Flexural behavior of steel reinforced engineered cementitious composite beams

In order to enhance the durability of steel encased concrete beams, a new type of steel reinforced engineered cementitious composite(SRECC) beam composed of steel shapes, steel bars and ECC is proposed. The theoretical analyses of the SRECC beam including crack propagation and stress-strain distributions along the depth of the composite beam in different loading stages are conducted. A theoretical model and simplified design method are proposed to calculate the load carrying capacity. Based on the proposed theoretical model, the relationship between the moment and corresponding curvature is derived. The theoretical results are verified with the finite element analysis. Finally, an extensive parametric study is performed to study the effect of the matrix type, steel shape ratio, reinforced bar ratio, ECC compressive strength and ECC tensile ductility on the mechanical behavior of SRECC beams. The results show that substitution concrete with ECC can effectively improve the bearing capacity and ductility of composite beams. The steel shape and longitudinal reinforcement can enhance the loading carrying capacity, while the ductility decreases with the increase of steel shape ratio. ECC compressive strength has significant effects on both load carrying capacity and ductility, and changing the ultimate strain of ECC results in a very limited variation in the mechanical behavior of SRECC beams.

Structural Behavior of Continuous Prestressed Steel Fiber Reinforced High Strength Concrete Beam

The flexural behaviors of continuous fully and partially prestressed steel fiber reinforced high strength concrete beams are studied by experiment and nonlinear finite element analysis. Three levels of partial prestress ratio （PPR） are considered, and three pairs of two-span continuous beams with box sections varying in size are designed. The major parameters involved in the study include the PPR and the fiber location. It is concluded that the prestressed high strength concrete beam exhibits satisfactory ductility; the influences of steel fiber on the crack behaviors for partially prestressed beams are not as obvious as those for fully prestressed ones; steel fibers can improve the structural stiffness after cracking for fully prestressed high strength concrete beams; the moment redistribution from mid-span to intermediate support in the first stage should be mainly considered in practical design.

Nonlinear Finite Element Analysis of Steel Fiber Reinforced Concrete Deep Beams

By the nonlinear finite element analysis （FEA） method, the mechanical properties of the steel fiber reinforced concrete （SFRC） deep beams were discussed in terms of the crack load and ultimate bearing capacity. In the simulation process, the ANSYS parametric design language （APDL） was used to set up the finite element model; the model of bond stress-slip relationship between steel bar and concrete was established. The nonlinear FEA results and test results demonstrated that the steel fiber can not only significantly improve the cracking load and ultimate bearing capacity of the concrete but also repress the development of the cracks. Meanwhile, good agreement was found between the experimental data and FEA results, if the unit type, the parameter model and the failure criterion are selected reasonably.

Seismic Behaviour of Beam-Column Joints of Precast and Partial Steel Reinforced Concrete

A beam-column joint of precast and partial steel reinforced concrete( PPSRC) is proposed for precast reinforced concrete frames. The PPSRC consists of partial steel and reinforced concrete. The partial steel is located in the core joint region and the connections between concrete members. This paper presents an experimental study of a series of PPSRC specimens. These specimens are tested under low cyclic loading.Experimental results demonstrate that the bearing capacity of the PPSRC specimens is 3 times that of the ordinary reinforced concrete( RC) beam-column joints. The strength and stiffness degradation rates are slower compared with that of the RC beam-column joints. In addition,the strength of the core joint region and the connections is higher than other parts of the PPSRC specimens. Beam failure occurs firstly for the PPSRC specimens,followed by column failure and connections failure. The failure of the core joint region occurs finally.Test results show that the seismic performance of the PPSRC is better than that of the ordinary RC beam-column joints.

Fatigue tests of composite beam by steel fiber reinforced self-stressing concrete in the hogging bending

Through the experiments of 7 T-section composite beams, steel fiber reinforced self-stressing concrete （SFRSC） as the composite beam in the composite layer was studied under the hogging bending. The tests simulated composite layer tensile strain under the hogging bending of inverted loading composite beams, giving the relationship under the different fatigue stress ratios between fatigue cycles and steel bar’s stress range, crack width, stiffness loss and damage, etc., in composite layer. This article established fatigue life equation, and analyzed SFRSC reinforced mechanism to crack width and stiffness loss. The results show that SFRSC as the composite beam concrete has excellent properties of crack resistance and tensile, can reinforce the fatigue crack width and stiffness loss of composite beams, and improve the durability and in normal use of composite beams in the hogging bending zone.

Interfacial Interaction of CFRP Reinforced Steel Beam Structures

Due to the increase of service life,the phenomenon of performance degradation of bridge structures becomes more and more common.It is important to strengthen the bridge structures so as to restore the resistance level and extend the normal service life.Carbon fiber reinforced polymer(CFRP)materials are thus used for the assembly reinforcement of bridges for the advantages of high strength,light weight,corrosion resistance and long-term stability of physical and chemical properties,etc.In view of this,based on the previous theoretical study and the established formula of the interfacial shear stress of CFRP reinforced steel beam and the normal stress of CFRP plate,this paper discusses the sensitive parameters that affect the interfacial interaction of CFRP strengthened beam structures.Through the analysis,the priority design indicators and suggestions are accordingly given for the design of reinforced beam structures.Young’s modulus of CFRP composite and shear modulus of the adhesive have the greatest influence on the interfacial interaction,which should be carefully considered.It is suggested that CFRP material with Ec close to 300 GPa and thickness no less than 3 mm,and adhesive material with Ga less than 5 GPa and 3-mm thickness can be adopted in CFRP reinforced steel beam.The conclusions of this paper can provide guidance for the interfacial damage control of CFRP reinforced steel beam structures.

Behavior of reinforced concrete beams and columns subjected to blast loading

In this study, the blast performance of steel reinforced concrete(RC) beams was experimentally and analytically investigated. The experiment consists of a total of 10 one-half-scale beams subjected to different levels of blast loading using live explosives. The reflected pressure-time histories were recorded and different damage levels and modes were observed. The blast resilience of the damaged beams was quantified by measuring the time-dependent displacements. Experiment results show that the damage in steel reinforced concrete beams with higher explosive mass is enhanced compared with that of the beams with smaller explosive mass at the same scaled distance. Based on the experiment data, an empirical expression is developed via dimensional analysis to correct the relationship between the midspan displacement and scaled distance. Besides, a complex single degree of freedom model(SDOF)incorporating complex features of the material behavior, high strain-rate effect and the column geometry was proposed and validated by test results.

Research on Flexural Behavior of Coral Aggregate Reinforced Concrete Beams

Through the flexural behavior test of coral aggregate reinforced concrete beams(CARCB) and ordinary Portland reinforced concrete beams(OPRCB), and based on the parameters of concrete types, concrete strength grades and reinforcement ratios, the crack development, failure mode, midspan deflection and flexural capacity were studied, the relationships of bending moment-midspan deflection, load-longitudinal tensile reinforcement strain, load-maximum crack width were established, and a calculation model for the flexural capacity of CARCB was suggested. The results showed that with the increase in the reinforcement ratio and concrete strength grade, the crack bending moment(Mcr)and ultimate bending moment(Mu) of CARCB gradually increased. The characteristics of CARCB and OPRCB are basically the same. Furthermore, through increasing the concrete strength grade and reinforcement ratio, Mcr/Mu could be increased to delay the cracking of CARCB. As the load increased, crack width(w) would also increase. At the beginning of the loading, w increased slowly. And then it increased rapidly when the load reached to the ultimate load, which then led to beam failure. Meanwhile, with a comprehensive consideration of the effects of steel corrosion on the loss of steel section and the decrease of steel yield strength, a more reasonable calculation model for the flexural capacity of CARCB was proposed.

Nonlinear behavior of concrete beams with hybrid FRP and stainless steel reinforcements

The full-range behavior of partially bonded, together with partially prestressed concrete beams containing fiber reinforced polymer （FRP） tendons and stainless steel reinforcing bars was simulated using a simplified theoretical model. The model assumes that a section in the beam has a trilinear moment--curvature relationship characterized by three particular points, initial cracking of concrete, yielding of non-prestressed steel, and crushing of concrete or rupturing of prestressing tendons. Predictions from the model were compared with the limited available test data, and a reasonable agreement was obtained. A detailed parametric study of the behavior of the prestressed concrete beams with hybrid FRP and stainless steel reinforcements was conducted. It can be concluded that the deformability of the beam can be enhanced by increasing the ultimate compressive strain of concrete, unhonded length of tendon, percentage of compressive reinforcement and partial prestress ratio, and decreasing the effective prestress in tendons, and increasing in ultimate compressive strain of concrete is the most efficient one. The deformability of the beam is almost directly proportional to the concrete ultimate strain provided the failure mode is concrete crushing, even though the concrete ultimate strain has less influence on the load-carrying capacity.

Seismic performance of steel reinforced ultra high-strength concrete composite frame joints

To investigate the seismic performance of a composite frame comprised of steel reinforced ultra high-strength concrete （SRUHSC） columns and steel reinforced concrete （SRC） beams, six interior frame joint specimens were designed and tested under low cyclically lateral load. The effects of the axial load ratio and volumetric stirrup ratio were studied on the characteristics of the frame joint performance including crack pattern, failure mode, ductility, energy dissipation capacity, strength degradation and rigidity degradation. It was found that all joint specimens behaved in a ductile manner with flexural-shear failure in the joint core region while plastic hinges appeared at the beam ends. The ductility and energy absorption capacity of joints increased as the axial load ratio decreased and the volumetric stirIup ratio increased. The displacement ductility coefficient and equivalent damping coefficient of the joints fell between the corresponding coefficients of the steel reinforced concrete （SRC） frame joint and RC frame joint. The axial load ratio and volumetric stirrup ratio have less influence on the strength degradation and more influence on the stiffness degradation. The stiffness of the joint degrades more significantly for a low volumetric stirrup ratio and high axial load ratio. The characteristics obtained from the SRUHSC composite frame joint specimens with better seismic performance may be a useful reference in future engineering applications.

Fatigue properties of special kind of reinforced concrete composite beams

The special reinforced concrete composite beam consists of a steel fiber reinforced self-stressing concrete composite layer and a reinforced concrete T-beam, and constructional bars are set up at their bonding interface. Fatigue properties of the composite beam under the action of negative moment were experimentally studied. Through inverted loading mode the load-beating state of a composite beam was simulated under the action of negative moment. With the ratios of constructional bars being 0, 0.082% and 0.164% respectively as parameters, the effects of constructional bars on the properties of composite beam, such as fatigue life, crack propagation, rigidity loss as well as damage behavior of bonding interface, were studied. The mechanism of the constructional bars on the fatigue properties of the composite beams and the restriction mechanism of crack widths and rigidity loss were analyzed. The test results show that the constructional bars can enhance the shear resistance of the bonding interface between composite layer and old concrete beam and restrict expanding of steel fiber reinforced self-stressing concrete, which are beneficial to synergistic action of composite layer and old concrete beam, to reducing the stress amplitude of bars and the crack width of composite layer, and to increasing the durability and fatigue life of the composite beam.

Durability of Reinforced Concrete Beams under Simultaneous Flexural Load in Corrosive Environment

The deterioration of concrete over time is the result of various mechanical, physical, chemical and biological processes, with the corrosion of reinforcement being the most serious problem of durability of reinforced concrete structures. Over the last 50 years, a tremendous effort has been spent by the international scientific community with laboratory research and experimental field studies in order to increase the resistance of concrete over corrosion. This paper presents an experimental study of the corrosion behaviour of reinforced concrete beams with simultaneous sustained flexural loading. For this purpose, 40 reinforced concrete beams of 5 different compositions were constructed and exposed in simulated harmful environmental conditions in 3 different stress ratios for a total period of 42 months. Their behavior against corrosion was determined via regular measurements of the electrical resistance of concrete (according to ASTM G57) and the corrosion potential of the steel-reinforced bars with the use of copper sulphate (CSE) as reference electrode (according to ASTM C876). A theoretical calculation of the corrosion rate was conducted based on the electrochemical measurements of the beams. The results indicate that the corrosion potential of steel decreased in time and more rapidly after the initiation of the corrosion process;the electrical resistance firstly increased, remained stable for a short period and then decreased with the corrosion development, as expected. An inversely proportional relationship of the water/cement ratio of a composition with its corrosion behaviour as well as an analogous relationship between the cement content of a composition and its corrosion behaviour was observed. Also, the corrosion rate of steel is increased gradually with increasing load.

Long-Term Loading Test of Reinforced Glulam Beam

Due to creep characteristics of wood,long-term loading can cause a significant stress loss of steel bars in rein-forced glulam beams and high long-term deflection of the beam midspan.In this study,15 glulam beams were subjected to a 90-day long-term loading test,and the effects of long-term loading value,reinforcement ratio and prestress level on the stress of steel bars,midspan long-term deflection,and other parameters were compared and analyzed.The main conclusions drawn from this study were that the long-term deflection of the reinforced glulam beams accounted for 22.5%,20.6%,and 18.2%of the total deflection respectively when the loading value was 20%,30%,and 40%of the estimated ultimate load under the long-term loading.The higher the loading level was,the smaller the proportion of the long-term deflection in the total deflection was.Compared with ordinary glulam beams,the long-term deflection of the reinforced glulam beam was even smaller.Under the condition of the constant loading level,the total stress value of the steel bars decreased by 17.5%,13.6%,and 9.1%,and the proportion of the long-term deflection of the beam midspan in the total deflection was 26.9%,24.2%,and 20.6%respectively when the reinforcement ratio was 2.05%,2.68%,and 3.39%.With the increase of the reinfor-cement ratio,the stress loss of the steel bars decreased,and the proportion of the long-term deflection decreased as well.When other conditions remained constant and the prestress level of the steel bars was 0 MPa,30 MPa,and 60 MPa,the total stress value of the steel bars decreased by 9.1%,9.4%,and 10.2%,respectively,and the propor-tion of the long-term deflection in the total deflection was 20.6%,26.1%,and 64.9%,respectively.With the increase of the prestress value,the stress loss of the steel bars increased,and the proportion of the long-term deflection increased as well.

Experimental Study on Force Behavior of Steel Rein forced Concrete Transfer Beam Structure with Basement of Large Space

Based on comparative test of two transfer story models, in one of which the transfer beam and basement column is constructed of steel reinforced concrete, and the other is constructed of ordinary reinforced concrete, its force behavior, ductility and failure mechanism under vertical and horizontal loads are studied. The results show that loading bearing and seismic behavior of transfer story structure with steel reinforced concrete beam and basement column is good. The relative design suggestion is put forward.

Experimental study and analysis on fatigue stiffness of RC beams strengthened with CFRP and steel plate

The objective of this work is to investigate the fatigue behavior of reinforced concrete(RC) beams strengthened with externally bonded carbon fiber reinforced polymer(CFRP) and steel plate. An experimental investigation and theoretical analysis were made on the law of deflection development and stiffness degradation, as well as the influence of fatigue load ranges. Test results indicate that the law of three-stage change under fatigue loading is followed by both midspan deflection and permanent deflection, which also have positive correlation with fatigue load amplitude. Fatigue stiffness of composite strengthened beams degrades gradually with the increasing of number of cycles. Based on the experimental results, a theoretical model by effective moment of inertia method is developed for calculating the sectional stiffness of such composite strengthened beams under fatigue loading, and the calculated results are in good agreement with the experimental results.

Experimental and Numerical Analysis of High-Strength Concrete Beams Including Steel Fibers and Large-Particle Recycled Coarse Aggregates

In order to study the performances of high-strength concrete beams including steel fibers and large-particle recycled aggregates,four different beams have been designed,tested experimentally and simulated numerically.As varying parameters,the replacement rates of recycled coarse aggregates and CFRP(carbon fiber reinforced polymer)sheets have been considered.The failure mode of these beams,related load deflection curves,stirrup strain and shear capacity have been determined through monotonic loading tests.The simulations have been conducted using the ABAQUS finite element software.The results show that the shear failure mode of recycled concrete beams is similar to that of ordinary concrete beams.The shear carrying capacity of high-strength concrete beams including steel fibers and large-particle recycled coarse aggregates grows with an increase in the replacement rate of recycled coarse aggregates.Reinforcement with CFRP sheets can significantly improve the beam’s shear carrying capacity and overall resistance to deformation.

预制装配式型钢混凝土梁抗剪承载力的智能模型研究

通过建立计算预制装配式型钢混凝土(PSRC)梁抗剪承载力的智能模型,在一定程度上提高了计算精度与适用性。基于BP人工神经网络算法,通过对影响PSRC梁抗剪承载力的相关参数进行梳理,选取14个主要影响参数作为输入层,以试算法确定隐含层节点数为5,初步构建了3层结构人工神经网络系统;以收集的76组试验数据作为学习样本,对构建的神经网络系统进行训练,建立了对PSRC梁及SRC梁抗剪承载力计算的N14-5-1智能模型。使用智能模型对6个PSRC梁构件及6个SRC梁构件进行抗剪承载力计算,并通过与规范公式计算结果、试验结果的对比分析,证明了智能模型具有良好的计算精度及较好的泛化能力,具有一定的工程参考意义。运用Garson算法对输入参数进行敏感性分析,结果表明箍筋间距、型钢屈服强度、箍筋屈服强度、型钢腹板含钢率对抗剪承载力影响较大。随着研究试验的开展,在收集更多具有代表性的试验数据以扩充学习样本后,可对智能模型进一步优化。

端钩型钢纤维混凝土简支梁受弯承载力试验

为改善普通钢筋混凝土梁自重大、易开裂、承载力低等缺点,在混凝土中常加入钢纤维,端钩型钢纤维,作为常见的一种高性能钢纤维得到广泛关注,中外学者针对端钩型钢纤维混凝土的基本力学性能开展了较多研究,而对端钩型钢纤维混凝土受弯构件的正截面受力性能有待深入研究。为研究端钩型钢纤维混凝土简支梁受弯性能,制作4根端钩型钢纤维混凝土梁及1根普通混凝土梁,对其进行受弯性能试验,根据试验得到的破坏形态、承载力、荷载-挠度曲线、荷载-应变曲线,分析端钩型钢纤维体积掺量对试件受弯承载力及破坏形态的影响。结果表明:端钩型钢纤维混凝土简支梁与一般混凝土简支梁受弯过程类似,均经历了弹性、开裂、带裂缝工作、破坏4个阶段;端钩型钢纤维混凝土简支梁与一般混凝土简支梁受弯过程均基本符合“平截面假定”;端钩型钢纤维限制了裂缝的产生和发展,使得纤维混凝土梁变形能力增强;与一般混凝土梁相比,端钩型钢纤维混凝土梁抗裂性及极限承载力得到提高,且构件承载力与钢纤维体积掺量基本呈现正相关;基于试验数据,对现行规范中开裂弯矩及极限承载力计算公式进行优化,开裂弯矩方面考虑对截面抵抗矩塑性影响系数进行修正,极限承载力方面引入纤维混凝土正截面承载力影响系数ζ,经修正计算值可较好吻合试验值。

配筋PVA-钢混杂纤维增强水泥基复合材料梁柱边节点抗震性能试验研究

改善工程材料韧性和耐久性,提高框架梁柱节点抵抗变形和破坏的能力,是提高框架结构抗震韧性的有效途径之一。采用PVA-钢混杂纤维增强水泥基复合材料代替普通混凝土应用到梁柱边节点,考虑轴压比和加密区体积配箍率的影响,设计6个配筋PVA-钢混杂纤维增强水泥基复合材料、1个配筋单掺PVA纤维增强水泥基复合材料和1个钢筋混凝土梁柱边节点试件进行拟静力试验,分析其破坏形态、滞回曲线、骨架曲线、延性、耗能能力、钢筋应变和梁端塑性铰区转角,探讨混杂纤维的加入对梁柱边节点抗震性能的影响。结果表明:与钢筋混凝土节点和单掺PVA纤维增强水泥基复合材料节点相比,PVA-钢混杂纤维增强水泥基复合材料节点的承载力高、变形能力大、延性好、耗能能力强,抗震性能显著提升。当试验轴压比从0.12增加到0.24,梁端塑性铰区产生一定的外移,塑性性能发挥更充分,同时试件的变形能力、延性、耗能能力增加。在加密区体积配箍率减小的情况下,试件仍表现出良好的抗震性能。

CFRP-OFBG板加固损伤钢梁抗弯疲劳试验及其寿命预测研究

为研究采用碳纤维增强复合材料(CFRP)加固后钢梁的疲劳性能,采用自主研发的具有自监测性能的智能碳纤维-光纤光栅板(CFRP-OFBG板)加固受损钢梁,在完成常幅荷载四点弯曲疲劳试验的基础上,研究不同应力幅作用下CFRP-OFBG板加固钢梁的疲劳性能。借助有限元方法,建立“三维实体”有限元模型,结合J积分计算方法求解得到加固钢梁裂纹尖端的应力强度因子,基于线弹性断裂力学理论建立疲劳裂纹扩展模型,对CFRP-OFBG板加固钢梁的疲劳裂纹扩展寿命进行预测。研究表明:CFRP-OFBG板的加固作用可有效提高受损钢梁的疲劳寿命,延缓裂纹扩展速率,改善裂纹尖端的受力状态,降低裂纹尖端的应力强度因子;在循环荷载作用下,CFRP-OFBG板加固试件的疲劳寿命均随着应力幅的增大呈现递减趋势。将试验结果与预测结果相比较,发现加固试件疲劳寿命预测值比试验值略高,分析认为,这主要是因为在有限元模拟时没有考虑到试验中CFRP-OFBG板的局部剥离。