Effect of Rolling Process on Comprehensive Properties of Corrosion Resistant Steel for Bottom Plate of Cargo Oil Tanks

A new kind of corrosion resistant steelfor cargo oiltanks（COT）was developed.The influences of finalrolling temperature,cooling rate,and finalcooling temperature on microstructure were investigated.The proper rolling process parameters were obtained through multi-pass thermalsimulation test.The finalrolling temperature is about 820 ℃,the finalcooling temperature is about 600 ℃,and the cooling rate should be controlled between 10 ℃/s and 20 ℃/s.Based on the above analysis of the results,three groups of rolling samples by thermo mechanicalcontrolprocess are prepared.The tensile strength,yield strength,and toughness of the corrosion resistant steelare measured,which meet the requirements of DH36 steel,it can instruct the actualrolling production.The corrosion behaviour is also researched by weight loss and electrochemicalimpedance spectroscopic method,and it is found that the steelhas good corrosion resistance performance,the best one is No.3 steel,the corrosion rate of which is about 1/4 of the accepted criterion.

Evolution of Through-Thickness Texture in Ultra Purified 17%Cr Ferritic Stainless Steels

Texture inhomogeneity usually takes place in ferritic stainless steels due to the lack of phase transformation and recrystallization during hot strip rolling,which can deteriorate the formability of final sheets.In order to work out the way of weakening texture inhomogeneity,conventional hot rolling and warm rolling processes have been carried out with an ultra purified ferritic stainless steel.The results showed that the evolution of through-thickness texture is closely dependent on rolling process,especially for the texture in the center layer.For both conventional and warm rolling processes,shear texture components were formed in the surface layers after hot rolling and annealing;sharp α-fiber and weakγ-fiber with the major component at{111}〈110〉 were developed in both cold rolled sheet surfaces,leading to the formation of inhomogeneousγ-fiber dominated by{111}〈112〉after recrystallization annealing.In the center layer of conventional rolled and annealed bands,strongα-fiber and weakγ-fiber textures were formed;the cold rolled textures were comprised of sharpα-fiber and weakγ-fiber with the major component at{111}〈110〉,and inhomogeneousγ-fiber dominated by{111}〈112〉 was formed after recrystallization annealing.By contrast,in the centre layer of warm rolled bands,the texture was comprised of weakα-fiber and sharpγ-fiber,andγ-fiber became the only component after annealing.The cold rolled texture displayed a sharpγ-fiber with the major component at{111}〈112〉and the intensity ofγ-fiber close to that ofα-fiber,resulting in the formation of a nearly homogeneousγ-fiber recrystallization texture in the center layer of the final sheet.