In this study,HEA/AI composite interlayer was used to fabricate Ti/Mg bimetal composites by solidliquid compound casting process.The Al layer was prepared on the surface of TC4 alloy by hot dipping,and the FeCoNiCr HE...In this study,HEA/AI composite interlayer was used to fabricate Ti/Mg bimetal composites by solidliquid compound casting process.The Al layer was prepared on the surface of TC4 alloy by hot dipping,and the FeCoNiCr HEA layer was prepared by magnetron sputtering onto the Al layer.The influence of the HEA layer thickness and pouring temperature on interface evolution was investigated based on SEM observation and thermodynamic analysis.Results indicate that the sluggish diffusion effect of HEA can effectively inhibit the interfacial diffusion between Al and Mg,which is conducive to the formation of solid solution,especially when the thickness of HEA is 800 nm.With the increase of casting temperature from 720 ℃ to 730 ℃,740℃,and 750 ℃,α-Al(Mg),α-Al(Mg)+Al3Mg2,Al3Mg2+Al12Mg17,and Al12Mg17+δ-Mg are formed at the interface of Ti/Mg bimetal,respectively.When the thickness of the HEA layer is 800 nm and the pouring temperature is 720 ℃,the bonding strength of the Ti/Mg bimetal can reach the maximum of 93.6 MPa.展开更多
To achieve Ti/Mg bimetallic composite with high strength and metallurgical bonding interface,Al interlayer and Zn/Al composite interlayer were used to prepare TC4/AZ91D bimetal composite with metallurgical bonding int...To achieve Ti/Mg bimetallic composite with high strength and metallurgical bonding interface,Al interlayer and Zn/Al composite interlayer were used to prepare TC4/AZ91D bimetal composite with metallurgical bonding interface by solid-liquid compound casting,respectively.Al interlayer was prepared on the surface of TC4 alloy by hot dipping,and Zn/Al composite interlayer was prepared by electroplating process.The results suggested that the phases across the interface were Al Ti andα(Al)+Mg_(21)(Al,Zn)_(17)when Zn/Al composite interlayer was used.When Al interlayer was used as interlayer,Al Mg Ti ternary structure and Al_(12)Mg_(17)+δ-Mg eutectic structure were the main phases at the interface.The shear strength of TC4/AZ91D bimetal with Zn/Al composite interlayer was much higher than that with pure Al interlayer,and the value of the shear strength was increased from 48.5 to 67.4 MPa.Thermodynamic models based on different compositions of the interface were established to explain the microstructure evolution of the interfacial zone.展开更多
The solubility of 2,3,4-trichloro-1,5-dinitrobenzene(TCDNB) was measured by a laser dynamic method over the temperature range from 278.15 K to 323.15 K under 0.1 MPa in fifteen mono-solvents(methanol,ethanol,isopropan...The solubility of 2,3,4-trichloro-1,5-dinitrobenzene(TCDNB) was measured by a laser dynamic method over the temperature range from 278.15 K to 323.15 K under 0.1 MPa in fifteen mono-solvents(methanol,ethanol,isopropanol,n-butanol,toluene,dichloromethane,chloroform,tetrachloromethane,1,2-dichloroethane,acetone,ethyl acetate,acetonitrile,N-methylpyrrolidone(NMP),N,Ndimethylformamide dimethyl sulfoxide(DMF),dimethyl sulfoxide(DMSO).The solubility of TCDNB could be increased with increasing temperature in fifteen mono-solvents.TCDNB solubility is in the following order at 298.15 K:NMP>DMF>DMSO>toluene>acetone>ethyl acetate>dichloromethane>1,2-dich loroethane>chloroform>acetonitrile>tetrachloromethane>methanol>ethanol>n-butanol>isopropanol.The KAT-LSER model was used to investigate the solvent effect,which revealed that the hydrogen bond acidity of solvents has a greater effect on TCDNB solubility.The van't Hoff model,the modified Apelblat model,theλh model,and the non-random two liquid(NRTL)model were used to correlate the solubility of TCDNB.The calculated solubility data agreed well with the experimental data,and the modified Apelblat model fit best.Furthermore,the van't Hoff and Gibbs equations were also used to calculate the dissolution thermodynamic properties of TCDNB in various solvents.TCDNB dissolution could be an enthalpy-driven,non-spontaneous,and endothermic process in fifteen mono-solvents.The determination and fitting solubility of TCDNB,as well as the calculation of its thermodynamic properties,would be critical in the purification and crystallization of its preparation process research.展开更多
A Ni-P coating was deposited on Cu substrate by electroless plating and the Al/Cu bimetal was produced by solid？liquid compound casting technology. The microstructure, mechanical properties and conductivity of Al/Cu ...A Ni-P coating was deposited on Cu substrate by electroless plating and the Al/Cu bimetal was produced by solid？liquid compound casting technology. The microstructure, mechanical properties and conductivity of Al/Cu joints with different process parameters （bonding temperature and preheating time） were investigated. The results showed that intermetallics formed at the interface and the thickness and variety increased with the increase of bonding temperature and preheating time. The Ni？P interlayer functioned as a diffusion barrier and protective film which effectively reduced the formation of intermetallics. The shear strength and conductivity of Al/Cu bimetal were reduced by increasing the thickness of intermetallics. In particular, the detrimental effect of Al2Cu phase was more obvious compared with the others. The sample preheated at 780 ℃ for 150 s exhibited the maximum shear strength and conductivity of 49.8 MPa and 5.29×10^5 S/cm, respectively.展开更多
The flow with solid-liquid two-phase media inside centrifugal pumps is very complicated and the relevant method for the hydraulic design is still immature so far. There exist two main problems in the operation of the ...The flow with solid-liquid two-phase media inside centrifugal pumps is very complicated and the relevant method for the hydraulic design is still immature so far. There exist two main problems in the operation of the two-phase flow pumps, i.e., low overall efficiency and severe abrasion. In this study, the three-dimensional, steady, incompressible, and turbulent solid-liquid two-phase flows in a low-specific-speed centrifugal pump are numerically simulated and analyzed by using a computational fluid dynamics （CFD） code based on the mixture model of the two-phase flow and the RNG k-~ two-equation turbulence model, in which the influences of rotation and curvature are fully taken into account. The coupling between impeller and volute is implemented by means of the frozen rotor method. The simulation results predicted indicate that the solid phase properties in two-phase flow, especially the concentration, the particle diameter and the density, have strong effects on the hydraulic performance of the pump. Both the pump head and the efficiency are reduced with increasing particle diameter or concentration. However, the effect of particle density on the performance is relatively minor. An obvious jet-wake flow structure is presented near the volute tongue and becomes more remarkable with increasing solid phase concentration. The suction side of the blade is subject to much more severe abrasion than the pressure side. The obtained results preliminarily reveal the characteristics of solid-liquid two-phase flow in the centrifugal pump, and are helpful for improvement and empirical correction in the hydraulic design of centrifugal pumps.展开更多
In this work,a new crystallization method was used to prepare two polymorphs of sulfamethazine-saccharin(SMT-SAC)cocrystal in bulk.The purity and crystal form of both polymorphs were confirmed by optical microscopy,sc...In this work,a new crystallization method was used to prepare two polymorphs of sulfamethazine-saccharin(SMT-SAC)cocrystal in bulk.The purity and crystal form of both polymorphs were confirmed by optical microscopy,scanning electron microscopy,powder X-ray diff raction,diff erential scanning calorimetry,and thermogravimetric analysis.Moreover,the solubility of the stable form(form Ⅱ)was determined by gravimetric analysis in nine pure solvents and one binary(acetoni-trile+2-propanol)solvent at temperatures ranging from 278.15 to 348.15 K at atmospheric pressure.Experimental data were correlated using the modified Apelblat model,theλh equation,the nonrandom two-liquid(NRTL)model,the Jouyban-Acree model,and the CNIBS/Redlich-Kister model.Finally,the apparent thermodynamic properties,such asΔ_(dis)G,Δ_(dis) H,andΔ_(dis) S,were calculated on the basis of the activity coefficient obtained by the NRTL model.All the models correlate well,and all the experimental and calculated results indicate that the dissolution behavior of SMT-SAC cocrystal form II is a spontaneous,endothermic,and entropy-driven process.展开更多
Limited by mining technology,mineral exploitation can produce large amounts of tailings.Heavy summer rainfall or seasonal freeze-thaw can lead to physical and chemical modification of tailing material in mountainous a...Limited by mining technology,mineral exploitation can produce large amounts of tailings.Heavy summer rainfall or seasonal freeze-thaw can lead to physical and chemical modification of tailing material in mountainous areas,resulting in fluidized tailings flow and severe disaster losses.Therefore,aiming at the problem of tailings fluidization catastrophe,this paper tried to reveal the rheological mechanism of tailings fluidization transformation by combining rheological tests and theoretical analysis.The results show that the yield stress increases with decreasing temperature,and when the density of debris flow(ρ)is more than 1.9 g/cm~3,this behavior becomes more pronounced as the density increases.The storage modulus decreases by at least two orders of magnitude at the solid-fluid transition under amplitude test sweep.Storage and loss modulus in the linear viscoelastic range and yield stress have an exponential growth relationship with sediment concentration.In addition,a stress constitutive relation and a new exponential law describing the evolution of yield stress required for solid-liquid transformation were proposed,and the relationship is further strengthened through a comprehensive analysis of existing results,which expands the evaluation application of the rheological characteristics of tailings flow.This paper provides a new insight into the rheological properties of tailing and how they occur through solid-liquid transition under different environments,which is beneficial to geological hazard prevention and the ecological remediation of the mining area.展开更多
基金financial supports from the National Natural Science Foundation of China (No. 51875062)China Postdoctoral Science Foundation (No. 2021M700567)。
文摘In this study,HEA/AI composite interlayer was used to fabricate Ti/Mg bimetal composites by solidliquid compound casting process.The Al layer was prepared on the surface of TC4 alloy by hot dipping,and the FeCoNiCr HEA layer was prepared by magnetron sputtering onto the Al layer.The influence of the HEA layer thickness and pouring temperature on interface evolution was investigated based on SEM observation and thermodynamic analysis.Results indicate that the sluggish diffusion effect of HEA can effectively inhibit the interfacial diffusion between Al and Mg,which is conducive to the formation of solid solution,especially when the thickness of HEA is 800 nm.With the increase of casting temperature from 720 ℃ to 730 ℃,740℃,and 750 ℃,α-Al(Mg),α-Al(Mg)+Al3Mg2,Al3Mg2+Al12Mg17,and Al12Mg17+δ-Mg are formed at the interface of Ti/Mg bimetal,respectively.When the thickness of the HEA layer is 800 nm and the pouring temperature is 720 ℃,the bonding strength of the Ti/Mg bimetal can reach the maximum of 93.6 MPa.
基金the financial support from the National Natural Science Foundation of China(No.51875062)。
文摘To achieve Ti/Mg bimetallic composite with high strength and metallurgical bonding interface,Al interlayer and Zn/Al composite interlayer were used to prepare TC4/AZ91D bimetal composite with metallurgical bonding interface by solid-liquid compound casting,respectively.Al interlayer was prepared on the surface of TC4 alloy by hot dipping,and Zn/Al composite interlayer was prepared by electroplating process.The results suggested that the phases across the interface were Al Ti andα(Al)+Mg_(21)(Al,Zn)_(17)when Zn/Al composite interlayer was used.When Al interlayer was used as interlayer,Al Mg Ti ternary structure and Al_(12)Mg_(17)+δ-Mg eutectic structure were the main phases at the interface.The shear strength of TC4/AZ91D bimetal with Zn/Al composite interlayer was much higher than that with pure Al interlayer,and the value of the shear strength was increased from 48.5 to 67.4 MPa.Thermodynamic models based on different compositions of the interface were established to explain the microstructure evolution of the interfacial zone.
文摘The solubility of 2,3,4-trichloro-1,5-dinitrobenzene(TCDNB) was measured by a laser dynamic method over the temperature range from 278.15 K to 323.15 K under 0.1 MPa in fifteen mono-solvents(methanol,ethanol,isopropanol,n-butanol,toluene,dichloromethane,chloroform,tetrachloromethane,1,2-dichloroethane,acetone,ethyl acetate,acetonitrile,N-methylpyrrolidone(NMP),N,Ndimethylformamide dimethyl sulfoxide(DMF),dimethyl sulfoxide(DMSO).The solubility of TCDNB could be increased with increasing temperature in fifteen mono-solvents.TCDNB solubility is in the following order at 298.15 K:NMP>DMF>DMSO>toluene>acetone>ethyl acetate>dichloromethane>1,2-dich loroethane>chloroform>acetonitrile>tetrachloromethane>methanol>ethanol>n-butanol>isopropanol.The KAT-LSER model was used to investigate the solvent effect,which revealed that the hydrogen bond acidity of solvents has a greater effect on TCDNB solubility.The van't Hoff model,the modified Apelblat model,theλh model,and the non-random two liquid(NRTL)model were used to correlate the solubility of TCDNB.The calculated solubility data agreed well with the experimental data,and the modified Apelblat model fit best.Furthermore,the van't Hoff and Gibbs equations were also used to calculate the dissolution thermodynamic properties of TCDNB in various solvents.TCDNB dissolution could be an enthalpy-driven,non-spontaneous,and endothermic process in fifteen mono-solvents.The determination and fitting solubility of TCDNB,as well as the calculation of its thermodynamic properties,would be critical in the purification and crystallization of its preparation process research.
基金Project(51571080)supported by the National Natural Science Foundation of China
文摘A Ni-P coating was deposited on Cu substrate by electroless plating and the Al/Cu bimetal was produced by solid？liquid compound casting technology. The microstructure, mechanical properties and conductivity of Al/Cu joints with different process parameters （bonding temperature and preheating time） were investigated. The results showed that intermetallics formed at the interface and the thickness and variety increased with the increase of bonding temperature and preheating time. The Ni？P interlayer functioned as a diffusion barrier and protective film which effectively reduced the formation of intermetallics. The shear strength and conductivity of Al/Cu bimetal were reduced by increasing the thickness of intermetallics. In particular, the detrimental effect of Al2Cu phase was more obvious compared with the others. The sample preheated at 780 ℃ for 150 s exhibited the maximum shear strength and conductivity of 49.8 MPa and 5.29×10^5 S/cm, respectively.
基金supported by National Natural Science Foundation of China (Grant No. 21076198)Zhejiang Provincial Natural Science Foundation of China (Granted No. R1100530)National Basic Research Program of China (973 Program,Grant No. 2009CB724303)
文摘The flow with solid-liquid two-phase media inside centrifugal pumps is very complicated and the relevant method for the hydraulic design is still immature so far. There exist two main problems in the operation of the two-phase flow pumps, i.e., low overall efficiency and severe abrasion. In this study, the three-dimensional, steady, incompressible, and turbulent solid-liquid two-phase flows in a low-specific-speed centrifugal pump are numerically simulated and analyzed by using a computational fluid dynamics （CFD） code based on the mixture model of the two-phase flow and the RNG k-~ two-equation turbulence model, in which the influences of rotation and curvature are fully taken into account. The coupling between impeller and volute is implemented by means of the frozen rotor method. The simulation results predicted indicate that the solid phase properties in two-phase flow, especially the concentration, the particle diameter and the density, have strong effects on the hydraulic performance of the pump. Both the pump head and the efficiency are reduced with increasing particle diameter or concentration. However, the effect of particle density on the performance is relatively minor. An obvious jet-wake flow structure is presented near the volute tongue and becomes more remarkable with increasing solid phase concentration. The suction side of the blade is subject to much more severe abrasion than the pressure side. The obtained results preliminarily reveal the characteristics of solid-liquid two-phase flow in the centrifugal pump, and are helpful for improvement and empirical correction in the hydraulic design of centrifugal pumps.
基金supported by the National Natural Science Foundation of China(No.21676196).
文摘In this work,a new crystallization method was used to prepare two polymorphs of sulfamethazine-saccharin(SMT-SAC)cocrystal in bulk.The purity and crystal form of both polymorphs were confirmed by optical microscopy,scanning electron microscopy,powder X-ray diff raction,diff erential scanning calorimetry,and thermogravimetric analysis.Moreover,the solubility of the stable form(form Ⅱ)was determined by gravimetric analysis in nine pure solvents and one binary(acetoni-trile+2-propanol)solvent at temperatures ranging from 278.15 to 348.15 K at atmospheric pressure.Experimental data were correlated using the modified Apelblat model,theλh equation,the nonrandom two-liquid(NRTL)model,the Jouyban-Acree model,and the CNIBS/Redlich-Kister model.Finally,the apparent thermodynamic properties,such asΔ_(dis)G,Δ_(dis) H,andΔ_(dis) S,were calculated on the basis of the activity coefficient obtained by the NRTL model.All the models correlate well,and all the experimental and calculated results indicate that the dissolution behavior of SMT-SAC cocrystal form II is a spontaneous,endothermic,and entropy-driven process.
基金supported by The National Nat ural Science Foundation of China(No.42207184)Nature Science Basic Research Plan in Shaanxi Provi nce of China(No.2022JQ-253)。
文摘Limited by mining technology,mineral exploitation can produce large amounts of tailings.Heavy summer rainfall or seasonal freeze-thaw can lead to physical and chemical modification of tailing material in mountainous areas,resulting in fluidized tailings flow and severe disaster losses.Therefore,aiming at the problem of tailings fluidization catastrophe,this paper tried to reveal the rheological mechanism of tailings fluidization transformation by combining rheological tests and theoretical analysis.The results show that the yield stress increases with decreasing temperature,and when the density of debris flow(ρ)is more than 1.9 g/cm~3,this behavior becomes more pronounced as the density increases.The storage modulus decreases by at least two orders of magnitude at the solid-fluid transition under amplitude test sweep.Storage and loss modulus in the linear viscoelastic range and yield stress have an exponential growth relationship with sediment concentration.In addition,a stress constitutive relation and a new exponential law describing the evolution of yield stress required for solid-liquid transformation were proposed,and the relationship is further strengthened through a comprehensive analysis of existing results,which expands the evaluation application of the rheological characteristics of tailings flow.This paper provides a new insight into the rheological properties of tailing and how they occur through solid-liquid transition under different environments,which is beneficial to geological hazard prevention and the ecological remediation of the mining area.