STUDY ON PHOTOCATALYTIC MECHANISM OF SOL-GEL-DERIVED Pb-DOPED TiO_2 THIN FILMS

Pb-doped TiO2 photocatalytic thin films were prepared on a soda-lime glass substrate via sol-gel method using TiO2 sol solution containing lead and characterized by X-ray photoelectron spectroscopy (XPS). The results showed that besides oxides of Ti(IV) there is a certain amount of oxides of To(?) and Ti(?) and Pb exists in the forms of PbTiO3 and PbO. The photocatalytic activity of the Pb-doped TiO2 films was evaluated by the photocatalytic decolorization of aqueous methyl orange and photocatalytic mechanism mas also analyzed.

Preparation of Nanometer-structured TiO_2 Thin Films by Sol-Gel Method

The transparent anatase TiO 2 nanometer thin films were prepared by the sol-gel method on soda-lime glass.X-ray diffraction,thermal analysis and UV-visible spectrophotometer were used to analyze the formation of the phases.Only increasing the heat-treatment time,the average grain size has no obvious change.The mechanism of grain growth in TiO 2 thin film is probably as follows:the grain of coating will become grain core later;TiO 2 sol constantly deposited on the surface of TiO 2 grain and formed membrane with increasing of coating cycle times;TiO 2 grain in the film grow steadily.

Preparation and Characterization of Sol-Gel Derived Au Nanoparticle Dispersed Y_2O_3∶Eu Films

Gold nanoparticles dispersed Y2O3 films were prepared through a sol-gel method by using yttrium acetate and Au nanoparticles colloid as precursors. The films were characterized by X-ray diffraction （XRD）, transmission electron microscopy （TEM） and UV-VIS absorption spectra. XRD patterns and TEM images of Y2O3 ＋ Au films give the same resuits on structure and particle size as that of pure Y2O3 films. The surface plasma resonance （SPR） of Au nanoparticles in Y2O3 ＋ Au film was observed around 550 nm in the absorption spectrum and its position shifts to red with increasing annealing temperature is caused by the increase of dielectric constant of Y2O3 matrix and the size of Au nanoparticles. The second and third order nonlinear optical effects of Y2O3 ＋ Au films were also observed. The photoluminescent properties of Y2O3 ： Eu ＋ Au films were investigated and results indicate that there exist an energy transfer from Eu^3 ＋ to Au nanoparticles and this energy transfer decreases the emission of Eu^3 ＋ in Y2O3 ： Eu ＋ Au film.

Surface Microstructure Characterization of Sol-gel Derived Porous TiO_2 Thin Films

Porous TiO2 thin films were prepared from alkoxide solutions with and without polyethylene glycol (PEG) by sol-get route on soda lime glass, and were characterized by atomic force microscopy (AFM), transmission electron microscopy (TEM) and X-ray diffraction (XRD). The results show that TiO2 film prepared from precursor solution without PEG is composed of spherical particles of about 100 nm and several nanometer mesoporous pores. With the increase of the amount of PEG added to the precursor solution, the diameter and the depth of the pores in the resultant films increas on the decomposition of PEG during heat-treatment, which lead to them increase of the surface roughness of the films. XRD and TEM results show that the single anatase phase is precipitated and there are some orientation effects in (101) direction.

Self-Cleaning Properties of Vanadium Doped TiO₂Sol-Gel Derived Thin Films

In this study, vanadium doped TiO2 thin films were deposited on glass substrates using a sol-gel dip-coating process. X-Ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and UV-Vis spectrophotometer were used to characterize the structural, chemical and the optical properties of the thin films. The photo-catalytic activities of films were investigated by methylene blue degradation. Water contact angle on the film surfaces was measured by a water contact angle analyzer. The results indicated that vanadium doping had a significant effect on the self-cleaning properties of TiO2 thin films.

Bactericidal and Photoeatalytie Activity of Fe^(3+)-TiO_2 Thin Films Prepared by the Sol-gel Method

Pure TiO2 thin films and iron doped TiO2 thin films on glass substrate were prepared by sol-gel method, and characterized by X-ray diffractometer （XRD）, thermo-gravimetric analysis （TG-DSC）, high resolution transmission electron microscope （HRTEM）, scanning electron microscope （SEM） and UV-Vis spectroscopy, respectively. The experimental results show that the pure TiO2 thin films and iron doped TiO2 thin films can destroy most of the escherichia coli and bacillus subtillis under the irradiation of 365 nm UV-light. However, the iron doped TiO2 thin film is a better photocatalyst than pure TiO2 thin film. The ultrastructural studies provide direct evidences for understanding the bactericidal mechanism of the TiO2 photocatalyst.

PBST/TiO_(2)/MgO复合薄膜的制备及性能

采用硅烷偶联剂γ-甲基丙烯酰氧基丙基三甲氧基硅烷(KH-570)对TiO_(2)/MgO NPs改性,采用溶液共混法制备了聚丁二酸-共-对苯二甲酸丁二醇酯(PBST)/TiO_(2)/MgO NPs纳米复合薄膜,并探讨了其在食品包装方面的应用。研究了改性TiO_(2)/MgO NPs对PBST基体机械、阻隔、抗菌和保鲜性能的影响。结果表明:复合膜的抗拉强度和水蒸汽透过率分别为29.39MPa和2.43×10^(-11) g·m/(m^(2)·s·Pa),相较PBST基体抗拉强度提高了24.32%,水蒸汽透过率降低了32.37%,且对金黄色葡萄球菌(S.aures)和大肠杆菌(E.coli)抑菌效果显著,分别达到98.7%和97.2%,并对圣女果有良好的保鲜性能,当改性后的TiO_(2)/MgO NPs质量含量为5%时,复合薄膜的性能最佳。

Preparation of CuYO2 Thin Films by Sol-Gel Method Using Copper Acetate and Yttrium Acetate as Metal Sources

Delafossite structured p-type wide bandgap semiconductor, CuYO2 thin films were prepared on SiO2 substrate by sol-gel method using copper (II) acetate and yttrium (III) acetate as source materials. The films preparation process was studied by varying annealing temperature after the preparation of gel films by spin coating, followed by thermal annealing at higher temperature. In the present work, one step annealing directly from Cu-Y-gel under nitrogen flow was used. X-ray diffraction (XRD) revealed that the film annealed at 800。C is significantly c-axis oriented, shows only (002) and (004) peaks at 15.6。 and 31.5。, respectively. The optical bandgap of 3.7 - 3.8 eV is estimated by (αhν)2 plot which is higher than previous works. In addition, the films with highly c-axis orientation showed photoluminescence (PL) at room temperature with very broad peak at 2.3 eV. The films annealed at different temperature showed different structural properties.

Preparations of TiO_2 film coated on foam nickel substrate by sol-gel processes and its photocatalytic activity for degradation of acetaldehyde

Anatase TiO2 films were successfully prepared on foam nickel substrates by sol-gel technique using tetrabutyl titanate as precursor. The characteristics of the TiO2 films were investigated by XPS, XRD, FE-SEM, TEM and UV-Vis absorption spectra. The photocatalytic activities of TiO2 films were investigated by photocatalytic degradation reactions of gaseous acetaldehyde, an indoor pollutant, under ultraviolet light irradiation. It was found that Ni^2＋ doping into TiO2 films due to the foam nickel substrates resulted in the extension of absorption edges of TiO2 films from UV region to visible light region. The pre-heating for foam nickel substrates resulted in the formation of NiO layer, which prevented effectively the injection of photogenerated electrons from TiO2 films to metal nickel. The TiO2 films displayed high photocatalytic activity for the degradation of acetaldehyde, and were enhanced by calcining the substrates and coating TiO2 films repeatedly. The high activity was mainly attributed to the improvement of the characteristics of substrate surface and the increase of active sites on photocatalyst.

Influences of working pressure on properties for TiO_2 films deposited by DC pulse magnetron sputtering

TiO2 films were deposited at room temperature by DC pulse magnetron sputtering system.The crystalline structures,morphological features and photocatalytic activity of TiO2 films were systematically investigated by X-ray diffraction（XRD）,atomic force microscopy（AFM） and ultraviolet spectrophotometer,respectively.The results indicated that working pressure was the key deposition parameter in？uencing the TiO2 film phase composition at room temperature,which directly affected its photocatalytic activity.With increasing working pressure,the target self-bias decreases monotonously.Therefore,low temperature TiO2 phase（anatase） could be deposited with high working pressure.The anatase TiO2 films deposited with 1.4 Pa working pressure displayed the highest photocatalytic activity by the decomposition of Methyl Orange solution,which the degradation rate reached the maximum（35%） after irradiation by ultraviolet light for 1 h.

Upconversion properties of Y_2O_3:Er films prepared by sol-gel method

Y2O3：Er^3＋ films were prepared by a simple sol-gel process. The structural properties of Y2O3：Er^3＋ films were characterized with X-ray diffraction, Fourier transform infrared spectroscopy and field emission scanning electron microscopy. The results indicated that the Y2O3：Er^3＋ films might have high upconversion efficiency because of their low vibrational energy. Under 785 and 980 nm laser excitation, the samples showed green （^2H11/2→^4I15/2, ^4S3/2→^4I15/2） and red （^4F9/2→^4I15/2） upconversion emissions. The upconversion mechanisms were studied in detail through laser power dependence. Excited state absorption and energy transfer process were discussed as possible upconversion mechanisms. The cross relaxation process in Er^3＋ was also investigated.

Nanostructure Study of TiO2 Films Prepared by Dip Coating Process

The microstructure properties of the sol-gel derived TiO2 films were studied by the atomic force microscopy (AFM). The films were prepared by dip coating process. The optical properties of the films were explained on the basis of the microstructure of the films.

Low-temperature Preparation of Photocatalytic TiO_2 Thin Films on Polymer Substrates by Direct Deposition from Anatase Sol

Anatase TiO2 sol was synthesized under mild conditions （75℃ and ambient pressure） by hydrolysis of titaniumn-butoxide in abundant acidic aqueous solution and subsequent reflux to enhance crystallization. At room temperature and in ambient atmosphere, crystalline TiO2 thin films were deposited on polymethylmethacrylate （PMMA）, SiO2-coated PMMA and SiO2-coated silicone rubber substrates from the as-prepared TiO2 sol by a dip-coating process. SiO2 layers prior to TiO2 thin films on polymer substrates could not only protect the substrates from the photocatalytic decomposition of the TiO2 thin films but also enhance the adhesion of the TiO2 thin films to the substrates. Field-emission type scanning electron microscope （FE-SEM） investigations revealed that the average particle sizes of the nanoparticles composing the TiO2 thin films were about 35-47 nm. The TiO2 thin films exhibited high photocatalytic activities in the degradation of reactive brilliant red dye X-3B in aqueous solution under aerated conditions. The preparation process of photocatalytic TiO2 thin films on the polymer substrates was quite simple and a low temperature route.

Preparation and Properties of Ag-TiO_2 Thin Films on Glass Substrates

Ag TiO 2 thin films were prepared on glasses.The morphology and structure of Ag TiO 2 films were investigated by XRD, SEM and FT IR.The photocatalytic and hydrophilic properties of Ag TiO 2 thin films were also evaluated by examining photocatalytic degradation dichlorophos under sunlight illumination and the change of contact angle respectively.The research results show that the Ag TiO 2 thin film is mainly composed of 20-100nm Ag and TiO 2 particles.The Ag TiO 2 thin films possess a super hydrophilic ability and higher photocatalytic activity than that of pure TiO 2 thin film.

Study on UV Shielding TiO_2 Thin Film Prepared by Sol-Gel Method

Titanium dioxide (TiO_2) thin films were prepared on microscopes slides by sol-gel and dip-coating processes from specially formulated sols.The results show that there exists anatase and rutile structure of TiO_2 when heat treatment temperature is 450℃,and at 800℃,TiO_2 particle size is of below 100 nm and rutile structure is presented.In the range of 360 nm～400 nm the transmittance of TiO_2 sol increases with the increasing of the concentration of Ti(OC_4H_9)_4 in ethanol solution. The transmittance of TiO_2 films with various number of the layer is measured to be 0% below 320 nm,and the three-layer TiO_2 film is of the best UV resistance in the range of 320 nm～400 nm.

The Effect of SiO_2 Additive on Super-hydrophilic Property of TiO_2-SiO_2 Thin Film by Sol-gel Method

TiO2-SiO2 thin films have been prepared on slide glass substrates by sol-gel method, and the effect of SiO2 additive on photo-generated hydrophilicity of TiO2 thin film was investigated by measuring the contact angle of water, the microstructure, the transmittance, the photocatalytic activity and the specific surface area . The results showed that 10mol% of SiO2 additive was the most effective for decreasing contact angle of water. The SiO2 additive of less than 30mol% has a suppressive effect on the crystal growth of anatase in calcinations, resulting in a large surface area. Consequently, the super-hydrophilicity was improved.

PREPARATION OF TiO_2 THIN FILMS BY MOCVD METHOD

Preparation of TiO2 thin films by MOCVD method is presented in this paper. A MOCVD system has been designed and built. A wide range of processing conditions are investigated to deposit TiO2 films on Si wafers starting from metal-organic precursor tetrabutyl titanate. Activation energy of the film formation （E） is obtained to be 23.6 kJ/mol. Structure of films is pure anatase when deposit temperatures are low, rutile forms at 700℃. The films also exhibit preferred crystallographic orientations which strongly depend on deposit conditions. Refractive index increases with increasing of film thickness and decreasing of deposit temperature.

Preparation and Characterization of Nano-ZnFe_2O_4/TiO_2 Films

The nano-ZnFe2O4/TiO2 films possess the functions of desulfurization and degradation for organic pollutants. The sols of ZnFe2O4/TiO2 were prepared by sol-gel method and coated on glass and porous ceramic by vertical coating and dipping-lift processes, respectively, and the samples were obtained after drying and sintering. The composition, appearance, absorption spectrum of the films, and the influence of the film on porous ceramic performances were analyzed using SEM, AFM, UVVis spectrometer, and mercury porosimeter, respectively, to determine the operation parameters of the multifunction porous ceramic elements for gas-purification.