In low-density steel,κ-carbides primarily precipitate in the form of nanoscale particles within austenite grains.However,their precipitation within ferrite matrix grains has not been comprehensively explored,and the ...In low-density steel,κ-carbides primarily precipitate in the form of nanoscale particles within austenite grains.However,their precipitation within ferrite matrix grains has not been comprehensively explored,and the second-phase evolution mechanism during aging remains unclear.In this study,the crystallographic characteristics and morphological evolution ofκ-carbides in Fe-28Mn-10Al-0.8C(wt%)low-density steel at different aging temperatures and times and the impacts of these changes on the steels’microhardness and properties were comprehensively analyzed.Under different heat treatment conditions,intragranularκ-carbides exhibited various morpho-logical and crystallographic characteristics,such as acicular,spherical,and short rod-like shapes.At the initial stage of aging,acicularκ-carbides primarily precipitated,accompanied by a few spherical carbides.κ-Carbides grew and coarsened with aging time,the spherical carbides were considerably reduced,and rod-like carbides coarsened.Vickers hardness testing demonstrated that the material’s hardness was affected by the volume fraction,morphology,and size ofκ-carbides.Extended aging at higher temperatures led to an increase in carbide size and volume fraction,resulting in a gradual rise in hardness.During deformation,the primary mechanisms for strengthening were dislocation strengthening and second-phase strengthening.Based on these findings,potential strategies for improving material strength are proposed.展开更多
基金supported by the National Key Research and Development Program of China(No.2023YFB3711702).
文摘In low-density steel,κ-carbides primarily precipitate in the form of nanoscale particles within austenite grains.However,their precipitation within ferrite matrix grains has not been comprehensively explored,and the second-phase evolution mechanism during aging remains unclear.In this study,the crystallographic characteristics and morphological evolution ofκ-carbides in Fe-28Mn-10Al-0.8C(wt%)low-density steel at different aging temperatures and times and the impacts of these changes on the steels’microhardness and properties were comprehensively analyzed.Under different heat treatment conditions,intragranularκ-carbides exhibited various morpho-logical and crystallographic characteristics,such as acicular,spherical,and short rod-like shapes.At the initial stage of aging,acicularκ-carbides primarily precipitated,accompanied by a few spherical carbides.κ-Carbides grew and coarsened with aging time,the spherical carbides were considerably reduced,and rod-like carbides coarsened.Vickers hardness testing demonstrated that the material’s hardness was affected by the volume fraction,morphology,and size ofκ-carbides.Extended aging at higher temperatures led to an increase in carbide size and volume fraction,resulting in a gradual rise in hardness.During deformation,the primary mechanisms for strengthening were dislocation strengthening and second-phase strengthening.Based on these findings,potential strategies for improving material strength are proposed.