This article reports a new generation of Q460 multi-functional construction structural steel,which has high strength(yield strength larger than 460 MPa),excellent toughness(higher than 110 J/cm^(2) at-60 ℃),lower yie...This article reports a new generation of Q460 multi-functional construction structural steel,which has high strength(yield strength larger than 460 MPa),excellent toughness(higher than 110 J/cm^(2) at-60 ℃),lower yield ratio(lower than 0.8),good fire resistance(yield strength at 600 ℃ larger than two-thirds of its room-temperature yield strength)and better corrosion resistance.The eff ects of finish cooling temperature(FCT)on the microstructure and properties were studied by scanning electron microscopy(SEM),transmission electron microscopy(TEM),emission electron probe micro-analysis(EPMA),electron backscattering diff raction(EBSD),tensile tester,impact tester,periodic immersion cycle acceleration test and electrochemical experiment.The results show that the strength and toughness are simultaneously improved by decreasing the FCT due to more lath-like bainite with large number of dislocations,refined martensite/austenite(M/A)with higher carbon concentration and increased high angle boundaries.In addition,the fire resistance of the newly developed Q460 steel is obviously better than the conventional one,which is mainly due to non-recrystallized lath-like bainite with high dislocation density at elevated temperature.The corrosion resistance of the new Q460 steel is also improved due to the addition of Cu and Cr.展开更多
基金financially supported by the Key Research and Development Program of Hebei Province of China(Grant No.18211019D)the"333 Talent Project"of Hebei(Grant No.A201803007)the Technical Development Program between HBIS Company Limited and NEU(Contract No.2019040200044)。
文摘This article reports a new generation of Q460 multi-functional construction structural steel,which has high strength(yield strength larger than 460 MPa),excellent toughness(higher than 110 J/cm^(2) at-60 ℃),lower yield ratio(lower than 0.8),good fire resistance(yield strength at 600 ℃ larger than two-thirds of its room-temperature yield strength)and better corrosion resistance.The eff ects of finish cooling temperature(FCT)on the microstructure and properties were studied by scanning electron microscopy(SEM),transmission electron microscopy(TEM),emission electron probe micro-analysis(EPMA),electron backscattering diff raction(EBSD),tensile tester,impact tester,periodic immersion cycle acceleration test and electrochemical experiment.The results show that the strength and toughness are simultaneously improved by decreasing the FCT due to more lath-like bainite with large number of dislocations,refined martensite/austenite(M/A)with higher carbon concentration and increased high angle boundaries.In addition,the fire resistance of the newly developed Q460 steel is obviously better than the conventional one,which is mainly due to non-recrystallized lath-like bainite with high dislocation density at elevated temperature.The corrosion resistance of the new Q460 steel is also improved due to the addition of Cu and Cr.