剂,采用自行研制的阳离子捕收剂Wely对辽宁海城地区的菱镁矿进行反浮选脱硅试验,并与常规菱镁矿反浮选捕收剂十二胺进行对比。结果显示:两种捕收剂适宜的矿浆pH均为5左右;在合适的用量下,两种捕收剂与水玻璃或六偏磷酸钠配合均可获得MgO品位>47%、SiO2含量<0.2%的菱镁矿精矿,但Wely所获MgO回收率比十二胺高2.15～4.06个百分点,可达77.15%～83.64%,证明Wely对硅酸盐矿物有更好的选择性捕收性能;水玻璃作抑制剂时所需用量达六偏磷酸钠的10倍,且精矿回收率较低,因此六偏磷酸钠更适合作为菱镁矿反浮选的抑制剂。

自生气凝胶泡沫体系单液法深部调剖剂可行性研究

本研究目的是利用以石灰水处理油田回注污水时产生的污泥,制备自生气凝胶泡沫体系,用作单液法深部调剖剂.在密闭容器中,含62%碳酸钙和15%碳酸镁的污泥,与8%盐酸或8%盐酸+3.2%水玻璃+起泡剂反应达到平衡的时间(16℃),随初始压力的增大按指数增大,0.8 MPa时反应基本不进行,与18%盐酸反应达到的平衡压力,随温度升高(14～60℃)略有增大(0.58～0.66 MPa).因此,此种泡沫体系的制备和注入应在加压条件下进行.以碳酸钙代替污泥与8%盐酸和3.2%水玻璃密闭反应,随碳酸钙量增大,体系pH值升高,成胶时间缩短,pH＞4时成胶时间≤4小时,生成的水玻璃凝胶泡沫细小而稳定.通过具有含污泥段的高渗透石英砂填砂管分别注入8.2%盐酸、8.2%盐酸+起泡剂、8.2%盐酸+3.2%水玻璃+起泡剂,测绘注入压力曲线,只有注入第3种体系时注入压力才会持续地大幅度升高,最大压力超过注水压力100倍以上,产生了很强的封堵效果.图4表2参7.

水玻璃无机堵剂研究

研究了作为堵剂的水玻璃的基本化学性质及封堵高温岩心的能力。所用水玻璃为工业品,模数3.17,有效物含量40%,用蒸馏水配成溶液,测定沉淀、凝胶生成量（体积分数）和胶凝时间。水玻璃具有温敏性、盐敏性及钙镁敏性,且受pH值的影响,实验结果如下：16%水玻璃在温度高于75℃或NaC l加量大于50 g/L、pH=8.0时生成沉淀,沉淀量随温度升高、盐加量增大而增大并最终大体上趋于不变,胶凝时间则发生相反的变化;在8-〈12 pH范围,加入1.0%CaC l2的8%水玻璃,50℃下在pH约为10时生成的沉淀最大;70℃下随CaC l2加量的增大（0.5%-2.0%）,8%水玻璃的沉淀量略有增大而凝胶量略有减小,沉淀为主要生成物,随MgC l2加量的增大（0.5%-2.0%）凝胶量不断减速少,成为次要生成物,沉淀量不断增多,成为主要生成物。在水测渗透率1.5-1.9μm2、长20 cm的填砂管中,在90℃下交替注入等体积的10%、20%或40%水玻璃和矿化度106.8 g/L的濮城油田注入水,共3个轮次,合计1 PV,封堵率分别为91.6%、96.1%、98.6%,残余阻力系数分别为11.9、25.6、71.4。

抑制剂对块状隐晶质石墨浮选试验影响研究

对原矿进行化学成分分析和矿物组成分析,该石墨矿的脉石主要为石英和伊利石,选用水玻璃和羧甲基纤维素钠为浮选抑制剂。通过对块状隐晶质石墨浮选中抑制剂添加地点及两种抑制剂用量试验,探索在1次粗选1次精选实验中抑制剂的最佳添加位置和用量,并对水玻璃和羧甲基纤维素钠这两种抑制剂的抑制机理进行了讨论。结果表明,在精选段添加抑制剂的尾矿固定碳含量损失较小,而且能得到相对较高品位及回收率的精矿。精选作业中抑制剂水玻璃和羧甲基纤维素钠用量均为500 g/t时,精矿固定碳含量与回收率分别为83.84%和76.05%,所获精矿各项工艺指标最佳。

速溶硅酸钠的生产与应用

速溶硅酸钠属粉状无定形多硅酸钠,因易溶于水,故称速溶硅酸钠。将液体硅酸钠用烧碱调整模数后,经喷雾干燥瞬间脱水而制得。生产工艺简单,易实现自动化操作,产品指标要求高,生产中必须严格控制工艺条件。速溶硅酸钠主要作为建材助剂用于电力建设中,如:电厂烟囱、锅炉、烟道内衬砌筑用的耐酸耐热胶泥材料;还广泛用于大型设备的耐酸防腐中,如:化工、冶金行业耐酸槽内衬用的耐酸胶泥材料,还可添加在粉煤灰水泥材料中作为助磨剂和粉煤灰的活化剂。随着经济的发展,速溶硅酸钠需求量越来越大,已引起建材与化工界的重视。

贵州某含铁泥化氧化锌矿的浮选试验研究

针对贵州某地含铁泥化氧化锌矿的特点,采用硫化-胺法浮选工艺进行了试验研究。结果表明,在不脱泥的情况下,磨矿粒度为-0.074 mm粒级占84%,矿浆pH=10.5左右,分散剂六偏磷酸钠用量为300 g/t,抑制剂水玻璃和淀粉的总用量为700 g/t,硫化剂硫化钠用量为7 kg/t,捕收剂十八胺的用量为150 g/t时,在锌给矿品位为6.54%条件下采用一粗三精两扫工艺,可获得锌品位36.58%,回收率为82.27%的锌精矿,有效实现了氧化锌的浮选。

某白钨尾矿中伴生萤石的选矿试验

江西某白钨浮选尾矿萤石、方解石含量均较高,CaF_2、CaCO_3含量分别为12.33%和9.79%,属于复杂难选伴生萤石二次资源。为从该二次资源中高效回收萤石,进行了详细的选矿试验。结果表明,酸性水玻璃+腐植酸钠组合使用可在浮选萤石时有效抑制方解石等脉石矿物。在氧化石蜡皂731总用量为1 150 g/t,酸性水玻璃+腐植酸钠总用量为(2 750+275)g/t的条件下,采用1次粗选、粗精矿再磨后6次精选、粗选尾矿和精选1尾矿各2次扫选流程处理试样,最终获得CaF_2品位95.26%、回收率85.37%的萤石精矿,较好地实现了从白钨尾矿中综合回收萤石的目标。

水玻璃/膨润土水性膨胀防火涂料的研究

为了改善水性防火涂料耐水性差的缺点,进一步延长防火涂料的耐燃时间,采用改性水玻璃和乳胶粉为成膜基料,以聚磷酸铵、三聚氰胺、季戊四醇为膨胀阻燃体系,滑石粉、钛白粉、玻璃微珠为填料制备了一种新型饰面膨胀防火涂料。结果表明,将15g水玻璃、5g钠基膨润土、0.5g三乙醇胺、0.5g二甲基硅油搅拌分散均匀,同时加入质量浓度为4%盐酸溶液调节体系pH值至8.5左右,制备成改性水玻璃与9g乳胶粉混合并用作为成膜基料,涂料的耐水时间为24h;对阻燃体系进行正交优化表明,当加入聚磷酸铵32g、三聚氰胺16g、季戊四醇11g时,涂料的耐火时间可达58min。

硅石的化学加工

硅石的化学加工是硅矿开发的一条重要途径。文中介绍了硅石与硅系化学品的衍生关系,重点介绍了硅石的高温碱熔法生产钠水玻璃、钾水玻璃、钾钠水玻璃的生产工艺,为以此为母体的硅石的加工奠定了基础。

利用氧氯化锆副产稀碱液制备五水偏硅酸钠

介绍了氧氯化锆稀碱液除杂后，用工业水玻璃补加ＳｉＯ２组分，经蒸发浓缩和控制结晶条件，使五水偏硅酸钠结晶析出，经分离、干燥得到产品。产品质量达到ＨＧ／Ｔ２５６８—９４的优级品标准；生产成本较常规原料生产工艺降低了２５％；本工艺开发成功，避免了该部分稀碱液排放对环境的污染，具有较好的经济和社会效益。

助洗剂的发展趋势

对助洗剂的进展作了扼要回顾 ,主要讨论了助洗剂的作用 ,三聚磷酸钠和膦酸盐 ,硅酸盐 ,沸石 ,碳酸盐和羧酸盐 ,寻找理想助洗剂组合 ,及助洗剂的发展趋势和展望等。

生活垃圾焚烧飞灰-粉煤灰基多孔保温材料的制备

以生活垃圾焚烧飞灰和粉煤灰作为原料,以油酸钠为稳泡剂、双氧水为发泡剂制备多孔保温材料,研究了原料配比、添加剂用量等因素对多孔保温材料抗压和隔热性能的影响。研究结果表明,在飞灰/粉煤灰配比1∶1、油酸钠用量0.4%、水玻璃模数2.5、水玻璃用量10%、双氧水用量2%、水添加量40%条件下,制备的多孔保温材料抗压和隔热性能优异,其抗压强度和导热系数分别为0.48 MPa和0.091 W/(m·K)。

丁二酸钠对氯化钙和水玻璃溶液的渗透性影响

采用正向渗透试验方法测定了氯化钙和水玻璃溶液添加丁二酸钠后溶液在粉尘介质中的渗透规律。该研究结果可有效利用氯化钙和水玻璃进行固土抑尘。

十二烷基磺酸钠对氯化钙和水玻璃溶液的渗透性影响

采用正向渗透试验方法测定了氯化钙和水玻璃溶液添加十二烷基磺酸钠后溶液在粉尘中的渗透规律。结果表明：对于重量比５％、１５％、２５％的Ｃａ－Ｃｌ２溶液，十二烷基磺酸钠的适宜添加量分别为０．３％～０．５％、０．２％～０．５％、０．２％～０．５％，此时溶液的渗透能力可分别提高约１０％、１０％、１５％。对于重量比５％、１５％、２５％的水玻璃溶液，十二烷基磺酸钠的适宜添加量为０．２％～０．４％、０．３％～０．４％、０．５％～０．６％，此时溶液的渗透能力可分别提高２５％、２０％、２２％。该结果对有效利用氯化钙和水玻璃进行固土抑尘具有重要意义。