Influence of Negative Bias Voltage on the Mechanical and Tribological Properties of MoS_2/Zr Composite Films 被引量:1
1
作者 宋文龙 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2011年第3期412-416,共5页
MoS2/Zr composite films were deposited on the cemented carbide YT14 (WC+14%TiC+6%Co) by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage ... MoS2/Zr composite films were deposited on the cemented carbide YT14 (WC+14%TiC+6%Co) by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage on the composite film properties,including adhesion strength,micro-hardness,thickness and tribological properties were investigated.The results showed that proper negative bias voltage could significantly improve the mechanical and tribological properties of composite films.The effects of negative bias voltage on film properties were also put forward.The optimal negative bias voltage was -200 V under this experiment conditions.The obtained composite films were dense,the adhesion strength was about 60 N,the thickness was about 2.4 μm,and the micro-hardness was about 9.0 GPa.The friction coefficient and wear rate was 0.12 and 2.1×10-7 cm3/N·m respectively after 60 m sliding operation against hardened steel under a load of 20 N and a sliding speed of 200 rev·min-1. 展开更多
关键词 medium-frequency magnetron sputtering multi-arc ion plating negative bias voltage MoS2/Zr composite films tribological properties
下载PDF
上一页 1 下一页 到第
使用帮助 返回顶部