The effect of yttria on the solid reaction mechanism of a CaHPO4·2H2O ＋ CaCO3 system at different temperatures was experimentally stud-ied. The samples with and without yttria were subjected to thermogravimetric...The effect of yttria on the solid reaction mechanism of a CaHPO4·2H2O ＋ CaCO3 system at different temperatures was experimentally stud-ied. The samples with and without yttria were subjected to thermogravimetric/differential scanning calorimetry measurement. The samples were heat treated at the temperatures corresponding to the peaks on the DSC spectra, and the resulted phase compositions were identified by X-ray diffraction. The transformation mechanism was deduced by comparing the phases obtained at different temperatures. The results show that the transformations at below 1073 K are not affected by yttria, but all those at above 1073 K are completely altered. The formation tem-perature of hydroxyapatite decreases by 134 K, and the decomposition temperature increases by 38 K. The polymorphous transformation of Ca3（PO4）2 from β phase to α phase increases by 47 K. The thermodynamic properties of the transformations at above 1073 K are also modi-fied by the addition of yttria; that is, the endothermal peaks are substituted by exothermal peaks.展开更多
文摘The effect of yttria on the solid reaction mechanism of a CaHPO4·2H2O ＋ CaCO3 system at different temperatures was experimentally stud-ied. The samples with and without yttria were subjected to thermogravimetric/differential scanning calorimetry measurement. The samples were heat treated at the temperatures corresponding to the peaks on the DSC spectra, and the resulted phase compositions were identified by X-ray diffraction. The transformation mechanism was deduced by comparing the phases obtained at different temperatures. The results show that the transformations at below 1073 K are not affected by yttria, but all those at above 1073 K are completely altered. The formation tem-perature of hydroxyapatite decreases by 134 K, and the decomposition temperature increases by 38 K. The polymorphous transformation of Ca3（PO4）2 from β phase to α phase increases by 47 K. The thermodynamic properties of the transformations at above 1073 K are also modi-fied by the addition of yttria; that is, the endothermal peaks are substituted by exothermal peaks.