The influence of solvent and the rate of addition of water on the characteristics of alumina-zirconia powders obtained by sol-gel method were investigated. The Al2O3-ZrO2 powders (1:1 molar ratio) were prepared using ...The influence of solvent and the rate of addition of water on the characteristics of alumina-zirconia powders obtained by sol-gel method were investigated. The Al2O3-ZrO2 powders (1:1 molar ratio) were prepared using aluminum tri-sec-butoxide and zirconium n-propoxide as precursors. Ethanol (EtOH), isopropanol (iPrOH) and isobutanol (iBuOH) were used as solvents. The Al2O3-ZrO2 powders were characterized by nitrogen physisorption (SBET), Fourier transformed infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscopy (SEM). Prepared oxides calcined at 700℃ showed high specific surface area (200 - 240 m2/g). Obtained results suggest that the homogeneity of the mixed oxides is favored by using a water addition rate of 0.06 and 0.10 mL/min with ethanol as solvent.展开更多
Li 2+ x RE x Si 1- x O 3(RE=Pr, Nd, Sm, Gd; x =0～0 15) samples were prepared by the sol gel method. DTA TG, XRD, TEM and A C impedance techniques were used to investigate the structure, sha...Li 2+ x RE x Si 1- x O 3(RE=Pr, Nd, Sm, Gd; x =0～0 15) samples were prepared by the sol gel method. DTA TG, XRD, TEM and A C impedance techniques were used to investigate the structure, shape, and ionic conductivity of these samples. The results show that the range of solid solution formation is in 0< x ≤0 09, in which the conductivity of these samples raises with the increasing amount of RE 2O 3 (RE=Pr, Nd, Sm, Gd) added, and the diameter of the powders is about 100 nm. Compared with the conventional solid state reaction, the sol gel method needs low temperature and presents high ionic conductivity.展开更多
Nanocrystalline rare earth mixed oxides DyFe x Co 1- x O 3- δ were prepared by sol gel method and characterized by X ray diffraction (XRD), thermogravimetric analysis (TG DTA) and scanning elec...Nanocrystalline rare earth mixed oxides DyFe x Co 1- x O 3- δ were prepared by sol gel method and characterized by X ray diffraction (XRD), thermogravimetric analysis (TG DTA) and scanning electron microscope (SEM). The results show that DyFe x Co 1- x O 3- δ has the structure of perovskite type at 800 ℃ for 2 h calcination. The conductivity of the materials at different temperature was measured by four probe instrumentation and two pole method. The results show that the conductivity of mixed oxides DyFe x Co 1- x O 3- δ is higher than those of un mixed oxides DyFeO 3 and DyCoO 3 and the conductivity is the best at x =0.8 in the matter of DyFe x Co 1- x O 3- δ . The conductivity of these materials always increases with the temperature rising and there is an apparent change between 600 and 800 ℃. However, the spinodals are different with different ration of Fe 3+ and Co 3+ . This kind of oxide is a conductive pottery material.展开更多
ZrO2 sizing nozzles with a basic Jormulation were prepared using 45% （by mass, the same hereinafter ） （ Mg, Y） - PSZ aggregate, 55% （ Mg, Y） - PSZ fines and 5% PVA binder. Al2O3 - ZrO2 composite powders （ 3%, ...ZrO2 sizing nozzles with a basic Jormulation were prepared using 45% （by mass, the same hereinafter ） （ Mg, Y） - PSZ aggregate, 55% （ Mg, Y） - PSZ fines and 5% PVA binder. Al2O3 - ZrO2 composite powders （ 3%, 6%, 9% and 12% ） prepared by sol - gel method were added to replace the equal amount of （ Mg, Y） - PSZfines. Effects of Al2O3 - ZrO2 composite powders on physical properties, phase composition and microstructure of the ZrO2 sizing nozzles were studied. The results show that： the performances of the modified sizing nozzles with 3% Al2O3 - ZrO2 composite powder are better than those of the nobles without composite powder used in current production process, and the thermal shock resistance of the ,former nozzles is six times of that of the latter one.展开更多
The growth of crystals of the high T c oxide superconductors has been hampe red by the complexities of the materials and their phase diagrams.The most common crys tal growth technique adopted for these oxides is the ...The growth of crystals of the high T c oxide superconductors has been hampe red by the complexities of the materials and their phase diagrams.The most common crys tal growth technique adopted for these oxides is the “flux”method,where the st arting materials are solved in a melt,which is usually formed by excess CuO and BaO or a KCl/NaCl mixture.The crystals are produced by slow cooling of the heate d solvent.This method,however,suffers from several disadvantages: (1) the crystals are contaminated with the crucible material, (2) the crystals are difficult to remove from the crucible, (3) the crystals contain flux inclusions.展开更多
通过溶胶-凝胶法合成了硅酸锆包裹氧化改性炭黑(Zr Si O4/C)色料,采用XRD、色度仪和TEM等分析手段对色料进行表征。研究了改性C的球磨方式、溶剂种类和成型压力等工艺因素对Zr Si O4合成及Zr Si O4/C色料色度的影响规律。结果表明:着色...通过溶胶-凝胶法合成了硅酸锆包裹氧化改性炭黑(Zr Si O4/C)色料,采用XRD、色度仪和TEM等分析手段对色料进行表征。研究了改性C的球磨方式、溶剂种类和成型压力等工艺因素对Zr Si O4合成及Zr Si O4/C色料色度的影响规律。结果表明:着色剂C粉的形貌对包裹色料的色度影响明显,手磨过筛后的C粉呈颗粒状,分布均匀,制得的色料黑度较高,而经过振动球磨后的C呈絮状,不宜进行包裹;水溶剂会导致异质聚合Si-O-Zr键断裂,形成同质聚合,不利于包裹体Zr Si O4的低温合成,从而影响色料的呈色;过高的成型压力阻碍了Zr Si O4合成过程中的Si F4气相传质,影响了Zr Si O4的正常生长,不利于炭黑包裹和色料的发色。展开更多
文摘The influence of solvent and the rate of addition of water on the characteristics of alumina-zirconia powders obtained by sol-gel method were investigated. The Al2O3-ZrO2 powders (1:1 molar ratio) were prepared using aluminum tri-sec-butoxide and zirconium n-propoxide as precursors. Ethanol (EtOH), isopropanol (iPrOH) and isobutanol (iBuOH) were used as solvents. The Al2O3-ZrO2 powders were characterized by nitrogen physisorption (SBET), Fourier transformed infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscopy (SEM). Prepared oxides calcined at 700℃ showed high specific surface area (200 - 240 m2/g). Obtained results suggest that the homogeneity of the mixed oxides is favored by using a water addition rate of 0.06 and 0.10 mL/min with ethanol as solvent.
文摘Li 2+ x RE x Si 1- x O 3(RE=Pr, Nd, Sm, Gd; x =0～0 15) samples were prepared by the sol gel method. DTA TG, XRD, TEM and A C impedance techniques were used to investigate the structure, shape, and ionic conductivity of these samples. The results show that the range of solid solution formation is in 0< x ≤0 09, in which the conductivity of these samples raises with the increasing amount of RE 2O 3 (RE=Pr, Nd, Sm, Gd) added, and the diameter of the powders is about 100 nm. Compared with the conventional solid state reaction, the sol gel method needs low temperature and presents high ionic conductivity.
文摘Nanocrystalline rare earth mixed oxides DyFe x Co 1- x O 3- δ were prepared by sol gel method and characterized by X ray diffraction (XRD), thermogravimetric analysis (TG DTA) and scanning electron microscope (SEM). The results show that DyFe x Co 1- x O 3- δ has the structure of perovskite type at 800 ℃ for 2 h calcination. The conductivity of the materials at different temperature was measured by four probe instrumentation and two pole method. The results show that the conductivity of mixed oxides DyFe x Co 1- x O 3- δ is higher than those of un mixed oxides DyFeO 3 and DyCoO 3 and the conductivity is the best at x =0.8 in the matter of DyFe x Co 1- x O 3- δ . The conductivity of these materials always increases with the temperature rising and there is an apparent change between 600 and 800 ℃. However, the spinodals are different with different ration of Fe 3+ and Co 3+ . This kind of oxide is a conductive pottery material.
基金financially supported by National Natural Science Foundation of China(Grant No.51372193)Natural Science Basic Research Fund of Shaanxi Province(Grant No.2014JM6224)
文摘ZrO2 sizing nozzles with a basic Jormulation were prepared using 45% （by mass, the same hereinafter ） （ Mg, Y） - PSZ aggregate, 55% （ Mg, Y） - PSZ fines and 5% PVA binder. Al2O3 - ZrO2 composite powders （ 3%, 6%, 9% and 12% ） prepared by sol - gel method were added to replace the equal amount of （ Mg, Y） - PSZfines. Effects of Al2O3 - ZrO2 composite powders on physical properties, phase composition and microstructure of the ZrO2 sizing nozzles were studied. The results show that： the performances of the modified sizing nozzles with 3% Al2O3 - ZrO2 composite powder are better than those of the nobles without composite powder used in current production process, and the thermal shock resistance of the ,former nozzles is six times of that of the latter one.
文摘The growth of crystals of the high T c oxide superconductors has been hampe red by the complexities of the materials and their phase diagrams.The most common crys tal growth technique adopted for these oxides is the “flux”method,where the st arting materials are solved in a melt,which is usually formed by excess CuO and BaO or a KCl/NaCl mixture.The crystals are produced by slow cooling of the heate d solvent.This method,however,suffers from several disadvantages: (1) the crystals are contaminated with the crucible material, (2) the crystals are difficult to remove from the crucible, (3) the crystals contain flux inclusions.
文摘通过溶胶-凝胶法合成了硅酸锆包裹氧化改性炭黑(Zr Si O4/C)色料,采用XRD、色度仪和TEM等分析手段对色料进行表征。研究了改性C的球磨方式、溶剂种类和成型压力等工艺因素对Zr Si O4合成及Zr Si O4/C色料色度的影响规律。结果表明:着色剂C粉的形貌对包裹色料的色度影响明显,手磨过筛后的C粉呈颗粒状,分布均匀,制得的色料黑度较高,而经过振动球磨后的C呈絮状,不宜进行包裹;水溶剂会导致异质聚合Si-O-Zr键断裂,形成同质聚合,不利于包裹体Zr Si O4的低温合成,从而影响色料的呈色;过高的成型压力阻碍了Zr Si O4合成过程中的Si F4气相传质,影响了Zr Si O4的正常生长,不利于炭黑包裹和色料的发色。