Preparation of special silicon steel grade MgO from hydromagnesite

A preparation technology of MgO powder used in special silicon steel from hydromagnesite mineral has been developed. The preparation technology includes the following steps： （1） calcining the hydromagnesite at 700-750°C for 1.5-2 h; （2） hydrating the calcined hydromagnesite to be slurry containing the solid-liquid ratio of 15-20 g？L？1; （3） acquiring Mg（HCO3）2 solution by carbonating the slurry, the carbonation temperature, CO2 pressure, and end point PH value of carbonation are less than 40°C, 0.4-0.6 MPa, and 7 respectively during the carbonation process; （4） preparing precipitated basic magnesium carbonate by thermally decomposing the Mg（HCO3）2 solution at 90-100°C; （5） obtaining the MgO product by calcining the precipitated basic magnesium carbonate at 850-950°C for 30-60 min, and adopting flowing nitrogen during the cooling process. By using this technology, more than 80wt% magnesium in hydromagnesite mineral can be extracted, and high-performance MgO products used in special silicon steel can be ob- tained.

特殊形貌MgO材料的研究

科技的发展、进步对材料的要求越来越高,随之而来的是各种特殊功能的复合材料的问世。作为复合材料,增强改性添加剂的特殊形貌MgO材料也获得了长足的发展。系统介绍了晶须MgO、纳米MgO及其他特殊形貌MgO的用途和制备方法。指出盐湖镁资源的综合利用和可持续发展并兼顾环境保护是今后研究开发的方向。

取向硅钢用特种氧化镁的应用研究

采用XRD、SEM和激光粒度仪等手段,观察并研究了不同特性氧化镁在硅钢表面形成硅酸镁底层形貌特点,并结合热力学和差热-失重分析了MgO-SiO2的反应机理。研究结果表明:粒度小,活性值高的特种氧化镁在高温退火过程中与基体表面氧化物生成的硅酸镁底层,界面中硅酸镁底层嵌入基体较多,表面致密,颗粒细小,有利于形成附着性能优良的硅酸镁底层。