Phase Transformation Strengthening of Hot Extruded Inconel 625 under High-temperature Load Environment

Microstructure evolution and properties of hot-extruded Inconel 625 alloy were investigated at different creep temperatures, aging time and strain rates. The experimental results indicate that the Inconel 625 alloy exhibits an excellent creep resistance at 700 ℃ and below. When the creep temperature rises to 750 ℃, the creep resistance falls drastically due to the failure of phase transformation strengthening and the precipitation of a large amount of δ phase and σ phase at the grain boundary. The special temperature-sensitive characteristics of Inconel 625 alloy play a very important role in its fracture. When the strain rate is 8.33×10^-3s^-1, the strength of the specimen is higher than that of other parameters attributed to the effect of phase transformation strengthening. With the increase of Ni3(Al, Ti), the phase transformation strengthening inhibits thickening of the stacking faults into twins and improves the overall mechanical properties of the alloy. With the increase of the aging time, the granular Cr-rich M23C6 carbides continue to precipitate at the grain boundary, which hinders the movement of the dislocations and obviously increases the strength of the samples. Especially, the yield strength increases several times.

Effect of secondary aging on microstructure and properties of cast Al-Cu-Mg alloy

To obtain better comprehensive properties of cast Al-Cu-Mg alloys,the secondary aging(T6I6)process(including initial aging,interrupted aging and re-aging stages)was optimized by an orthogonal method.The microstructures of the optimized Al-Cu-Mg alloy were observed by means of scanning electron microscopy and transmission electron microscopy,and the properties were investigated by hardness measurements,tensile tests,exfoliation corrosion tests,and intergranular corrosion tests.Results show that the S phase andθ’phase simultaneously exist in the T6I6 treated alloy.Appropriately increasing the temperature of the interrupted aging in the T6I6 process can improve the mechanical properties and corrosion resistance of Al-Cu-Mg alloy.The optimal comprehensive properties(tensile strength of 443.6 MPa,hardness of 161.6 HV)of the alloy are obtained by initial aging at 180℃for 2 h,interrupted aging at 90℃for 30 min,and re-aging at 170℃for 4 h.

Effect of Strengthening Phase on Deformation Behaviour during Uniaxial Tension of Hot-rolled Dual Phase Steel

Two kinds of C-Si-Mn-Cr series tested steels were designed to obtain dual phase microstructures of ferrite （F） ＋martcnsite （M） or ferrite （F）-bainite （B） with different mechanical properties. Effects of strengthening phase on yielding and fracture behaviours during uniaxial tension of dual phase steel were discussed. Compared with hot-rolled martensite dual phase steel, ferrite-bainite dual phase steel has high ratio of yield strength to tensile strength （YS/TS） and low elongation. During necking process of uniaxial tension, microvoids of ferrite-martensite steel are generated by fracture of ferrite/martensite boundary or martensite islands with irregular shape. But ferrite matrix elongated remarkably along deformation direction, and strengthening phase also coordinated with ferrite matrix. Compatible de formation between ferrite and bainite is distinct. Ferrite-bainite dual phase steel has fine and less microvoid, and phase boundary of ferrite and bainite is beneficial for restraining generation and extending of microvoid.

High strength and deformation stability achieved in CrCoNi alloy containing deformable oxides

Hard secondary phases usually strengthen alloys at the expense of ductility.In this work,we made a dual-phase CrCoNi-O alloy containing a face centered cubic matrix and chromium oxide.On one side,the dispersed chromium oxide nano-particles impeded dislocation movement and increased the strength of the alloy.On another side,the spreading lattice distortion in CrCoNi-O high entropy solution locally relieved the severe interfacial mismatch and led to nanoscale variation of interfacial strain at the matrix-oxide interface,which facilitated dislocations’transmission from one phase to another.Consequently,unlike the strong but brittle oxide nanoparticles used before,the oxide phase here can afford significant dislocation activities during material’s plastic deformation.Comparing the mechanical properties of CrCoNi-O alloys with and without chromium oxide particles,it was found that the yield strength of the dual-phase samples was twice of the single phase CrCoNi-O alloy and strong strain hardening was obtained with ultra-high deformation stability.High density of nanotwins formed in dual-phase samples under high stress,resulting in significant strain hardening according to the well-known twinning-induced plasticity(TWIP)effect.Our results shed light on optimizing the combination of strength and plasticity of compounds by modulating the variation of interfacial strain field based on the spreading lattice distortion.

Upgrade Rolling Based on Ultra Fast Cooling Technology for C-Mn Steel

By measuring the expansion curves of a C-Mn steel at different cooling rates by using an MMS-300 thermo- mechanical simulator, continuous cooling transformation curves were obtained. The new process ＂ultra fast cooling＋ laminar cooling＂ was simulated and the effects of ultra fast cooling ending temperature on microstructure had also been investigated. The hot rolling experiment was done by adopting ＂high temperature rolling-[-forepart ultra fast cooling＂ technologies at laboratory scale. The results revealed that ultra fast cooling can delay the decrease of disloca- tion density and refine ferrite grains. Diversity control of the microstructure and phase transformation strengthening can be realized by changing the ultra fast cooling ending temperature. With the decrease of ultra fast cooling ending temperature, the strength and toughness increase, but plasticity does not decrease obviously. The new technique can improve the yield strength by over 50 MPa. Therefore, the upgrade of mechanical properties of C-Mn steel can be realized by using ＂high temperature rolling＋ ultra fast cooling＋laminar cooling＂ technique. Compared with ＂low temperature rolling with large deformation degree＂ technique, this new technology can decrease the roiling force and in- crease the production efficiency.