The γ＇-Fe4N films on Cu underlayers are deposited on the glass and Si substrates by dc magnetron reactive sputtering. The effects of Cu underlayer on the structure, morphology and magnetic properties of the γ＇-Fe4...The γ＇-Fe4N films on Cu underlayers are deposited on the glass and Si substrates by dc magnetron reactive sputtering. The effects of Cu underlayer on the structure, morphology and magnetic properties of the γ＇-Fe4N films are studied. The single-phase γ＇-Fe4N films with Cu underlayers on the glass substrate are obtained, while the mixture of Fe and γ＇-Fe4N is observed on the Si substrate. In comparison with the films without Cu underlayers, the grains of the films with Cu underlayers exhibit a non-uniform size distribution and give rise to a rougher surface. The magnetic measurements indicate that the γ＇-Fe4N films show a good soft ferromagnetic behavior. The enhanced coercivity in the films with Cu underlayers is observed due to the deterioration of the crystallographic structure as well as the rougher surface.展开更多
The structure and magnetic properties of Fe76.5Si13.5B9Cu1 alloys with a nanocrystalline (NC) bcc Fe(Si) phase trom about 23 to 46 nm in diameter, which were first formed into amorphous ribbons and then annealed at va...The structure and magnetic properties of Fe76.5Si13.5B9Cu1 alloys with a nanocrystalline (NC) bcc Fe(Si) phase trom about 23 to 46 nm in diameter, which were first formed into amorphous ribbons and then annealed at various temperatures between 703 and 773 K, have been investigated. At annealing temperatures from 703 to 748 K, the single NC bcc(Si) phase is obtained in the crystallized alloys. The grain size and the Si-content in the NC bcc Fe(Si) phase for the alloys annealed at different temperatures are presented. The soft magnetic properties and the saturation magnetostriction for the alloys with the NC bcc Fe(Si) phase are also measured. The results show that, the saturation magnetizotion and the permeability are improved for the alloys with only the NC bcc Fe(Si) phase and become better with decreasing of the NC bcc phase size, and the saturation magnetostriction declines for the alloys with increasing Si-content in the NC bcc Fe(Si) phase.展开更多
基金Supported by the National Natural Science Foundation of China under Grant Nos 61434002,61204097,11274214 and 51301099the National High-Tech Research and Development Program of China under Grant No 2014AA032904+1 种基金the Chang Jiang Scholars and Innovative Team Development Plan by the Ministry of Education under Grant No IRT1156the Specialized Research Fund for the Doctoral Program of Higher Education of China under Grant Nos 20121404130001 and 20121404120003
文摘The γ＇-Fe4N films on Cu underlayers are deposited on the glass and Si substrates by dc magnetron reactive sputtering. The effects of Cu underlayer on the structure, morphology and magnetic properties of the γ＇-Fe4N films are studied. The single-phase γ＇-Fe4N films with Cu underlayers on the glass substrate are obtained, while the mixture of Fe and γ＇-Fe4N is observed on the Si substrate. In comparison with the films without Cu underlayers, the grains of the films with Cu underlayers exhibit a non-uniform size distribution and give rise to a rougher surface. The magnetic measurements indicate that the γ＇-Fe4N films show a good soft ferromagnetic behavior. The enhanced coercivity in the films with Cu underlayers is observed due to the deterioration of the crystallographic structure as well as the rougher surface.
文摘The structure and magnetic properties of Fe76.5Si13.5B9Cu1 alloys with a nanocrystalline (NC) bcc Fe(Si) phase trom about 23 to 46 nm in diameter, which were first formed into amorphous ribbons and then annealed at various temperatures between 703 and 773 K, have been investigated. At annealing temperatures from 703 to 748 K, the single NC bcc(Si) phase is obtained in the crystallized alloys. The grain size and the Si-content in the NC bcc Fe(Si) phase for the alloys annealed at different temperatures are presented. The soft magnetic properties and the saturation magnetostriction for the alloys with the NC bcc Fe(Si) phase are also measured. The results show that, the saturation magnetizotion and the permeability are improved for the alloys with only the NC bcc Fe(Si) phase and become better with decreasing of the NC bcc phase size, and the saturation magnetostriction declines for the alloys with increasing Si-content in the NC bcc Fe(Si) phase.