The solid solutions of In^(3+) doped M-type strontium hexaferrites were produced using a conventional solid-state reaction method,and Rietveld analysis of the neutron diffraction patterns was conducted.In^(3+) cations...The solid solutions of In^(3+) doped M-type strontium hexaferrites were produced using a conventional solid-state reaction method,and Rietveld analysis of the neutron diffraction patterns was conducted.In^(3+) cations occupy octahedral (4f_(Ⅵ)and 12 k) and tetrahedral (4f_(Ⅳ)) positions (SG=P6_(3)/mmc(No.194)).The average particle size is 837–650 nm.Curie tempearature (T_(C)) of the compounds monotonically decreased down to~520 K with increasing x.A frustrated magnetic state was detected from ZFC and FC magnetizations.saturation magnetization (M_(s)) and effective magnetocrystalline anisotropy coefficient (k_(eff)) were determined using the law of approach to saturation.A real permittivity (ε″) maximum of~3.3 at~45.5 GHz and an imaginary permittivity (ε′) of~1.6 at~42.3 GHz were observed for x=0.1.A real permeability (μ′) maximum of~1.5 at~36.2 GHz was observed for x=0.Aμ″imaginary permeability maximum of~0.8 at~38.3 GHz was observed for x=0.1.The interpretation of the results is based on the type of dielectric polarization and the natural ferromagnetic resonance features.展开更多
High temperature steam(H_(2)O)electrolysis via a solid oxide electrolysis cell is an efficient way to produce hydrogen(H_(2))because of its high energy conversion efficiency as well as simple and green process,especia...High temperature steam(H_(2)O)electrolysis via a solid oxide electrolysis cell is an efficient way to produce hydrogen(H_(2))because of its high energy conversion efficiency as well as simple and green process,especially when the electrolysis process is combined with integrated gasification fuel cell technology or derived by renewable energy.However,about 60%-70%of the electricity input is consumed to overcome the large oxygen potential gradient but not for electrolysis to split H_(2)O to produce H_(2)due to the addition of safe gas such as H_(2)in the fuel electrode.In this work,Sr_(2)Fe_(1.5)Mo_(0.5)O_(6)-δ-Ce_(0.8)Sm_(0.2)O_(1.95)(SFM-SDC)ceramic composite material has been developed as fuel electrode to avoid the use of safe gas,and the open circuit voltage(OCV)has been effectively lowered from 1030 to 78 mV when the feeding gas in the fuel electrode is shifted from 3%H_(2)O-97%H_(2)to 3%H_(2)O-97%N_(2),reasonably resulting in a significantly increased electrolysis efficiency.In addition,it is also demonstrated that the electrolysis current density is greatly enhanced by increasing the humidity in the fuel electrode and the working temperature.A considerable electrolysis current density of−0.54 A/cm^(2)is obtained at 800°C and 0.4 V for the symmetrical electrolyzer by exposing SFM-SDC fuel electrode to 23%H_(2)O-77%N_(2),and durability test at 800°C for 35 h demonstrates a relatively stable electrochemical performance for steam electrolysis under the same operation condition without safe gas and a constant electrolysis current density of−0.060 A/cm2.Our findings achieved in this work indicate that SFM-SDC is a highly promising fuel electrode for steam electrolysis.展开更多
基金conducted with financial support from the Russian Science Foundation (Agreement No. 19-19-00694 of 06 May 2019)。
文摘The solid solutions of In^(3+) doped M-type strontium hexaferrites were produced using a conventional solid-state reaction method,and Rietveld analysis of the neutron diffraction patterns was conducted.In^(3+) cations occupy octahedral (4f_(Ⅵ)and 12 k) and tetrahedral (4f_(Ⅳ)) positions (SG=P6_(3)/mmc(No.194)).The average particle size is 837–650 nm.Curie tempearature (T_(C)) of the compounds monotonically decreased down to~520 K with increasing x.A frustrated magnetic state was detected from ZFC and FC magnetizations.saturation magnetization (M_(s)) and effective magnetocrystalline anisotropy coefficient (k_(eff)) were determined using the law of approach to saturation.A real permittivity (ε″) maximum of~3.3 at~45.5 GHz and an imaginary permittivity (ε′) of~1.6 at~42.3 GHz were observed for x=0.1.A real permeability (μ′) maximum of~1.5 at~36.2 GHz was observed for x=0.Aμ″imaginary permeability maximum of~0.8 at~38.3 GHz was observed for x=0.1.The interpretation of the results is based on the type of dielectric polarization and the natural ferromagnetic resonance features.
基金This work was supported by National Natural Science Foundation of China(51602228,51502207).
文摘High temperature steam(H_(2)O)electrolysis via a solid oxide electrolysis cell is an efficient way to produce hydrogen(H_(2))because of its high energy conversion efficiency as well as simple and green process,especially when the electrolysis process is combined with integrated gasification fuel cell technology or derived by renewable energy.However,about 60%-70%of the electricity input is consumed to overcome the large oxygen potential gradient but not for electrolysis to split H_(2)O to produce H_(2)due to the addition of safe gas such as H_(2)in the fuel electrode.In this work,Sr_(2)Fe_(1.5)Mo_(0.5)O_(6)-δ-Ce_(0.8)Sm_(0.2)O_(1.95)(SFM-SDC)ceramic composite material has been developed as fuel electrode to avoid the use of safe gas,and the open circuit voltage(OCV)has been effectively lowered from 1030 to 78 mV when the feeding gas in the fuel electrode is shifted from 3%H_(2)O-97%H_(2)to 3%H_(2)O-97%N_(2),reasonably resulting in a significantly increased electrolysis efficiency.In addition,it is also demonstrated that the electrolysis current density is greatly enhanced by increasing the humidity in the fuel electrode and the working temperature.A considerable electrolysis current density of−0.54 A/cm^(2)is obtained at 800°C and 0.4 V for the symmetrical electrolyzer by exposing SFM-SDC fuel electrode to 23%H_(2)O-77%N_(2),and durability test at 800°C for 35 h demonstrates a relatively stable electrochemical performance for steam electrolysis under the same operation condition without safe gas and a constant electrolysis current density of−0.060 A/cm2.Our findings achieved in this work indicate that SFM-SDC is a highly promising fuel electrode for steam electrolysis.