185℃高温热处理对水曲柳木材物理性能的影响

对经过185℃生产性高温热处理的水曲柳木材的物理性能指标进行了测定,并以素材为对照,对其密度、吸湿性和尺寸稳定性进行了分析。结果表明,处理材的绝干与气干密度相对素材略有下降,吸湿性则明显低于素材,且与素材之间的平衡含水率差值随相对湿度增大而增大,而在温度60℃、相对湿度分别为40%(干燥)、80%(潮湿)的环境中平衡后,处理材的弦、径向湿涨率相对素材均有不同程度的下降,两种环境下处理材的体积抗涨率分别达到了55.53%、47.34%,尺寸稳定性得到显著改善。

高温热处理对水曲柳材色的影响

The color change of ash wood(Fraxinus mandshurica)before and after high temperature heat treatment were investigated with WSC-S color difference meter in this paper.The results showed that:the color of treated wood is affected by the processing temperature,the higher the temperature,the darker the appearance,moreover,the change in L component can be used for quantitative analysis on color change.The color of treated ash wood by suitable processing temperature could be simulated to some valuable wood,for example,teak wood,some rosewood species,etc.The color of treated wood could be well replicated from laboratory scale experiments to commercial scale production.

185℃高温热处理对水曲柳木材力学性能的影响

对经过185℃生产性高温热处理的水曲柳木材的力学性能进行测试和分析。结果表明:与素材一样,处理材弦径向弹性模量之间没有显著差异;高温热处理对水曲柳木材弦向弯曲强度和横纹抗压强度有不利影响,而弦向弹性模量、顺纹抗压强度、表面硬度等受此种工艺的影响很小。若将处理材与素材在实际使用情况下的力学性能进行比较,处理材除了在弦向弯曲强度上仍比素材低,上述各项力学性能均高于素材。

实木地板坯料加工技术现状及趋势分析

实木地板坯料的质量直接影响着实木地板产品的质量及合格率。作者对实木地板坯料使用的木材来源以及锯解、干燥等加工技术进行归纳分析,并对实木地板坯料加工技术的发展趋势进行展望。

实木地板木材干燥技术

本文重点介绍了地板锯材或毛料的常规窑干技术,同时详细说明了地板锯材含水率基准的制定和修正。文中推荐了部分常用进口木材实木地板的窑干基准(厚度25 mm)及其窑干工艺规程,供相关单位参考。

实木地板坯料杀虫、灭菌湿热处理过程温度变化特性

利用木材常规干燥试验机对5种常用实木地板坯料的杀虫、灭菌湿热平衡处理工艺过程进行模拟,分析其温度变化特性。地板坯料随加热介质(湿空气)温度先线性快速升高后逐渐趋于波动稳定。不同树种地板坯料的稳定维持温度值较一致。湿热处理过程介质湿度增加,加热均匀性提高,地板坯料更易达到和保持稳定温度。以11.5%作为地板坯料平衡含水率目标值设置湿热处理的温、湿度条件,以地板坯料稳定维持温度最低值作判据,所制定的S1~S3(60~70℃/RH 72.3%~90.4%)和S4~S6(75~85℃/RH 76.7%~92.9%)工艺分别达到杀虫、灭菌的温度要求。