Effect of icosahedral phase formation on the stress corrosion cracking(SCC)behaviors of the as-cast Mg-8%Li(in wt.%)based alloys

Through exploring the stress corrosion cracking(SCC)behaviors of the as-cast Mg-8%Li and Mg-8%Li-6%Zn-1.2%Y alloys in a 0.1 M NaCl solution,it revealed that the SCC susceptibility index(I_(SCC))of the Mg-8%Li alloy was 47%,whilst the I_(SCC)of the Mg-8%Li-6%Zn-1.2%Y alloy was 68%.Surface,cross-sectional and fractography observations indicated that for the Mg-8%Li alloy,theα-Mg/β-Li interfaces acted as the preferential crack initiation sites and propagation paths during the SCC process.With regard to the Mg-8%Li-6%Zn-1.2%Y alloy,the crack initiation sites included the I-phase and the interfaces of I-phase/β-Li andα-Mg/β-Li,and the preferential propagation paths were the I-phase/β-Li andα-Mg/β-Li interfaces.Moreover,the SCC of the two alloys was concerned with hydrogen embrittlement(HE)mechanism.

Stress corrosion cracking of magnesium alloys:A review

Magnesium(Mg)alloys have been widely used in automobile,aviation,computer,and other fields due to their lightweight,high specific strength and stiffness,low pollution,and good electromagnetic shielding performance.However,the chemical stability of Mg alloys is poor,especially in the corrosive medium environment with high stress corrosion sensitivity,which causes sudden damage to structural components and restricts their application field.In recent years,owing to the increasing failure rate of engineering structures caused by stress corrosion of Mg alloys,it has become necessary to understand and pay more attention to the stress corrosion cracking(SCC)behavior of Mg alloys.In this paper,the SCC mechanisms and test methods of Mg alloys have been summarized.The recent research progress on SCC of Mg alloys has been reviewed from the aspects of alloying,preparation process,surface modification,corrosive medium,and strain rate.More importantly,future research trends in the field of SCC of Mg alloys have also been proposed.

Investigation of Stress Corrosion Cracking Initiation of 7A52 Aluminum Alloy

The stress corrosion cracking（SCC） behaviour of 7A52 aluminum alloy in air and in 3.5% NaCl solution was researched by slow strain rate test（SSRT） and SEM-EDS. The SCC susceptibility was estimated with the loss of the reduction in area. The experimental results indicate that the SCC susceptibility of 7A52 aluminum alloy in 3.5% chloride solution is the highest at strain rate of 1×10-6 s-1. The lowest one is under the condition of 1×10-5 s-1. Stress concentration and anode dissolving around Al-Fe-Mn intermetallics initiate micropores which will result in microcracks. The existence of intermetallics in the microstructure may play an important role in understanding the SCC initiation mechanisms of 7A52 aluminum alloy.

Effect of hydrogen on the stress corrosion cracking behavior of X80 pipeline steel in Ku'erle soil simulated solution

Hydrogen was a key factor resulting in stress corrosion cracking （SCC） of X80 pipeline steel in Ku＇erle soil simulated solution. In this article, the effect of hydrogen on the SCC susceptibility of X80 steel was investigated further by slow strain rate tensile test, the surface fractures were observed using scanning electron microscopy （SEM）, and the fracture mechanism of SCC was discussed. The results indicate that hydrogen increases the SCC susceptibility. The SEM micrographs of hydrogen precharged samples presents a brittle quasi-cleavage feature, and pits facilitate the transgranular crack initiation. In the electrochemical impedance spectroscopy （EIS） measurement, the decreased polarization resistance and the pitting resistance of samples with hydrogen indicate that hydrogen increases the dissolution rate and deteriorates the pitting corrosion resistance. The potentiodynamic polarization curves present that hydrogen also accelerates the dissolution rate of the crack tip.

Effect of pre-deformation on the stress corrosion cracking susceptibility of aluminum alloy 2519

The effects of pre-deformation and strain rate on the stress corrosion cracking （SCC） behavior of aluminum alloy 2519 in air and in 3.5% NaCI water solution were investigated by means of slow strain rate tension （SSRT）, scanning electron microscopy （SEM）, and transmission electron microscopy （TEM）. The results indicate that the alloy is susceptible to SCC in 3.5% NaCI water solution and not in air. At the same pre-deformation, the alloy is more susceptible to SCC at 1.33 × 10^-5 s^-1 than at 6.66 × 10^-5 s^-1. Moreover, it is more susceptible to SCC at free pre-deformation than at 10% pre-deformation at the same strain rate. The number of 0 precipitated along the grain boundaries is reduced and distributed discontinuously, at the same time, the precipitate-free zones （PFZ） become narrow and the susceptibility to stress corrosion cracking is reduced after 10% pre-deformation.

Stress Corrosion Cracking of Nitrogen-containing Stainless Steel 316LN in High Temperature Water Environments

Stress corrosion cracking （SCC） of stainless steels and Ni-based alloys in high temperature water coolant is one of the key problems affecting the safe operation of nuclear power plants （NPPs）. The nitrogen-added stainless steel is a kind of possible candidate materials for mitigating SCC since reducing the carbon content and adding nitrogen to offset the loss in strength caused by the decrease in carbon content can mitigate the problem of sensitization. However, the reports of SCC of nitrogen-added stainless steels in high temperature water are few available. The effects of applied potential and sensitization treatment on the SCC of a newly developed nitrogen-containing stainless steel （SS） 316LN in high temperature water doped with chloride at 250 ℃ were studied by using slow strain rate tests （SSRTs）. The SSRT results are compared with our data previously published for 316 SS without nitrogen and 304NG SS with nitrogen, and the possible mechanism affecting the SCC behaviors of the studied steels is also discussed based on SSRT and microstucture analysis results. The susceptibility to cracking of 316LN SS normally increases with increasing potential. The susceptibility to SCC of 316LN SS was less than that of 316 SS and 304NG SS. Sensitization treatment at 700℃ for 30 h showed little effect on the S CC of 316LN S S and significant effect on the S CC of 316 S S. The predominant cracking mode for the 316LN S S in both annealed state and the state after the sensitization treatment was transgranular. The presented conditions of mitigating stress corrosion cracking are some useful information for the safe use of 316LN SS in NPPs.

Effect of deteriorated microstructures on stress corrosion cracking of X70 pipeline steel in acidic soil environment

In order to investigate stress corrosion cracking （SCC） of X70 pipeline steel and its weld joint area in acidic soil environ- ment in China, two simulating methods were used： one was to obtain bad microstructures in heat affected zone by annealing at 1300 ℃ for 10 min and then, quenching in water; the other was to get different simulating solutions of acidic soil in Yingtan in south- east China. The SCC susceptibilities of X70 pipeline steel before and after quenching in the simulating solutions were analyzed using slow stain rate test （SSRT） and potentiodynamic polarization technique to investigate the SCC electrochemical mechanism of different microstructures further. The results show that SCC appears in the original microstructure and the quenched microstructure as the polarization potential decreases. Hydrogen revolution accelerates SCC of the two tested materials within the range of-850 mV to -1200 mV vs. SCE. Microstructural hardening and grain coarsening also increase SCC. The SCC mechanisms are different, anodic dissolution is the key of causing SCC as the polarization potential is higher than the null current potential, and hydrogen embrittlement will play a more important role to SCC as the polarization potential lower than the null current potential.

Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking

The hydrogen permeation behavior and stress corrosion cracking （SCC） susceptibility of precharged 7075-T6 A1 alloy were inves- tigated in this paper. Devanthan-Stachurski （D-S） cell tests were used to measure the apparent hydrogen diffusivity and hydrogen permeation current density of specimens immersed in 3.5wt% NaCl solution. Electrochemical experiment results show that the SCC susceptibility is low during anodic polarization. Both corrosion pits and hydrogen-induced cracking are evident in scanning electron microscope images after the specimens have been charging for 24 h.

Stress corrosion cracking of X80 pipeline steel exposed to high pH solutions with different concentrations of bicarbonate

Susceptibilities to stress corrosion cracking （SCC） of X80 pipeline steel in high pH solutions with various concentrations of HC03 at a passive potential of-0.2 V vs. SCE were investigated by slow strain rate tensile （SSRT） test. The SCC mechanism and the effect of HC03 were discussed with the aid of electrochemical techniques. It is indicated that X80 steel shows enhunced susceptibility to SCC with the concentration of HCO3 increasing from 0.15 to 1.00 mol/L, and the susceptibility can be evaluated in terms of current density at -0.2 V vs. SCE. The SCC behavior is controlled by the dissolution-based mechanism in these circumstances. Increasing the concentration of HCO3 not only increases the risk of rupture of passive films but also promotes the anodic dissolution of crack tips. Besides, little susceptibility to SCC is found in dilute solution containing 0.05 mol/L HCO3 for X80 steel. This can be attributed to the inhibited repassivation of passive films, manifesting as a more intensive dissolution in the non-crack tip areas than at the crack tips.

Stress corrosion cracking susceptibility of a high strength Mg-7%Gd-5%Y-1%Nd-0.5%Zr alloy

Through performing the tensile tests with different strain rates in 3.5 wt.%NaCl solution,the stress corrosion cracking(SCC)behavior and the effect of strain rate on the SCC susceptibility of an extruded Mg-7%Gd-5%Y-1%Nd-0.5%Zr(EW75)alloy have been investigated.Results demonstrate that the alloy is susceptible to SCC when the strain rate is lower than 5×10^(−6) s^(−1).At the strain rate of 1×10^(−6) s^(−1),the SCC susceptibility index(I_(SCC))is 0.96 and the elongation-to-failure(ε_(f))is only 0.11%.Fractography indicates that the brittle quasi-cleavage feature is very obvious and become more pronounced with decreasing the strain rate.Further analysis confirms that the cracking mode is predominantly transgranular,but the partial intergranular cracking at some localized area can also occur.Meanwhile,it seems that the crack propagation path is unrelated to the existing phase particles.

EFFECT OF POTENTIAL ON INTERACTION BETWEEN STRESS CORROSION CRACKING AND CORROSION FATIGUE OF AUSTENITIC STAINLESS STEEL IN BOILING 42% MgCl_2 SOLUTION

The environment-sensitive fracture behaviour of 0Cr18Ni9Ti austenitic stainless steel in boiling 42% MgCl_2 under the specific load of low frequency and high mean stress was inves- tigated from the relations and differences of crack growth rates and fractographs between stress corrosion fatigue and stress corrosion cracking.The interaction between stress corro- sion cracking and corrosion fatigue was also studied from fracture characteristics with empha- sis on the effects of applied potential on the interaction.

An investigation on the performance of stress corrosion cracking in aluminum-copper alloy welded joint

With the resistance to stress corrosion of the base metal as a reference, the contrast result of stress corrosion cracking （ SCC） susceptibility of aluminum-copper alloy 2219 and 2014 welded joints under different welding processes （ VP-TIG welding, HF-TIG hybrid welding, laser-TIG hybrid welding and laser HF-TIG hybrid welding） is obtained via the slow strain rate testing （ SSRT） , scanning electron microscope （ SEM） and microstructure observation auxiliary technologies. Test results show that the joints of aluminum alloy 2219, welded by hybrid welding processes, have superior resistance to stress corrosion compared to those welded by the VP-TIG welding process in varying degrees, especially, the joint welded by the laser HF-TIG hybrid welding process, where the resistance to stress corrosion is almost the same as that of the base material. However, the HF or laser hybrid welding effect is not significant under the same welding conditions for welded joints of aluminum alloy 2014.

Behavior of Stress Corrosion Cracking in a Magnesium Alloy

Slow strain rate testing （SSRT） was employed to study the stress corrosion cracking （SCC） behavior of ZE41 magnesium alloy in 0.01 M NaCl solution. Smooth tensile specimens with different thicknesses were strained dynamically in both longitudinal and transverse direction under permanent immersions at a strain rate of 10-6 s-1. It is found that ZE41 magnesium alloy is susceptible to SCC in 0.01 M NaCl solution. The SCC susceptibility of the thinner specimen is lower than that of the thicker specimen. Also, the longitudinal specimens are slightly more susceptible to SCC than the transverse specimens. The SCC mechanism of magnesium alloy is attributed to the combination of anodic dissolution with hydrogen embrittlement.

Effect of cathodic potential on stress corrosion cracking behavior of 21Cr2NiMo steel in simulated seawater

This study aims at providing systematically insights to clarify the impact of cathodic polarization on the stress corrosion cracking(SCC)behavior of 21 Cr2 NiMo steel.Slow-strain-rate tensile tests demonstrated that 21 Cr2 NiMo steel is highly sensitive to hydrogen embrittlement at strong cathodic polarization.The lowest SCC susceptibility occurred at-775 mV vs.SCE,whereas the SCC susceptibility was remarkably higher at potentials below-950 mV vs.SCE.Scanning electron microscopy(SEM)and electron backscattered diffraction(EBSD)revealed that the cathodic potential decline caused a transition from transgranular to intergranular mode in the fracture path.The intergranular mode transformed from bainite boundaries separation to prior austenitic grain boundaries separation under stronger cathodic polarization.Furthermore,corrosion pits promoted the nucleation of SCC cracks.In conclusion,with the decrease in the applied potential,the SCC mechanism transformed from the combination of hydrogen embrittlement and anodic dissolution to typical hydrogen embrittlement.

Localized Corrosion and Stress Corrosion Cracking Behavior of AA7003 in a 3.5 wt% NaCl Aqueous Solution

The microstructure,localized corrosion (LC) and stress corrosion cracking (SCC) behavior of 7003 aluminum alloy (AA7003) under various aging treatments (peak aging (PA),double peak aging (DPA),regression and re-aging (RRA)) were investigated by means of transmission electron microscope (TEM),scanning electron microscopy (SEM),electrochemical impendence spectroscopy (EIS) and slow strain rate tensile test.The results of TEM showed a discontinuous distribution of grain boundary precipitates of AA7003 under DPA and RRA treatments,which is beneficial for increasing the resistance of LC and SCC.Meanwhile,LC was found initiating firstly on intermetallics which caused the dissolution of surrounding matrix,then pitting holes were formed and developed into matrix.In addition,the SCC process of AA7003 could be divided into two stages,i e,initial pre-cracking and breeding cracking.The EIS analysis,cross-section morphologies and fracture surfaces of specimens indicated that DPA and RRA treatments significantly decreased the crack growth rate during breeding cracking stage,especially for RRA treatment.

Effects of applied potential on the stress corrosion cracking behavior of 7003 aluminum alloy in acid and alkaline chloride solutions

Potentiodynamic polarization tests and slow strain rate test（SSRT） in combination with fracture morphology observations were conducted to investigate the stress corrosion cracking（SCC） behavior of 7003 aluminum alloy（AA7003） in acid and alkaline chloride solutions under various applied potentials（Ea）. The results show that AA7003 is to a certain extent susceptible to SCC via anodic dissolution（AD） at open-circuit potential（OCP） and is highly susceptible to hydrogen embrittlement（HE） at high negative Ea in the solutions with p H levels of 4 and 11. The susceptibility increases with negative shift in the potential when Ea is less than-1000 m V vs. SCE. However, the susceptibility distinctly decreases because of the inhibition of AD when Ea is equal to-1000 m V vs. SCE. In addition, the SCC susceptibility of AA7003 in the acid chloride solution is higher than that in the alkaline solution at each potential. Moreover, the effect of hydrogen on SCC increases with increasing hydrogen ion concentration.

Stress Corrosion Cracking and Passive Film-inducedTensile Stress in α-Ti

α-Ti foil with a protective layer formed on one side was deflected during corrosion in a methanol solution containing 0.6 mol/L KCI and then a tensile stress was generated at or near the metal passive film interface. The in situ TEM observation showed that corrosion process could facil- itate dislocation emission and motion. Adding 10% H2O into the methanol solution decreased the passive film-induced stress from 320 MPa to zero, and the susceptibility to SCC measured in slow strain rate tests decreased correspondingly from 98% to zero.

Relativity between corrosion-induced stress and stress corrosion cracking of brass in an ammonia solution

The susceptibility to stress corrosion cracking (SCC) of brass in an ammoniasolution with various pH values or under various applied potentials was measured at slow strain ratetests. The additive stress in the same solution was measured using two methods. The resultsindicate that the variation of the susceptibility to SCC with pH value or with potential is in anexcellent agreement with the corrosion (passive film or dezincification layer)-induced stress. WhenpH >= 7, the corrosion-induced tensile stress and the susceptibility to SCC have maximum values andhardly change with increasing the pH value. However, when pH <7, both the corrosion-induced tensilestress and the susceptibility to SCC reduce rapidly with decreasing the pH value. Both thecorrosion-induced tensile stress and the susceptibility to SCC have maximum values at theopen-circuit potential, decrease slightly under the anodic polarization, and reduce gradually tozero under the cathodic polarization.

Effect of Retrogression and Reaging on Stress Corrosion Cracking of Spray Formed Al Alloy

Stress corrosion cracking (SCC) resistance of a spray formed Al-Zn-Mg-Cu alloy underwent retrogression and reaging (RRA) was studied by slow strain rate tests in dry air and 3.5 wt% NaCl solution. The results showed that after RRA treatment, interrupted η phases at grain boundaries and slightly wide precipitate free zones could decrease SCC susceptibility of the alloy. Lots of reticular dislocations appeared in deformation process could prevent hydrogen induced cracking, and then SCC. Abundance transgranular dispersive η' phases separated out again promoted tensile strength to 759.4 MPa. The fracture ways of the specimens were dimple fracture in dry air and sub-cleavage fracture in 3.5% NaCl solution.

Evaluation of Stress Corrosion Cracking Damage to an API 5L X52 Pipeline Transporting Ammonia: A Case Study

The high number of leak events that took place in recent years at a 25.4 cm (10”)&Oslash;pipeline transporting anhydrous liquid ammonia, located in the Southeast of Mexico, was the main reason to carry out a number of field studies and laboratory tests that helped establish not only the failure causes but also mitigation and control solutions. The performed activities included direct evaluation at failure sites, total repair programs, metallographic studies and pipeline flexibility analyses. The obtained results were useful to conclude that the failures obeyed a cracking mechanism by Stress Corrosion Cracking (SCC) which was caused by the combined effect of different factors: high stress resistance, high hardness of the base metal with a microstructure prone to brittleness and residual strains originated during the pipeline construction. From the operative, logistic and financial standpoints, it is not feasible to release the stress of approximately 22 km of pipeline. Therefore, the only viable solution is to install a new pipeline with suitable fabrication, construction and installation specifications aimed at preventing the SCC phenomenon.