Influence of Carbides and Strain-induced Martensite on Wear Resistance of Austenitic Medium Manganese Steels

The abrasive wear behaviour of austenitic medium manganese steels was studied under weak corrosion-abrasive wear simulating the liner plate in wet metallic ore bail mill under non-severe impact-loading working condition. Results show that the work-hardening mechanism and the wear resistance of high carbon austenitic medium manganese steels differ from those of medium carbon austenitic medium manganese steel. Under non-severe impact and weak corrosion-abrasive wear,the wear resistances of high carbon and medium carbon austenitic medium manganese steels are 50-90% and 20-40% higher than that of Hadfield steel respectively.

RESIDUAL AUSTENITE AND STRAIN-INDUCED MARTENSITE IN LASER HARDENING LAYER ON GRAY IRON

The distribution of residual austenite in the laser hardening laver on the gray cast iron and the change in the amount of residual austenite during sliding wearing have been investigated by X-ray diffractometer.The thin foils of the hardening layer worn down have been observed by electron microscopy.It was revealed that two types of martensite are strain-induced by slid- ing wearing under load of 1.72 MPa on the hardening layer of residual austenite.The strain induced martensite is profitable to improve the sliding wearing resistance.

Predicting the Volume Fraction of Martensite in Welded Mild Steel Joint Reinforced with Titanium Alloy Powder

Welded mild steel is used in different applications in engineering. To strengthen the joint, the weld can be reinforced by adding titanium alloy powder to the joint. This results in the formation of incomplete martensite in a welded joint. The incomplete martensite affects mechanical properties. Therefore, this study aims to predict the volume fraction of martensite in reinforced butt welded joints to understand complex phenomena during microstructure formation. To do so, a combination of the finite element method to predict temperature history, and the Koistinen and Marburger equation, were used to predict the volume fraction of martensite. The martensite start temperature was calculated using chemical elements obtained from the dilution-based mixture rule. The curve shape of martensite evolution was observed to be relatively linear due to the small quantity of martensite volume fraction. The simulated result correlated with experimental work documented in the literature. The model can be used in other powder addition techniques where the martensite can be observed in the final microstructure.

Pre-existing orthorhombic embryos-induced hexagonal-orthorhombic martensitic transformation in MnNiSi_(1-x)(CoNiGe)_x alloy

The thermal-elastic martensitic transformation from high-temperature Ni_(2)In-type hexagonal structure to low-temperature TiNiSi-type orthorhombic structure has been widely studied in MnMX(M=Ni or Co,and X=Ge or Si)alloys.However,the answer to how the orthorhombic martensite nucleates and grows within the hexagonal parent is still unclear.In this work,the hexagonal-orthorhombic martensitic transformation in a Co and Ge co-substituted MnNiSi is investigated.One can find some orthorhombic laths embedded in the hexagonal parent at a temperature above the martensitic transformation start temperature(M_(s)).With the the sample cooing to M_(s),the laths turn broader,indicating that the martensitic transformation starts from these pre-existing orthorhombic laths.Microstructure observation suggests that these pre-existing orthorhombic laths do not originate from the hexagonal-orthorhombic martensitic transformation because of the difference between atomic occupations of doping elements in the hexagonal parent and those in the preexisting orthorhombic laths.The phenomenological crystallographic theory and experimental investigations prove that the pre-existing orthorhombic lath and generated orthorhombic martensite have the same crystallography relationship to the hexagonal parent.Therefore,the orthorhombic martensite can take these pre-existing laths as embryos and grow up.This work implies that the martensitic transformation in MnNiSi_(1-x)(CoNiGe)_(x) alloy is initiated by orthorhombic embryos.

Microstructure and martensitic transformation in quaternary NiTiHfV alloy

The effect of age hardening on the microstructure,martensitic transformation behavior,and shape memory properties of the(Ni_(50)Ti_(30)Hf_(20))_(95)V_(5)alloy was investigated by scanning electron microscopy,transmission electron microscopy,X-ray diffraction,differential scanning calorimetry,microhardness,and bending tests.The results demonstrate a significant influence of V addition on the microstructure of the alloy.V addition leads to the formation of a(Ni,V)_(2)(Ti,Hf)-type Laves phase,which coexists with B19'martensite at room temperature.Aging at 550℃results in precipitation hardening due to the formation of nano-scale orthorhombic H-phase,with the peak hardness observed after 3 h of aging.The alloy at peak hardness state exhibits higher transformation strain and lower unrecovered strain compared to the solution-treated sample.The aged sample achieves a maximum transformation strain of 1.56%under 500 MPa.

Description of martensitic transformation kinetics in Fe-C-X(X = Ni,Cr,Mn,Si) system by a modified model

Controlling the content of athermal martensite and retained austenite is important to improving the mechanical properties of high-strength steels,but a mechanism for the accurate description of martensitic transformation during the cooling process must be addressed.At present,frequently used semi-empirical kinetics models suffer from huge errors at the beginning of transformation,and most of them fail to exhibit the sigmoidal shape characteristic of transformation curves.To describe the martensitic transformation process accurately,based on the Magee model,we introduced the changes in the nucleation activation energy of martensite with temperature,which led to the varying nucleation rates of this model during martensitic transformation.According to the calculation results,the relative error of the modified model for the martensitic transformation kinetics curves of Fe-C-X(X = Ni,Cr,Mn,Si) alloys reached 9.5% compared with those measured via the thermal expansion method.The relative error was approximately reduced by two-thirds compared with that of the Magee model.The incorporation of nucleation activation energy into the kinetics model contributes to the improvement of its precision.

Unveiling the cellular microstructure-property relations in martensitic stainless steel via laser powder bed fusion

Laser powder bed fusion(LPBF)is a widely recognized additive manufacturing technology that can fabricate complex components rapidly through layer-by-layer formation.However,there is a paucity of research on the effect of laser scanning speed on the cellular microstructure and mechanical properties of martensitic stainless steel.This study systematically investigated the influence of laser scanning speed on the cellular microstructure and mechanical properties of a developed Fe11Cr8Ni5Co3Mo martensitic stainless steel produced by LPBF.The results show that increasing the laser scanning speed from 400 to 1000 mm/s does not lead to a noticeable change in the phase fraction,but it reduces the average size of the cellular microstructure from 0.60 to 0.35μm.The scanning speeds of 400 and 1000 mm/s both had adverse effects on performances of sample,resulting in inadequate fusion and keyhole defects respectively.The optimal scanning speed for fabricating samples was determined to be 800 mm/s,which obtained the highest room temperature tensile strength and elongation,with the ultimate tensile strength measured at(1088.3±2.0)MPa and the elongation of(16.76±0.10)%.Furthermore,the mechanism of the evolution of surface morphology,defects,and energy input were clarified,and the relationship between cellular microstructure size and mechanical properties was also established.

Effect of strain-induced martensitic phase transformation on the formability of nitrogen-alloyed metastable austenitic stainless steels

Strain-induced martensitic phase transformation and its influence on the forrnability of newly developed nitrogen-alloyed metastable austenitic stainless steels were systematically investigated. Yield strength for the as- received steels bearing low nickel content was around 300 MPa and their elongation ratios varied from 55.2% to 61.7%. Erichsen numbers of these samples differed from 13.82 to 14.57 mm. Although its Cu content was lower than that of other samples, steel D2 exhibited better plasticity and formability, which was attributed to ~/--,c~＇ martensitic phase transformation. EBSD, XRD, and magnetism tests showed that increases in deformation ratio gradually increased the α＇ martensite phase of a sample ,thereby contributing to its strain and inducing the optimal transformation-induced plasticity effect. An Meeo/5o temperature of around 20 ℃, which is close to the deformation temperature,provided the austenite with adequate stability and gradually transformed it into martensite, thereby endowing lean ASS with better formability.

Grain boundary engineering for enhancing intergranular damage resistance of ferritic/martensitic steel P92

Ferritic/martensitic(F/M)steel is widely used as a structural material in thermal and nuclear power plants.However,it is susceptible to intergranular damage,which is a critical issue,under service conditions.In this study,to improve the resistance to intergranular damage of F/M steel,a thermomechanical process(TMP)was employed to achieve a grain boundary engineering(GBE)microstructure in F/M steel P92.The TMP,including cold-rolling thickness reduction of 6%,9%,and 12%,followed by austenitization at 1323 K for 40 min and tempering at 1053 K for 45 min,was applied to the as-received(AR)P92 steel.The prior austenite grain(PAG)size,prior austenite grain boundary character distribution(GBCD),and connectivity of prior austenite grain boundaries(PAGBs)were investigated.Compared to the AR specimen,the PAG size did not change significantly.The fraction of coincident site lattice boundaries(CSLBs,3≤Σ≤29)and Σ3^(n) boundaries along PAGBs decreased with increasing reduction ratio because the recrystallization fraction increased with increasing reduction ratio.The PAGB connectivity of the 6%deformed specimen slightly deteriorated compared with that of the AR specimen.Moreover,potentiodynamic polarization studies revealed that the intergranular damage resistance of the studied steel could be improved by increasing the fraction of CSLBs along the PAGBs,indicating that the TMP,which involves low deformation,could enhance the intergranular damage resistance.

Reverse Transformation Behavior of Martensite Formed during Cooling Proce under Constant Stress in TiNi Alloys

The reverse transformation temperature and recovery strain ratio of the martensite formed during the cooling process under a constant stress in TiNi shape memory alloy wires are studied in this paper. Results show that a higher level of the applied constant stress during the cooling process will induce martensite with a higher reverse martensitic transformation start temperature As and a smaller recovery strain ratio. Similarly, a prestrain at the room temperature elevates the As temperature and decreases the recovery strain ratio. However, the As temperature and the recovery strain ratio of the martensite formed during the cooling process under a constant stress are lower than those of the martensite formed by prestrain at the room temperature.

Antiphase boundary-like structure in α′′ martensite of TC21 titanium alloy

The morphology and formation mechanism of the substructure of martensite in TC21 alloy was investigated by XRD and TEM. The results showed that the martensitic transformation from β to α＂ occurs upon quenching after solution treatment between 960-1000 ℃. The antiphase boundary （APB）-like structure was observed clearly in the α＂ martensite plates. The APB-like contrasts exist along the （001） and （020） planes of α＂ martensite. This APB-like structure of α＂ martensite was identified as a kind of stacking fault with an APB-like morphology induced by martensitic transformation and not by order/disorder transition. During martensitic transformation, martensitic domains nucleate and grow, eventually encounter each other, resulting in the formation of the APBdike contrast.

Bar martensite性能与强化途径

按其组织形态马氏体(martensite)组织可以分为条状马氏体(bar martensite)、片状马氏体和蝶状马氏体等。其中条状马氏体又再分为扁条状板条马氏体和薄板状板条马氏体。Wc∠0.2%的钢淬火处理后形成以条状马氏体为主的马氏体混合组织。条状马氏体组织具有强韧结合的综合机械性能。强化工艺为淬火后低温回火。

Precipitation behavior and martensite lath coarsening during tempering of T/P92 ferritic heat-resistant steel

Tempering is an important process for T/P92 ferritic heat-resistant steel from the viewpoint of microstructure control, as it facili- tates the formation of final tempered martensite under serving conditions. In this study, we have gained deeper insights on the mechanism underlying the microstructural evolution during tempering treatment, including the precipitation of carbides and the coarsening of martensite laths, as systematically analyzed by optical microscopy, transmission electron microscopy, and high-resolution transmission electron mi- croscopy. The chemical composition of the precipitates was analyzed using energy dispersive X-ray spectroscopy. Results indicate the for- mation of M3C （cementite） precipitates under normalized conditions. However, they tend to dissolve within a short time of tempering, owing to their low thermal stability. This phenomenon was substantiated by X-ray diffraction analysis. Besides, we could observe the precipitation of fine carbonitrides （MX） along the dislocations. The mechanism of carbon diffusion controlled growth of M23C6 can be expressed by the Zener＇s equation. The movement of Y-junctions was determined to be the fundamental mechanism underlying the martensite lath coarsening process. Vickers hardness was estimated to determine their mechanical properties. Based on the comprehensive analysis of both the micro- structural evolution and hardness variation, the process of tempering can be separated into three steps.

Interface Migration between Martensite and Austenite during Quenching and Partitioning (Q&P) Process

An Fe-0.2C-1.5Si-1.67Mn steel was subjected to quenching and partitioning （Q＆P） process, and the interface migration between martensite and austenite at an elevated partitioning temperature was observed. The interface migration is excluded in constrained paraequilibrium （CPE） model. Based on ＂endpoint＂ predicted by CPE model the thermodynamic condition of interface migration is analyzed, that is, the difference in the chemical potential of iron in both ferrite （martenisite） and austenite produces the driving force of the iron atoms to migrate from one phase to the other phase. In addition, the interface migration can change the austenite fraction; as a result, the austenite fraction at partitioning temperature may be higher than that at quenching temperature through the interface migration, but this phenomenon cannot be explained by CPE model.

Apparent Morphologies and Nature of Packet Martensite in High Carbon Steels

The apparent morphologies of packet martensite in eight high carbon steels were researched by using optical microscope, scanning electron microscope, and transmission electron microscope. It was found that the apparent morphologies, substructures, and habit plane of packet martensite in high carbon steels are entirely different from that in low carbon steels; the substructures of packet martensite in high carbon steels possess fully twinned structure, while the substructures of individual coarse martensite plates in these steels bear both fully and partially twinned structures. The formation reason for apparent morphologies, substructures and two habit planes （i. e, { 111 }, and { 225}r） of high carbon martensite were discussed in detail.

STABILIZATION OF MARTENSITE IN Cu-Zn-Al ALLOY AND ITS REVERSE SHAPE MEMORY EFFECT

ＩＮＴＲＯＤＵＣＴＩＯＮＴｈｅｓｔａｂｉｌｉｚａｔｉｏｎｏｆｍａｒｔｅｎｓｉｔｅｒｅｆｅｒｓｔｏｔｈｅｐｈｅｎｏｍｅｎｏｎｔｈａｔｔｈｅｒｅｖｅｒｓｅｔｒａｎｓｆｏｒｍａｔｉｏｎｓｔａｒｔａｎｄｆｉｎｉｓｈｔｅｍｐｅｒａｔｕｒｅｓ（ＡｓａｎｄＡｆ）ｉ...

EFFECT OF COPPER AND BORON CONTENT ON STRAIN-INDUCED Nb(C,N) PRECIPITATION IN ULCB STEELS AT HOT DEFORMATION TEMPERATURE

The stress relaxation curves of Ultra-Low Carbon Bainitic(ULCB) steels with different Cu and B contents were measured by using Gleeble-1500 dynamic thermal-mechanical simulator. The results show that Cu and B added can accelerate the strain-induced precipitation reaction, and the effect of Cu and B is even more obvious with Cu and B combined addition or Cu content increased. The TEM analysis of precipitate engendered at the temperature of 850℃ C indicate that Nb(C,N) precipitate nucleates dominantly on the dislocation line, and grows with holding time extended while the precipitate particle size increases from 5 nm to 17 nm.

Role of thermal martensite in shape memory effect of CoAl and CoNi alloys

To address the role of the HCP martensite in CoAl and CoNi shape memory alloys, the relationship between the shape memory effect （SME） and the content of the thermal and stress-induced HCP martensite was investigated in the solution-treated CoAl and CoNi alloys. In-situ optical observations were employed to investigate the contents of thermal HCP martensite before and after deep cooling and its influence on the stress-induced HCP martensite transformation and SME. The results show that the SME in both the CoAl and the CoNi alloys results from the stress-induced HCP martensite. The role of the thermal HCP martensite in both of them is the strengthening of the matrix. The much higher yield strength in the solution-treated CoAl alloy due to solution strengthening of Al is responsible for its better SME compared with the CoNi alloy.

ORDER STATE AND STABILITY OF MARTENSITE IN AN AIR-QUENCHED Cu-Zn-Al ALLOY

ＯＲＤＥＲＳＴＡＴＥＡＮＤＳＴＡＢＩＬＩＴＹＯＦＭＡＲＴＥＮＳＩＴＥＩＮＡＮＡＩＲ－ＱＵＥＮＣＨＥＤＣｕ－Ｚｎ－ＡｌＡＬＬＯＹ￥ＷａｎｇＭｉｎｇｐｕ；ＪｉｎＺｈａｎｐｅｎｇ；ＹｉｎＺｈｉｍｉｎ；ＸｕＧｅｎｙｉｎ（ＤｅｐａｒｔｍｅｎｔｏｆＭａｔｅｒｉａ...

Ultra-high cycle fatigue behavior of high strength steel with carbide-free bainite/martensite complex microstructure

The ultra-high cycle fatigue behavior of a novel high strength steel with carbide-free bainite/martensite （CFB/M） complex microstructure was studied. The ultra-high cycle fatigue properties were measured by ultrasonic fatigue testing equipment at a frequency of 20 kHz. It is found that there is no horizontal part in the S-N curve and fatigue fracture occurs when the life of specimens exceeds 10^7 cycles. In addition, the origination of fatigue cracks tends to transfer from the surface to interior of specimens as the fatigue cycle exceeds 10^7, and the fatigue crack originations of many specimens are not induced by inclusions, but by some kind of ＂soft structure＂. It is shown that the studied high strength steel performs good ultra-high cycle fatigue properties. The ultra-high fatigue mechanism was discussed and it is suggested that specific CFB/M complex microstructure of the studied steel contributes to its superior properties.